CN106393839A - Multi-color shuttle woven label badge and making method thereof - Google Patents
Multi-color shuttle woven label badge and making method thereof Download PDFInfo
- Publication number
- CN106393839A CN106393839A CN201610808429.2A CN201610808429A CN106393839A CN 106393839 A CN106393839 A CN 106393839A CN 201610808429 A CN201610808429 A CN 201610808429A CN 106393839 A CN106393839 A CN 106393839A
- Authority
- CN
- China
- Prior art keywords
- woven label
- woven
- layer
- piao
- chapter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a multi-color shuttle woven label badge and a making method thereof. The woven label badge is composed of an ironing-pressing integrated woven label layer, a hot melt adhesive film layer and a fusible interlining layer, wherein the hot melt adhesive film layer is arranged between the back side of the woven label layer and the slurry point surface of the fusible interlining layer. The above three layers are integrated into one through ironing and pressing and then undergo laser cutting to form an individual woven label badge. The woven label badge made in the invention is smooth, stable in structure, slightly elastic, comfortable in handle, resistant to washing and free of wrinkling and deformation.
Description
Technical field
The invention belongs to textile garment adjuvant technical field, more particularly to a kind of polychrome tatting mark chapter and its making side
Method.
Background technology
Woven label with embroider be all with yarn show character pattern content, product good color fastness, resistance to wash water, soft relax
Suitable.Woven label is compared with embroidery, and woven label more can show micro-content, therefore, much need to show the embroidery of fine and smooth pattern, can be with woven label
Embroider object for patch, bound edge embroiders ready-made clothes.We will be individual for the woven label embroidering object as patch, referred to as woven label chapter.
Woven label is relatively soft, easily stretchable deformation, and existing woven label chapter way is in woven label back side hot pressure last layer adhesive lining Piao
Support, stablizes the shape of woven label chapter, so that follow-up embroidery operation.But for the woven label more than color shuttle, woven label is thicker, back side float
Many, Piao is bad with woven label degree of adhesion for adhesive lining, can peel off, deform, wrinkling after wash water, impact ready-made clothes quality.
Content of the invention
Based on this, in order to overcome the defect of above-mentioned prior art, the invention provides a kind of polychrome tatting mark chapter and its system
Make method.
In order to realize foregoing invention purpose, this invention takes technical scheme below：
A kind of polychrome tatting mark chapter, woven label layer, PUR film layer and adhesive lining Piao's layer that described woven label chapter is unified by hot pressure
Composition, described PUR film layer is arranged between the back side of described woven label layer and the slurry point face of described adhesive lining Piao's layer.Described knit
Mark layer is woven label chapter main body, carries label information；Described PUR film layer bonding woven label layer plain layer with lining, and firm woven label knot
Structure；Described adhesive lining Piao's layer supports and stablizes woven label chapter main body, and avoids the impact to ready-made clothes for the hot melt adhesive film.
Wherein in some embodiments, the material of described PUR film layer is TPU.
Wherein in some embodiments, the woven label of described woven label chapter is by 1 warp systems and 3～12 weft systems structures
Become, its end count is 140～152 pieces/inch, or 280～304 pieces/inch, filling density is 120～228 pieces/inch；Warp thread thickness is
50D～100D Polyester Yarns, weft yarn thickness is 50D～100D Polyester Yarns.
Wherein in some embodiments, the material of described adhesive lining Piao's layer is PET non-woven fabrics.
Present invention also offers the manufacture method of above-mentioned polychrome tatting mark chapter, comprise the following steps：
(1), woven label writes flower design：Woven label write complete in colored software woven label write flower design, the knitting needle group of flat woven mark
Piece number knitted is not more than 32 pieces, and piece number of the knitting needle tissue of the woven mark of satin face is not more than 64 pieces；
(2), weave：During weaving, warp tension is 35～45g；Weft tension is 5～20g；Woven label board heat setting temperature
For 140 DEG C～150 DEG C；
(3), hot pressure：By adhesive lining Piao, hot melt adhesive film, the unification of woven label hot pressure, its hot pressure temperature is 120 DEG C～130 DEG C, scalds
15～20 seconds pressure time, pressure 20～30N/cm2；
(4), radium-shine cutting：According to woven label chapter required form, shape woven label chapter individual.
Wherein in some embodiments, in step (1), when color shuttle quantity is more than 4, skew subnetting can be done.
Wherein in some embodiments, in step (3), the operational approach of described hot pressure unification is：By adhesive lining Piao, hot melt
After glued membrane, woven label are put successively, with the unification of flat garment press hot pressure.
Wherein in some embodiments, in step (3), the operational approach of described hot pressure unification is：First by hot melt adhesive film with
After adhesive lining Piao unites two into one through continuous way boiling hot Piao machine, then unify with woven label hot pressure.
Compared with prior art, the invention has the advantages that：
1st, the woven label chapter of the present invention increased one layer of hot melt adhesive film in the middle of woven label layer and adhesive lining Piao's layer, and hot melt adhesive film is very
Bond well woven label and adhesive lining Piao, penetrated into the woven label back side, make woven label Stability Analysis of Structures, during wash water, will not shell
From, will not be wrinkling, and there is certain elasticity, shape recovery back is good, is unlikely to deform, and keeps the smooth of woven label chapter；Woven label chapter is to wrap
The form that side is embroidered sews on ready-made clothes, it is to avoid people's phenomenon is scraped at edge；
2nd, the woven label chapter of the present invention is in manufacturing process, when woven label writes flower design, the knitting needle tissue of flat woven mark
Piece number is not more than 32 pieces, and piece number of the knitting needle tissue of the woven mark of satin face is not more than 64 pieces, woven label back filling floating fail to grow up in
6mm so that woven label structure relative close, beneficial to the bonding of woven label and lining Piao；
3rd, the manufacture method of the woven label chapter of the present invention, by using suitable hot pressure through weft tension, controls woven label woven
Hot pressure temperature when setting temperature is higher than three-in-one, thus the thermal contraction phenomenon during reducing hot pressure, makes woven label shape steady
Fixed.
Brief description
Fig. 1 is the embodiment of the present invention 1, in embodiment 2 woven label chapter structural representation, wherein 1 is woven label, and 101 is to carry
The woven label front of label information, 2 is hot melt adhesive film, and 3 is adhesive lining Piao, and 301 is the slurry point face of adhesive lining Piao；
Fig. 2 is the full pattern figure of polychrome tatting mark chapter in the embodiment of the present invention 1；
Fig. 3 is the full pattern figure of polychrome tatting mark chapter in the embodiment of the present invention 2.
Specific embodiment
It is further discussed below the present invention below in conjunction with the accompanying drawings with specific embodiment, the present invention does not address part and is applied to existing skill
Art.
The specific embodiment of the present invention is given below, but embodiment is merely to be described in further detail this explanation, not
Limit the claim of the present invention.
Embodiment 1
Woven label chapter technological parameter in the present embodiment is：Woven label is that satin face is woven to be made, the long 85mm of woven label, wide 50mm；After cutting
Long 80mm, width 45mm after cutting.Woven label style warp thread number 576, weft yarn number 488；292 pieces/inch of woven label end count, 146/English of filling density
Very little；Woven label warp thread is that 50D is white, and woven label weft yarn is, the 1st color shuttle white _ Polyester Yarns 75D (woven label ground), shuttle number 488, the 2nd Se Suobai
Color _ Polyester Yarns 75D (word is white, brave body is white), shuttle number the 488, the 3rd color shuttle yellow _ Polyester Yarns 75D (brave yellowish body color), shuttle number 488,
4 Se Suose _ Polyester Yarns 75D (brave body is orange), shuttle number 436；5th color shuttle brown _ Polyester Yarns 75D (brave body brown), shuttle number
418；Woven label total shuttle number is 2318.
The manufacture method of the woven label chapter of the present embodiment, specifically includes following steps:
(1), woven label writes flower design：First write, in woven label, the editor completing woven label pattern design in colored software；Organized again
Control.Its organizational controls rule is：1st color shuttle white woven label " " be organized as 8 piece 5 flying filling face tissue；2nd color shuttle white lining
Be organized as 16 piece 5 fly through covering weave；3rd color shuttle yellow knitting needle be organized as 48 piece 37 fly through covering weave, the 4th Se Suose net
Shuttle be organized as 48 piece 37 fly through covering weave broadwise offset 16 interlacing points, the 5th color shuttle brown knitting needle be organized as 48 piece 37 fly
Offset 32 interlacing points through covering weave broadwise, the 3rd, the 4th, the 5th color fusiformis becomes skew subnetting.Maximum piece of the present embodiment knitting needle tissue
Number is 48 pieces, and the floating of woven label back filling is failed to grow up in 5mm so that woven label structure relative close, viscous beneficial to woven label and lining Piao
Close.
(2), weave：After the completion of woven label writes flower design, make electronics stricture of vagina version, made with the satin face of burning side machine is woven.During weaving
Warp tension is 35～45g；Weft tension is 5～20g；Woven label board heat setting temperature is 140 DEG C～150 DEG C.
(3), hot pressure：As shown in figure 1, being the structural representation of woven label chapter, it is with flat garment press, by woven label 1
Carrying label information woven label front 101 down, place hot melt adhesive film 2 above woven label 1, then cover above hot melt adhesive film 2
Lid adhesive lining Piao 3, the slurry point face 301 of adhesive lining Piao 3 down, is unified through hot pressure after putting successively.Its hot pressure temperature be 120 DEG C～
130 DEG C, 15～20 seconds hot pressure time, pressure 20～30N/cm2.
(4), radium-shine cutting：According to woven label chapter required form, shape woven label chapter individuality (Fig. 2).
The present embodiment obtains by 1 warp systems and the woven woven label of 5 weft systems, close structure, and clear patterns are thin
Greasy, embroider and can not possibly embody.1 layer of woven label that polychrome tatting mark chapter is unified by hot pressure, adhesive lining Piao 3 layers and hot melt adhesive film 2
Layer composition, 2 layers of described hot melt adhesive film is arranged between the back side and the slurry point face 301 of described adhesive lining Piao's layer of 1 layer of described woven label.
Described woven label layer is woven label chapter main body, and woven label front 101 carries label information；Described PUR film layer bonding woven label layer and lining Piao
Layer, and firm woven label structure；Described adhesive lining Piao's layer supports and stablizes woven label chapter main body, and avoids the shadow to ready-made clothes for the hot melt adhesive film
Ring.Woven label adds hot melt adhesive film, adhesive lining Piao totally three layers of material hot pressure unification, more radium-shine cutting forming woven label chapter individuality (Fig. 2),
Woven label chapter is smooth, and stable, percent thermal shrinkage is little, somewhat resilient, resistance to wash water, wrinkle resistant, indeformable.Woven label chapter is in the form of bound edge embroidery
Sew on ready-made clothes, it is to avoid people's phenomenon is scraped at edge, ready-made clothes quality is high.
Embodiment 2
Woven label chapter technological parameter in the present embodiment is：Woven label is made for flat woven, the long 66mm of woven label, wide 66mm；After cutting
Long 63mm, width 63mm after cutting.Woven label style warp thread number 384, weft yarn number 384；146 pieces/inch of woven label end count, 146/English of filling density
Very little；Woven label warp thread is that 75D is white, and woven label weft yarn is, the 1st color shuttle is cream-coloured _ Polyester Yarns 100D (woven label ground), shuttle number 384, and the 2nd color shuttle
White _ Polyester Yarns 100D (chapter word is white), shuttle number the 384, the 3rd color shuttle black _ Polyester Yarns 100 (word), shuttle number 384；4th color shuttle ash
Color _ Polyester Yarns 100D (ox head), shuttle number 92；5th color shuttle redness _ Polyester Yarns 100 (chapter), shuttle number 104；Woven label total shuttle number is
1348.
The manufacture method of the woven label chapter of the present embodiment, specifically includes following steps:
(1), woven label writes flower design：First write, in woven label, the editor completing woven label pattern design in colored software；Organized again
Control.Its organizational controls rule is：The cream-coloured woven label of 1st color shuttle " " be organized as 5 piece 2 flying filling face tissue；2nd color shuttle white lining
Be organized as 10 piece 7 fly through covering weave；3rd color shuttle black knitting needle be organized as 20 piece 7 fly through covering weave, the 4th color shuttle Lycoperdon polymorphum Vitt net
Shuttle be organized as 20 piece 7 flying through covering weave, the 5th color shuttle redness knitting needle be organized as 20 piece 7 flying through covering weave.The present embodiment knitting needle
The maximum piece number of tissue is 20 pieces, and the floating of woven label back filling is failed to grow up in 4mm so that woven label structure relative close, beneficial to woven label
Bonding with lining Piao.
(2), weave：After the completion of woven label writes flower design, make electronics stricture of vagina version, made with the flat woven burning side machine.During weaving
Warp tension is 35～45g；Weft tension is 5～20g；Woven label board heat setting temperature is 140 DEG C～150 DEG C.
(3), hot pressure：As shown in figure 1, being the structural representation of woven label chapter, it can be first by hot melt adhesive film 2 and adhesive lining Piao 3
After uniting two into one through continuous way boiling hot Piao machine, then on flat garment press, it is covered in above woven label 1, carry knitting of label information
Mark front 101 is unified through hot pressure down.Its hot pressure temperature is 120 DEG C～130 DEG C, 15～20 seconds hot pressure time, pressure 20～
30N/cm2.
(4), radium-shine cutting：According to woven label chapter required form, shape woven label chapter individuality (Fig. 3).
The woven label that the present embodiment obtains is woven by 5 color shuttles, woven label layer that polychrome tatting mark chapter is unified by hot pressure, viscous
Close the plain layer of lining and PUR film layer composition, described PUR film layer is arranged at the back side of described woven label layer and described adhesive lining Piao's layer
Slurry point face between.Described woven label layer is woven label chapter main body, and woven label front carries label information；Described PUR film layer bonding is knitted
Mark layer plain layer with lining, and firm woven label structure；Described adhesive lining Piao's layer supports and stablizes woven label chapter main body, and avoids hot melt adhesive film
Impact to ready-made clothes.Unify through three layers of material hot pressure, more radium-shine cutting forming woven label chapter is individual (Fig. 3), woven label chapter is smooth, structure
Stable, somewhat resilient, comfortable feel, resistance to wash water, wrinkle resistant, indeformable.
Each technical characteristic of embodiment described above can arbitrarily be combined, for making description succinct, not to above-mentioned reality
The all possible combination of each technical characteristic applied in example is all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all it is considered to be the scope of this specification record.
Embodiment described above only have expressed the several embodiments of the present invention, and its description is more concrete and detailed, but simultaneously
Can not therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
Say, without departing from the inventive concept of the premise, some deformation can also be made and improve, these broadly fall into the protection of the present invention
Scope.Therefore, the protection domain of patent of the present invention should be defined by claims.
Claims (8)
1. a kind of polychrome tatting mark chapter it is characterised in that described woven label chapter unified by hot pressure woven label layer, PUR film layer and viscous
Close lining plain layer composition, described PUR film layer be arranged at the back side of described woven label layer and described adhesive lining Piao's layer slurry point face it
Between.
2. polychrome tatting mark chapter according to claim 1 is it is characterised in that the material of described PUR film layer is TPU.
3. polychrome tatting mark chapter according to claim 1 is it is characterised in that the woven label of described woven label chapter is by 1 warp thread system
System is constituted with 3～12 weft systems, and its end count is 140～152 pieces/inch, or 280～304 pieces/inch, and filling density is 120～
228 pieces/inch；Warp thread thickness is 50D～100D Polyester Yarns, and weft yarn thickness is 50D～100D Polyester Yarns.
4. polychrome tatting mark chapter according to claim 1 it is characterised in that described adhesive lining Piao layer material be PET no
Spin cloth.
5. the manufacture method of the polychrome tatting mark chapter described in any one of Claims 1 to 4 is it is characterised in that comprise the following steps：
(1), woven label writes flower design：Woven label write complete in colored software woven label write flower design, flat woven mark knitting needle tissue
Piece number is not more than 32 pieces, and piece number of the knitting needle tissue of the woven mark of satin face is not more than 64 pieces；
(2), weave：During weaving, warp tension is 35～45g；Weft tension is 5～20g；Woven label board heat setting temperature is 140
DEG C～150 DEG C；
(3), hot pressure：By adhesive lining Piao, hot melt adhesive film, the unification of woven label hot pressure, its hot pressure temperature is 120 DEG C～130 DEG C, during hot pressure
Between 15～20 seconds, pressure 20～30N/cm2；
(4), radium-shine cutting forming.
6. the manufacture method of polychrome tatting mark chapter according to claim 5 is it is characterised in that in step (1), when color shuttle number
When amount is more than 4, do skew subnetting.
7. the manufacture method of polychrome tatting mark chapter according to claim 5 is it is characterised in that in step (3), described hot pressure
Unification operational approach be：After adhesive lining Piao, hot melt adhesive film, woven label are put successively, with the unification of flat garment press hot pressure.
8. the manufacture method of polychrome tatting mark chapter according to claim 5 is it is characterised in that in step (3), described hot pressure
Unification operational approach be：First hot melt adhesive film and adhesive lining Piao is scalded after Piao's machine unites two into one through continuous way, then with woven label hot pressure
Unification.