CN106396382B - Utilize the rich in variety glaze porcelain and its manufacture craft of limestone tailing preparation - Google Patents
Utilize the rich in variety glaze porcelain and its manufacture craft of limestone tailing preparation Download PDFInfo
- Publication number
- CN106396382B CN106396382B CN201610796119.3A CN201610796119A CN106396382B CN 106396382 B CN106396382 B CN 106396382B CN 201610796119 A CN201610796119 A CN 201610796119A CN 106396382 B CN106396382 B CN 106396382B
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- rich
- variety
- limestone tailing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to technical field of ceramic production, and in particular to a kind of rich in variety glaze porcelain and its manufacture craft using limestone tailing preparation.The rich in variety glaze porcelain that this kind is prepared using limestone tailing, including ceramic body and the rich in variety glaze being set on ceramic body, rich in variety glaze includes calcined limestone tailing powder, quartz, Red Stone Ware, nickel oxide, zirconium silicate powder, talcum, lead silicate, titanium oxide, lithium carbonate, di-iron trioxide, copper oxide, manganese oxide.It is above-mentioned to prepare desert glaze porcelain using Quartz Tails, its glaze paint is unglazed, with red background color, and by glowing purple in red background color, a particle is uniformly distributed in glaze paint, glaze paint feel is coarse, give deep, starry sky impression, this kind riot of colour glaze is prepared using limestone tailing, using waste material, reduces energy consumption, with great society, environment protection significance, meet Development Models of Circular Economy in Urban.
Description
Technical field
The invention belongs to technical field of ceramic production, and in particular to a kind of rich in variety glaze prepared using limestone tailing
Porcelain and its manufacture craft.
Background technique
With the rapid development of ceramics, lime stone is largely exploited and is utilized, and generates nearly hundred tons of waste limestone every year
Tailing, these waste residue materials of the tailing for removing of digging up mine include barren rock, tailing, crumb powder etc. and lime stone coating, interlayer,
Mountain skin soil, crack soil etc..These waste residues after exploitation had both occupied stockyard arable land, and had caused secondary environmental pollution, and waste preciousness
Non-renewable mineral resources, there are production safeties and environmentally friendly accident potential, have seriously affected agricultural and people's lives and properties
Safety, greatly waste mineral resources, and destroy ecological environment.
Therefore, the comprehensive utilization of waste limestone tailing is essential, also becomes the weight that Production of Ceramics producer faces
Hang-up.
Summary of the invention
To solve the above-mentioned problems, the present invention provides a kind of rich in variety glaze porcelains prepared using limestone tailing.
For achieving the above object, the present invention provides using limestone tailing preparation rich in variety glaze porcelain,
It is characterized in that, including ceramic body and the rich in variety glaze being set on ceramic body, the riot of colour glaze is according to parts by weight
It counts as follows: calcined limestone tailing powder 30-40,10-15 parts of quartz, 10-15 parts of Red Stone Ware, 5-10 parts of nickel oxide, zirconium silicate
5-10 parts of powder, 5-10 parts of talcum, 1-5 parts of lead silicate, 1-5 parts of titanium oxide, 1-5 parts of lithium carbonate, 1-5 parts of di-iron trioxide, oxygen
Change copper 1-5,1-5 parts of manganese oxide.
Optimization, rich in variety glaze is as follows in parts by weight: calcined limestone tailing powder 38, quartzy 11 parts, boccaro
14 parts of soil, 5 parts of nickel oxide, 9 parts of zirconium silicate powder, 6 parts of talcum, 2 parts of lead silicate, 5 parts of titanium oxide, 2 parts of lithium carbonate, three oxidations two
4 parts of iron, copper oxide 3,1 part of manganese oxide.
Optimization, rich in variety glaze is as follows in parts by weight: calcined limestone tailing powder 33, quartzy 13 parts, boccaro
Soil 14 parts, 8 parts of nickel oxide, 9 parts of zirconium silicate powder, 5 parts of talcum, 3 parts of lead silicate, 3 parts of titanium oxide, 3 parts of lithium carbonate, three oxidation
Two 2 parts of iron, copper oxide 3,4 parts of manganese oxide.
Optimization, rich in variety glaze is as follows in parts by weight: calcined limestone tailing powder 35, quartzy 14 parts, boccaro
12 parts of soil, 6 parts of nickel oxide, 7 parts of zirconium silicate powder, 8 parts of talcum, 5 parts of lead silicate, 4 parts of titanium oxide, 2 parts of lithium carbonate, three oxidations two
2 parts of iron, copper oxide 3,2 parts of manganese oxide.
Utilize the manufacture craft of the rich in variety glaze porcelain of limestone tailing preparation, which comprises the following steps:
Step 1 will be sieved after limestone tailing screening, crushing, calcining；
Raw material is uniformly mixed, is crushed, wet ball mill according to rich in variety glaze composition of raw materials weighing and proportioning by step 2, is made
Glaze slip；
Step 3 makes ceramic body, waits ceramic body surface natural air drying；
Ceramic body made from step 3 is put into biscuiting in kiln and formed, biscuit is made by step 4；
Step 5 applies riot of colour glaze glaze slip made from step 2 after band biscuit is cooling on biscuit；
Step 6, kiln-firing after ceramic blank drying, strongly reducing atmosphere firing, firing temperature are 1280-1300 DEG C, kiln
After furnace is warming up to firing temperature, cease fire, slow cooling.
Further, in step 1 limestone tailing calcination temperature be 200-300 DEG C, calcination time 1-2 hours, after calcining
100 mesh of fruit.
Further, expect when rich in variety glaze wet ball mill in step 2: ball: water=1:2:1.2
Further, glaze slip is adjusted to 45-60 Baume degrees when step 4 glazing.
Further, in step 4 glazing with a thickness of 1-1.5mm.
Further, after kiln reaches firing temperature, 30-40 minutes are kept the temperature, in slow cooling.
Seen from the above description, provided by the invention to prepare desert glaze porcelain using Quartz Tails, glaze paint is unglazed, has
Red background color, and by glowing purple in red background color, a particle is uniformly distributed in glaze paint, glaze paint feel is coarse,
Give deep, starry sky impression, this kind riot of colour glaze is prepared using limestone tailing, using waste material, reduces energy consumption, tool
There are great society, environment protection significance, meets Development Models of Circular Economy in Urban.
Specific embodiment
For a better understanding of the technical solution of the present invention, being discussed further below with reference to embodiment to the present invention.
The present invention provides the rich in variety glaze porcelains using limestone tailing preparation, including ceramic body and are set to pottery
Rich in variety glaze on porcelain billet body, the riot of colour glaze are as follows in parts by weight: calcined limestone tailing powder 30-40,
10-15 parts quartzy, 10-15 parts of Red Stone Ware, 5-10 parts of nickel oxide, 5-10 parts of zirconium silicate powder, 5-10 parts of talcum, lead silicate 1-5
Part, 1-5 parts of titanium oxide, 1-5 parts of lithium carbonate, 1-5 parts of di-iron trioxide, copper oxide 1-5,1-5 parts of manganese oxide.
Utilize the manufacture craft of the rich in variety glaze porcelain of limestone tailing preparation, comprising the following steps:
Step 1 will be sieved after limestone tailing screening, crushing, calcining, and limestone tailing calcination temperature is 200-300
DEG C, calcination time 1-2 hours, calcine 100 mesh of consequence；
Raw material is uniformly mixed, is crushed, wet ball mill according to rich in variety glaze composition of raw materials weighing and proportioning by step 2, is made
Glaze slip, when purple thousand red glaze wet ball mill, expect: ball: water=1:2:1.2；
Step 3 makes ceramic body, waits ceramic body surface natural air drying；
Ceramic body made from step 3 is put into biscuiting in kiln and formed, biscuit is made by step 4；
Step 5 after band biscuit is cooling, applies riot of colour glaze glaze slip made from step 2 on biscuit, glaze slip tune when glazing
Whole is 45-60 Baume degrees, glazing with a thickness of 1-1.5mm；
Step 6, kiln-firing after ceramic blank drying, strongly reducing atmosphere firing, firing temperature are 1280-1300 DEG C, kiln
Furnace keeps the temperature 30-40 minutes after being warming up to firing temperature, in slow cooling, ceases fire, slow cooling.
Specific embodiment one:
Rich in variety glaze is as follows in parts by weight: calcined limestone tailing powder 38, quartz 11 parts, 14 parts of Red Stone Ware,
5 parts of nickel oxide, 9 parts of zirconium silicate powder, 6 parts of talcum, 2 parts of lead silicate, 5 parts of titanium oxide, 2 parts of lithium carbonate, 4 parts of di-iron trioxide,
1 part of copper oxide 3, manganese oxide.
Specific embodiment two:
Rich in variety glaze is as follows in parts by weight: calcined limestone tailing powder 33, quartz 13 parts, 14 parts of Red Stone Ware,
8 parts of nickel oxide, 9 parts of zirconium silicate powder, 5 parts of talcum, 3 parts of lead silicate, 3 parts of titanium oxide, 3 parts of lithium carbonate, di-iron trioxide 2
Part, copper oxide 3,4 parts of manganese oxide.
Specific embodiment three:
Rich in variety glaze is as follows in parts by weight: calcined limestone tailing powder 35, quartz 14 parts, 12 parts of Red Stone Ware,
6 parts of nickel oxide, 7 parts of zirconium silicate powder, 8 parts of talcum, 5 parts of lead silicate, 4 parts of titanium oxide, 2 parts of lithium carbonate, 2 parts of di-iron trioxide,
2 parts of copper oxide 3, manganese oxide.
Seen from the above description, provided by the invention to prepare desert glaze porcelain using Quartz Tails, glaze paint is unglazed, has
Red background color, and by glowing purple in red background color, a particle is uniformly distributed in glaze paint, glaze paint feel is coarse,
Give deep, starry sky impression, this kind riot of colour glaze is prepared using limestone tailing, using waste material, reduces energy consumption, tool
There are great society, environment protection significance, meets Development Models of Circular Economy in Urban.
The above is only the preferred embodiment of the present invention, therefore cannot be limited the scope of implementation of the present invention with this, i.e., according to
Equivalent changes and modifications made by scope of the present invention patent and description should still belong to the model that the invention patent covers
In enclosing.
Claims (4)
1. utilizing the rich in variety glaze porcelain of limestone tailing preparation, which is characterized in that including ceramic body and be set to ceramics
Rich in variety glaze on green body, the riot of colour glaze are as follows in parts by weight: calcined limestone tailing powder 30-40, stone
10-15 parts of English, 10-15 parts of Red Stone Ware, 5-10 parts of nickel oxide, 5-10 parts of zirconium silicate powder, 5-10 parts of talcum, 1-5 parts of lead silicate,
1-5 parts of titanium oxide, 1-5 parts of lithium carbonate, 1-5 parts of di-iron trioxide, copper oxide 1-5,1-5 parts of manganese oxide.
2. the rich in variety glaze porcelain according to claim 1 prepared using limestone tailing, which is characterized in that described ten thousand
Purple thousand red glaze are as follows in parts by weight: calcined limestone tailing powder 38,11 parts of quartz, 14 parts of Red Stone Ware, 5 parts of nickel oxide,
9 parts of zirconium silicate powder, 6 parts of talcum, 2 parts of lead silicate, 5 parts of titanium oxide, 2 parts of lithium carbonate, 4 parts of di-iron trioxide, copper oxide 3, oxygen
Change 1 part of manganese.
3. the rich in variety glaze porcelain according to claim 1 prepared using limestone tailing, which is characterized in that described ten thousand
Purple thousand red glaze are as follows in parts by weight: calcined limestone tailing powder 33,13 parts of quartz, 14 parts of Red Stone Ware, 8 parts of nickel oxide,
9 parts of zirconium silicate powder, 5 parts of talcum, 3 parts of lead silicate, 3 parts of titanium oxide, 3 parts of lithium carbonate, 2 parts of di-iron trioxide, copper oxide 3, oxygen
Change 4 parts of manganese.
4. the rich in variety glaze porcelain according to claim 1 prepared using limestone tailing, which is characterized in that described ten thousand
Purple thousand red glaze are as follows in parts by weight: calcined limestone tailing powder 35,14 parts of quartz, 12 parts of Red Stone Ware, 6 parts of nickel oxide,
7 parts of zirconium silicate powder, 8 parts of talcum, 5 parts of lead silicate, 4 parts of titanium oxide, 2 parts of lithium carbonate, 2 parts of di-iron trioxide, copper oxide 3, oxygen
Change 2 parts of manganese.