CN106478043A - A kind of building composite board of environment-friendly insulating waterproof and preparation method thereof - Google Patents
A kind of building composite board of environment-friendly insulating waterproof and preparation method thereof Download PDFInfo
- Publication number
- CN106478043A CN106478043A CN201610891969.1A CN201610891969A CN106478043A CN 106478043 A CN106478043 A CN 106478043A CN 201610891969 A CN201610891969 A CN 201610891969A CN 106478043 A CN106478043 A CN 106478043A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite board
- environment
- building composite
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of building composite board of environment-friendly insulating waterproof and preparation method thereof, it is prepared from including by the raw material of following weight portion：30 50 parts of portland cement, 10 15 parts of fiber, 5 10 parts of montmorillonite powder, 8 15 parts of rutile titanium white lead, 12 15 parts of modifying epoxy resin by organosilicon, 12 18 parts of Gypsum Fibrosum, 15 25 parts of tripolycyanamide, 49 parts of polyester fiber, 10 20 parts of sodium silicate solution, 2 10 parts of polyacrylamide, 18 parts of tributyl phosphate, 11 17 parts of acrylate, 28 parts of light-weight aggregate.Preparation process is simple of the present invention, cheap, the building composite board of the environment-friendly insulating waterproof preparing has the advantages that light capacity, waterproof, high insulating effect, and its chemical stability is strong, nontoxic, tasteless, is a kind of preferable insulation material.
Description
Technical field
The present invention relates to construction material manufacture technology field and in particular to a kind of building composite board of environment-friendly insulating waterproof and
Its preparation method.
Background technology
Construction material can be divided into structural material, ornament materials and some proprietary materials.Structural material include timber, bamboo wood,
Stone material, portland cement, concrete, metal, brick and tile, pottery, glass, engineering plastics, composite etc.；Ornament materials includes
Various coating, paint, coating, veneer, assorted ceramic tile, there is glass of special-effect etc.；Proprietary material refers to for waterproof, prevents
Damp, anti-corrosion, fire prevention, fire-retardant, sound insulation, heat-insulated, insulation, sealing etc..Insulation material has many types, and range of application is also very wide.Than
More common has：Glass wool product, the resistance to heat-insulation blanket of dimension, heat insulation foam glass, polyurethane etc..The purposes of glass wool product is had time
Adjust insulation, airduct insulation, steel construction insulation, boiler insulation, cleaner unit, steam pipeline heat-insulation etc..The purposes tieing up resistance to heat-insulation blanket has
The heat-insulation and heat-preservation of the industry Thermal Equipment such as oil, chemical industry, thermoelectricity, iron and steel, non-ferrous metal, industrial furnace and protection.Exterior-wall heat insulation material
Material has silicate heat-protective coatings, ceramic thermal insulation material, glue powder polyphenyl particle, hard-foam polyurethane warming plate etc..Above-mentioned insulation material
Application in require that insulation material possesses more good heat-insulating property, resistance to compression, rupture strength and water resistance.
At present, domestic existing insulation material manufacturing enterprise nearly thousand, product has more than ten big class, up to a hundred kinds, according to combustion
Burn performance and be broadly divided into A level and B level.A level fire-retardant heat-insulation material includes foam glass board, stone(mine)cotton plate, glass
Cotton plate, microporous calcium silicate, expansion montmorillonite powder product, glass bead product, expanded vermiculite product, aerating coagulation product, light collection
Material foamed concrete product, various inorganic heat preservation powder (as YT inorganic active wall insulation powder, glass bead etc.),
The inorganic adiabator such as inorganic heat preservation slurry.In B level, main inclusion styrofoam, hard-foam polyurethane plate, phenolic-aldehyde heat-insulation board etc. are organic
Matter adiabator.And in Chinese building design and construction, more than 90% all employs extrusion molding polystyrene polyfoam
(XPS), the organic matter such as molded polystyrene foams plastics (EPS), RPUF (PU) adiabator, makees
Heat insulating material for external for exterior wall.EPS, XPS, PU belong to organic insulation material, and maximum advantage is exactly light weight, insulation, heat-insulated
Property is good；Maximum defect is exactly to prevent fires, poor stability, easily aging, easy firing, and during burning, smog is big, toxicity is big, bearing, makes
With the time limit, fire line all not as inorganic heat insulation material.And inorganic heat insulation material generally existing intensity is relatively low, insulation efficiency slightly
The defects such as difference, water absorption rate height, but have that fire protection flame retarding, deformation coefficient be little, aging resistance, stable performance and plinth course and float coat
In conjunction with preferable, long service life, difficulty of construction is little, eco-environmental prote is good, can with cycling and reutilization the advantages of.For this reason, being badly in need of big
Power research and development should have the new building insulation material of inorganic and organic bi-material advantage concurrently.
Content of the invention
For solving the above problems, the invention provides a kind of building composite board of environment-friendly insulating waterproof and preparation method thereof.
For achieving the above object, the technical scheme that the present invention takes is：
A kind of building composite board of environment-friendly insulating waterproof, is prepared from including by the raw material of following weight portion：Portland cement 35-
45 parts, fiber 14-25 part, montmorillonite powder 6-11 part, rutile titanium white lead 9-22 part, modifying epoxy resin by organosilicon 15-25 part,
Gypsum Fibrosum 10-19 part, tripolycyanamide 14-27 part, polyester fiber 5-11 part, sodium silicate solution 12-22 part, polyacrylamide 1-8 part,
Tributyl phosphate 2-6 part, acrylate 9-15 part, light-weight aggregate 1-7 part, surfactant 2-4 part, waterproofing agent 2-6 part, modification
Additive 2-5 part, defoamer 1-3 part and water 2-15 part.
Further, a kind of building composite board of environment-friendly insulating waterproof, is prepared from including by the raw material of following weight portion：
Portland cement 37-40 part, fiber 15-23 part, montmorillonite powder 8-10 part, rutile titanium white lead 11-18 part, organic silicon modified epoxy
Oxygen tree fat 16-24 part, Gypsum Fibrosum 13-17 part, tripolycyanamide 15-25 part, polyester fiber 6-10 part, sodium silicate solution 14-20 part, poly-
Acrylamide 2-7 part, tributyl phosphate 3-5 part, acrylate 11-14 part, light-weight aggregate 2-6 part, surfactant 3-4 part, anti-
Water preparation 3-5 part, property-modifying additive 3-5 part, defoamer 2-3 part and water 4-10 part.
Further, described surfactant is naphthalene sulphonate formaldehyde polymer.
Further, described waterproofing agent is melamine system waterproofing agent.
Further, described property-modifying additive is barium stearate.
Further, described defoamer is silicon ether Copolymer.
Further, a kind of preparation method of the building composite board of environment-friendly insulating waterproof it is characterised in that preparation process such as
Under：
S1:By portland cement 37-40 part, fiber 15-23 part, montmorillonite powder 8-10 part, rutile titanium white lead 11-18 part, have
Machine silicon modified epoxy resin 16-24 part, Gypsum Fibrosum 13-17 part, tripolycyanamide 15-25 part, polyester fiber 6-10 part, light-weight aggregate 2-6
Part is pulverized with pulverizer respectively, and the mesh number being crushed to above-mentioned each composition is 200-300 mesh, standby；
S2：Portland cement after step S1 is pulverized, fiber, montmorillonite powder, rutile titanium white lead, silicon-modified epoxy
Add water in resin, Gypsum Fibrosum, tripolycyanamide, polyester fiber, light-weight aggregate addition cement paste agitated kettle and be stirred, be sufficiently stirred for
To mixture；
S3：Add sodium silicate solution 14-20 part, polyacrylamide 2-7 part, tributyl phosphate 3-5 part, acrylic acid in step s 2
Ester 11-14 part, surfactant 3-4 part, waterproofing agent 3-5 part, property-modifying additive 3-5 part, defoamer 2-3 part and water 4-10
Part；Carry out high-speed stirred, stir dissolving, net slurry is obtained；It is subsequently poured in mould and carry out foaming and intumescing；
S4：Material board mould extrusion forming after step S3 is foamed, pressure is 80-90MPa, prepares environmental protection and protects
The building composite board of warm waterproof.
Further, a kind of building composite board of environment-friendly insulating waterproof, is prepared from by the raw material of following weight portion：Silicic acid
37 parts of salt cement, 15 parts of fiber, 8 parts of montmorillonite powder, 11 parts of rutile titanium white lead, 16 parts of modifying epoxy resin by organosilicon, Gypsum Fibrosum
13 parts, 15 parts of tripolycyanamide, 6 parts of polyester fiber, 14 parts of sodium silicate solution, 2 parts of polyacrylamide, 3 parts of tributyl phosphate, propylene
11 parts of acid esters, 2 parts of light-weight aggregate, 3 parts of surfactant, 3 parts of waterproofing agent, 3 parts of property-modifying additive, 2 parts of defoamer and 4 parts of water.
Further, a kind of building composite board of environment-friendly insulating waterproof, is prepared from by the raw material of following weight portion：Silicic acid
38 parts of salt cement, 18 parts of fiber, 8 parts of montmorillonite powder, 16 parts of rutile titanium white lead, 18 parts of modifying epoxy resin by organosilicon, Gypsum Fibrosum
15 parts, 16 parts of tripolycyanamide, 8 parts of polyester fiber, 17 parts of sodium silicate solution, 5 parts of polyacrylamide, 4 parts of tributyl phosphate, propylene
14 parts of acid esters, 4 parts of light-weight aggregate, 4 parts of surfactant, 4 parts of waterproofing agent, 4 parts of property-modifying additive, 2 parts of defoamer and 4 parts of water.
Preparation process is simple of the present invention, cheap, the building composite board of the environment-friendly insulating waterproof preparing has
Light capacity, waterproof, the advantage of high insulating effect, and its chemical stability is strong, nontoxic, tasteless, it is a kind of preferable insulation material.
The present invention has the beneficial effect that：
A, secure and non-combustible, environmental protection.Eliminate impact combustibility and poisonous element in material composition, so that this material is reached
Do not fire the requirement of A1 level, to compensate for poor, ageing-resistant and poisonous as the fire protecting performance of insulation material with organic material simultaneously
Shortcoming.
B, there is excellent thermal and insulating performance and mechanical performance, water absorption rate is relatively low, compensate for common inorganic and protect
Adiabator heat conductivity is high, rigidity is big and bibulous shortcoming.
C, density small intensity height alleviate product weight, and consumptive material is few, and yield loss rate is low, deposit conveniently, reduce logistics fortune
Defeated and warehouse cost.
D, this warming plate production technology process are brief, can continuous operation it is easy to implement and the standard controlling beneficial to product
Change, standardization, large-scale production.
E, the insulating board for building of the present invention are capable of the advantage of effectively comprehensive tradition organic board and inorganic plate, can reach
The heat-insulating property grade of organic material, has an inorganic material performance such as not so simultaneously again, durability, good weatherability, can with build
Build the same life-span.
Specific embodiment
In order that objects and advantages of the present invention become more apparent, with reference to embodiments the present invention is carried out detailed further
Explanation.It should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
The present invention includes being prepared from by the raw material of following weight portion：Portland cement 35-45 part, fiber 14-25 part, illiteracy
De- stone powder 6-11 part, rutile titanium white lead 9-22 part, modifying epoxy resin by organosilicon 15-25 part, Gypsum Fibrosum 10-19 part, melamine
Amine 14-27 part, polyester fiber 5-11 part, sodium silicate solution 12-22 part, polyacrylamide 1-8 part, tributyl phosphate 2-6 part, third
Olefin(e) acid ester 9-15 part, light-weight aggregate 1-7 part, surfactant 2-4 part, waterproofing agent 2-6 part, property-modifying additive 2-5 part, defoamer
1-3 part and water 2-15 part.
A kind of building composite board of environment-friendly insulating waterproof, is prepared from including by the raw material of following weight portion：Silicate cement
Mud 37-40 part, fiber 15-23 part, montmorillonite powder 8-10 part, rutile titanium white lead 11-18 part, modifying epoxy resin by organosilicon
16-24 part, Gypsum Fibrosum 13-17 part, tripolycyanamide 15-25 part, polyester fiber 6-10 part, sodium silicate solution 14-20 part, polyacrylamide
Amine 2-7 part, tributyl phosphate 3-5 part, acrylate 11-14 part, light-weight aggregate 2-6 part, surfactant 3-4 part, waterproofing agent 3-
5 parts, property-modifying additive 3-5 part, defoamer 2-3 part and water 4-10 part.
Described surfactant is naphthalene sulphonate formaldehyde polymer.
Described waterproofing agent is melamine system waterproofing agent.
Described property-modifying additive is barium stearate.
Described defoamer is silicon ether Copolymer.
A kind of preparation method of the building composite board of environment-friendly insulating waterproof is it is characterised in that preparation process is as follows：
S1:By portland cement 37-40 part, fiber 15-23 part, montmorillonite powder 8-10 part, rutile titanium white lead 11-18 part, have
Machine silicon modified epoxy resin 16-24 part, Gypsum Fibrosum 13-17 part, tripolycyanamide 15-25 part, polyester fiber 6-10 part, light-weight aggregate 2-6
Part is pulverized with pulverizer respectively, and the mesh number being crushed to above-mentioned each composition is 200-300 mesh, standby；
S2：Portland cement after step S1 is pulverized, fiber, montmorillonite powder, rutile titanium white lead, silicon-modified epoxy
Add water in resin, Gypsum Fibrosum, tripolycyanamide, polyester fiber, light-weight aggregate addition cement paste agitated kettle and be stirred, be sufficiently stirred for
To mixture；
S3：Add sodium silicate solution 14-20 part, polyacrylamide 2-7 part, tributyl phosphate 3-5 part, acrylic acid in step s 2
Ester 11-14 part, surfactant 3-4 part, waterproofing agent 3-5 part, property-modifying additive 3-5 part, defoamer 2-3 part and water 4-10
Part；Carry out high-speed stirred, stir dissolving, net slurry is obtained；It is subsequently poured in mould and carry out foaming and intumescing；
S4：Material board mould extrusion forming after step S3 is foamed, pressure is 80-90MPa, prepares environmental protection and protects
The building composite board of warm waterproof.
It is prepared from by the raw material of following weight portion：37 parts of portland cement, 15 parts of fiber, 8 parts of montmorillonite powder, rutile
11 parts of titanium dioxide, 16 parts of modifying epoxy resin by organosilicon, 13 parts of Gypsum Fibrosum, 15 parts of tripolycyanamide, 6 parts of polyester fiber, sodium silicate are molten
14 parts of liquid, 2 parts of polyacrylamide, 3 parts of tributyl phosphate, 11 parts of acrylate, 2 parts of light-weight aggregate, 3 parts of surfactant, waterproof
3 parts of agent, 3 parts of property-modifying additive, 2 parts of defoamer and 4 parts of water.
, it is prepared from by the raw material of following weight portion：38 parts of portland cement, 18 parts of fiber, 8 parts of montmorillonite powder, golden red
16 parts of stone titanium dioxide, 18 parts of modifying epoxy resin by organosilicon, 15 parts of Gypsum Fibrosum, 16 parts of tripolycyanamide, 8 parts of polyester fiber, sodium silicate
17 parts of solution, 5 parts of polyacrylamide, 4 parts of tributyl phosphate, 14 parts of acrylate, 4 parts of light-weight aggregate, 4 parts of surfactant, anti-
4 parts of water preparation, 4 parts of property-modifying additive, 2 parts of defoamer and 4 parts of water.
Embodiment 1：
S1:By 40 parts of portland cement, 15 parts of fiber, 10 parts of montmorillonite powder, 18 parts of rutile titanium white lead, organic silicon modified epoxy
16 parts of oxygen tree fat, 13 parts of Gypsum Fibrosum, 15 parts of tripolycyanamide, 10 parts of polyester fiber, 6 parts of light-weight aggregate are pulverized with pulverizer respectively, pulverize
Mesh number to above-mentioned each composition is 200-300 mesh, standby；
S2：Portland cement after step S1 is pulverized, fiber, montmorillonite powder, rutile titanium white lead, silicon-modified epoxy
Add water in resin, Gypsum Fibrosum, tripolycyanamide, polyester fiber, light-weight aggregate addition cement paste agitated kettle and be stirred, be sufficiently stirred for
To mixture；
S3：In step s 2 add 20 parts of sodium silicate solution, 7 parts of polyacrylamide, 5 parts of tributyl phosphate, 14 parts of acrylate,
4 parts of surfactant, 5 parts of waterproofing agent, 3 parts of property-modifying additive, 3 parts of defoamer and 10 parts of water；Carry out high-speed stirred, stirring is all
Even dissolving, is obtained net slurry；It is subsequently poured in mould and carry out foaming and intumescing；
S4：Material board mould extrusion forming after step S3 is foamed, pressure is 80-90MPa, prepares environmental protection and protects
The building composite board of warm waterproof.
Embodiment 2：
S1:By 37 parts of portland cement, 15 parts of fiber, 8 parts of montmorillonite powder, 11 parts of rutile titanium white lead, silicon-modified epoxy
16 parts of resin, 13 parts of Gypsum Fibrosum, 15 parts of tripolycyanamide, 6 parts of polyester fiber, 2 parts of light-weight aggregate are pulverized with pulverizer respectively, are crushed to
The mesh number of each composition stated is 200-300 mesh, standby；
S2：Portland cement after step S1 is pulverized, fiber, montmorillonite powder, rutile titanium white lead, silicon-modified epoxy
Add water in resin, Gypsum Fibrosum, tripolycyanamide, polyester fiber, light-weight aggregate addition cement paste agitated kettle and be stirred, be sufficiently stirred for
To mixture；
S3：In step s 2 add 14 parts of sodium silicate solution, 2 parts of polyacrylamide, 3 parts of tributyl phosphate, 11 parts of acrylate,
3 parts of surfactant, 3 parts of waterproofing agent, 3 parts of property-modifying additive, 2 parts of defoamer and 4 parts of water；Carry out high-speed stirred, stirring is all
Even dissolving, is obtained net slurry；It is subsequently poured in mould and carry out foaming and intumescing；
S4：Material board mould extrusion forming after step S3 is foamed, pressure is 80-90MPa, prepares environmental protection and protects
The building composite board of warm waterproof.
Embodiment 3：
S1:By 38 parts of portland cement, 18 parts of fiber, 8 parts of montmorillonite powder, 16 parts of rutile titanium white lead, silicon-modified epoxy
18 parts of resin, 15 parts of Gypsum Fibrosum, 16 parts of tripolycyanamide, 8 parts of polyester fiber, 4 parts of light-weight aggregate are pulverized with pulverizer respectively, are crushed to
The mesh number of each composition stated is 200-300 mesh, standby；
S2：Portland cement after step S1 is pulverized, fiber, montmorillonite powder, rutile titanium white lead, silicon-modified epoxy
Add water in resin, Gypsum Fibrosum, tripolycyanamide, polyester fiber, light-weight aggregate addition cement paste agitated kettle and be stirred, be sufficiently stirred for
To mixture；
S3：In step s 2 add 17 parts of sodium silicate solution, 5 parts of polyacrylamide, 4 parts of tributyl phosphate, 14 parts of acrylate,
4 parts of surfactant, 4 parts of waterproofing agent, 4 parts of property-modifying additive, 2 parts of defoamer and 4 parts of water；Carry out high-speed stirred, stir
Dissolving, is obtained net slurry；It is subsequently poured in mould and carry out foaming and intumescing；
S4：Material board mould extrusion forming after step S3 is foamed, pressure is 80-90MPa, prepares environmental protection and protects
The building composite board of warm waterproof.
Low cost of the present invention, energy-conserving and environment-protective, make easily；Both it is easy to construct, good water-proof effect, there is high the preventing of comparison again
Water intensity, self-shield power is strong, easy to use；There is ageing-resistant, corrosion-resistant, puncture-resistant performance well simultaneously, and improve
The tension intensity of material.
The present invention adopt portland cement, fiber, montmorillonite powder, rutile titanium white lead, modifying epoxy resin by organosilicon, three
Poly cyanamid, polyester fiber, sodium silicate solution, polyacrylamide, tributyl phosphate, acrylate, light-weight aggregate, chromium boride, synthesis
The effective proportioning of rubber, construction material has the effect of moistureproof leakage-proof and seepage-proof, it can be avoided that the erosion to building of water and salinity, carries
The high water-proof function of construction wall；And good water-proof effect, low price, garbage can be utilized, economic and environment-friendly.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (9)
1. a kind of building composite board of environment-friendly insulating waterproof is it is characterised in that include being prepared from by the raw material of following weight portion：
Portland cement 35-45 part, fiber 14-25 part, montmorillonite powder 6-11 part, rutile titanium white lead 9-22 part, organic silicon modified epoxy
Oxygen tree fat 15-25 part, Gypsum Fibrosum 10-19 part, tripolycyanamide 14-27 part, polyester fiber 5-11 part, sodium silicate solution 12-22 part, poly-
Acrylamide 1-8 part, tributyl phosphate 2-6 part, acrylate 9-15 part, light-weight aggregate 1-7 part, surfactant 2-4 part, waterproof
Agent 2-6 part, property-modifying additive 2-5 part, defoamer 1-3 part and water 2-15 part.
2. a kind of building composite board of environment-friendly insulating waterproof according to claim 1 is it is characterised in that include by following heavy
The raw material of amount part is prepared from：Portland cement 37-40 part, fiber 15-23 part, montmorillonite powder 8-10 part, rutile titanium white lead
11-18 part, modifying epoxy resin by organosilicon 16-24 part, Gypsum Fibrosum 13-17 part, tripolycyanamide 15-25 part, polyester fiber 6-10 part,
Sodium silicate solution 14-20 part, polyacrylamide 2-7 part, tributyl phosphate 3-5 part, acrylate 11-14 part, light-weight aggregate 2-6
Part, surfactant 3-4 part, waterproofing agent 3-5 part, property-modifying additive 3-5 part, defoamer 2-3 part and water 4-10 part.
3. a kind of building composite board of environment-friendly insulating waterproof according to claim 1 is it is characterised in that described surface activity
Agent is naphthalene sulphonate formaldehyde polymer.
4. a kind of building composite board of environment-friendly insulating waterproof according to claim 1 is it is characterised in that described waterproofing agent is
Melamine system waterproofing agent.
5. a kind of building composite board of environment-friendly insulating waterproof according to claim 1 is it is characterised in that described modification is added
Agent is barium stearate.
6. a kind of building composite board of environment-friendly insulating waterproof according to claim 1 is it is characterised in that described defoamer is
Silicon ether Copolymer.
7. the preparation method of the building composite board of a kind of environment-friendly insulating waterproof according to claim 1-6 any one, its
It is characterised by, preparation process is as follows：
S1:By portland cement 37-40 part, fiber 15-23 part, montmorillonite powder 8-10 part, rutile titanium white lead 11-18 part, have
Machine silicon modified epoxy resin 16-24 part, Gypsum Fibrosum 13-17 part, tripolycyanamide 15-25 part, polyester fiber 6-10 part, light-weight aggregate 2-6
Part is pulverized with pulverizer respectively, and the mesh number being crushed to above-mentioned each composition is 200-300 mesh, standby；
S2：Portland cement after step S1 is pulverized, fiber, montmorillonite powder, rutile titanium white lead, silicon-modified epoxy
Add water in resin, Gypsum Fibrosum, tripolycyanamide, polyester fiber, light-weight aggregate addition cement paste agitated kettle and be stirred, be sufficiently stirred for
To mixture；
S3：Add sodium silicate solution 14-20 part, polyacrylamide 2-7 part, tributyl phosphate 3-5 part, acrylic acid in step s 2
Ester 11-14 part, surfactant 3-4 part, waterproofing agent 3-5 part, property-modifying additive 3-5 part, defoamer 2-3 part and water 4-10
Part；Carry out high-speed stirred, stir dissolving, net slurry is obtained；It is subsequently poured in mould and carry out foaming and intumescing；
S4：Material board mould extrusion forming after step S3 is foamed, pressure is 80-90MPa, prepares environmental protection and protects
The building composite board of warm waterproof.
8. a kind of environment-friendly insulating waterproof according to claim 1-6 any one building composite board it is characterised in that by
The raw material of following weight portion is prepared from：37 parts of portland cement, 15 parts of fiber, 8 parts of montmorillonite powder, rutile titanium white lead 11
Part, 16 parts of modifying epoxy resin by organosilicon, 13 parts of Gypsum Fibrosum, 15 parts of tripolycyanamide, 6 parts of polyester fiber, 14 parts of sodium silicate solution, poly-
2 parts of acrylamide, 3 parts of tributyl phosphate, 11 parts of acrylate, 2 parts of light-weight aggregate, 3 parts of surfactant, 3 parts of waterproofing agent, change
3 parts of additive of property, 2 parts of defoamer and 4 parts of water.
9. a kind of environment-friendly insulating waterproof according to claim 1-6 any one building composite board it is characterised in that by
The raw material of following weight portion is prepared from：38 parts of portland cement, 18 parts of fiber, 8 parts of montmorillonite powder, rutile titanium white lead 16
Part, 18 parts of modifying epoxy resin by organosilicon, 15 parts of Gypsum Fibrosum, 16 parts of tripolycyanamide, 8 parts of polyester fiber, 17 parts of sodium silicate solution, poly-
5 parts of acrylamide, 4 parts of tributyl phosphate, 14 parts of acrylate, 4 parts of light-weight aggregate, 4 parts of surfactant, 4 parts of waterproofing agent, modification
4 parts of additive, 2 parts of defoamer and 4 parts of water.