CN106396602B - 一种防火防潮环保门 - Google Patents
一种防火防潮环保门 Download PDFInfo
- Publication number
- CN106396602B CN106396602B CN201610776626.0A CN201610776626A CN106396602B CN 106396602 B CN106396602 B CN 106396602B CN 201610776626 A CN201610776626 A CN 201610776626A CN 106396602 B CN106396602 B CN 106396602B
- Authority
- CN
- China
- Prior art keywords
- proof
- baume degrees
- door
- solution
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种防火防潮环保门，属于门板技术领域，由下述组分组成：活性氧化镁、波美度为22‑30的氯化镁溶液、木屑、菱镁抗返卤剂、波美度为5‑15的磷酸三钠溶液、波美度为5‑15的六偏磷酸钠溶液、玻璃纤维网和涤纶线；采用本发明的材料制作的门，其耐火温度为1320℃以上，耐火时间为3.5h以上，其耐火的极限温度达1520℃，而且完全不能燃烧，安全性能高；另外，本发明制备的门，21d抗折强度≥4.5MPa,抗压强度≥12.6MPa，强度高，坚韧如石，不变形，不腐蚀；其导热系数≤0.030W/(m.k)；含水率≤0.13％，吸水膨胀率≤1.0％，使用数年也无集结水珠无返潮返卤现象，防潮防返卤性能强，使用寿命可达50‑80年，同时，本产品不含尿醛树脂等有害原料，环保无异味，还能有效隔热、隔音。
Description
技术领域
本发明涉及门板技术领域，尤其涉及一种防火防潮环保材料及采用该材料制得的门。
背景技术
目前，市场上的大多数门都是常规木质门，这种木质门一般都具有容易上潮、变形、开裂，易腐蚀、易燃等缺点，而且实木门的成本也较高，树木的砍伐也不利于环保。
为了解决上述问题，本领域对于门的材料进行了大量的研究。其中，采用活性氧化镁、氯化镁溶液为主要原料的门，已经有大量报道和应用，比如公开号CN 104446316 A、CN102503350 A、CN 104909823 A、CN 102584115 A和CN 104310942 A等。由于这类材料的门都是磷镁制品，返卤是其最显著的缺点之一，上述的专利报道针对吸潮返卤的缺点进行了一定的改进，但是其防潮性能有待进一步提高。另外，这类材料的门，往往还存在防火阻燃性能不佳的问题。现有的门，一般仅仅满足《防火门GB12955-2008》中对防火门填充材料的燃烧性不燃(A1 级) 以及烟气毒性AQ1 ，而对于耐火温度和耐火时间，往往不能满足新的更高的要求。
发明内容
本发明的目的之一，就在于提供一种防火防潮环保门材料，以解决上述问题。
为了实现上述目的，本发明采用的技术方案是这样的：一种防火防潮环保门材料，由下述重量百分比的组分组成：
活性氧化镁 30-40%
波美度为22-30的氯化镁溶液 50-60%
木屑 1.0-1.5%
菱镁抗返卤剂 2.5-3.5%
波美度为5-15的磷酸三钠溶液 0.6-0.8%
波美度为5-15的六偏磷酸钠溶液 0.6-0.8%
玻璃纤维网 3.0-4.0%
涤纶线 0.5-0.6%。
其中，活性氧化镁优选MgO质量百分含量大于90%，“波美度为22-30”是指采用波美度比重计测得的比重，其余的类似表述也是如此。磷镁促进剂的量一般为氧化镁重量的8%-18%。
本发明的发明人通过大量实验证明，采用合适比例的活性氧化镁和氯化镁，并辅以适量的菱镁抗返卤剂、磷酸三钠和六偏磷酸钠，可以明显提高含卤素门的防火耐热性能，同时也能够明显提高其防潮性能和耐腐蚀性能，从而提高其作为门的安全性、舒适性和经久耐用性能。
作为优选的技术方案：由下述重量百分比的组分组成：
活性氧化镁 36.11%
波美度为22-30的氯化镁溶液 54.17%
木屑 1.28%
菱镁抗返卤剂 2.89%
波美度为5-15的磷酸三钠溶液 0.69%
波美度为5-15的六偏磷酸钠溶液 0.69%
玻璃纤维网 3.61%
涤纶线 0.56%。
本发明的目的之二，在于提供一种采用上述材料制得的门，采用的技术方案：这种门的制备方法为：
（1）按所述比例称量活性氧化镁、氯化镁溶液、磷镁促进剂、磷酸三钠溶液、六偏磷酸钠溶液，然后混合，搅拌均匀后待用；
（2）在设置好角钢的模具上打上脱模剂，晾干，将步骤（1）所得的混合物均匀刷在模具及角钢内侧，再放上玻璃纤维网和涤纶线，再用步骤（1）所得混合物在玻璃纤维网和涤纶上刷涂，边缘用有木屑与步骤（1）的混合物充分搅拌后填充，将另一个无角钢的相同模具按照第一个模具的步骤操作完成后合上，压平；
（3）常温养护8-12小时后脱模，修边，成型，即得。
本发明的制备方法简单，易于操作，成本低；整体模压成型，无接缝。
与现有技术相比，本发明的优点在于：采用本发明的材料制作的门，其耐火温度为1320℃以上，耐火时间为3.5h以上，其耐火的极限温度达1520℃，而且完全不能燃烧，安全性能高；另外，本发明制备的门，21d抗折强度≥4.5MPa, 抗压强度≥12.6MPa，强度高，坚韧如石，不变形，不腐蚀；其导热系数≤0.030W/(m.k)；含水率≤0.1％，吸水膨胀率≤1.0％，使用数年也无集结水珠无返潮返卤现象，防潮防返卤性能强，使用寿命可达50-80年，同时，本产品不含尿醛树脂等有害原料，环保无异味，还能有效隔热、隔音。
具体实施方式
下面将结合实施例对本发明作进一步说明。
实施例1：
一种防火防潮环保门，其材料由下述重量的组分组成：
活性氧化镁 13kg
波美度为26的氯化镁溶液 19.5kg
木屑 0.46kg
菱镁抗返卤剂 1.04kg
波美度为10的磷酸三钠溶液 0.25kg
波美度为10的六偏磷酸钠溶液 0.25kg
玻璃纤维网 1.3kg
涤纶线 0.2kg；
制备方法为：
（1）按所述比例称量活性氧化镁、氯化镁溶液、磷镁促进剂、磷酸三钠溶液、六偏磷酸钠溶液，然后混合，搅拌均匀后待用；
（2）用铁角钢在工作台面上按照门的大小在模具上架好并固定，然后打上脱模剂，晾干，将步骤（1）所得的混合物均匀刷在模具及铁角钢内侧，再放上玻璃纤维网和涤纶线，再用步骤（1）所得混合物在玻璃纤维网和涤纶上刷涂，边缘用有木屑与步骤（1）的混合物充分搅拌后填充，将另一个无角钢的相同模具按照第一个模具的步骤操作完成后合上，压平；
（3）常温养护10小时后脱模，修边，成型，即得“产品A”。
实施例2：
一种防火防潮环保门，其材料由下述重量份的组分组成：
活性氧化镁 10.8kg
波美度为22的氯化镁溶液 21.6kg
木屑或刨花 0.36kg
菱镁抗返卤剂 1.26kg
波美度为5的磷酸三钠溶液 0.216kg
波美度为5的六偏磷酸钠溶液 0.216kg
玻璃纤维网 1.44kg
涤纶 0.216kg；
制备方法为：
（1）按所述比例称量活性氧化镁、氯化镁溶液、磷镁促进剂、磷酸三钠溶液、六偏磷酸钠溶液，然后混合，搅拌均匀后待用；
（2）用铁角钢在工作台面上按照门的大小在模具上架好并固定，然后打上脱模剂，晾干，将步骤（1）所得的混合物均匀刷在模具及铁角钢内侧，再放上玻璃纤维网和涤纶线，再用步骤（1）所得混合物在玻璃纤维网和涤纶上刷涂，边缘用有木屑与步骤（1）的混合物充分搅拌后填充，将另一个无角钢的相同模具按照第一个模具的步骤操作完成后合上，压平；
（3）常温养护8小时后脱模，修边，成型，即得“产品B”。
实施例3：
一种防火防潮环保门，其材料由下述重量份的组分组成：
活性氧化镁 14.5kg
波美度为30的氯化镁溶液 18kg
木屑或刨花 0.54kg
菱镁抗返卤剂 0.09kg
波美度为15的磷酸三钠溶液 0.288kg
波美度为15的六偏磷酸钠溶液 0.288kg
玻璃纤维网 1.08kg
涤纶线 0.18kg；
制备方法为：
（1）按所述比例称量活性氧化镁、氯化镁溶液、磷镁促进剂、磷酸三钠溶液、六偏磷酸钠溶液，然后混合，搅拌均匀后待用；
（2）用铁角钢在工作台面上按照门的大小在模具上架好并固定，然后打上脱模剂，晾干，将步骤（1）所得的混合物均匀刷在模具及铁角钢内侧，再放上玻璃纤维网和涤纶，再用步骤（1）所得混合物在玻璃纤维网和涤纶上刷涂，边缘用有木屑与步骤（1）的混合物充分搅拌后填充，将另一个无角钢的相同模具按照第一个模具的步骤操作完成后合上，压平；
（3）常温养护10小时后脱模，修边，成型，即得“产品C”。
性能测试
将实施例1-3所得的产品A、产品B和产品C按照行业测试标准进行相关性能测试，其结果见表1
表1 产品性能测试结果
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种防火防潮环保门材料，其特征在于：由下述重量百分比的组分组成：
活性氧化镁 36.11%
波美度为22-30的氯化镁溶液 54.17%
木屑 1.28%
菱镁抗返卤剂 2.89%
波美度为5-15的磷酸三钠溶液 0.69%
波美度为5-15的六偏磷酸钠溶液 0.69%
玻璃纤维网 3.61%
涤纶线 0.56%。
2.采用权利要求1的材料制得的门，其特征在于，其制备方法为：
（1）按所述比例称量活性氧化镁、氯化镁溶液、菱镁抗返卤剂、磷酸三钠溶液、六偏磷酸钠溶液，然后混合，搅拌均匀后待用；
（2）在设置好角钢的模具上打上脱模剂，晾干，将步骤（1）所得的混合物均匀刷在模具及角钢内侧，再放上玻璃纤维网和涤纶线，再用步骤（1）所得混合物在玻璃纤维网和涤纶线上刷涂，边缘用木屑与步骤（1）的混合物充分搅拌后填充，将另一个无角钢的相同模具按照第一个模具的步骤操作完成后合上，压平；
（3）常温养护8-12小时后脱模，修边，成型，即得。