CN106498712A - 电磁波吸收网格材料及其制备方法 - Google Patents
电磁波吸收网格材料及其制备方法 Download PDFInfo
- Publication number
- CN106498712A CN106498712A CN201611103081.3A CN201611103081A CN106498712A CN 106498712 A CN106498712 A CN 106498712A CN 201611103081 A CN201611103081 A CN 201611103081A CN 106498712 A CN106498712 A CN 106498712A
- Authority
- CN
- China
- Prior art keywords
- grid material
- electro
- wave absorption
- magnetic wave
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明是关于一种电磁波吸收网格材料及其制备方法，其制备方法包括：1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；2)将基体网格材料浸渍于所述吸波浸渍胶液，取出干燥，得到电磁波吸收网格材料；其中，吸波浸渍胶液的组分，以重量百分比计，包括：胶黏剂：5‑40％；吸波剂：0.1‑50％；溶剂：40‑90％。本发明电磁波吸收网格材料制备方法简单，具有更宽的吸波带宽及更强的吸波效能。
Description
技术领域
本发明涉及一种电磁波吸收材料领域，特别是涉及一种电磁波吸收网格材料及其制备方法。
背景技术
随着科学技术的快速发展，以及电子、电气设备越来越广泛的应用于通信、工业、科研、医疗以及广播等诸多领域，人类的居住环境和工作环境几乎被电子、电器及通讯设备所包围，这些设备工作时产生的电磁辐射导致空间电磁环境日益恶化。电磁辐射污染已经成为一种人类无法感知却存在巨大潜在危害的新型污染。电磁波吸收建筑材料是可以通过能量转化或干涉作用等将电磁能转化为热能的一种功能型建材，可以合理有效地控制建筑空间的电磁辐射背景强度，降低电磁辐射的危害。针对日益严重的电磁污染问题，开发具有频带宽、吸收强、厚度薄的电磁波吸收建筑材料将成为吸波建材研究的主要方向。
目前对吸波建材的研究主要是通过吸波建材的结构设计来提高吸波性能，包括设计层板结构、蜂窝结构、角锥结构以及填充空心多孔材料改变微观孔隙度等。但是通过结构设计制备的吸波建材大多存在厚度大、吸波性能差的问题，难以在不同基体的建筑材料中使用。
发明内容
本发明的主要目的在于，提供一种新型的电磁波吸收网格材料及其制备方法，所要解决的技术问题是使其制备方法简单，吸波性能好，吸波频带宽，从而更加适于实用。
本发明的目的及解决其技术问题是采用以下技术方案来实现的。依据本发明提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将基体网格材料浸渍于所述吸波浸渍胶液，取出干燥，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：5-40％；
吸波剂：0.1-50％；
溶剂：40-90％。
本发明的目的及解决其技术问题还可采用以下技术措施进一步实现。
优选的，前述的电磁波吸收网格材料的制备方法，其中所述的胶黏剂为水溶性胶黏剂。
优选的，前述的电磁波吸收网格材料的制备方法，其中所述的吸波剂为石墨、炭黑、纳米二氧化锰、铁氧体粉、羰基铁粉和纳米金属粉中的至少一种。
优选的，前述的电磁波吸收网格材料的制备方法，其中所述的溶剂为水、醇类或芳香烃类溶剂。
优选的，前述的电磁波吸收网格材料的制备方法，其中所述的基体网格材料为玻璃纤维网格材料或玄武岩纤维网格材料。
优选的，前述的电磁波吸收网格材料的制备方法，其中所述的基体网格材料的网孔形状为圆形或多边形。
优选的，前述的电磁波吸收网格材料的制备方法，其中所述的基体网格材料的网孔的面积为2-324mm2。
本发明的目的及解决其技术问题还采用以下的技术方案来实现。依据本发明提出的一种电磁波吸收网格材料，由上述的方法制备而得。
本发明的目的及解决其技术问题还可采用以下技术措施进一步实现。
优选的，前述的电磁波吸收网格材料，其中所述的电磁波吸收网格材料的最小反射率为-26～-16.7dB。
借由上述技术方案，本发明电磁波吸收网格材料及其制备方法至少具有下列优点：
1)本发明通过浸渍法制备电磁波吸收网格材料，制备方法简单，原料价格低廉；
2)本发明采用玻璃纤维网格材料或玄武岩纤维网格材料，纤维表面进行介电材料包覆后会形成介电损耗层，不易形成发达的导电网络影响电磁波入射；此外，介电层与纤维形成的谐振腔会对电磁波产生谐振效应，同时电磁波会在各个纤维表面介电层之间发生多次反射，实现吸波性能的提升，本发明制备的电磁波吸收网格材料能够实现在2-18GHz频率范围内反射率低于-5dB，最小反射率可达到-27dB；
3)本发明的电磁波吸收网格材料能够应用于建筑施工或建筑材料，可以降低建筑材料厚度，并实现对电磁波的有效吸收。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，并可依照说明书的内容予以实施，以下以本发明的较佳实施例详细说明如后。
具体实施方式
为更进一步阐述本发明为达成预定发明目的所采取的技术手段及功效,以下结合较佳实施例，对依据本发明提出的电磁波吸收网格材料及其制备方法其具体实施方式、结构、特征及其功效，详细说明如后。在下述说明中，不同的“一实施例”或“实施例”指的不一定是同一实施例。此外，一或多个实施例中的特定特征、结构、或特点可由任何合适形式组合。
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将基体网格材料浸渍于所述吸波浸渍胶液一次或多次浸渍，使其表面涂覆一层吸波浸渍胶液，取出干燥，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：5-40％；
吸波剂：0.1-50％；
溶剂：40-90％。
其中，胶黏剂为水溶性固态、液态或溶剂型胶黏剂，包括聚乙烯醇、纯丙乳液、苯丙乳液、聚乙烯醇等。
吸波剂为石墨、炭黑、纳米二氧化锰、铁氧体粉、羰基铁粉和纳米金属粉中的至少一种。
溶剂为水、醇类或芳香烃类溶剂。
基体网格材料为玻璃纤维网格材料或玄武岩纤维网格材料，网孔形状为圆形或多边形，网孔的面积为2-324mm2，孔径为2-18mm。本发明采用玻璃纤维网格材料或玄武岩纤维网格材料，纤维表面进行介电材料包覆后会形成介电损耗层，不易形成发达的导电网络影响电磁波入射；此外，介电层与纤维形成的谐振腔会对电磁波产生谐振效应，同时电磁波会在各个纤维表面介电层之间发生多次反射，实现吸波性能的提升。
本发明的基体材料还可以选用玻璃纤维三维织物，得到的电磁波吸收网格材料的最小反射率可达到-26dB，在2-18GHz频率范围内反射率低于-5dB。
本发明的另一实施例提出一种电磁波吸收网格材料，由上述的方法制备而得，最小反射率为-26～-16.7dB。
实施例1
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玻璃纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复两次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：9.9％，为聚乙烯醇；
吸波剂：0.1％，为炭黑；
溶剂：90％，为水。
玻璃纤维网格材料的网格的网孔形状为正方形，网孔边长为18mm，面积为324mm2。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-17.5dB，反射率低于-5dB频率范围为2-5GHz、9-18GHz。
实施例2
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玄武岩纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复三次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：40％，为纯丙乳液；
吸波剂：20％，为5％石墨和15％羰基铁粉；
溶剂：40％，为甲醇。
玄武岩纤维网格材料的网格的网孔形状为正方形，网孔边长为18mm，面积为324mm2。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-18.6dB，反射率低于-5dB频率范围为3-6GHz、8-18GHz。
实施例3
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玻璃纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复两次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：40％，为苯丙乳液；
吸波剂：15％，为2％炭黑和13％铁氧体粉；
溶剂：45％，为水。
玻璃纤维网格材料的网格的网孔形状为六边形，网孔边长为8mm。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-27dB，反射率低于-5dB频率范围为2-7GHz、8-18GHz。
实施例4
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玻璃纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复四次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：8％，为聚乙烯醇；
吸波剂：20％，为3％炭黑和17％纳米二氧化锰；
溶剂：72％，为水。
玻璃纤维网格材料的网格的网孔形状为正方形，网孔边长为10mm。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-25.5dB，反射率低于-5dB频率范围为2-18GHz。
实施例5
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玻璃纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复一次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：5％，为纯丙乳液；
吸波剂：50％，为20％炭黑和30％纳米金属粉；
溶剂：45％，为水。
玻璃纤维网格材料的网格的网孔形状为正方形，网孔边长为6mm。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-19.8dB，反射率低于-5dB频率范围为2-4GHz、6-18GHz。
实施例6
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玻璃纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复三次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：60％，为聚乙烯醇；
吸波剂：30％，为20％石墨和30％纳米金属粉；
溶剂：45％，为水。
玻璃纤维网格材料的网格的网孔形状为正方形，网孔边长为12mm。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-16.7dB，反射率低于-5dB频率范围为3-6GHz、8-18GHz。
实施例7
本发明的一个实施例提出的一种电磁波吸收网格材料的制备方法，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将玻璃纤维网格材料浸渍于所述吸波浸渍胶液，使其表面涂覆一层吸波浸渍胶液，取出干燥，上述过程重复三次，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：8％，为聚乙烯醇；
吸波剂：20％，为3％炭黑和17％纳米二氧化锰；
溶剂：72％，为水。
玻璃纤维网格材料的网格的网孔形状为圆形，网孔直径为12mm。
本发明的一个实施例提出的一种电磁波吸收网格材料，由上述的方法制备而得。采用弓形反射法测试电磁波吸收网格材料的电磁波吸收性能，最小反射率为-26dB，反射率低于-5dB频率范围为2-18GHz。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。
Claims (9)
1.一种电磁波吸收网格材料的制备方法，其特征在于，其包括：
1)将胶黏剂、吸波剂均匀分散在溶剂中，得到吸波浸渍胶液；
2)将基体网格材料浸渍于所述吸波浸渍胶液，取出干燥，得到电磁波吸收网格材料；
其中，吸波浸渍胶液的组分，以重量百分比计，包括：
胶黏剂：5-40％；
吸波剂：0.1-50％；
溶剂：40-90％。
2.根据权利要求1所述的电磁波吸收网格材料的制备方法，其特征在于，所述的胶黏剂为水溶性胶黏剂。
3.根据权利要求1所述的电磁波吸收网格材料的制备方法，其特征在于，所述的吸波剂为石墨、炭黑、纳米二氧化锰、铁氧体粉、羰基铁粉和纳米金属粉中的至少一种。
4.根据权利要求1所述的电磁波吸收网格材料的制备方法，其特征在于，所述的溶剂为水、醇类或芳香烃类溶剂。
5.根据权利要求1所述的电磁波吸收网格材料的制备方法，其特征在于，所述的基体网格材料为玻璃纤维网格材料或玄武岩纤维网格材料。
6.根据权利要求5所述的电磁波吸收网格材料的制备方法，其特征在于，所述的基体网格材料的网孔形状为圆形或多边形。
7.根据权利要求5所述的电磁波吸收网格材料的制备方法，其特征在于，所述的基体网格材料的网孔的面积为2-324mm2。
8.一种电磁波吸收网格材料，其特征在于，由权利要求1-7任一项所述的方法制备而得。
9.根据权利要求8所述的电磁波吸收网格材料，其特征在于，所述的电磁波吸收网格材料的最小反射率为-26～-16.7dB。