CN106082824B - A kind of architecture exterior wall insulating materials - Google Patents
A kind of architecture exterior wall insulating materials Download PDFInfo
- Publication number
- CN106082824B CN106082824B CN201610446409.5A CN201610446409A CN106082824B CN 106082824 B CN106082824 B CN 106082824B CN 201610446409 A CN201610446409 A CN 201610446409A CN 106082824 B CN106082824 B CN 106082824B
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation material
- agent
- flyash
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of architecture exterior wall insulating materials, the insulation material is made up of marble dust, cullet, thermosetting plastics, plaster of Paris, cement, flyash, exciting agent, air entraining agent, wood chip, mica powder, oyster shell whiting and polystyrene foam；The parts by weight of material form：3 parts~9 parts of 20 parts~50 parts of cement, 20 parts~50 parts of flyash, 1 part~8 parts of exciting agent, 1 part~8 parts of marble dust, 1 part~8 parts of phenolic resin, 1 part~8 parts of urea-formaldehyde plastics, 1 part~5 parts of air entraining agent, 0.1 part~2 parts of cullet, 5 parts~25 parts of plaster of Paris, 20 parts~50 parts of wood chip, 1 part~8 parts of mica powder, 1 part~5 parts of oyster shell whiting and polystyrene foam.Cost of the present invention is low, heat insulation effect is good, steady quality, environment-protecting and non-poisonous, service life is long, environmental suitability is strong.
Description
Technical field
The present invention relates to building material technical field, specifically a kind of architecture exterior wall insulating materials.
Background technology
Traditional architecture only pays attention to the popularization of its performance, and the lifting for building inherent value is failed to pay close attention.It is " green
After color building " theory proposes, domestic construction industry starts to walk environmental transformation road, and many building internal structure external structures are carried out
Green optimization processing, the comprehensive performance for improving building.Insulation material is the basic element for building environmental protection and energy saving, not
Come quality, performance, value of insulation material etc. by General Promotion, these are all that engineering unit needs that pays close attention to ask in construction period
Topic.Building trade has become the Importance Industry chain of market economy in recent years, and architectural engineering and its appurtenance are to national economy
Income level improves and has played facilitation.Insulation material is the basic composition of projects construction, and quality of materials and performance are determined
The use value of whole building thing is determined, construction material is that the goods and materials of architectural engineering construction ensure, the utilization of new material will promote
Enter the optimization and upgrading of building structure performance, provide the user superior social living environment.For different insulation materials, construction
Personnel will need reasonable selection according to specific structure, allow the performance of each material to perform to maximum.
Exterior wall is the formal structure of building, and external wall structure is related to the aesthetic value of building, overall structure is applied
The influence of work efficiency fruit is very big.Generally, the requirement of high temperature resistance is can reach using external wall body thermal insulation material, in time overheat temperature
Degree is transferred to outdoor, maintains the equilibrium of internal temperature.
Patent No. CN201110150832.8 Chinese patent discloses a kind of low-thermal-conductivity inorganic foaming thermal insulation material,
The particle of low heat conductivity is added in inorganic foamed material, using the low heat conductivity of filler particles, reduces the heat conduction system of section bar
Number；Waterproofing agent is smeared in Surface of profile, so as to solve the problems, such as that section bar raises thermal conductivity factor because of water suction；Prepared with the present invention
Section bar, inside is filled with closed aperture, so as to reduce the thermal conductivity factor of section bar, maintains the low heat-conducting effect of section bar.And
And enough inorganic matters can be retained and obtain high intensity, while reduce organic granular and obtain excellent anti-flammability, have and apply
The characteristics of work is convenient, and process costs are low, and Fire retardant grade is high, but technology stability is poor, heat insulation effect is limited.
Patent No. CN201110335931.3 Chinese patent discloses a kind of Siliceous heat-insulation composite material for wall, and it is
Be made up of base-material and water, base-material mainly have closed-cell expanded perlite, cement, plaster of Paris, alumina silicate fibre, brucite fiber,
The recessed soil of the inorganic mineral such as slag wool fiber fiber, high stick, re-dispersible glue powder, hydroxypropyl methyl cellulose auxiliary agent and hydrophobic
Agent, the weight ratio of base-material and water is 1 during use：1.2~1.3.Product is indefinite form powdery insulation material, has good energy-conservation
Insulation, heat-insulated, sound-absorbing and flame-retardant reach the fire prevention of A1 levels, seismic crack, crack resistance, pliability and weatherability；Not with wall
Learn reaction, intensity is high, it is indeformable, do not ftracture, not hollowing, do not fall off, ageing resistace is good, performance and wall same life-span；
The present invention is green nontoxic, suitable for the inside and outside wall thermal insulation of various wall base materials, party wall insulation and roofing, basement,
The heat insulation heat preservation energy-saving engineering such as garage, stair, corridor, passageway for fire apparatus.But the cost of the invention product is high, application has
Limit.
The content of the invention
The present invention be directed to above technical problem, there is provided a kind of cost is low, heat insulation effect well, steady quality, it is environment-protecting and non-poisonous,
The architecture exterior wall insulating materials that service life is long, environmental suitability is strong.
The present invention is achieved through the following technical solutions：A kind of architecture exterior wall insulating materials, by marble dust, cullet,
Thermosetting plastics, plaster of Paris, cement, flyash, exciting agent, air entraining agent, wood chip, mica powder, oyster shell whiting and polystyrene bubble
Foam forms；The parts by weight of material form：20 parts~50 parts of cement, 20 parts~50 parts of flyash, 1 part~8 parts of exciting agent, Dali
1 part~8 parts of stone powder, 1 part~8 parts of phenolic resin, 1 part~8 parts of urea-formaldehyde plastics, 1 part~5 parts of air entraining agent, 0.1 part of cullet~
2 parts, 5 parts~25 parts of plaster of Paris, 20 parts~50 parts of wood chip, 1 part~8 parts of mica powder, 1 part~5 parts of oyster shell whiting and polystyrene
3 parts~9 parts of foam.
Further, air entraining agent is the mixture of rosin resin and alkylbenzenesulfonate.
Further, the ratio of air entraining agent composition is：Rosin resin accounts for the 20% of air entraining agent gross weight, alkyl benzene sulphonate
Salt accounts for the 80% of air entraining agent gross weight.
A kind of architecture exterior wall insulating materials, its parts by weight composition are：40 parts~50 parts of cement, 40 parts~50 parts of flyash,
1 part~8 parts of exciting agent, 1 part~8 parts of marble dust, 6 parts~16 parts of thermosetting plastics, 0.2 part~0.5 part of rosin resin, alkane
0.8 part~2 parts of base benzene sulfonate, 1 part~2 parts of salt cullet, 15 parts~25 parts of plaster of Paris, 40 parts~50 parts of wood chip, mica
3 parts~5 parts of 4 parts~8 parts of powder, 4 parts~5 parts of oyster shell whiting and polystyrene foam.
Further, thermosetting plastics is made up of phenolic resin and urea-formaldehyde plastics.
A kind of architecture exterior wall insulating materials, its parts by weight composition are：45 parts~50 parts of cement, 45 parts~50 parts of flyash,
1 part~5 parts of exciting agent, 1 part~5 parts of marble dust, 5 parts~8 parts of phenolic resin, 1 part~5 parts of urea-formaldehyde plastics, rosin resin
0.2 part~0.5 part, 0.8 part~2 parts of alkylbenzenesulfonate, 1 part~2 parts of salt cullet, 15 parts~20 parts of plaster of Paris, wood chip
3 parts~5 parts of 45 parts~50 parts, 4 parts~8 parts of mica powder, 4 parts~5 parts of oyster shell whiting and polystyrene foam.
Further, the parts by weight composition of insulation material is：48 parts of cement, 47 parts of flyash, 4 parts of exciting agent, marble
5 parts of powder, 6 parts of phenolic resin, 3 parts of urea-formaldehyde plastics, 0.5 part of rosin resin, 2 parts of alkylbenzenesulfonate, 1.5 parts of salt cullet,
4 parts of 18 parts of plaster of Paris, 48 parts of wood chip, 5 parts of mica powder, 5 parts of oyster shell whiting and polystyrene foam.
Further, wood chip is sawdust or wood shavings powder, and the particle diameter of wood chip is 1mm~2mm.
Further, exciting agent is FJ type exciting agents.
Further, alkylbenzenesulfonate is sodium alkyl benzene sulfonate.
Wherein each component is act as：
Cement is a kind of powdery hydraulicity inorganic coagulation material, add water stir after into slurry, can harden in atmosphere or
Preferably hardened in water, and can the materials such as sand, stone is cemented together securely, its cementation in insulation material.
Flyash be coal dust formed after high-temp combustion one kind like pozzolana mixed material.It is the generating of burning coal
Factory wears into coal less than 100 microns of coal dust, and spray into burner hearth with preheated air is burnt into suspended state, and generation is contaminated with largely not
The high-temperature flue gas of combustion things, flyash is just obtained through dust collect plant trapping.The chemical composition of flyash is similar to clayey, mainly
Composition is silica, alundum (Al2O3), di-iron trioxide, calcium oxide and uncompleted burned carbon.The adding coal ash in insulation material
Substantial amounts of cement and fine aggregate are saved；Reduce water consumption；Improve the workability of insulation material mix；Strengthen thermal insulating material
The pumpability of material；Reduce creeping for insulation material；Reduce the heat of hydration, heat energy dilatancy；Improve insulation material impermeability；Increase
Add the modified of insulation material.
Marble is mainly made up of calcite, lime stone, serpentine and dolomite, its main component based on calcium carbonate,
Account for more than 50%.Other also have magnesium carbonate, calcium oxide, manganese oxide and silica etc..The composition of cullet chemical oxide
For Na2O·CaO·6SiO2, main component is silica, is widely used in building, and marble dust and cullet are used for
Strengthen the hardness after insulation material solidification in insulation material.
Thermosetting plastics refers to solidify under heated or other conditions or the plastics with insoluble (molten) characteristic, the present invention
Using the main component of phenolic resin and urea-formaldehyde plastics as thermosets in insulation material, Lauxite cost is cheap, face
Color is shallow, hardness is high, oil resistant, anti-mildew, there is preferable insulating properties and temperature tolerance, and one important application of phenolic resin is exactly as viscous
Tie agent.Phenolic resin be it is a kind of multi-functional, with various organic and inorganic filler can be compatible material, design is correctly
Phenolic resin, wetting speed is especially fast, and can provide required mechanical strength, heat resistance for insulation material after cross-linking
Energy.
Gypsum is monoclinic system mineral, and main chemical compositions are calcium sulfate (CaSO4) hydrate.Gypsum is a kind of purposes
Extensive industrial materials and construction material, in the present invention for insulation material retarder.
Air entraining agent is concrete mix is introduced air during mixing and stirring and form a large amount of small, closings and stablize gas
The additive of bubble.Add insulation material as air entraining agent using rosin resin and alkylbenzenesulfonate in the present invention and using
During air chamber formation.
Wood chip can strengthen the heat-insulating property of insulation material, be auxiliary material important in the present invention.
Mica has higher dielectric strength and larger resistance, relatively low dielectric loss and arc resistant, Inverter fed motor etc.
Excellent dielectric properties, and quality is hard, high mechanical strength, and high temperature resistant and temperature drastically change and have acid and alkali-resistance etc. good
Physical and chemical performance, it is possible to increase the heat-insulated and fire resistance of insulation material.Oyster shell whiting particulate has unique cavity body structure, belongs to
Calcium carbonate, add the thermal insulation of insulation material.
Polystyrene foam plastics is based on polystyrene resin, adds the additives such as foaming agent and is made, it is mesh
A kind of preceding most commonly used padded coaming.Good with mechanical strength, shock-absorbing capacity is excellent；Processability is good, is readily molded into type；
The advantages that color is good, and thermal adaptability is strong, and radioresistance is excellent, cushioning effect is played in insulation material of the present invention.
Advantages of the present invention：
The present invention is green nontoxic, does not contain harmful composition, and applied widely, manufacturing cost is low, and material is protected
Temp effect is good, can persistently keep heat insulation effect, and rear difficult for drop-off, service life length is combined with wall.
Embodiment
It should be noted that in the case where not conflicting, the feature in embodiment and embodiment in the application can phase
Mutually combination.The present invention is described in detail below in conjunction with embodiment.
Embodiment 1
Cement 48kg, flyash 47kg, FJ type exciting agent 4kg, marble dust 5kg, phenolic resin 6kg, urea-formaldehyde plastics
3kg, rosin resin 0.5kg, sodium alkyl benzene sulfonate 2kg, cullet 1.5kg, plaster of Paris 18kg, the sawdust that particle diameter is 1mm
48kg, mica powder 5kg, oyster shell whiting 5kg and polystyrene foam 4kg.The proportioning of each component in this experimental example, prepared material
There is larger compression strength while insulation.
Embodiment 2
Cement 45kg, flyash 45kg, FJ type exciting agent 1kg, marble dust 1kg, phenolic resin 5kg, urea-formaldehyde plastics
1kg, rosin resin 0.2kg, alkylbenzenesulfonate 0.8kg, cullet 1kg, plaster of Paris 15kg, the sawdust that particle diameter is 1.5mm
45kg, mica powder 4kg, oyster shell whiting 4kg and polystyrene foam 3kg.The proportioning of each component in this experimental example, prepared material
There is preferable cubical contraction while insulation.
Embodiment 3
Cement 50kg, flyash 50kg, exciting agent 5kg, marble dust 5kg, phenolic resin 8kg, urea-formaldehyde plastics 5kg,
Rosin resin 0.5kg, alkylbenzenesulfonate 2kg, salt cullet 2kg, plaster of Paris 20kg, sawdust 50kg, the cloud that particle diameter is 2mm
Female powder 8kg, oyster shell whiting 5kg and polystyrene foam 5kg.The proportioning of each component in this experimental example, prepared material are being incubated
While there is preferable cubical contraction and tensile strength.
Embodiment 4
Cement 47.5kg, flyash 47.5kg, exciting agent 3kg, marble dust 3kg, phenolic resin 6.5kg, ureaformaldehyde modeling
Material 3kg, rosin resin 0.35kg, alkylbenzenesulfonate 1.4kg, salt cullet 1.5kg, plaster of Paris 17.5kg, particle diameter are
1.2mm sawdust 47.5kg, mica powder 6kg, oyster shell whiting 4.5kg and polystyrene foam 4kg.Each component matches somebody with somebody in this experimental example
Than prepared material has preferable cubical contraction and suitable dry density while insulation, has a wide range of application.
Embodiment 5
Cement 400g, flyash 400g, exciting agent 10g, marble dust 10g, thermosetting plastics 60g, rosin resin 2g,
The wood shavings powder 400g, mica powder 40g, shellfish that alkylbenzenesulfonate 8g, salt cullet 10g, plaster of Paris 150g, particle diameter are 1mm
Shell powder 40g and polystyrene foam 30g.The proportioning of each component in this experimental example, prepared material have while insulation
Preferable cubical contraction, built suitable for ice box.
Embodiment 6
Cement 500g, flyash 500g, exciting agent 80g, marble dust 80g, thermosetting plastics 160g, rosin resin
The wood shavings powder 500g, mica powder 80g, shellfish that 5g, alkylbenzenesulfonate 20g, salt cullet 20g, gypsum 250g, particle diameter are 2mm
Shell powder 50g and polystyrene foam 50g.The proportioning of each component in this experimental example, prepared material have while insulation
Preferable cubical contraction and tensile strength, suitable for the building of day and night temperature major region.
Embodiment 7
Cement 450g, flyash 450g, exciting agent 45g, marble dust 45g, thermosetting plastics 110g, rosin resin
3.5g, alkylbenzenesulfonate 14g, salt cullet 15g, gypsum 200g, wood chip 450g, mica powder 60g, oyster shell whiting 45g and polyphenyl
Vinyl foam 40g.The proportioning of each component in this experimental example, prepared material have preferable volume contraction while insulation
Rate and tensile strength, suitable for the building of day and night temperature major region.
Embodiment 8
Cement 200g, flyash 200g, exciting agent 10g, marble dust 10g, thermosetting plastics 20g, air entraining agent 10g,
Cullet 1g, plaster of Paris 50g, wood chip 200g, mica powder 10g, oyster shell whiting 10g and polystyrene foam 30g.In this experimental example
The proportioning of each component, prepared material has preferable cubical contraction and tensile strength while insulation, suitable for daytime
The building of night temperature difference major region.
Embodiment 9
Cement 500g, flyash 500g, exciting agent 80g, marble dust 80g, thermosetting plastics 160g, air entraining agent 50g,
Cullet 20g, plaster of Paris 250g, wood chip 500g, mica powder 80g, oyster shell whiting 50g and polystyrene foam 90g.This experimental example
The proportioning of middle each component, prepared material have preferable cubical contraction and tensile strength while insulation, are applied to
The building of cool region.
Embodiment 10
Cement 350g, flyash 350g, exciting agent 450g, marble dust 450g, thermosetting plastics 90g, air entraining agent
30g, cullet 1.1g, plaster of Paris 150g, wood chip 350g, mica powder 45g, oyster shell whiting 30g and polystyrene foam 60g.This
The proportioning of each component in experimental example, prepared material have preferable cubical contraction and tensile strength while insulation,
Suitable for the building of day and night temperature major region.
Test example 1
1st, performance data
This insulation material uses embodiment material as test sample, and national standard product is control, by test, as a result such as following table
It is shown.
The performance data of table 1
In summary, the prepared insulation material properties of present invention experiment are superior to national standard product material.
Test example 2
The heat insulation effect test of exterior wall heat-preserving system
1. the preparation of building exterior wall heat preserving system
To be coated 1 time using insulation back cover coating first in exterior wall surface, exterior-wall heat insulation back cover layer, thickness 200 are obtained
Micron, then coated 1~2 time using exterior-wall heat insulation basic unit cream on the outside of exterior-wall heat insulation back cover layer, obtain exterior-wall heat insulation basic unit, it is thick
Spend for 4mm, that is, obtain building exterior wall heat preserving system.
2. heat insulation effect is tested
1) subjects：Exterior wall heat-preserving system；Comparison other：The common coating decoration of wall
2) test method：
A. cubic tin one is taken, the outside construction outer wall heat preservation system coating in cubic some face of tin is (outer
Wall insulation back cover layer, exterior-wall heat insulation basic unit, exterior-wall heat insulation top coat layer), finally it is coated with common external wall waterproof finish paint 2 times.At this
The outside in another face of cubic tin corresponds to the common exterior coating of market of construction purchase, and Specific construction step and method are shown in
Table 2.
B. after the completion of conserving, water, 50 DEG C of constant temperature are added in cubic tin.
C. with infrared temperature Testing gun test constructed exterior wall heat-preserving system hull-skin temperature and test constructed it is general
The hull-skin temperature of logical wall finishing system, experimental result are shown in Table 3.
D. 20 ± 2 DEG C of test environment temperature, the closed environment of humidity 30%~70%.
The external wall construction of table 2 contrasts
| Material/operation | Construction thickness | Operation |
| The material of embodiment 1 | 30 microns | Apply 1 time |
| The material of embodiment 2 | 30 microns | Apply 1 time |
| The material of embodiment 3 | 30 microns | Apply 1 time |
| The material of embodiment 4 | 30 microns | Apply 1 time |
| The material of embodiment 5 | 30 microns | Apply 1 time |
| The material of embodiment 6 | 30 microns | Apply 1 time |
| The material of embodiment 7 | 30 microns | Apply 1 time |
| The material of embodiment 8 | 30 microns | Apply 1 time |
| The material of embodiment 9 | 30 microns | Apply 1 time |
| The material of embodiment 10 | 30 microns | Apply 1 time |
| National standard product material | 30 microns | Apply 1 time |
3) result of the test：
Result of the test is as shown in table 3 below.
The experimental result of table 3 contrasts (50 DEG C)
In summary, the prepared insulation material heat-insulating property of present invention experiment is better than national standard product material.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (8)
1. a kind of architecture exterior wall insulating materials, it is characterised in that the insulation material is by marble dust, cullet, thermosetting
Plastics, plaster of Paris, cement, flyash, exciting agent, air entraining agent, wood chip, mica powder, oyster shell whiting and polystyrene foam composition；
The parts by weight of material form：20 parts~50 parts of cement, 20 parts~50 parts of flyash, 1 part~8 parts of exciting agent, marble dust 1
Part~8 parts, 2 parts~16 parts of thermosetting plastics, 1 part~5 parts of air entraining agent, 0.1 part~2 parts of cullet, plaster of Paris 5 parts~25
Part, 20 parts~50 parts of wood chip, 1 part~8 parts of mica powder, 1 part~5 parts of oyster shell whiting and 3 parts~9 parts of polystyrene foam；It is described to draw
Gas agent is the mixture of rosin resin and alkylbenzenesulfonate；The ratio of air entraining agent composition is：Rosin resin accounts for air entraining agent
The 20% of gross weight, alkylbenzenesulfonate account for the 80% of air entraining agent gross weight.
2. a kind of architecture exterior wall insulating materials, it is characterised in that the parts by weight of insulation material, which form, is：40 parts~50 parts of cement,
40 parts~50 parts of flyash, 1 part~8 parts of exciting agent, 1 part~8 parts of marble dust, 6 parts~16 parts of thermosetting plastics, rosin tree
0.2 part~0.5 part of fat, 0.8 part~2 parts of alkylbenzenesulfonate, 1 part~2 parts of salt cullet, 15 parts~25 parts of plaster of Paris, wood
3 parts~5 parts of 40 parts~50 parts of bits, 4 parts~8 parts of mica powder, 4 parts~5 parts of oyster shell whiting and polystyrene foam.
3. insulation material according to claim 2, it is characterised in that the thermosetting plastics is moulded by phenolic resin and ureaformaldehyde
Material composition.
4. a kind of architecture exterior wall insulating materials, it is characterised in that the parts by weight of insulation material, which form, is：45 parts~50 parts of cement,
45 parts~50 parts of flyash, 1 part~5 parts of exciting agent, 1 part~5 parts of marble dust, 5 parts~8 parts of phenolic resin, urea-formaldehyde plastics 1
Part~5 parts, 0.2 part~0.5 part of rosin resin, 0.8 part~2 parts of alkylbenzenesulfonate, 1 part~2 parts of salt cullet, plaster of Paris
15 parts~20 parts, 45 parts~50 parts of wood chip, 4 parts~8 parts of mica powder, 4 parts~5 parts of oyster shell whiting and polystyrene foam 3 parts~5
Part.
5. insulation material according to claim 4, it is characterised in that the parts by weight of insulation material, which form, is：48 parts of cement,
47 parts of flyash, 4 parts of exciting agent, 5 parts of marble dust, 6 parts of phenolic resin, 3 parts of urea-formaldehyde plastics, 0.5 part of rosin resin, alkyl
2 parts of benzene sulfonate, 1.5 parts of salt cullet, 18 parts of plaster of Paris, 48 parts of wood chip, 5 parts of mica powder, 5 parts of oyster shell whiting and polystyrene
4 parts of foam.
6. insulation material according to claim 5, it is characterised in that the wood chip is sawdust or wood shavings powder, the wood
The particle diameter of bits is 1mm~2mm.
7. insulation material according to claim 5, it is characterised in that the exciting agent is FJ type exciting agents.
8. insulation material according to claim 5, it is characterised in that the alkylbenzenesulfonate is sodium alkyl benzene sulfonate.