CN106435659A - 一种电镀锌用光亮剂 - Google Patents
一种电镀锌用光亮剂 Download PDFInfo
- Publication number
- CN106435659A CN106435659A CN201611047870.XA CN201611047870A CN106435659A CN 106435659 A CN106435659 A CN 106435659A CN 201611047870 A CN201611047870 A CN 201611047870A CN 106435659 A CN106435659 A CN 106435659A
- Authority
- CN
- China
- Prior art keywords
- brightener
- electro
- galvanizing
- dichlorobenzaldehyde
- carboxylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种电镀锌用光亮剂,其特征在于其配方组分按照质量百分比为:1‑苄基吡啶嗡‑3‑羧酸盐49%‑51%、氯化胆碱19%‑21%、尿素14%‑16%、2.4‑二氯苯甲醛14%‑16%。本发明解决碱性电镀锌锌镀层光亮的问题,从而解决目前酸性电镀锌对设备腐蚀严重的问题。
Description
技术领域
本发明涉及电镀领域,具体涉及一种电镀锌用光亮剂。
技术背景
锌镀层具有抗腐蚀、无毒性和可焊性,被广泛应用于各工业领域,特别是电子工业领域。由于对六价铬、镉等重金属的限制,镀锌工业得到更加广泛的应用。目前的电镀锌工艺基本上都采用酸性镀锌工艺,该工艺有对设备腐蚀严重的问题。碱性镀锌解决了酸性镀锌的对设备的腐蚀问题,但是目前碱性电镀锌工艺得到的锌镀层光亮性差而一直没有得到广泛的应用。
有鉴于上述的缺陷,本设计人,积极加以研究创新,以期创设一种电镀锌用光亮剂,使其更具有产业上的利用价值。
发明内容
为解决上述技术问题,本发明的目的是提供一种电镀锌用光亮剂。
本发明的技术方案如下:
一种电镀锌用光亮剂,其特征在于其配方组分按照质量百分比为:1-苄基吡啶嗡-3-羧酸盐49%-51%、氯化胆碱19%-21%、尿素14%-16%、2.4-二氯苯甲醛14%-16%。
一种电镀锌用光亮剂的制备方法,其特征在于:将1-苄基吡啶嗡-3-羧酸盐、氯化胆碱、尿素、2.4-二氯苯甲醛加入到反应釜中混合后搅拌均匀,再按400~500ml/L的比例加入质量分数40%的氢氧化钠溶液,调节pH值达到6.5~7.0,加温至70~75℃,保温1个小时后降至室温,通过过滤机进行过滤,再将过滤后的沉淀物料加入甩干机中进行甩干,再放入烘干机中进行烘干,即制的光亮剂成品。
借由上述方案,本发明至少具有以下优点:
本发明的有益效果是:解决碱性电镀锌锌镀层光亮的问题,从而解决目前酸性电镀锌对设备腐蚀严重的问题。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步详细描述。以下实施例用于说明本发明,但不用来限制本发明的范围。
实施例1
按照1-苄基吡啶嗡-3-羧酸盐51%、氯化胆碱21%、尿素14%、2.4-二氯苯甲醛14%的质量百分比加入到反应釜中混合后搅拌均匀,再按500ml/L的比例加入质量分数40%的氢氧化钠溶液,调节pH值达到7.0,加温至75℃,保温1个小时后降至室温,通过过滤机进行过滤,再将过滤后的沉淀物料加入甩干机中进行甩干,再放入烘干机中进行烘干,即制的光亮剂成品。
实施例2
按照1-苄基吡啶嗡-3-羧酸盐49%、氯化胆碱19%、尿素16%、2.4-二氯苯甲醛16%的质量百分比加入到反应釜中混合后搅拌均匀,再按400ml/L的比例加入质量分数40%的氢氧化钠溶液,调节pH值达到6.5,加温至70℃,保温1个小时后降至室温,通过过滤机进行过滤,再将过滤后的沉淀物料加入甩干机中进行甩干,再放入烘干机中进行烘干,即制的光亮剂成品。
实施例3
按照1-苄基吡啶嗡-3-羧酸盐50%、氯化胆碱20%、尿素15%、2.4-二氯苯甲醛15%的质量百分比加入到反应釜中混合后搅拌均匀,再按450ml/L的比例加入质量分数40%的氢氧化钠溶液,调节pH值达到6.8,加温至72℃,保温1个小时后降至室温,通过过滤机进行过滤,再将过滤后的沉淀物料加入甩干机中进行甩干,再放入烘干机中进行烘干,即制的光亮剂成品。
本发明的有益效果是:解决碱性电镀锌锌镀层光亮的问题,从而解决目前酸性电镀锌对设备腐蚀严重的问题。
以上所述仅是本发明的优选实施方式,并不用于限制本发明,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和变型,这些改进和变型也应视为本发明的保护范围。
Claims (2)
1.一种电镀锌用光亮剂,其特征在于其配方组分按照质量百分比为:1-苄基吡啶嗡-3-羧酸盐49%-51%、氯化胆碱19%-21%、尿素14%-16%、2.4-二氯苯甲醛14%-16%。
2.一种电镀锌用光亮剂的制备方法,其特征在于:将1-苄基吡啶嗡-3-羧酸盐、氯化胆碱、尿素、2.4-二氯苯甲醛加入到反应釜中混合后搅拌均匀,再按400~500ml/L的比例加入质量分数40%的氢氧化钠溶液,调节pH值达到6.5~7.0,加温至70~75℃,保温1个小时后降至室温,通过过滤机进行过滤,再将过滤后的沉淀物料加入甩干机中进行甩干,再放入烘干机中进行烘干,即制的光亮剂成品。