CN106433280A - Nanometer negative ion environmental-protection coating - Google Patents
Nanometer negative ion environmental-protection coating Download PDFInfo
- Publication number
- CN106433280A CN106433280A CN201510477002.4A CN201510477002A CN106433280A CN 106433280 A CN106433280 A CN 106433280A CN 201510477002 A CN201510477002 A CN 201510477002A CN 106433280 A CN106433280 A CN 106433280A
- Authority
- CN
- China
- Prior art keywords
- parts
- nanometer
- protection coating
- environmental
- negative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a nanometer negative ion environmental-protection coating, which is characterized by being prepared from the following components in parts by weight: 10 to 30 parts of emulsion, 10 to 50 parts of deionized water, 1 to 5 parts of negative ion additive, 15 to 25 parts of titanium dioxide, 0.5 to 5 parts of accessory ingredient, and 1 to 15 parts of filler. When being coated in any indoor site, the nanometer negative ion environmental-protection coating not only achieves a decorative effect, but also can durably and effectively adsorb indoor air pollutants, releases a large number of negative oxygen ions at the same time for cleaning air, and builds a healthy environment of a natural air anion bar indoors completely for comprehensively caring life health of people. The nanometer negative ion environmental-protection coating provided by the invention is beneficial to durably improving the indoor environment, purifying indoor air, bacterium-resisting, disinfecting, purifying volatile organic cancerogens such as formaldehyde, methylbenzene, benzene, sulphur and ammonia indoors, and removing peculiar smells such as stinks, musty taste and smoke flavor; can durably release the negative oxygen ions for building the natural air anion bar indoors, and has a health-care effect for making people healthier; can effectively adsorb for a long time and settle particulate pollution of PM2.5 (Particulate Matter2.5) entering indoor from outdoor so as to enable people to escape from an outdoor haze air environment.
Description
Technical field
The present invention relates to nanometer, negative-ion, environmental-protection coating.
Background technology
In modern society, all one's life of people averagely has more than 60% time and spends indoors, and this ratio is high in city
Reach 80%.Therefore, the relation of IAQ (indoor air quality) and health very closely that is to say, that：The living environment of people, determines
The health of people！
Generally, room air pollution mainly includes this several big class：
First, gas pollutant
1st, carbon monoxide, nitrogen oxides and the strong carcinogen that such as stir-frying in kitchen produces.
2nd, the poisonous and harmful substance that house decorative material, cosmetics, furniture etc. distribute, such as formaldehyde, propylene are fine, ether-ether class, three
Volatile organic matters such as vinyl chloride etc..
3rd, the carbon dioxide (500 liters/day/people) of human body exhalation itself and the lactic acid Organic substance that distributes of skin etc..
4th, cigarette smell, according to surveying and determination, on the damage ratio road of an indoor cigarette, the pollution of an automobile is also big to people's harm.
2nd, microorgranic contaminant
As the microorganism pollution air such as antibacterial, pollen, dust mite, funguses.
3rd, outdoor contaminated air
As haze gets in (especially in the northern area of China) by window.
The superposition of this several pollutant above, cause China's majority cities living environment as office, market, family room,
The pollution of the room airs such as school, kindergarten, has a strong impact on the healthy of people.
How to dispel indoor pollutant, improve IAQ (indoor air quality), ensure that people's is healthy, be always that people want with the modern times
The great livelihood issues that technological meanses, modern science and technology material solve.
Content of the invention
An object of the present invention is to overcome deficiency of the prior art, providing a kind of nano-negative ion reducing indoor pollution
Environmental protection coating material.
For realizing object above, the present invention is achieved through the following technical solutions：
Nanometer, negative-ion, environmental-protection coating is it is characterised in that include component according to weight portion：Emulsion 10-30 part；Deionized water 10-50
Part；Anionic additive 1-5 part, titanium dioxide 15-25 part；Auxiliary agent 0.5-5 part；Filler 1-15 part.
According to a preferred embodiment of the invention, described auxiliary agent is selected from dispersant 0.1-0.5 part, wetting agent 0.05-0.3 part, froth breaking
Agent 0.1-1.0 part, thickening agent 0.5-1.0 part, one or more of antibacterial 0.05-0.5 part.
According to a preferred embodiment of the invention, also include cellulose 0.05-5 part.
According to a preferred embodiment of the invention, described filler is selected from one or more of Kaolin 2-7 part and mica powder 1-5 part.
According to a preferred embodiment of the invention, described anionic additive is selected from tourmaline powder, rare earth element, kieselguhr, Gu Hai
One or more of rock, gull rock.
According to a preferred embodiment of the invention, described rare earth element be selected from bastnasite, monazite, phosphorus yttrium stone, euxenite,
One or more of gadolinite, cerine, cerite.
According to a preferred embodiment of the invention, described anionic additive is selected from tourmaline powder and rare earth element, described rare earth element
With the weight of tourmaline than for 1-3：1.
According to a preferred embodiment of the invention, described anionic additive particle diameter is 50-1000 nanometer.
Nanometer, negative-ion, environmental-protection coating in the present invention, brushing, in any interior place, had both been played decorative effect, and can persistently have been had again
Effect absorption indoor air pollutants, discharge a large amount of negative oxygen ions, fresh air simultaneously, make interior be completely in a natural oxygen-bar
Health environment, take good care of the life and health of people comprehensively.Lasting improvement indoor environment in the present invention, purifies the air of a room, and resists
Bacterium is sterilized, and purifies and occupies the volatility organic carcinogen such as indoor formaldehyde, toluene, benzene, sulfur, ammonia, dispels stink, musty, oil smoke
The abnormal flavour such as taste.Persistency releasing negative oxygen ion, builds indoor natural oxygen-bar, has oxygen and gives birth to health maintenance effect, the body making one is more
Health.Permanently effective absorption, settles the dust pollution of the PM2.5 being got in by outdoor, allows people to hide empty from outdoor haze
Compression ring border.
Specific embodiment
Embodiment 1
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：10 parts of emulsion；10 parts of deionized water；Anion adds
Plus 1 part of agent, 15 parts of titanium dioxide；0.1 part of dispersant, 0.05 part of wetting agent, 0.1 part of defoamer, 0.5 part of thickening agent,
In 0.05 part of antibacterial, 0.05 part of cellulose；2 parts of Kaolin, 1 part of mica powder.Anionic additive particle diameter is 50-100
The kieselguhr of nanometer.
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：Emulsion 10-30 part；Deionized water 10-50 part；Bear from
Sub- additive 1-5 part, titanium dioxide 15-25 part；Dispersant 0.1-0.5 part, wetting agent 0.05-0.3 part, defoamer 0.1-1.0
Part, thickening agent 0.5-1.0 part, antibacterial 0.05-0.5 part, cellulose 0.05-5 part, Kaolin 2-7 part and mica powder 1-5
Part, anionic additive particle diameter is the kieselguhr of 50-100 nanometer.
Embodiment 2
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：30 parts of emulsion；50 parts of deionized water；Anion adds
5 parts of agent, 25 parts of titanium dioxide；0.5 part of dispersant, 0.3 part of wetting agent, 1.0 parts of defoamer, 1.0 parts of thickening agent, sterilization
0.5 part of agent, 5 parts of cellulose, 7 parts of Kaolin, 5 parts of mica powder, anionic additive is selected from the sea-gull of 100-200 nanometer
Stone.
Embodiment 3
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：20 parts of emulsion；30 parts of deionized water；Anion adds
3 parts of agent, 20 parts of titanium dioxide；0.3 part of dispersant, 0.2 part of wetting agent, 0.5 part of defoamer, 0.8 part of thickening agent, sterilization
0.2 part of agent, 2 parts of cellulose, 3 parts of Kaolin and 2 parts of mica powder, it is 500-1000 that described anionic additive is selected from particle diameter
The kieselguhr of nanometer.
Embodiment 4
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：28 parts of emulsion；13 parts of deionized water；Anion adds
2 parts of agent, 17 parts of titanium dioxide；0.15 part of dispersant, 0.1 part of wetting agent, 1.0 parts of defoamer, 0.8 part of thickening agent, kills
0.05 part of microbial inoculum, 0.8 part of cellulose, 2 parts of Kaolin, 5 parts of mica powder.It is 200-300 that anionic additive is selected from particle diameter
The kieselguhr of nanometer.
Embodiment 5
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：25 parts of emulsion；50 parts of deionized water；Anion adds
4 parts of agent, 15 parts of titanium dioxide；0.2 part of dispersant, 0.3 part of wetting agent, 0.3 part of defoamer, 0.6 part of thickening agent, sterilization
0.09 part of agent, 4 parts of cellulose, 6 parts of Kaolin, 4 parts of mica powder.It is 50-200 that described anionic additive is selected from particle diameter
The ancient marial rocks of nanometer.
Embodiment 6
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：13 parts of emulsion；42 parts of deionized water；Anion adds
3 parts of agent, 18 parts of titanium dioxide；0.3 part of dispersant, 0.2 part of wetting agent, 0.4 part of defoamer, 0.7 part of thickening agent, sterilization
0.2 part of agent, 2 parts of cellulose, 3 parts of Kaolin, 1 part of mica powder.It is 100-150 that described anionic additive is selected from particle diameter
The monazite of nanometer.
Embodiment 7
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：23 parts of emulsion；37 parts of deionized water；Anion adds
2.8 parts of agent, 21 parts of titanium dioxide；0.2 part of dispersant, 0.15 part of wetting agent, 0.8 part of defoamer, 0.2 part of thickening agent, kills
0.15 part of microbial inoculum, 4 parts of cellulose, 2 parts of Kaolin, 2 parts of mica powder.It is 50 200 that described anionic additive is selected from particle diameter
The phosphorus yttrium stone of nanometer.
Embodiment 8
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：18 parts of emulsion；29 parts of deionized water；Anion adds
1.5 parts of agent, 22 parts of titanium dioxide；0.4 part of dispersant, 0.23 part of wetting agent, 1.2 parts of defoamer, 0.9 part of thickening agent, kills
0.15 part of microbial inoculum, 4 parts of cellulose, 2 parts of Kaolin, 2 parts of mica powder.It is 350 500 that described anionic additive is selected from particle diameter
The tourmaline of nanometer.
Embodiment 9
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：15 parts of emulsion；35 parts of deionized water；Anion adds
2.5 parts of agent, 18 parts of titanium dioxide；0.27 part of dispersant, 0.15 part of wetting agent, 0.8 part of defoamer, 0.8 part of thickening agent, kills
0.3 part of microbial inoculum, 3 parts of cellulose, 2 parts of Kaolin.The monazite that described anionic additive is 100 150 nanometers selected from particle diameter
With tourmaline, the two weight is than for 1：1.
Embodiment 10
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：23 parts of emulsion；37 parts of deionized water；Anion adds
2.8 parts of agent, 21 parts of titanium dioxide；0.2 part of dispersant, 0.15 part of wetting agent, 0.8 part of defoamer, 0.2 part of thickening agent, kills
0.15 part of microbial inoculum, 4 parts of cellulose, 2 parts of Kaolin, 2 parts of mica powder.It is 350 400 that described anionic additive is selected from particle diameter
The phosphorus yttrium stone of nanometer and tourmaline, the two weight ratio is for 3：1.
Embodiment 11
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：18 parts of emulsion；29 parts of deionized water；Anion adds
1.5 parts of agent, 22 parts of titanium dioxide；0.4 part of dispersant, 0.23 part of wetting agent, 1.2 parts of defoamer, 0.9 part of thickening agent, kills
0.15 part of microbial inoculum, 4 parts of cellulose, 2 parts of Kaolin, 2 parts of mica powder.It is 350 450 that described anionic additive is selected from particle diameter
The euxenite of nanometer and tourmaline, the two weight ratio is for 2：1.
Embodiment 12
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：28 parts of emulsion；13 parts of deionized water；Anion adds
2 parts of agent, 17 parts of titanium dioxide；0.15 part of dispersant, 0.1 part of wetting agent, 1.0 parts of defoamer, 0.8 part of thickening agent, sterilization
0.05 part of agent, 0.8 part of cellulose, 2 parts of Kaolin, 5 parts of mica powder.Anionic additive is received for 200 300 selected from particle diameter
The bastnasite of rice and tourmaline, the two weight ratio is for 1.8：1.
Embodiment 13
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：22 parts of emulsion；46 parts of deionized water；Anion adds
4 parts of agent, 14 parts of titanium dioxide；0.2 part of dispersant, 0.3 part of wetting agent, 0.1 part of defoamer, 0.8 part of thickening agent, sterilization
0.09 part of agent, 4 parts of cellulose, 5 parts of Kaolin, 2 parts of mica powder.It is 50-200 that described anionic additive is selected from particle diameter
The monazite of nanometer, tourmaline and ancient marial rocks, three's weight ratio is for 2.2：1：2.
Embodiment 14
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：30 parts of emulsion；50 parts of deionized water；Anion adds
5 parts of agent, 25 parts of titanium dioxide；0.5 part of dispersant, 0.3 part of wetting agent, 1.0 parts of defoamer, 1.0 parts of thickening agent, antibacterial
0.5 part, 5 parts of cellulose, 7 parts of Kaolin, 5 parts of mica powder, anionic additive be selected from 100 200 nanometers cerite and
Gull rock, the two weight is than for 1：1.
Embodiment 15
Nanometer, negative-ion, environmental-protection coating, includes component according to weight portion：13 parts of emulsion；18 parts of deionized water；Anion adds
Plus 1.8 parts of agent, 15 parts of titanium dioxide；0.1 part of dispersant, 0.15 part of wetting agent, 0.1 part of defoamer, thickening agent 0.5
Part, in 0.05 part of antibacterial, 0.2 part of cellulose；2 parts of Kaolin, 1 part of mica powder.Anionic additive particle diameter is 50-100
The tourmaline of nanometer and kieselguhr, the two amount ratio is 1.5：1.
Used in the present invention, emulsion, dispersant, wetting agent, defoamer, thickening agent and antibacterial all can adopt existing skill
Conventional product in art, does not affect the purpose of the present invention and realizes.After testing, no matter which kind of concrete material is above component adopt,
Telling on of anion is not affected.
Nanometer, negative-ion, environmental-protection coating in the present invention, brushing, in any interior place, had both been played decorative effect, and can persistently have been had again
Effect absorption indoor air pollutants, discharge a large amount of negative oxygen ions, fresh air simultaneously, make interior be completely in a natural oxygen-bar
Health environment, take good care of the life and health of people comprehensively.Lasting improvement indoor environment in the present invention, purifies the air of a room, and resists
Bacterium is sterilized, and purifies and occupies the volatility organic carcinogen such as indoor formaldehyde, toluene, benzene, sulfur, ammonia, dispels stink, musty, oil smoke
The abnormal flavour such as taste.Persistency releasing negative oxygen ion, builds indoor natural oxygen-bar, has oxygen and gives birth to health maintenance effect, the body making one is more
Health.Permanently effective absorption, settles the dust pollution of the PM2.5 being got in by outdoor, allows people to hide empty from outdoor haze
Compression ring border.
After testing, the nanometer, negative-ion, environmental-protection coating in the present invention, can produce negative oxygen ion 4000-10000/cubic centimetre/
Second, the interior such as more than 98% formaldehyde, benzene harmful chemical can be removed, being capable of Adsorption medicated cigarette, oil smoke, seafood etc.
Life peculiar smell.
Embodiment in the present invention is only used for that the present invention will be described, does not constitute the restriction to right, this area
Other substantially equivalent replacements that interior technical staff is contemplated that, all in the scope of the present invention.
Claims (8)
1. nanometer, negative-ion, environmental-protection coating is it is characterised in that include component according to weight portion：Emulsion 10-30 part；Deionized water 10-50
Part；Anionic additive 1-5 part, titanium dioxide 15-25 part；Auxiliary agent 0.5-5 part；Filler 1-15 part.
2. nanometer, negative-ion, environmental-protection coating according to claim 1 is it is characterised in that described auxiliary agent is selected from dispersant 0.1-0.5
Part, wetting agent 0.05-0.3 part, defoamer 0.1-1.0 part, thickening agent 0.5-1.0 part, in antibacterial 0.05-0.5 part
One or more.
3. nanometer, negative-ion, environmental-protection coating according to claim 1 is it is characterised in that also include cellulose 0.05-5 part.
4. nanometer, negative-ion, environmental-protection coating according to claim 1 it is characterised in that described filler be selected from Kaolin 2-7 part and
One or more of mica powder 1-5 part.
5. nanometer, negative-ion, environmental-protection coating according to claim 1 is it is characterised in that described anionic additive is selected from tourmaline
One or more of powder, rare earth element, kieselguhr, ancient marial rocks, gull rock.
6. nanometer, negative-ion, environmental-protection coating according to claim 6 it is characterised in that described rare earth element be selected from bastnasite,
One or more of monazite, phosphorus yttrium stone, euxenite, gadolinite, cerine, cerite.
7. nanometer, negative-ion, environmental-protection coating according to claim 6 is it is characterised in that described anionic additive is selected from tourmaline
Powder and rare earth element, the weight of described rare earth element and tourmaline is than for 1-3：1.
8. the nanometer, negative-ion, environmental-protection coating according to claim 1,6 or 7 is it is characterised in that described anionic additive grain
Footpath is 50-1000 nanometer.