CN106479193A - A kind of preparation method of metal pan leakage-stopping composition - Google Patents
A kind of preparation method of metal pan leakage-stopping composition Download PDFInfo
- Publication number
- CN106479193A CN106479193A CN201610891996.9A CN201610891996A CN106479193A CN 106479193 A CN106479193 A CN 106479193A CN 201610891996 A CN201610891996 A CN 201610891996A CN 106479193 A CN106479193 A CN 106479193A
- Authority
- CN
- China
- Prior art keywords
- pot
- hole
- powder
- compositionss
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to compositionss preparing technical field, it is related to a kind of preparation method of the metal pan leakage-stopping composition blocking occasion for metal pan leak, weighs Semen sojae atricolor powder, clay, Pulvis Talci, coal dust, avian albumen and water；Solid material was milled into respectively the powder of 200 mesh sieves；Above-mentioned each mixed raw material is obtained compositionss blending stock；Compositionss blending stock is filled up and passes a pot hole, then will be smooth for the compositionss blending stock passing outside pot hole compacting；At the pot hole of closure inside pot, cover type smears vegetable oil, and then dry pot bakes；Smear one layer of vegetable oil after being polished in the pot Dong Chu blocking inside pot surface with sand paper again, realize the leak stopping in metal pan hole；Its primary raw material is：Semen sojae atricolor powder, clay, Pulvis Talci, coal dust, avian albumen, water and vegetable oil；The fineness of powder of each raw material is respectively less than 200 mesh；Formula is simple, reasonable mixture ratio, and raw material is easy to get, preparation process is simple, strong adaptability, repairs speed soon, applied environment is friendly.
Description
Technical field：
The invention belongs to compositionss preparing technical field, it is related to a kind of metal pan blocking occasion for metal pan leak and blocks up
The preparation method of leakage compositionss, after compositionss are in harmonious proportion, closure leak is again through baking and realizing long-term leak stopping and squeegee.
Background technology：
The pot of container used in daily life, especially metal material, spoon, basin and kettle etc., can go out during use
The defects such as existing crackle, gap and leak, these little defects directly affects this product and use, and lead to the lost of life, and these
Little defect is not enough to change new product again, and therefore, people are economical and convenient, typically can select viscous benefit mode by crackle or leakage
Hole etc. is filled, and occurs in that various stickers or viscous benefit articles for use therewith on market, and a lot of blocking methods also accordingly go out：
(1) rivet patching, can to a certain degree with scope in repair container leak, but its relatively be suitable for thickness the container of a bit, through riveting
After nail is repaired, convex surface is too high, and using inconvenience, rivet is also easily damaged, and easily makes hole shake crackle during rivet clasp；(2) soldering
Method, the method carrys out soldering using soldering, not only high cost, and when temperature is higher, soldering will melt Automatic-falling, and the fusing point of stannum is
231.89 DEG C, boil water and can only achieve 100 DEG C, and fried can reach more than 300 DEG C, stannum will melt it is possible to burn
Water but can not be fried；(3) glue aluminium foil strip method, easy to use, but it is afraid of water, non-refractory, easy Automatic-falling；(4) directly weld
Connect method it has not been convenient to, crackle and crack etc. easily occur again.The above method all can to a certain degree be repaiied with specific occasion
Mend container gap and leak etc., but go back some in particular cases, its plugging effect is not good.China Patent No. is CN03112597.2
Disclose a kind of anti-leak agent for metal container, be prepared from from industrial chemicals and raw mineral materials, have no toxic side effect, high temperature resistant, fit
Ying Xingqiang.And Semen sojae atricolor powder, viscosity is higher, thermoviscosity good stability, then mixes with clay and Pulvis Talci, and its viscosity strengthens.Therefore
Invention a kind of with Semen sojae atricolor powder as primary raw material, and preparation process is simple, the preparation side of practical metal pan leakage-stopping composition
Method is very promising.
Content of the invention：
It is an object of the invention to the shortcoming overcoming prior art to exist, seek to design one kind using Semen sojae atricolor powder and other things
Matter is mixed in proportion the preparation method of the metal pan leakage-stopping composition made for raw material, for metal pan under higher temperature occasion
Fracture hole leak stopping.
The concrete technology step that metal pan leakage-stopping composition according to the present invention realizes leak stopping is：
(1) raw material choice：Component weighs Semen sojae atricolor powder, clay, Pulvis Talci, coal dust, avian albumen and water by weight；Fowl egg are cleaned
From the fowl egg originating in 5 days, remove egg yolk composition；Again by other solid materials be milled into respectively 200 mesh sieves powder standby；
(2) compositionss are in harmonious proportion：Each raw material standby for step (1) is mixed and pinches and can become bulk to handss, unclamp handss and can tie up
Hold former shape state, obtain compositionss blending stock；
(3) pot hole closure：By wiped clean inside and outside at pot hole, take compositionss blending stock, it is outwards filled out from pot hole inboard
Expire and pass a pot hole, it is 1-2mm that the outside of pot passes pot thickness, and extends to the periphery 0.5-1mm along hole, then will pass pot
Compositionss blending stock compacting outside hole smooths so as to area is more than pot hole area；Tight more than the compositionss blending stock of pot hole area
Pot around patch pot hole, makes external seal in pot hole；
(4) oiling bakes：At the pot hole of closure inside pot, cover type smears vegetable oil, and then dry pot bakes to closure
At pot hole, compositionss blending stock is coke black and becomes hard, stops baking, is naturally down to room temperature；
(5) polishing in pot：With sand paper, the pot Dong Chu blocking inside pot surface is carried out uniform grinding to flat smooth again
Cover type smears one layer of vegetable oil, wherein allows and places under vegetable oil normal temperature condition 2-5 days, then can recover to use, realize gold
Belong to the leak stopping in pot hole.
In metal pan leakage-stopping composition according to the present invention, each raw material weight component is：Semen sojae atricolor powder 60-70 part, clay 30-
50 parts, Pulvis Talci 3-5 part, coal dust 2-3 part, avian albumen 20-50 part, water 10-30 part, vegetable oil 2-3 part；The powder of each raw material is thin
Degree is respectively less than 200 mesh.
Semen sojae atricolor powder according to the present invention adopts Semen Glyciness, first removes cortex, then is milled into powder with pulverizer, then crosses 200
Mesh sieve obtains Semen sojae atricolor powder；Clay used is the no grains of sand clay of firing brick-and tile, and its water content weight ratio, during less than 12%, grinds
Make powder and cross 200 mesh sieve gained；The fineness that described Pulvis Talci is commercially available is the Pulvis Talci of 200 mesh；Coal dust is selected commercially available
Coal is milled into powder after 200 mesh sieve gained；Described avian albumen is one kind or many of Ovum Gallus domesticus album, Ovum Anas domestica album and goose albumen
Kind；Described vegetable oil is one or more of Semen Ricini oil, soybean oil, Oleum Arachidis hypogaeae semen and Petiolus Trachycarpi oil.
Compared with prior art, composite formula is simple, reasonable mixture ratio, and raw material is easy to get, preparation process is simple for the present invention, fits
Ying Xingqiang, easy to use, repair speed soon, applied environment is friendly.
Specific embodiment：
Below by embodiment, the invention will be further described.
Embodiment 1：
In the metal pan leakage-stopping composition that the present embodiment is related to, each raw material weight component is：60 parts of Semen sojae atricolor powder, 30 parts of clay,
3 parts of Pulvis Talci, 2 parts of coal dust, 20 parts of avian albumen, 10 parts of water, 2 parts of vegetable oil；The fineness of powder of each raw material is 150 mesh；Its tool
Body technology step is：
(1) raw material choice：Component weighs Semen sojae atricolor powder, clay, Pulvis Talci, coal dust, avian albumen and water by weight；Fowl egg are cleaned
From the fowl egg originating in 5 days, remove egg yolk composition；Again by other solid materials be milled into respectively 200 mesh sieves powder standby；
(2) compositionss are in harmonious proportion：Each raw material standby for step (1) is mixed and pinches and can become bulk to handss, unclamp handss and can tie up
Hold former shape state, obtain compositionss blending stock；
(3) pot hole closure：By wiped clean inside and outside at pot hole, take compositionss blending stock, it is outwards filled out from pot hole inboard
Expire and pass a pot hole, it is 1-2mm that the outside of pot passes pot thickness, and extends to the periphery 0.5-1mm along hole, then will pass pot
Compositionss blending stock compacting outside hole smooths so as to area is more than pot hole area；Tight more than the compositionss blending stock of pot hole area
Pot around patch pot hole, makes external seal in pot hole；
(4) oiling bakes：At the pot hole of closure inside pot, cover type smears vegetable oil, and then dry pot bakes to closure
At pot hole, compositionss blending stock is coke black and becomes hard, stops baking, is naturally down to room temperature；
(5) polishing in pot：With sand paper, the pot Dong Chu blocking inside pot surface is carried out uniform grinding to flat smooth again
Cover type smears one layer of vegetable oil, wherein allows and places under vegetable oil normal temperature condition 2-5 days, then can recover to use, realize gold
Belong to the leak stopping in pot hole.
The Semen sojae atricolor powder that the present embodiment is related to adopts Semen Glyciness, first removes cortex, then is milled into powder with pulverizer, then mistake
200 mesh sieves obtain Semen sojae atricolor powder；Clay used is the no grains of sand clay of firing brick-and tile, and its water content weight is than less than 12%
When, it is milled into powder and cross 200 mesh sieve gained；The fineness that described Pulvis Talci is commercially available is the Pulvis Talci of 200 mesh；Coal dust selects city
The coal sold is milled into powder after 200 mesh sieve gained；Described avian albumen is Ovum Gallus domesticus album；Described vegetable oil is Semen Ricini
Oil.
Embodiment 2：
In the metal pan leakage-stopping composition that the present embodiment is related to, each raw material weight component is：63 parts of Semen sojae atricolor powder, 35 parts of clay,
3 parts of Pulvis Talci, 2 parts of coal dust, 26 parts of avian albumen, 15 parts of water, 2 parts of vegetable oil；The fineness of powder of each raw material is 120 mesh；This reality
Applying the avian albumen that example is related to is goose albumen；Described vegetable oil is soybean oil；Its concrete technology step and methods for using them is with enforcement
Example 1.
Embodiment 3：
In the metal pan leakage-stopping composition that the present embodiment is related to, each raw material weight component is：65 parts of Semen sojae atricolor powder, 40 parts of clay,
4 parts of Pulvis Talci, 3 parts of coal dust, 30 parts of avian albumen, 20 parts of water, 3 parts of vegetable oil；The fineness of powder of each raw material is 180 mesh；This reality
Applying the avian albumen that example is related to is goose albumen；Described vegetable oil is Oleum Arachidis hypogaeae semen；Its concrete technology step and methods for using them is with enforcement
Example 1；Tianjin Zhang, there is the circular pan hole of an a diameter of 1mm pot bottom of household metal titanium pan, using this reality
Apply metal pan leakage-stopping composition and its processing step of example preparation, after the completion of the mending-leakage of pot hole, daily use, use after mending-leakage
3 years, excellent at titanium pot leak stopping, illustrate that the metal pan leakage-stopping composition that this method is produced has what good leak stopping was squeegeeed
Effect, and free from extraneous odour, harmless.
Embodiment 4：
In the metal pan leakage-stopping composition that the present embodiment is related to, each raw material weight component is：70 parts of Semen sojae atricolor powder, 50 parts of clay,
5 parts of Pulvis Talci, 3 parts of coal dust, 50 parts of avian albumen, 30 parts of water, 3 parts of vegetable oil；The fineness of powder of each raw material is 190 mesh；This reality
Applying the avian albumen that example is related to is Ovum Anas domestica album；Described vegetable oil is Petiolus Trachycarpi oil；Its concrete technology step and methods for using them is with enforcement
Example 1；Products application manufactured in the present embodiment in leaky iron deep fryer, when carrying out fried pot up to more than 300 DEG C, and
Through the use more than 12 months for 60 restaurants, still no Traces of Water Leakage, the normal use of pot hole, illustrate that the metal pan that this method is produced is blocked up
Leakage compositionss are not only glued and are mended firmly, and high temperature resistant, and persistency is good.
Claims (2)
1. a kind of preparation method of metal pan leakage-stopping composition is it is characterised in that concrete technology step is：
(1) raw material choice：Component weighs Semen sojae atricolor powder, clay, Pulvis Talci, coal dust, avian albumen and water by weight；Avian albumen is selected from and produces
Fowl egg in 5 days, remove egg yolk composition；Again by other solid materials be milled into respectively 200 mesh sieves powder standby；
(2) compositionss are in harmonious proportion：Each raw material standby for step (1) is mixed and pinches and can become bulk to handss, unclamp handss be able to maintain that former
Group's shape state, obtains compositionss blending stock；
(3) pot hole closure：By wiped clean inside and outside at pot hole, take compositionss blending stock, it is outwards filled up simultaneously from pot hole inboard
Pass a pot hole, it is 1-2mm that the outside of pot passes pot thickness, and extends to the periphery 0.5-1mm along hole, then will pass outside pot hole
The compacting of compositionss blending stock smooth so as to area is more than pot hole area；It is close to pot more than the compositionss blending stock of pot hole area
Pot around hole, makes external seal in pot hole；
(4) oiling bakes：At the pot hole of closure inside pot, cover type smears vegetable oil, and then dry pot bakes to the pot hole of closure
Place's compositionss blending stock is coke black and becomes hard, stops baking, is naturally down to room temperature；
(5) polishing in pot：With sand paper, the pot Dong Chu blocking inside pot surface is carried out uniform grinding to cover again to flat smooth
Formula smears one layer of vegetable oil, wherein allows and places under vegetable oil normal temperature condition 2-5 days, then can recover to use, realize metal pan
The leak stopping in hole；
Each raw material weight component is：Semen sojae atricolor powder 60-70 part, clay 30-50 part, Pulvis Talci 3-5 part, coal dust 2-3 part, avian albumen
20-50 part, water 10-30 part, vegetable oil 2-3 part；The fineness of powder of each raw material is respectively less than 200 mesh.
2. the preparation method of metal pan leakage-stopping composition according to claim 1 is it is characterised in that described Semen sojae atricolor powder is adopted
With Semen Glyciness, first remove cortex, then be milled into powder with pulverizer, then cross 200 mesh sieves and obtain Semen sojae atricolor powder；Clay used is to fire
The no grains of sand clay of brick and tile, its water content weight ratio, during less than 12%, is milled into powder and crosses 200 mesh sieve gained；Described
The fineness that Pulvis Talci is commercially available is the Pulvis Talci of 200 mesh；Coal dust is milled into powder after 200 mesh sieve institutes from commercially available coal
?；Described avian albumen is one or more of Ovum Gallus domesticus album, Ovum Anas domestica album and goose albumen；Described vegetable oil is Semen Ricini oil, big
One or more of Oleum Glycines, Oleum Arachidis hypogaeae semen and Petiolus Trachycarpi oil.