CN106436445A - Preparation method of double-layer antimicrobial breathable tipping paper for cigarettes - Google Patents

Preparation method of double-layer antimicrobial breathable tipping paper for cigarettes Download PDF

Info

Publication number
CN106436445A
CN106436445A CN201610919074.4A CN201610919074A CN106436445A CN 106436445 A CN106436445 A CN 106436445A CN 201610919074 A CN201610919074 A CN 201610919074A CN 106436445 A CN106436445 A CN 106436445A
Authority
CN
China
Prior art keywords
paper
wood pulp
mixing
pulp
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610919074.4A
Other languages
Chinese (zh)
Other versions
CN106436445B (en
Inventor
吴迪
邹宇帆
徐越
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Quanzhou iron unique furniture Co., Ltd.
Original Assignee
吴迪
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 吴迪 filed Critical 吴迪
Priority to CN201610919074.4A priority Critical patent/CN106436445B/en
Publication of CN106436445A publication Critical patent/CN106436445A/en
Application granted granted Critical
Publication of CN106436445B publication Critical patent/CN106436445B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a preparation method of double-layer antimicrobial breathable tipping paper for cigarettes and belongs to the technical field of preparation of tipping paper for cigarettes. The method includes the steps that after masson pine wood pulp and birch wood pulp are beaten, the masson pine wood pulp, the birch wood pulp, talcum powder and the like are subjected to mixing and sheet papermaking treatment, dry paper is obtained through squeezing and drying for use, banan fibers and aqueous alkali are mixed, filter residues are obtained after suction filtration, after squeezing and aging, the filter residues and carbon disulfide are subjected to mixing and yellowing treatment, the mixture is mixed with the aqueous alkali, a banana viscose solution is prepared, and after the surface of the dry paper for use is coated with the banana viscose solution, the tipping paper for cigarettes is obtained through pressing and drying. The preparation method has the advantages that preparation steps are simple, no hair or powder shedding phenomenon is generated in the preparation process, and the problem that surface strength of finished paper is low is effectively solved; the tipping paper for cigarettes is high in breathability and has high printing suitability, and the antimicrobial rate reaches 95.6% or above.

Description

A kind of preparation method of the ventilative cigarette tipping paper of double-layer antimicrobial
Technical field
The preparation method of cigarette tipping paper the present invention relates to a kind of double-layer antimicrobial is breathed freely, belongs to cigarette tipping paper technology of preparing Field.
Background technology
With the continuous improvement of China's national life quality and level of consumption, the cigarette consumption idea of people becomes Change.On the premise of smoking consumption is ensured, people increasingly focus on the low evil of Medicated cigarette and health-care effect, and this is low harm cigarette Development with health promoting cigarette creates good condition.Cigarette body paper is used as the cigarette package of filter tipped cigarette mouth rod outer package Material, because its outward appearance is similar to Masson Pine stricture of vagina also known as tipping base paper, belongs to special industrial paper.Cigarette body paper is through printing（Apply Cloth）After cutting, become tipping paper, be commonly called as cork paper.Production cigarette body paper, water absorption on the one hand to paper, smooth Degree and physical strength have higher requirements, to meet typography and reach printing effect；On the other hand paper must also be ensured Porosity, improves the permeability of paper.Cigarette body paper is typically with masson pine（Generally softwood pulp, or A certain amount of jute pulp of adapted or hardwood pulp）For raw material, control beating degree, weight in wet base, AKD applying glue, using titanium dioxide, Calcium Carbonate Be filled with, with slurry after send long mesh paper making machine to be manufactured paper with pulp.But easy hair and powder dropping in preparation process, becomes paper surface strength to reduce, printability Can be deteriorated, air permeability is low, and antibiotic property is poor.
Content of the invention
The technical problem to be solved：For easy hair and powder dropping in current cigarette tipping paper preparation process, become paper Surface strength reduces, and printing quality is deteriorated, and air permeability is low, the drawbacks of antibiotic property difference, there is provided a kind of by masson's pine wood pulp, birch After wood pulp beating, after processing with compound sheets such as Pulvis Talci, standby through squeezing, the dry paper that must dry, then banana fiber is taken with alkali Solution mixes, and sucking filtration obtains filtering residue, through squeezing, after aging, process with Carbon bisulfide mixing yellow, then is mixed to prepare perfume (or spice) with aqueous slkali Any of several broadleaf plants viscose solution, be coated on standby dry paper surface after, repressed, dry cigarette tipping paper.Preparation process of the present invention Simply, in preparation process, no hair and powder dropping phenomenon occurs；Cigarette tipping paper surface strength height of the present invention, with preferable printability Energy and anti-microbial property, while with higher air permeability, be worthy to be popularized and use.
For solving above-mentioned technical problem, the present invention using technical scheme as described below is：
（1）200～300g masson's pine wood pulp and 150～200g birch wood pulp is weighed, being separately added in double-arc spline fiberizer is carried out Beating, it is 80～90% to be beaten to masson's pine wood pulp mass fraction, and it is 80 that beating degree is 60～70 ° of SR, birch pulp quality fraction ～90%, beating degree is 60～70 ° of SR, the masson's pine wood pulp after beating and birch wood pulp is mixed, is stirred 30～40min, obtain mixed Close wood pulp；
（2）Mixing 15～20% Pulvis Talci of pulp quality, 1～3% sun of mixing pulp quality is separately added into in above-mentioned mixing wood pulp Ionic starch and mixing 5～7% nano titanium oxide of pulp quality, after stirring 20～30min of mixing, are placed in handsheet in handsheet machine Processing, l Water Paper page is obtained, l Water Paper page is placed in hydraulic press, 30～50s is squeezed under 5～8MPa, after the completion of waiting to squeeze, put 20～30min is dry at 100～105 DEG C, paper must be dry, standby；
（3）Weigh 250～300g banana fiber, in mass ratio 1:5 with 25% sodium hydroxide solution hybrid infusion 60 of mass fraction～ 100min, subsequent sucking filtration obtains filtering residue, is put in squeezer, squeezes 25～35min, the filtering residue after squeezing is existed under 4～6MPa 20～25 DEG C of 3～5h of aging at temperature, add 28～30% Carbon bisulfide of filtering residue quality in the filtering residue after aging, and yellow processes 60 ～90min, obtains yellow thing, and by volume 1:10 add 5% sodium hydroxide solution of mass fraction, stirring mixing 20 in yellow thing ～30min, obtains Fructus Musae viscose solution；
（4）Above-mentioned Fructus Musae viscose solution is evenly applied to step（2）Standby dries paper surface, and coated weight is 120～150g/ m2, be put into after coating in paper machine, vacuum be 0.1～0.3kPa, pressing pressure be 4～6MPa under the conditions of, compacting 30～ 60s, dries after compacting complete, you can obtain the ventilative cigarette tipping paper of double-layer antimicrobial.
Double-layer antimicrobial obtained in the present invention breathes freely cigarette tipping paper machine direction tensile strength for 2.46～2.72kN m-1, breathe freely Spend for 2.450～2.862 μm（Pa·s）-1, it is 11.2～12.3% that percentage elongation is 1.92～2.08%, ash, and water absorption is 13.8～15.6g/m2, arsenic content≤0.8mg/kg, lead content≤4.5mg/kg, total plate count≤182cfu/g.
The present invention is compared with additive method, and Advantageous Effects are：
（1）Preparation process of the present invention is simple, and in preparation process, no hair and powder dropping phenomenon occurs, and efficiently solves into paper surface strength Reduction problem；
（2）Cigarette tipping paper air permeability height of the present invention, with stronger printing quality, antibiotic rate reaches more than 95.6%.
Specific embodiment
Weigh 200～300g masson's pine wood pulp and 150～200g birch wood pulp first, be separately added in double-arc spline fiberizer It is beaten, it is 80～90% to be beaten to masson's pine wood pulp mass fraction, and beating degree is 60～70 ° of SR, birch pulp quality fraction For 80～90%, beating degree is to mix 60～70 ° of SR, by the masson's pine wood pulp after beating and birch wood pulp, stirs 30～40min, Wood pulp must be mixed；State then up and in mixing wood pulp, be separately added into mixing 15～20% Pulvis Talci of pulp quality, mixing pulp quality 1～3% cationic starch and mixing 5～7% nano titanium oxide of pulp quality, after stirring 20～30min of mixing, are placed in handsheet machine Middle handsheet is processed, and obtains l Water Paper page, l Water Paper page is placed in hydraulic press, squeezes 30～50s under 5～8MPa, after the completion of waiting to squeeze, It is placed at 100～105 DEG C and 20～30min is dry, paper must be dry, standby；250～300g banana fiber is weighed again, by matter Amount compares 1:5 obtain filtering residue, are put into squeezer with 25% sodium hydroxide solution 60～100min of hybrid infusion of mass fraction, subsequent sucking filtration In, 25～35min is squeezed under 4～6kPa, by the filtering residue after squeezing in 20～25 DEG C of 3～5h of aging at temperature, to after aging 28～30% Carbon bisulfide of filtering residue quality is added in filtering residue, and yellow processes 60～90min, obtains yellow thing, by volume 1:10 to Huang 5% sodium hydroxide solution of mass fraction is added in compound, and stirring mixes 20～30min, obtains Fructus Musae viscose solution；Finally will be above-mentioned Fructus Musae viscose solution be evenly applied to standby dry paper surface, coated weight be2, it is put into after coating in paper machine, It is, under the conditions of 0.1～0.3MPa, pressing pressure is 4～6MPa, to suppress 30～60s in vacuum, dries after compacting complete, you can Obtain the ventilative cigarette tipping paper of double-layer antimicrobial.
Example 1
Weigh 200g masson's pine wood pulp and 150g birch wood pulp first, be separately added in double-arc spline fiberizer and be beaten, beating It is 80% to masson's pine wood pulp mass fraction, it is 80% that beating degree is 60 ° of SR, birch pulp quality fraction, beating degree is 60 ° of SR, Masson's pine wood pulp after beating and birch wood pulp are mixed, 30min is stirred, obtains mixing wood pulp；Stated in mixing wood pulp then up It is separately added into mixing 15% Pulvis Talci of pulp quality, mixing 1% cationic starch of pulp quality and 5% nanometer two of pulp quality of mixing Titanium oxide, after stirring mixing 20min, is placed in handsheet in handsheet machine and processes, obtain l Water Paper page, l Water Paper page is placed in hydraulic press, 30s is squeezed under 5MPa, after the completion of waiting to squeeze, be placed at 100 DEG C and 20min is dry, paper must be dry, standby；250g is weighed again Banana fiber, in mass ratio 1:5 obtain filtering residue, put with 25% sodium hydroxide solution hybrid infusion 60min of mass fraction, subsequent sucking filtration Enter in squeezer, 25min is squeezed under 4MPa, by the filtering residue after squeezing in 20 DEG C of aging at temperature 3h, in the filtering residue after aging 28% Carbon bisulfide of filtering residue quality is added, yellow processes 60min, yellow thing is obtained, by volume 1:10 add quality in yellow thing 5% sodium hydroxide solution of fraction, stirring mixing 20min, obtain Fructus Musae viscose solution；Finally above-mentioned Fructus Musae viscose solution is uniformly applied Be overlying on standby dry paper surface, coated weight be2, it is put into after coating in paper machine, is 0.1MPa in vacuum, compacting pressure Under the conditions of power is 4kPa, 30s is suppressed, dry after compacting complete, you can obtain the ventilative cigarette tipping paper of double-layer antimicrobial.System of the present invention Standby step is simple, and in preparation process, no hair and powder dropping phenomenon occurs, and efficiently solves into paper surface strength and reduces problem；Cigarette is with connecing Paper permeating degree height, with stronger printing quality, antibiotic rate reaches 95.69%；The ventilative cigarette tipping paper of obtained double-layer antimicrobial is indulged Zeeil tensile strength Z is 2.46kN m-1, air permeability be 2.450 μm（Pa·s）-1, it is 11.2% that percentage elongation is 1.92%, ash, Water absorption is 13.8g/m2, it is 4.5mg/kg that arsenic content is 0.8mg/kg, lead content, and total plate count is 182cfu/g.
Example 2
Weigh 250g masson's pine wood pulp and 175g birch wood pulp first, be separately added in double-arc spline fiberizer and be beaten, beating It is 85% to masson's pine wood pulp mass fraction, it is 85% that beating degree is 65 ° of SR, birch pulp quality fraction, beating degree is 65 ° of SR, Masson's pine wood pulp after beating and birch wood pulp are mixed, 35min is stirred, obtains mixing wood pulp；Stated in mixing wood pulp then up It is separately added into mixing 18% Pulvis Talci of pulp quality, mixing 2% cationic starch of pulp quality and 6% nanometer two of pulp quality of mixing Titanium oxide, after stirring mixing 25min, is placed in handsheet in handsheet machine and processes, obtain l Water Paper page, l Water Paper page is placed in hydraulic press, 40s is squeezed under 7MPa, after the completion of waiting to squeeze, be placed at 103 DEG C and 25min is dry, paper must be dry, standby；275g is weighed again Banana fiber, in mass ratio 1:5 obtain filtering residue, put with 25% sodium hydroxide solution hybrid infusion 80min of mass fraction, subsequent sucking filtration Enter in squeezer, 30min is squeezed under 5MPa, by the filtering residue after squeezing in 23 DEG C of aging at temperature 4h, in the filtering residue after aging 29% Carbon bisulfide of filtering residue quality is added, yellow processes 75min, yellow thing is obtained, by volume 1:10 add quality in yellow thing 5% sodium hydroxide solution of fraction, stirring mixing 25min, obtain Fructus Musae viscose solution；Finally above-mentioned Fructus Musae viscose solution is uniformly applied Be overlying on standby dry paper surface, coated weight be2, it is put into after coating in paper machine, is 0.2MPa in vacuum, compacting pressure Under the conditions of power is 5kPa, 45s is suppressed, dry after compacting complete, you can obtain the ventilative cigarette tipping paper of double-layer antimicrobial.System of the present invention Standby step is simple, and in preparation process, no hair and powder dropping phenomenon occurs, and efficiently solves into paper surface strength and reduces problem；Cigarette is with connecing Paper permeating degree height, with stronger printing quality, antibiotic rate reaches 95.75%；The ventilative cigarette tipping paper of obtained double-layer antimicrobial is indulged Zeeil tensile strength Z is 2.59kN m-1, air permeability be 2.648 μm（Pa·s）-1, it is 11.7% that percentage elongation is 2.01%, ash, Water absorption is 14.7g/m2, it is 4.1mg/kg that arsenic content is 0.7mg/kg, lead content, and total plate count is 179cfu/g.
Example 3
Weigh 300g masson's pine wood pulp and 200g birch wood pulp first, be separately added in double-arc spline fiberizer and be beaten, beating It is 90% to masson's pine wood pulp mass fraction, it is 90% that beating degree is 70 ° of SR, birch pulp quality fraction, beating degree is 70 ° of SR, Masson's pine wood pulp after beating and birch wood pulp are mixed, 40min is stirred, obtains mixing wood pulp；Stated in mixing wood pulp then up It is separately added into mixing 20% Pulvis Talci of pulp quality, mixing 3% cationic starch of pulp quality and 7% nanometer two of pulp quality of mixing Titanium oxide, after stirring mixing 30min, is placed in handsheet in handsheet machine and processes, obtain l Water Paper page, l Water Paper page is placed in hydraulic press, 50s is squeezed under 8MPa, after the completion of waiting to squeeze, be placed at 105 DEG C and 30min is dry, paper must be dry, standby；300g is weighed again Banana fiber, in mass ratio 1:5 obtain filtering residue, put with 25% sodium hydroxide solution hybrid infusion 100min of mass fraction, subsequent sucking filtration Enter in squeezer, 35min is squeezed under 6MPa, by the filtering residue after squeezing in 25 DEG C of aging at temperature 5h, in the filtering residue after aging 30% Carbon bisulfide of filtering residue quality is added, yellow processes 90min, yellow thing is obtained, by volume 1:10 add quality in yellow thing 5% sodium hydroxide solution of fraction, stirring mixing 30min, obtain Fructus Musae viscose solution；Finally above-mentioned Fructus Musae viscose solution is uniformly applied Be overlying on standby dry paper surface, coated weight be2, it is put into after coating in paper machine, is 0.3MPa in vacuum, compacting pressure Under the conditions of power is 6kPa, 60s is suppressed, dry after compacting complete, you can obtain the ventilative cigarette tipping paper of double-layer antimicrobial.System of the present invention Standby step is simple, and in preparation process, no hair and powder dropping phenomenon occurs, and efficiently solves into paper surface strength and reduces problem；Cigarette is with connecing Paper permeating degree height, with stronger printing quality, antibiotic rate reaches 96.05%；The ventilative cigarette tipping paper of obtained double-layer antimicrobial is indulged Zeeil tensile strength Z is 2.72kN m-1, air permeability be 2.862 μm（Pa·s）-1, it is 12.3% that percentage elongation is 2.08%, ash, Water absorption is 15.6g/m2, it is 3.9mg/kg that arsenic content is 0.6mg/kg, lead content, and total plate count is 175cfu/g.

Claims (1)

1. a kind of double-layer antimicrobial is breathed freely the preparation method of cigarette tipping paper, it is characterised in that concrete preparation process is：
（1）200～300g masson's pine wood pulp and 150～200g birch wood pulp is weighed, being separately added in double-arc spline fiberizer is carried out Beating, it is 80～90% to be beaten to masson's pine wood pulp mass fraction, and it is 80 that beating degree is 60～70 ° of SR, birch pulp quality fraction ～90%, beating degree is 60～70 ° of SR, the masson's pine wood pulp after beating and birch wood pulp is mixed, is stirred 30～40min, obtain mixed Close wood pulp；
（2）Mixing 15～20% Pulvis Talci of pulp quality, 1～3% sun of mixing pulp quality is separately added into in above-mentioned mixing wood pulp Ionic starch and mixing 5～7% nano titanium oxide of pulp quality, after stirring 20～30min of mixing, are placed in handsheet in handsheet machine Processing, l Water Paper page is obtained, l Water Paper page is placed in hydraulic press, 30～50s is squeezed under 5～8MPa, after the completion of waiting to squeeze, put 20～30min is dry at 100～105 DEG C, paper must be dry, standby；
（3）Weigh 250～300g banana fiber, in mass ratio 1:5 with 25% sodium hydroxide solution hybrid infusion 60 of mass fraction～ 100min, subsequent sucking filtration obtains filtering residue, is put in squeezer, squeezes 25～35min, the filtering residue after squeezing is existed under 4～6MPa 20～25 DEG C of 3～5h of aging at temperature, add 28～30% Carbon bisulfide of filtering residue quality in the filtering residue after aging, and yellow processes 60 ～90min, obtains yellow thing, and by volume 1:10 add 5% sodium hydroxide solution of mass fraction, stirring mixing 20 in yellow thing ～30min, obtains Fructus Musae viscose solution；
（4）Above-mentioned Fructus Musae viscose solution is evenly applied to step（2）Standby dries paper surface, and coated weight is 120～150g/ m2, be put into after coating in paper machine, vacuum be 0.1～0.3kPa, pressing pressure be 4～6MPa under the conditions of, compacting 30～ 60s, dries after compacting complete, you can obtain the ventilative cigarette tipping paper of double-layer antimicrobial.
CN201610919074.4A 2016-10-21 2016-10-21 A kind of double-layer antimicrobial is breathed freely the preparation method of cigarette tipping paper Expired - Fee Related CN106436445B (en)