CN106396403A - Bone china glaze - Google Patents
Bone china glaze Download PDFInfo
- Publication number
- CN106396403A CN106396403A CN201510452185.4A CN201510452185A CN106396403A CN 106396403 A CN106396403 A CN 106396403A CN 201510452185 A CN201510452185 A CN 201510452185A CN 106396403 A CN106396403 A CN 106396403A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- bone china
- calcite
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technical field of porcelain glazes, particularly to a bone china glaze, which comprises, by mass, 20-30 parts of kaolin, 15-20 parts of aluminum oxide, 3-9 parts of calcite, 3.5-6.8 parts of zinc oxide, 2.1-5.4 parts of calcium carbonate, 5-12 parts of ceramic fiber, 3-8 parts of a silane coupling agent, 4-10 parts of zirconium silicate, 3.6-4.8 parts of talc powder, and 12-18 parts of glass micro-bead. According to the present invention, with the use of the formula, the product obtained through the bone china glaze has characteristics of good translucency, soft glaze surface color and less defects, the glaze has strong fluidity during the firing process, the glaze surface quality and the product quality are high, the component cost is low, and the method is easy to promote and apply.
Description
Technical field
The present invention relates to glaze technical field, particularly a kind of Bone China Glaze.
Background technology
Construction sanitary ceramic industry is focused on using advanced glaze technology very much, and domestic large quantities of specialties
The very strong ceramic glaze of property and preparing ceramic clinker, colorant company.In construction sanitary ceramic product, glaze used is got over
Come more rich and varied, the glaze product that most pottery enterprises use at present, classification can be as follows with rough classification with purposes：
1st, lead glaze and leadless glaze；2nd, raw glaze and fritted glaze；3rd, once-firing or twice firing glaze；4th, porcelain
Brick, tableware, sanitary ceramics and electroceramics glaze；5th, by the leaching glaze of enameling method division, glaze spraying, pour glaze；6、
High-temperature glaze and low temperature glaze；7th, highly expanded glaze and Low Thermal Expantion Glaze；8th, firing atmosphere oxidizing flame, neutral flame and also
Former flame；9th, coloured glaze and colourless glaze；10th, clear frit and opaque glaze；11st, bright glaze, mat glaze, half nothing
Light glaze or figure glaze etc..
Content of the invention
The technical problem to be solved in the invention is to provide a kind of Bone China Glaze.
For solving above-mentioned technical problem, a kind of Bone China Glaze of the present invention, according to mass fraction meter include with
Lower component：Kaolin 20-30 part, alundum (Al2O3) 15-20 part, calcite 3-9 part, zinc oxide 3.5-6.8
Part, calcium carbonate 2.1-5.4 part, ceramic fibre 5-12 part, silane coupler 3-8 part, zirconium silicate 4-10
Part, talcum powder 3.6-4.8 part, glass microballoon 12-18 part.
Further, include following components according to mass fraction meter：20 parts of kaolin, 15 parts of alundum (Al2O3),
3 parts of calcite, 3.5 parts of zinc oxide, 2.1 parts of calcium carbonate, 5 parts of ceramic fibre, 3 parts of silane coupler,
4 parts of zirconium silicate, 3.6 parts of talcum powder, 12 parts of glass microballoon.
Further, include following components according to mass fraction meter：30 parts of kaolin, 20 parts of alundum (Al2O3),
9 parts of calcite, 6.8 parts of zinc oxide, 5.4 parts of calcium carbonate, 12 parts of ceramic fibre, 8 parts of silane coupler,
10 parts of zirconium silicate, 4.8 parts of talcum powder, 18 parts of glass microballoon.
Further, include following components according to mass fraction meter：23 parts of kaolin, 16 parts of alundum (Al2O3),
5 parts of calcite, 4.3 parts of zinc oxide, 2.8 parts of calcium carbonate, 9 parts of ceramic fibre, 5 parts of silane coupler,
6 parts of zirconium silicate, 4.1 parts of talcum powder, 15 parts of glass microballoon.
Further, include following components according to mass fraction meter：28 parts of kaolin, 19 parts of alundum (Al2O3),
8 parts of calcite, 5.2 parts of zinc oxide, 4.3 parts of calcium carbonate, 11 parts of ceramic fibre, 6 parts of silane coupler,
9 parts of zirconium silicate, 4.6 parts of talcum powder, 17 parts of glass microballoon.
After above-mentioned formula, the Bone China Glaze of the present invention, product translucence is good, and glaze paint color and luster is soft,
Defect is few, and glaze mobility in sintering process is strong, and glaze quality and product quality are high；In addition, the present invention
Composition low cost, easy to utilize.
Specific embodiment
A kind of Bone China Glaze of the present invention, includes following components according to mass fraction meter：Kaolin 20-30 part,
Alundum (Al2O3) 15-20 part, calcite 3-9 part, zinc oxide 3.5-6.8 part, calcium carbonate 2.1-5.4 part,
Ceramic fibre 5-12 part, silane coupler 3-8 part, zirconium silicate 4-10 part, talcum powder 3.6-4.8 part,
Glass microballoon 12-18 part.
Embodiment one：
Include following components according to mass fraction meter：20 parts of kaolin, 15 parts of alundum (Al2O3), calcite 3
Part, 3.5 parts of zinc oxide, 2.1 parts of calcium carbonate, 5 parts of ceramic fibre, 3 parts of silane coupler, zirconium silicate 4
Part, 3.6 parts of talcum powder, 12 parts of glass microballoon.
Embodiment two：
Include following components according to mass fraction meter：30 parts of kaolin, 20 parts of alundum (Al2O3), calcite 9
Part, 6.8 parts of zinc oxide, 5.4 parts of calcium carbonate, 12 parts of ceramic fibre, 8 parts of silane coupler, zirconium silicate
10 parts, 4.8 parts of talcum powder, 18 parts of glass microballoon.
Embodiment three：
Include following components according to mass fraction meter：23 parts of kaolin, 16 parts of alundum (Al2O3), calcite 5
Part, 4.3 parts of zinc oxide, 2.8 parts of calcium carbonate, 9 parts of ceramic fibre, 5 parts of silane coupler, zirconium silicate 6
Part, 4.1 parts of talcum powder, 15 parts of glass microballoon.
Embodiment four：
Include following components according to mass fraction meter：28 parts of kaolin, 19 parts of alundum (Al2O3), calcite 8
Part, 5.2 parts of zinc oxide, 4.3 parts of calcium carbonate, 11 parts of ceramic fibre, 6 parts of silane coupler, zirconium silicate
9 parts, 4.6 parts of talcum powder, 17 parts of glass microballoon.
Although the foregoing describing the specific embodiment of the present invention, those skilled in the art should manage
Solution, these are merely illustrative of, and can make various changes or modifications to present embodiment, without departing from send out
Bright principle and essence, protection scope of the present invention is only limited by the claims that follow.
Claims (5)
1. a kind of Bone China Glaze is it is characterised in that include following components according to mass fraction meter：Kaolin 20-30
Part, alundum (Al2O3) 15-20 part, calcite 3-9 part, zinc oxide 3.5-6.8 part, calcium carbonate 2.1-5.4
Part, ceramic fibre 5-12 part, silane coupler 3-8 part, zirconium silicate 4-10 part, talcum powder 3.6-4.8
Part, glass microballoon 12-18 part.
2. according to a kind of Bone China Glaze described in claim 1 it is characterised in that including according to mass fraction meter
Following components：20 parts of kaolin, 15 parts of alundum (Al2O3), 3 parts of calcite, 3.5 parts of zinc oxide, carbon
2.1 parts of sour calcium, 5 parts of ceramic fibre, 3 parts of silane coupler, 4 parts of zirconium silicate, 3.6 parts of talcum powder,
12 parts of glass microballoon.
3. according to a kind of Bone China Glaze described in claim 1 it is characterised in that including according to mass fraction meter
Following components：30 parts of kaolin, 20 parts of alundum (Al2O3), 9 parts of calcite, 6.8 parts of zinc oxide, carbon
5.4 parts of sour calcium, 12 parts of ceramic fibre, 8 parts of silane coupler, 10 parts of zirconium silicate, 4.8 parts of talcum powder,
18 parts of glass microballoon.
4. according to a kind of Bone China Glaze described in claim 1 it is characterised in that including according to mass fraction meter
Following components：23 parts of kaolin, 16 parts of alundum (Al2O3), 5 parts of calcite, 4.3 parts of zinc oxide, carbon
2.8 parts of sour calcium, 9 parts of ceramic fibre, 5 parts of silane coupler, 6 parts of zirconium silicate, 4.1 parts of talcum powder,
15 parts of glass microballoon.
5. according to a kind of Bone China Glaze described in claim 1 it is characterised in that including according to mass fraction meter
Following components：28 parts of kaolin, 19 parts of alundum (Al2O3), 8 parts of calcite, 5.2 parts of zinc oxide, carbon
4.3 parts of sour calcium, 11 parts of ceramic fibre, 6 parts of silane coupler, 9 parts of zirconium silicate, 4.6 parts of talcum powder,
17 parts of glass microballoon.