CN106450500A - 一种铅酸胶体蓄电池电解质 - Google Patents

一种铅酸胶体蓄电池电解质 Download PDF

Info

Publication number
CN106450500A
CN106450500A CN201611096215.3A CN201611096215A CN106450500A CN 106450500 A CN106450500 A CN 106450500A CN 201611096215 A CN201611096215 A CN 201611096215A CN 106450500 A CN106450500 A CN 106450500A
Authority
CN
China
Prior art keywords
storage battery
colloid storage
battery electrolyte
acid
plumbic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201611096215.3A
Other languages
English (en)
Other versions
CN106450500B (zh
Inventor
汪建中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Wanlong Power Technology R&d Co Ltd
Original Assignee
Changshu Wanlong Power Technology R&d Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu Wanlong Power Technology R&d Co Ltd filed Critical Changshu Wanlong Power Technology R&d Co Ltd
Priority to CN201611096215.3A priority Critical patent/CN106450500B/zh
Publication of CN106450500A publication Critical patent/CN106450500A/zh
Application granted granted Critical
Publication of CN106450500B publication Critical patent/CN106450500B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铅酸胶体蓄电池电解质，包括如下重量百分比的组分：气相法二氧化硅10～20%、混合硫酸盐1～1.5%、磷酸2～5%、高分子稳定剂1～3%、超细玻璃纤维1～2%、碳纳米管0.5～1.5%、余量为浓硫酸溶液。本发明一种铅酸胶体蓄电池电解质，通过合理的原料选择和配方设计，使得电解质具有电池容量大、内阻小、不析水漏酸等优点，使用安全，有效提高了铅酸胶体蓄电池的使用寿命和使用安全性能。

Description

一种铅酸胶体蓄电池电解质
技术领域
本发明涉及蓄电池领域，特别是涉及一种铅酸胶体蓄电池电解质。
背景技术
铅酸蓄电池以其经济性在动力、通讯、电力等领域得到了广泛的应用。尤其是胶体铅酸蓄电池在结构上能够做到密封，在充放电时没有酸雾的发生，使用也更加方便。铅酸胶体蓄电池的电解质呈胶体状态，是一种性能更为优异的富液式密封蓄电池，是影响胶体蓄电池容量和循环寿命的关键因素。目前，胶体铅酸蓄电池的电解液主要是由一定量的硅溶胶或气相 SiO2分散在硫酸中形成的胶体。前者制备的电解质存在稳定性差、触变性不佳、易水化、易龟裂等缺点；后者成本较高，电解液的性能很大程度上取决于气相 SiO2的利用程度，而且用这种胶体灌注的蓄电池易出现电池容量低、内阻大、胶体易水化等问题。
发明内容
本发明主要解决的技术问题是提供一种铅酸胶体蓄电池电解质，能够解决现有铅酸胶体蓄电池存在的上述缺点。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种铅酸胶体蓄电池电解质，包括如下重量百分比的组分：气相法二氧化硅10～20%、混合硫酸盐1～1.5%、磷酸2～5%、高分子稳定剂1～3%、超细玻璃纤维1～2%、碳纳米管0.5～1.5%、浓硫酸溶液20～35%，余量为去离子水。
在本发明一个较佳实施例中，所述混合硫酸盐包括硫酸钴、硫酸钐和硫酸亚锡。
在本发明一个较佳实施例中，所述硫酸钴、硫酸钐和硫酸亚锡的质量比为1：1.5～2：1.5～2。
在本发明一个较佳实施例中，所述高分子稳定剂包括聚乙烯纯、聚丙烯酰胺和聚丙烯酸钾。
在本发明一个较佳实施例中，所述聚乙烯纯、聚丙烯酰胺和聚丙烯酸钾的质量比为2～3：1：1～2。
在本发明一个较佳实施例中，所述浓硫酸的质量浓度为40～55%。
本发明的有益效果是：本发明一种铅酸胶体蓄电池电解质，通过合理的原料选择和配方设计，使得电解质具有电池容量大、内阻小、不析水、不漏酸等优点，使用安全，有效提高了铅酸胶体蓄电池的使用寿命和使用安全性能。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明实施例包括：
实施例1
一种铅酸胶体蓄电池电解质，包括如下重量百分比的组分：气相法二氧化硅10%、混合硫酸盐1%、磷酸2%、高分子稳定剂1%、超细玻璃纤维1%、碳纳米管0.5%、质量浓度40～55%的浓硫酸溶液20%，余量为去离子水。
其中，所述混合硫酸盐包括质量比为1：1.5：1.5的硫酸钴、硫酸钐和硫酸亚锡；所述高分子稳定剂包括质量比为2：1：1的聚乙烯纯、聚丙烯酰胺和聚丙烯酸钾。
实施例2
一种铅酸胶体蓄电池电解质，包括如下重量百分比的组分：气相法二氧化硅20%、混合硫酸盐1.5%、磷酸5%、高分子稳定剂3%、超细玻璃纤维2%、碳纳米管1.5%、质量浓度40～55%的浓硫酸溶液35%，余量为去离子水。
其中，所述混合硫酸盐包括质量比为1：2：2的硫酸钴、硫酸钐和硫酸亚锡；所述高分子稳定剂包括质量比为3：1：2的聚乙烯纯、聚丙烯酰胺和聚丙烯酸钾。
上述电解质的凝胶时间短，0.5～1h，凝结后的质量好，表面均匀，有弹性，无液体析出。
由上述电解质制备的蓄电池，具有使用安全，自放电小、耐深放电性能优良、循环使用寿命长、内阻小、可靠性能突出等优点，且使用过程中无渗漏酸雾、酸液现象，使用安全环保。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (6)

1.一种铅酸胶体蓄电池电解质，其特征在于，包括如下重量百分比的组分：气相法二氧化硅10～20%、混合硫酸盐1～1.5%、磷酸2～5%、高分子稳定剂1～3%、超细玻璃纤维1～2%、碳纳米管0.5～1.5%、浓硫酸溶液20～35%，余量为去离子水。
2.根据权利要求1所述的铅酸胶体蓄电池电解质，其特征在于，所述混合硫酸盐包括硫酸钴、硫酸钐和硫酸亚锡。
3.根据权利要求2所述的铅酸胶体蓄电池电解质，其特征在于，所述硫酸钴、硫酸钐和硫酸亚锡的质量比为1：1.5～2：1.5～2。
4.根据权利要求1所述的铅酸胶体蓄电池电解质，其特征在于，所述高分子稳定剂包括聚乙烯纯、聚丙烯酰胺和聚丙烯酸钾。
5.根据权利要求4所述的铅酸胶体蓄电池电解质，其特征在于，所述聚乙烯纯、聚丙烯酰胺和聚丙烯酸钾的质量比为2～3：1：1～2。
6.根据权利要求1所述的铅酸胶体蓄电池电解质，其特征在于，所述浓硫酸的质量浓度为40～55%。
CN201611096215.3A 2016-12-02 2016-12-02 一种铅酸胶体蓄电池电解质 Active CN106450500B (zh)