CN106435933A - Infant cotton and hemp pinafore fabric structure - Google Patents
Infant cotton and hemp pinafore fabric structure Download PDFInfo
- Publication number
- CN106435933A CN106435933A CN201610862066.0A CN201610862066A CN106435933A CN 106435933 A CN106435933 A CN 106435933A CN 201610862066 A CN201610862066 A CN 201610862066A CN 106435933 A CN106435933 A CN 106435933A
- Authority
- CN
- China
- Prior art keywords
- cotton
- fiber
- flax fiber
- accounts
- baby
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an infant cotton and hemp pinafore fabric structure. The infant cotton and hemp pinafore fabric structure is formed by interweaving warp yarns and weft yarns, wherein the warp yarns are formed by blending and weaving cotton fibers and hemp fibers, the weft yarns are formed by blending and weaving cotton fibers and apocynum venetum fibers, the cotton fibers account for 72-88% and the hemp fibers account for 12-28% in the warp yarns, and the cotton fibers account for 65-70% and apocynum venetum fibers account for 30-35% in the weft yarns. An infant pinafore is obtained through warp and weft interweaving after cotton and hemp fiber blending, the fabric can have good hand feeling quality without follow-up finishing process, and the hemp fibers can be applied to infant pinafore processing and are mild and non-irritant to the tender skin of an infant, especially used in the skin wiping process after saliva of the infant is much or milk overflows or the infant regurgitates milk. The infant cotton and hemp pinafore fabric structure can help the infant to be in a good hygienic and healthy state, also has a certain antibacterial and anti-inflammatory effect and a skin discomfort relieving effect.
Description
Technical field：
The present invention relates to textile processing technical field, is specifically related to a kind of baby's linen-cotton Dribble towel fabric construction.
Background technology：
Dribble towel, also known as food meal pocket, Baby bibses, baby's muffler, is the infant article for making of waterproof material.Nascent
Baby due to salivary gland secretion function not perfect enough, salivation amount is few, so typically will not sialorrhea.After 4 months, saliva
Secretion increases, and after June, deciduous teeth start eruption, can stimulate gingiva epineural, increase with making salivary gland secretion reflexive, and now
Children swallow the ability of saliva and are not yet formed, and excessive saliva independently will not be flowed out from bicker side, because saliva slant acidity,
And containing some digestive enzyme and other materials, have certain stimulation to skin.
Flaxen fiber has the advantage that other fibers hardly match：With good moisture absorption wet dissipation and ventilative function, heat conduction
Heat is fast, nice and cool well-pressed, not next to the skin, quality of perspiring is light, strength is big, Vermins-proof mildew-proof, electrostatic are few, fabric is difficult pollution, tone is soft
The features such as excretion of generous, rough, suitable human body skin and secretion, liked by people, but its fiber of flaxen fiber is fibre
Cellulose fiber, basic chemical composition is cellulose, and other also have the non-fiber such as pectic substance, hemicellulose, lignin, fatty waxiness
Material (is referred to as " colloid "), and they are all together with cellulose association.Available fiber is taken out, is first had to itself and these
Colloid separates (referred to as degumming).In the chemical composition of various flaxen fibers, content of cellulose is all 75% or so, and comfortableness is poor, seldom
It is applied in infant use textile processing next to the skin.
Content of the invention：
The present invention is directed to the deficiencies in the prior art, provides a kind of fabric construction of cotton ramie blended spinning, and will be applied to baby children
Youngster's Dribble towel manufacture field, the skin tender to baby is gently non-stimulated, especially skin after the more or excessive milk spitting milk of baby's saliva
The wiping process of skin, can both help baby to keep good hygiene and health state, and act on certain inhibiting bacteria and diminishing inflammation,
Alleviate effect of skin discomfort.
For achieving the above object, the present invention is employed the following technical solutions：
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber blending woven is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 72-88%, and flax fiber accounts for 12-28%；
In described parallel, cotton fiber accounts for 65-70%, and apocynum fibre accounts for 30-35%.
Preferably, in described warp, cotton fiber accounts for 72-82%, and flax fiber accounts for 18-28%；
In described parallel, cotton fiber accounts for 65-68%, and apocynum fibre accounts for 32-35%.
Preferably, the flax fiber is that modified flax fiber, flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed in ferrum sulfuricum oxydatum solutum and is soaked 30-50 minute；
3rd step：Flax fiber after immersion is put into heating 3-5 minute in microwave oven；
4th step：Flax fiber is immersed in immersion 30-45 minute in Carbocisteine solution；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 60-90 minute.
Preferably, the apocynum fibre is that modified apocynum fibre, apocynum fibre method of modifying includes following step
Suddenly：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：Etherifying agent 2,3- epoxypropyltrimethylchloride chloride solution, stirring, liter will be added in apocynum fibre
Temperature, at a temperature of 30-50 DEG C, reacts 24-36 hour, adjusts PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Preferably, the flax fiber is scutched line.
Preferably, the mass concentration of the ferrum sulfuricum oxydatum solutum is 3-15%；
The mass concentration of the Carbocisteine solution is 2.5-3%.
Preferably, 2, the 3- epoxypropyltrimethylchloride chloride solution is that 2,3- epoxypropyltrimethylchloride chloride is water-soluble
Liquid, its mass concentration is 1-1.8%.
Cellulose is the main chemical composition of flaxen fiber, and the chemical structural formula of macromole is identical with cotton fiber, uses viscosimetry
Measure the degree of polymerization about 2000～2500 of ramee.The flaxen fiber that exists for of cellulose components provides three important changes
Performance is learned, its flaxen fiber to acquisition with spinning property is particularly significant：The acidic hydrolysises performance, the alkalescence of cellulose of cellulose
Degraded and alkali cellulose are generated, the oxidation of cellulose.
Flaxen fiber is a kind of high-tenacity low-elongation fiber, and its fracture strength is that (cotton fiber is 2.6- to 5.0-7.0cN/dtex
4.5, silkworm silk is 3.0-3.5).This is primarily due to flaxen fiber and is mainly phloem fiber, and phloem fiber is the basic bone of plant
Frame, has higher degree of crystallinity and the degree of orientation, and fibril is radially distributed in layer structure along fiber again.For example Caulis et Folium Lini has 90%
Degree of crystallinity and be close to 80% the degree of orientation.Just because of it has so high degree of crystallinity and the degree of orientation, flaxen fiber is made to become all
Fibre breakage splits the minimum fiber of percentage elongation；In addition, this construction features makes flaxen fiber obtain very big initial moduluss, than
Cotton fiber is high 1.5-2.0 times, and higher than silkworm silk 3 times, higher than wool fiber 8-10 times, therefore flaxen fiber is harder, does not deform easily；
But while also making flaxen fiber become the very poor fiber of elastic recovery rate, even if only 2% deformation, elastic recovery rate also only has
48%, and cotton fiber, with wool fiber in mutually an equal amount of deformation, elastic recovery rate can reach 74% and 99.
Flaxen fiber is applied in the processing of infant Dribble towel, needs to overcome its coarse fiber texture and elastic recovery rate
Low, the problem of comfortableness difference, the present invention improves the compliance of cotton fibriia, for baby mouth by blending and modified method
More enzyme content in water and acid pungent play good corrosion-resistant effect, while giving infant skin by wiping
Good bacteriostasis antibiosis effect, alleviates the redness discomfort for causing on infant skin top layer as saliva is covered, with higher reality
The property used.
The invention has the advantages that：
(1) present invention improves the compliance of cotton fibriia, for more in baby's saliva by blending and modified method
Enzyme content and acid pungent play good corrosion-resistant effect, while giving infant skin good suppression by wiping
Bacterium antibacterial effect, alleviates the redness discomfort for causing on infant skin top layer as saliva is covered, with higher practicality.
(2) present invention Dribble towel for baby is through knitting device after cotton fiber with flax fiber blending, it is not necessary to through follow-up
Arrangement process just can give fabric good hand feeling quality, and flaxen fiber is applied in the processing of baby's Dribble towel, for baby
Tender skin is gently non-stimulated, and especially after the more or excessive milk spitting milk of baby's saliva, the wiping process of skin, can both help
Baby keeps good hygiene and health state, and acts on certain inhibiting bacteria and diminishing inflammation, alleviates effect of skin discomfort.
(3) raw material green of the present invention is easy to get, and processing method is simply efficient, and finished product has good natural colour, it is not necessary to
Later stage bleaching or dyeing both can reduce power consumption of polymer processing with certain natural aesthetic feeling, improve the economic benefit of processing.
(4) fabric of the present invention can significantly improve the corrosivity of its mouthful of water after longitude and latitude establishment, increase its service life,
There is higher market popularization value.
(5) fabric construction preparation method of the present invention is simple, fabric just can be given without the arrangement processing by the later stage
Good bacteriostasis antibiosis effect.
Specific embodiment：
In order to be better understood from the present invention, below by embodiment, the present invention is further described, and embodiment is served only for solution
The present invention is released, any restriction will not be constituted to the present invention.
Embodiment 1
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 72%, and flax fiber accounts for 28%；
In described parallel, cotton fiber accounts for 65%, and apocynum fibre accounts for 35%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 30 minutes 3%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 3 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration soaks 30 points 2.5%) in being
Clock；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 60 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1%), stirring, heats up, at a temperature of 30 DEG C DEG C, reacts 24 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Embodiment 2
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 88%, and flax fiber accounts for 12%；
In described parallel, cotton fiber accounts for 70%, and apocynum fibre accounts for 30%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 50 minutes 15%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 5 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration is soaked 45 minutes 3%) in being；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 90 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1.8%), stirring, heats up, at a temperature of 50 DEG C, reacts 36 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Embodiment 3
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 72%, and flax fiber accounts for 28%；
In described parallel, cotton fiber accounts for 65%, and apocynum fibre accounts for 35%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 40 minutes 5%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 3 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration is soaked 35 minutes 3%) in being；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 90 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1.8%), stirring, heats up, at a temperature of 40 DEG C, reacts 24 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Embodiment 4
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 82%, and flax fiber accounts for 18%；
In described parallel, cotton fiber accounts for 68%, and apocynum fibre accounts for 32%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 40 minutes 10%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 5 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration is soaked 40 minutes 3%) in being；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 80 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1.5%), stirring, heats up, at a temperature of 40 DEG C, reacts 30 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Embodiment 5
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 75%, and flax fiber accounts for 25%；
In described parallel, cotton fiber accounts for 68%, and apocynum fibre accounts for 32%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 45 minutes 13%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 4 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration soaks 35 points 2.8%) in being
Clock；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 70 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1.2%), stirring, heats up, at a temperature of 40 DEG C, reacts 29 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Embodiment 6
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 78%, and flax fiber accounts for 22%；
In described parallel, cotton fiber accounts for 67%, and apocynum fibre accounts for 33%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 40 minutes 12%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 5 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration soaks 45 points 2.5%) in being
Clock；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 80 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1-1.8%), stirring, heat up, at a temperature of 35 DEG C, react 30 hours, after cooling with 1mol/L HCl adjust PH in
Property；
3rd step：Dry and dry.
Embodiment 7
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 82%, and flax fiber accounts for 18%；
In described parallel, cotton fiber accounts for 68%, and apocynum fibre accounts for 32%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 50 minutes 8%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 4 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration soaks 45 points 2.8%) in being
Clock；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 60 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1.5%), stirring, heats up, at a temperature of 30 DEG C, reacts 36 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Embodiment 8
A kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, and described warp is by cotton fibre
Peacekeeping flax fiber (scutched line) braiding is formed, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
In described warp, cotton fiber accounts for 72%, and flax fiber accounts for 18%；
In described parallel, cotton fiber accounts for 65%, and apocynum fibre accounts for 35%.
Wherein flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed ferrum sulfuricum oxydatum solutum, and (mass concentration is soaked 50 minutes 14%) in being；
3rd step：Flax fiber after immersion is put in microwave oven and is heated 5 minutes；
4th step：Flax fiber is immersed in Carbocisteine solution, and (mass concentration soaks 30 points 2.5%) in being
Clock；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 90 minutes.
Apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：By etherifying agent 2,3- epoxypropyltrimethylchloride chloride aqueous solution is added in apocynum fibre, (quality is dense
Spend for 1.8%), stirring, heats up, at a temperature of 50 DEG C, reacts 24 hours, adjust PH to neutrality with 1mol/L HCl after cooling；
3rd step：Dry and dry.
Comparative example 1
The fabric construction that is mutually worked out by warp and parallel, in described warp, cotton fiber accounts for 72%, flax fiber
Account for 18%；In described parallel, cotton fiber accounts for 65%, and apocynum fibre accounts for 35%.
Wherein cotton fiber and flax fiber, apocynum fibre are natural fiber, without arrangement.
Comparative example 2
The fabric construction that is mutually worked out by warp and parallel, in described warp, cotton fiber accounts for 72%, flax fiber
Account for 18%；In described parallel, cotton fiber accounts for 65%, and apocynum fibre accounts for 35%.
Wherein cotton fiber and flax fiber are natural fiber, without arrangement, the modification process of apocynum fibre
With reference to 8 method of embodiment.
Comparative example 3
The fabric construction that is mutually worked out by warp and parallel, in described warp, cotton fiber accounts for 72%, flax fiber
Account for 18%；In described parallel, cotton fiber accounts for 65%, and apocynum fibre accounts for 35%.
Wherein cotton fiber and Herba Apocyni veneti are natural fiber, without arrangement, the modification process reference of flax fiber
8 method of embodiment.
Comparative example 4
Pure cotton fabric.
Comparative example 5
The fabric construction that is mutually worked out by warp and parallel, described warp is flax fiber；Described parallel is
Apocynum fibre, fiber is all without arrangement.
Fabric described in above-described embodiment and comparative example was given baby volunteer using 7-10 days, is counted which and use rear skin
The red and swollen uncomfortable number of times for occurring, while by the method for sensory evaluation, its comfortableness and flexibility are evaluated, with comparative example 4
The comfortable feel of pure cotton fabric and flexibility be that 10 parts, the fabric feeling of comparative example 5 and flexibility carry out sense organ for 1 point and comment
Valency.
Table one：Fabric improves situation and feel and flexible appraisal for the discomfort of infant skin
| Skin discomfort % | Feel | Flexibility | |
| Embodiment 1 | 0 | 10 | 10 |
| Embodiment 2 | 0 | 10 | 9 |
| Embodiment 3 | 0 | 10 | 10 |
| Embodiment 4 | 0 | 10 | 9 |
| Embodiment 5 | 0 | 10 | 10 |
| Embodiment 6 | 0 | 10 | 10 |
| Embodiment 7 | 0 | 10 | 10 |
| Embodiment 8 | 0 | 10 | 10 |
| Comparative example 1 | 13 | 6 | 7 |
| Comparative example 2 | 8 | 7 | 7 |
| Comparative example 3 | 12 | 8 | 6 |
| Comparative example 4 | 36 | 10 | 10 |
| Comparative example 5 | 12 | 1 | 1 |
The Dribble towel fabric construction that the embodiment of the present invention is prepared has feel and the flexibility for being close to pure cotton fabric, with
When take into account specific to flaxen fiber and breathe freely and antibacterial bacteriostatic performance, for skin discomfort, there is certain and mitigation.
The structure that the present invention is worked out by composite fibre longitude and latitude mutually, improves the comfortableness of fabric, and it is good to give which
Biocidal property, alleviate infant skin discomfort, can preferably improve its comfortableness and hand feeling quality by modified, have
Prominent substantive distinguishing features and significant progress.
Collect baby's saliva to soak fabric, the loss in mechanical strength for testing fiber under room temperature leads.
Table two：Fabric corrosion resistance tests (strength loss %)
| Time | 0h | 24h | 48h |
| Embodiment 1 | 0 | 3.45 | 16.16 |
| Embodiment 2 | 0 | 3.72 | 19.44 |
| Embodiment 3 | 0 | 4.46 | 16.74 |
| Embodiment 4 | 0 | 3.69 | 16.90 |
| Embodiment 5 | 0 | 3.89 | 19.85 |
| Embodiment 6 | 0 | 3.39 | 14.98 |
| Embodiment 7 | 0 | 3.39 | 15.74 |
| Embodiment 8 | 0 | 3.97 | 13.81 |
| Comparative example 1 | 0 | 4.68 | 25.91 |
| Comparative example 2 | 0 | 6.42 | 30.59 |
| Comparative example 3 | 0 | 5.12 | 19.68 |
| Comparative example 4 | 0 | 35.14 | 62.14 |
| Comparative example 5 | 0 | 44.35 | 84.18 |
Longitude and latitude establishment is carried out through the mode of the present invention, can effectively alleviate the corrosion resistance of fabric, fabric is more textile to be knitted
For thing or pure linen, corrosion resistance is obviously improved.
Claims (7)
1. a kind of baby's linen-cotton Dribble towel fabric construction, is mutually woven by warp and parallel and forms, it is characterised in that：Described warp
Line is formed by cotton fiber and flax fiber blending woven, and described parallel is formed by cotton fiber and apocynum fibre blending woven；
Wherein, in described warp, cotton fiber accounts for 72-88%, and flax fiber accounts for 12-28%；In described parallel, cotton fiber accounts for 65-
70%, apocynum fibre accounts for 30-35%.
2. a kind of baby's linen-cotton Dribble towel fabric construction according to claim 1, it is characterised in that：Cotton in described warp
Fiber accounts for 72-82%, and flax fiber accounts for 18-28%；In described parallel, cotton fiber accounts for 65-68%, and apocynum fibre accounts for 32-
35%.
3. a kind of baby's linen-cotton Dribble towel fabric construction according to claim 1 and 2, it is characterised in that Caulis et Folium Lini fibre
Tie up as modified flax fiber, flax fiber method of modifying is comprised the following steps：
The first step：Shredding process is carried out to flax fiber, removes debris；
Second step：Flax fiber is immersed in ferrum sulfuricum oxydatum solutum and is soaked 30-50 minute；
3rd step：Flax fiber after immersion is put into heating 3-5 minute in microwave oven；
4th step：Flax fiber is immersed in immersion 30-45 minute in Carbocisteine solution；
5th step：The flax fiber of gained is washed with clear water to neutrality；
6th step：Dry 60-90 minute.
4. a kind of baby's linen-cotton Dribble towel fabric construction according to claim 1 and 2, it is characterised in that the Herba Apocyni veneti
Fiber is modified apocynum fibre, and apocynum fibre method of modifying is comprised the following steps：
The first step：Shredding process is carried out to apocynum fibre, removes debris；
Second step：Etherifying agent 2,3- epoxypropyltrimethylchloride chloride solution will be added in apocynum fibre, stir, heat up,
At a temperature of 30-50 DEG C, 24-36 hour being reacted, after cooling, PH is adjusted to neutrality with 1mol/L HCl；
3rd step：Dry and dry.
5. a kind of baby's linen-cotton Dribble towel fabric construction according to claim 1 and 2, it is characterised in that：Caulis et Folium Lini fibre
Tie up as scutched line.
6. a kind of baby's linen-cotton Dribble towel fabric construction according to claim 3, it is characterised in that：The ferrum sulfuricum oxydatum solutum
Mass concentration be 3-15%；The mass concentration of the Carbocisteine solution is 2.5-3%.
7. a kind of baby's linen-cotton Dribble towel fabric construction according to claim 4, it is characterised in that：2, the 3- epoxy third
Base trimethyl ammonia chloride ammonium salt solution is 2,3- epoxypropyltrimethylchloride chloride aqueous solution, and its mass concentration is 1-1.8%.