CN106396481A - 一种天然植物提取液抑制病菌保鲜涂料及其制备方法 - Google Patents
一种天然植物提取液抑制病菌保鲜涂料及其制备方法 Download PDFInfo
- Publication number
- CN106396481A CN106396481A CN201610794546.8A CN201610794546A CN106396481A CN 106396481 A CN106396481 A CN 106396481A CN 201610794546 A CN201610794546 A CN 201610794546A CN 106396481 A CN106396481 A CN 106396481A
- Authority
- CN
- China
- Prior art keywords
- extraction liquid
- natural botanical
- botanical extraction
- germ
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种天然植物提取液抑制病菌保鲜涂料及其制备方法，所述天然植物提取液抑制病菌保鲜涂料，按重量份计的下述组分：水性合成树脂乳液30‑60份，填料15.3‑25份，纤维素0.1‑0.2份，润湿剂0.1‑0.5份，分散剂0.2‑0.4份，消泡剂0.2‑0.6份，天然植物提取液5‑20份，植物精油2‑10份，去离子水10‑30份，植物复合粉10‑30份，钛白粉100‑250份，增稠剂0.1‑0.8份，流平剂0.3‑0.8份，pH调节剂0.1‑0.3份，成膜助剂0.1‑0.15份。本发明具有高效杀菌、抑制病菌的形成。
Description
技术领域
本发明属于涂料领域，具体涉及一种天然植物提取液抑制病菌保鲜涂料及其制备方法。
背景技术
目前内墙墙面水漆在常规性能和环保方面已经相对稳定和成熟，伴随人们生活水平的提高对本行业的技术要求也越来越高，常规的内墙漆已经不能达到人们的要求，因此对涂料的功能性方面进行发展。
虽然关于植物提取液抑制果蔬后病原菌的研究较多，但关于果蔬保鲜过程中天然植物提取液应用在涂料中的研究还较少，不同的果蔬主要致病菌、采后生理、储藏保鲜条件均有一定的差异，确定天然植物提取液用在涂料中对不同果蔬保鲜程度的最佳应用条件和技术十分必要。
实验测试表明，天然植物提取液可以取代目前内墙常规涂料中的杀菌剂、防腐剂，且经过测试50-200mg/L的百里香精油对草莓病菌真菌Botrytis cinerea和Phizopusstolonifer的抑制率分别为26.5％-90.5％和5.5％-65.8％,0，4和0.5山苍子、肉桂、丁香油完全可以抑制黄曲霉、毛霉、青霉等8种霉。
发明内容
为解决上述问题，本发明的目的是提供即在于克服现有技术的缺点，提供一种具有高效杀菌抑菌的天然植物提取液抑制病菌保鲜涂料及其制备方法。
为实现上述技术目的，本发明采用的技术方案如下：本发明的一种天然植物提取液抑制病菌保鲜涂料，包括按重量份计的下述组分：
进一步地，所述水性合成树脂乳液为醋酸乙烯-乙烯共聚乳，所述醋酸乙烯-乙烯共聚乳液的固含量为54％-56％，最低成膜温度在0℃。
进一步地，所述润湿剂为聚氧乙烯烷基酚醚，聚氧乙烯脂肪醇醚，聚氧乙烯聚氧丙烯嵌段共聚物中的任意一种，所述增稠剂为碱溶涨类和聚丙烯酸酯中的任意一种。
更进一步地，所述分散剂为聚丙烯酸铵盐类；所述消泡剂为矿物油类中的任意一种；所述钛白粉为金红石钛白粉；所述流平剂为聚氨酯类流平剂；所述填料为煅烧高岭土、硅藻土、重质碳酸钙中的一种或多种的组合。
进一步地，所述天然植物提取液为丁香、山苍子、肉桂的复配后的水提取液，所述丁香、山苍子、肉桂的质量比为2:1:1。
进一步地，植物复合粉是由艾草、杜仲、桂皮的混合物，所述艾草、杜仲、桂皮的质量比为3:1:1；植物复合粉为400-800目。
本发明所述的天然植物提取液抑制病菌保鲜涂料的制备方法，包括如下步骤：
(1)按照所述的质量百分比称取上述物质，依次将去离子水加入反应罐A中，以100-200rpm的速度搅拌，升温至50℃，加入天然植物提取液，以100-200rpm的速度搅拌15min；停机保温24h，将植物渣滤出留天然植物提取液备用；
(2)按照配方量，在反应罐B中依次缓慢加入反应罐A中滤得的天然植物提取液、植物精油、去离子水、pH调节剂，分散剂，消泡剂，润湿剂，以500-800rpm的速度搅拌2min至均匀；
(3)按照配方量，依次将填料、植物复合粉加入反应罐B中，提高分散速度以800-1200rpm的速度搅拌20分钟至漆浆均匀；
(4)按照配方量，在反应罐B中缓慢加入乳液，流平剂，以800-1200rpm的速度搅拌5分钟，测初始粘度，根据初始粘度，加入配方量的增稠剂进行增稠至25℃、斯托默粘度计80-100KU，制得天然植物提取液抑制病菌保鲜涂料。
进一步地，制备所述植物复合粉：将艾草、杜仲、桂皮按照3:1:1复配，在80℃干燥仓烘干4h，用粉碎机混合粉碎至400-800目得到植物复合粉。
进一步地，制备所述天然植物提取液：将丁香、山苍子、肉桂捣碎装入150ml的圆底烧瓶中，加入80ml水，按蒸馏装置连接好，加热回流，提取液随水蒸气一同冷凝于恒压滴液漏斗中，2h后，反应结束，将恒压滴液漏斗中的水放入圆底烧瓶中，液层用无水硫酸钠干燥，得到复配后的水提取液。
更进一步地，制备百里香精油：将百里香捣碎装入150ml的圆底烧瓶中，加入80ml水，按蒸馏装置连接好，加热回流，提取液随水蒸气一同冷凝于恒压滴液漏斗中，2h后，反应结束，将恒压滴液漏斗中的水放入圆底烧瓶中，液层用无水硫酸钠干燥，得到百里香精油；提取后所述百里香精油与水的质量比为2:1，所述百里香精油的主要成分为松油烯-4-醇、α-松油醇与水2％的稀释比例。
有益效果：本发明具有高效杀菌、低生物毒性、保鲜天然植物提取液可以抑制病菌的形成。充分发挥天然植物提取液有效成分能够抑制细菌、真菌繁殖，使植物提取液的有效成分在涂层中缓慢释放，长期发挥作用。
与现有技术相比，本发明具有如下优点：
(1)目前市面上的保鲜措施有两种，一种利用冷库低温保鲜；另一种在果蔬上涂蘸一些防腐剂等产品来达到保鲜效果；然而这两中方法都对果蔬本身造成影响，冷库低温储存食物会使食物本身的口感和味觉变差同时释放氟利昂有毒气体造成环境污染，另一种保鲜会使人们的身体健康受到影响。
(2)本发明在施工上是直接涂刷在储藏室墙面上，不直接接触果蔬，不会使果蔬产生毒素，影响人们的身体健康，另一方面，储藏室刷涂本产品后，温度不会太低，因此不会影响果蔬的口感，同时不会释放有毒气体、环保、节约能源。天然植物提取液为丁香、山苍子、肉桂2:1:1比例复配后的水提取液，可以破坏病菌的形成。
具体实施方式
以下通过实施例进一步说明本发明。应该理解的是，这些实施例是本发明的阐释和举例，并不以任何形式限制本发明的范围。
实施例1
本发明的一种天然植物提取液抑制病菌保鲜涂料，包括按重量份计的下述组分：
所述水性合成树脂乳液为醋酸乙烯-乙烯共聚乳。所述醋酸乙烯-乙烯共聚乳液的固含量为54-56％，本发明所述醋酸乙烯-乙烯共聚乳液为已知产品，可购自瓦克化学EZ3010。
所述润湿剂为烷基聚氧乙烯醚。为科莱恩的LCN407。
所述分散剂为聚丙烯酸氨盐类。为陶氏的963。
所述消泡剂为巴斯夫的A10。
所述钛白粉为氯化法生产的金红石钛白粉，为龙蟒的LR996；
所述填料为煅烧高岭土、硅藻土、重质碳酸钙多种的组合；所述煅烧高岭土为山西金宇的煅烧高岭土DB80，所述硅藻土为赛力特硅藻土499，所述重质碳酸钙为广福的重质碳酸钙CC-700。
所述增稠剂为碱溶涨类和聚丙烯酸酯中的任意一种；
所述流平剂为无溶剂聚氨酯类流平剂，具体如法国高泰的2025。
所述植物精油为百里香中提取的植物精油，植物精油主要成分为松油烯-4-醇、α-松油醇，其使用时，所述植物精油与水的稀释比例范围为10％-50％，与水最佳稀释比例为20％；所述天然植物提取液为丁香、山苍子、肉桂的复配后的水提取液，所述丁香、山苍子、肉桂的质量比为2:1:1。
植物复合粉是由艾草、杜仲、桂皮的混合物，所述艾草、杜仲、桂皮的质量比为3:1:1；植物复合粉为400-800目。
所述的成膜助剂选自齐鲁伊斯曼特种化工有限公司，此类成膜助剂可TEXANOL。
所述pH调节剂选自陶氏化学的AMP-95。
本发明所述的天然植物提取液抑制病菌保鲜涂料的制备方法，包括如下步骤：
(1)按照所述的质量百分比称取上述物质，依次将去离子水加入反应罐A中，以100rpm的速度搅拌，升温至50℃，缓慢加入山苍子及丁香，以100rpm的速度搅拌15min；停机保温24h，将植物渣滤出留天然植物提取液备用；把百里香放入蒸馏装置中提取百里香精油，提取后的百里香精油与水2:1的比例混合备用；将艾草、杜仲、桂皮按照3:1:1复配，在80℃干燥仓烘干4h，用粉碎机混合粉碎至600目得到植物复合粉。
(2)按照配方量，在反应罐B中依次缓慢加入反应罐A中滤得的天然植物提取液、百里香精油、去离子水、pH调节剂，分散剂，消泡剂，润湿剂，以500rpm的速度搅拌2min至均匀；
(3)按照配方量，依次将填料、植物复合粉加入反应罐B中，提高分散速度以600rpm的速度搅拌20分钟至漆浆均匀；
(4)按照配方量，在反应罐B中缓慢加入乳液，流平剂，以800rpm的速度搅拌5分钟，测初始粘度，根据初始粘度，加入配方量的增稠剂进行增稠至25℃、斯托默粘度计80KU，制得天然植物提取液抑制病菌保鲜涂料。
制备所述植物复合粉：将植物复合粉在温度为80℃干燥仓内烘干4h，用粉碎机混合粉碎至800目。
制备所述天然植物提取液：将丁香、山苍子、肉桂捣碎装入150ml的圆底烧瓶中，加入80ml水，按蒸馏装置连接好，加热回流，提取液随水蒸气一同冷凝于恒压滴液漏斗中，2h后，反应结束，将恒压滴液漏斗中的水放入圆底烧瓶中，液层用无水硫酸钠干燥，得到复配后的水提取液。
制备植物精油：将百里香捣碎装入150ml的圆底烧瓶中，加入80ml水，按蒸馏装置连接好，加热回流，提取液随水蒸气一同冷凝于恒压滴液漏斗中，2h后，反应结束，将恒压滴液漏斗中的水放入圆底烧瓶中，液层用无水硫酸钠干燥，得到百里香精油；其主要成分为松油烯-4-醇、α-松油醇与水2％的稀释比例。
将实施例1制得天然植物提取液抑制病菌保鲜涂料进行检测，得到表1如下：
表1
实施例2
实施例2与实施例1的区别在于：
本发明的一种天然植物提取液抑制病菌保鲜涂料，包括按重量份计的下述组分：
所述增稠剂为聚丙烯酸酯。
所述润湿剂为聚氧乙烯烷基酚醚。
所述填料为煅烧高岭土。
本发明所述的本发明所述的天然植物提取液抑制病菌保鲜涂料的制备方法，包括如下步骤：
在步骤(1)中，按照所述的质量百分比称取上述物质，依次将去离子水加入反应罐A中，以150rpm的速度搅拌，升温至50℃，缓慢加入山苍子及丁香，以150rpm的速度搅拌15min；停机保温24h，将植物渣滤出留天然植物提取液备用；把百里香放入蒸馏装置中提取百里香精油，提取后的百里香精油与水2:1的比例混合备用；将艾草、杜仲、桂皮按照3:1:1复配，在80℃干燥仓烘干4h，用粉碎机混合粉碎至800目得到植物复合粉。
在步骤(2)中，按照配方量，在反应罐B中依次缓慢加入反应罐A中滤得的天然植物提取液、百里香精油、去离子水、pH调节剂，分散剂，消泡剂，润湿剂，以500rpm的速度搅拌2min至均匀；
在步骤(3)中，按照配方量，依次将填料、植物复合粉加入反应罐B中，提高分散速度以1000rpm的速度搅拌20分钟至漆浆均匀；
在步骤(4)中，按照配方量，在反应罐B中缓慢加入乳液，流平剂，以1000rpm的速度搅拌5分钟，测初始粘度，根据初始粘度，加入配方量的增稠剂进行增稠至25℃、斯托默粘度计100KU，制得天然植物提取液抑制病菌保鲜涂料。
将实施例2制得天然植物提取液抑制病菌保鲜涂料进行检测，得到表2如下：
表2
实施例3
实施例3与实施例1的区别在于：本发明的一种天然植物提取液抑制病菌保鲜涂料，包括按重量份计的下述组分：
所述润湿剂为聚氧乙烯聚氧丙烯嵌段共聚物。
所述填料为重质碳酸钙。
本发明所述的天然植物提取液抑制病菌保鲜涂料的制备方法，包括如下步骤：
在步骤(1)中，按照权利要求1所述的质量百分比称取上述物质，依次将去离子水加入反应罐A中，以200rpm的速度搅拌，升温至50℃，缓慢加入山苍子及丁香，以200rpm的速度搅拌15min；停机保温24h，将植物渣滤出留天然植物提取液备用；把百里香放入蒸馏装置中提取百里香精油，提取后的百里香精油与水2:1的比例混合备用；将艾草、杜仲、桂皮按照3:1:1复配，在80℃干燥仓烘干4h，用粉碎机混合粉碎至700目得到植物复合粉。
在步骤(2)中，按照配方量，在反应罐B中依次缓慢加入反应罐A中滤得的天然植物提取液、百里香精油、去离子水、PH调节剂，分散剂，消泡剂，润湿剂，以800rpm的速度搅拌2min至均匀；
在步骤(3)中，按照配方量，依次将填料、植物复合粉加入反应罐B中，提高分散速度以1200rpm的速度搅拌20分钟至漆浆均匀；
在步骤(4)中，按照配方量，在反应罐B中缓慢加入乳液，流平剂，以1200rpm的速度搅拌5分钟，测初始粘度，根据初始粘度，加入配方量的增稠剂进行增稠至25℃、斯托默粘度计90KU，制得天然植物提取液抑制病菌保鲜涂料。
将实施例3制得天然植物提取液抑制病菌保鲜涂料进行检测，得到表3如下：
表3
由表1、表2和表3可知，在满足了常规内墙涂料的基础性能的基础上，同时具有能够抑制细菌、真菌繁殖，破坏病菌的形成，同时植物提取液的有效成分在涂层中缓慢释放，长期发挥作用。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，本发明要求保护范围由所附的权利要求书、说明书及其等效物界定。
Claims (10)
1.一种天然植物提取液抑制病菌保鲜涂料，其特征在于包括按重量份计的下述组分：
2.根据权利要求1所述的天然植物提取液抑制病菌保鲜涂料，其特征在于：所述水性合成树脂乳液为醋酸乙烯-乙烯共聚乳，所述醋酸乙烯-乙烯共聚乳液的固含量为54％-56％，最低成膜温度在0℃。
3.根据权利要求1所述的天然植物提取液抑制病菌保鲜涂料，其特征在于：所述润湿剂为烷基聚氧乙烯醚，聚氧乙烯脂肪醇醚，聚氧乙烯聚氧丙烯嵌段共聚物中的任意一种，所述增稠剂为碱溶涨类和聚丙烯酸酯中的任意一种，所述纤维素为羟乙基纤维素。
4.根据权利要求1所述的天然植物提取液抑制病菌保鲜涂料，其特征在于：所述分散剂为聚丙烯酸铵盐类；所述消泡剂为矿物油类中的任意一种；所述钛白粉为金红石钛白粉；所述流平剂为聚氨酯类流平剂；所述填料为煅烧高岭土、硅藻土、重质碳酸钙中的一种或多种的组合。
5.根据权利要求1所述的天然植物提取液抑制病菌保鲜涂料，其特征在于：所述天然植物提取液为丁香、山苍子、肉桂的复配后的水提取液，所述丁香、山苍子、肉桂的质量比为2:1:1。
6.根据权利要求1所述的天然植物提取液抑制病菌保鲜涂料，其特征在于：植物复合粉是由艾草、杜仲、桂皮的混合物，所述艾草、杜仲、桂皮的质量比为3:1:1；植物复合粉为400-800目。
7.权利要求1至6任一项所述的天然植物提取液抑制病菌保鲜涂料的制备方法，其特征在于包括如下步骤：
(1)按照权利要求1所述的质量百分比称取上述物质，依次将去离子水加入反应罐A中，以100-200rpm的速度搅拌，升温至50℃，加入天然植物提取液，以100-200rpm的速度搅拌15min；停机保温24h，将植物渣滤出留天然植物提取液备用；
(2)按照配方量，在反应罐B中依次缓慢加入天然植物提取液、植物精油、去离子水、pH调节剂，分散剂，消泡剂，润湿剂，以500-800rpm的速度搅拌2min至均匀；
(3)按照配方量，依次将填料、植物复合粉加入反应罐B中，提高分散速度以800-1200rpm的速度搅拌20分钟至漆浆均匀；
(4)按照配方量，在反应罐B中缓慢加入乳液，流平剂，以800-1200rpm的速度搅拌5分钟，测初始粘度，根据初始粘度，加入配方量的增稠剂进行增稠至25℃、斯托默粘度计80-100KU，制得天然植物提取液抑制病菌保鲜涂料。
8.根据权利要求7所述的天然植物提取液抑制病菌保鲜涂料的制备方法，其特征在于：制备所述植物复合粉：将艾草、杜仲、桂皮按照3:1:1复配，在80℃干燥仓烘干4h，用粉碎机混合粉碎至400-800目得到植物复合粉。
9.根据权利要求8所述的天然植物提取液抑制病菌保鲜涂料的制备方法，其特征在于：制备所述天然植物提取液：将丁香、山苍子、肉桂捣碎装入150ml的圆底烧瓶中，加入80ml水，按蒸馏装置连接好，加热回流，提取液随水蒸气一同冷凝于恒压滴液漏斗中，2h后，反应结束，将恒压滴液漏斗中的水放入圆底烧瓶中，液层用无水硫酸钠干燥，得到复配后的水提取液。
10.根据权利要求8所述的天然植物提取液抑制病菌保鲜涂料的制备方法，其特征在于：制备百里香精油：将百里香捣碎装入150ml的圆底烧瓶中，加入80ml水，按蒸馏装置连接好，加热回流，提取液随水蒸气一同冷凝于恒压滴液漏斗中，2h后，反应结束，将恒压滴液漏斗中的水放入圆底烧瓶中，液层用无水硫酸钠干燥，得到百里香精油；提取后所述百里香精油与水的质量比为2:1，所述百里香精油的主要成分为松油烯-4-醇、α-松油醇与水2％的稀释比例。