CN106381969A - Simulated granite external wall panel and preparation method for same - Google Patents
Simulated granite external wall panel and preparation method for same Download PDFInfo
- Publication number
- CN106381969A CN106381969A CN201610769336.3A CN201610769336A CN106381969A CN 106381969 A CN106381969 A CN 106381969A CN 201610769336 A CN201610769336 A CN 201610769336A CN 106381969 A CN106381969 A CN 106381969A
- Authority
- CN
- China
- Prior art keywords
- bed
- parts
- side fascia
- cement
- artificial granite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a simulated granite external wall panel and a preparation method for the same. The simulated granite external wall panel comprises a base material layer, a middle material layer and a surface material layer, wherein middle material layer is arranged between the base material layer and the surface material layer; the base material layer is mainly composed of the following raw material: cement, silica fume, coal ash, silica sand, polypropylene fiber and additives; the middle material layer is mainly made of the following raw material of cement, silica fume, coal ash, construction waste powder, polypropylene fibers, magnesium oxide, talcum powder, bamboo fibers, diatomite, coal gangue, calcined kaolin, gypsum and additives; and the surface material layer is made of the following raw material of cement, silica fume, coal ash, black sand, white sand, iron oxide red, iron oxide black, master slices, silver slices and additives. The simulated granite external wall panel has excellent product performance and beautiful and elegant appearance; the material used requires low cost, so production cost can be reduced; and the preparation method is simple and can be easily applied; and production period can be shortened and production efficiency can be improved.
Description
Technical field
The present invention relates to building material field, particularly to a kind of artificial granite Side fascia and preparation method thereof.
Background technology
At present external wall decorative material is by many kinds, such as marble, granite, coating, pottery, metal, glass etc..But this
Several ornament materials have the shortcomings that very big.Coating is from heavy and light, but resistance to soiling, durability are particularly poor.Ceramic mosaic is breathed freely
Property poor, occur freeze-thaw damage probability big, to hurt sb.'s feelings after coming off hidden danger in high-altitude.Complexity installed by the materials such as stone material, metal, glass, makes
High price is expensive, does not popularize.
The information being disclosed in this background section is merely intended to increase the understanding of the general background to the present invention, and should not
Recognize when being considered or imply in any form that this information structure has been the prior art well known to persons skilled in the art.
Content of the invention
It is an object of the invention to provide a kind of artificial granite Side fascia, thus overcome existing Side fascia cost height, install
Complicated shortcoming.
Another object of the present invention is to the preparation method of artificial granite Side fascia.
For achieving the above object, the invention provides a kind of artificial granite Side fascia, described artificial granite Side fascia includes
Initial bed, the middle bed of material and precoat, between described middle bed of material setting and described initial bed and precoat；Described initial bed mainly by
Following raw material is prepared from：Cement, SILICA FUME, flyash, quartz sand, polypropylene fibre and additive；The described middle bed of material is main
It is prepared from the following materials：Cement, SILICA FUME, flyash, building waste powder, polypropylene fibre, magnesium oxide, Pulvis Talci,
Bamboo fibre, kieselguhr, gangue, calcined kaolin, Gypsum Fibrosum and additive；Described precoat mainly prepared by following raw material and
Become：Cement, SILICA FUME, flyash, black sand, white sand, iron oxide red, iron oxide black, golden master slice, silver-colored master slice and additive.
Preferably, in technique scheme, described initial bed is mainly prepared from the following materials, and counts by weight,
Cement 100-150 part, SILICA FUME 5-20 part, flyash 15-30 part, quartz sand 30-50 part, polypropylene fibre 1-5 part and additional
Agent 5-10 part；
Preferably, in technique scheme, the described middle bed of material is mainly prepared from the following materials, and counts by weight,
Cement 100-150 part, SILICA FUME 4-26 part, flyash 15-30 part, building waste powder 30-50 part, polypropylene fibre 2-8 part,
Magnesium oxide 1-10 part, Pulvis Talci 15-30 part, bamboo fibre 15-30 part, kieselguhr 15-30 part, gangue 10-15 part, calcining kaolinite
Native 5-20 part, Gypsum Fibrosum 13-28 part and additive 5-10 part.
Preferably, in technique scheme, described precoat is mainly prepared from the following materials, and counts by weight,
Cement 100-150 part, SILICA FUME 5-20 part, flyash 15-30 part, black sand 40-60 part, white sand 40-60 part, iron oxide red 1-5 part, ferrum
Black 1-5 part, golden master slice 0.5-2 part, silver-colored master slice 0.5-2 part and additive 5-10 part.
Preferably, in technique scheme, described additive is mainly made up by weight of following component：Polycarboxylic acids subtract
Water preparation 0.1-1 part, boric acid 0.1-1 part, cellulose ether 0.1-0.5 part, defoamer 0.1-1 part.
Preferably, in technique scheme, described cellulose ether is methylcellulose, hydroxyethylmethyl-cellulose, carboxylic first
One of base cellulose or ethyl cellulose.
Preferably, in technique scheme, described defoamer is mainly made up by weight of following component：Epoxy chloropropionate
Alkane 10-20 part, Tissuemat E 1-5 part, polyoxyethylene polyoxypropylene glycerin ether 5-10 part and polyacrylamide 5-10 part.
Preferably, in technique scheme, in described initial bed and the described middle bed of material, it is equipped with fiberglass gridding cloth.
A kind of preparation method of artificial granite Side fascia, comprises the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added blender according to respective material rate and water
Middle stirring 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance and obtain product.
Preferably, in technique scheme, described maintenance be temperature 30-80 DEG C, relative humidity be 70-90% environment
Under, carry out maintenance 2-5 days.
Compared with prior art, the present invention has the advantages that：The artificial granite Side fascia that the present invention is obtained, it is joined
Fang Heli, prepared product does not contain radioactivity stone material and harmful paint, reaches artificial granite effect by material intrinsic colour.Product
Excellent performance, specious generous.Material therefor is cheap, reduces production cost.Preparation method is simple, convenient to carry out it is easy to
Grasp, and with short production cycle, improve production efficiency.
Specific embodiment
With reference to specific embodiment, the specific embodiment of the present invention is described in detail, it is to be understood that this
Bright protection domain is not limited by specific embodiment.
Embodiment 1
A kind of artificial granite Side fascia, described artificial granite Side fascia includes initial bed, the middle bed of material and precoat, described in
Between bed of material setting and described initial bed and precoat.
Described initial bed is mainly prepared from the following materials, and counts by weight, 130 parts of cement, 11 parts of SILICA FUME, powder
23 parts of coal ash, 43 parts of quartz sand, 3 parts of polypropylene fibre and 7 parts of additive；
The described middle bed of material is mainly prepared from the following materials, and counts by weight, 120 parts of cement, 21 parts of SILICA FUME, powder
17 parts of coal ash, 40 parts of building waste powder, 6 parts of polypropylene fibre, 7 parts of magnesium oxide, 22 parts of Pulvis Talci, 26 parts of bamboo fibre, diatom
21 parts of soil, 12 parts of gangue, 11 parts of calcined kaolin, 18 parts of Gypsum Fibrosum and 8 parts of additive.
Described precoat is mainly prepared from the following materials, and counts by weight, 130 parts of cement, 13 parts of SILICA FUME, powder
22 parts of coal ash, 50 parts of black sand, 54 parts of white sand, 3 parts of iron oxide red, iron black 3 parts, golden 1 part of master slice, 1.5 parts of silver-colored master slice and 7 parts of additive.
Described additive is mainly made up by weight of following component：0.5 part of polycarboxylate water-reducer, 0.5 part of boric acid, fibre
Plain 0.4 part of the ether of dimension, 0.7 part of defoamer.
Described defoamer is mainly made up by weight of following component：13 parts of epoxychloropropane, 3 parts of Tissuemat E, poly-
7 parts of oxygen ethylene polypropylene glycerol aether and 7 parts of polyacrylamide.
Described cellulose ether is methylcellulose.
It is equipped with fiberglass gridding cloth in described initial bed and the described middle bed of material.
A kind of preparation method of artificial granite Side fascia, comprises the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added blender according to respective material rate and water
Middle stirring 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance, maintenance is to be in temperature 50-60 DEG C, relative humidity
Under 75-80% environment, carry out maintenance 3 days, obtain product, according to construction requirement, size of all sizes can be cut into.
The wallboard that detection above-described embodiment is made, wallboard strength=15.3MPa, comprcssive strength=13.7MPa, tensile strength
=7.7MPa.
Embodiment 2
A kind of artificial granite Side fascia, described artificial granite Side fascia includes initial bed, the middle bed of material and precoat, described in
Between bed of material setting and described initial bed and precoat.
Described initial bed is mainly prepared from the following materials, and counts by weight, 100 parts of cement, 20 parts of SILICA FUME, powder
15 parts of coal ash, 50 parts of quartz sand, 5 parts of polypropylene fibre and 5 parts of additive；
The described middle bed of material is mainly prepared from the following materials, and counts by weight, cement 100-150 part, SILICA FUME 4-
26 parts, flyash 15-30 part, building waste powder 30-50 part, polypropylene fibre 2-8 part, magnesium oxide 1-10 part, Pulvis Talci 15-
30 parts, bamboo fibre 15-30 part, kieselguhr 15-30 part, gangue 10-15 part, calcined kaolin 5-20 part, Gypsum Fibrosum 13-28 part and
Additive 5-10 part.
Described precoat is mainly prepared from the following materials, and counts by weight, 100 parts of cement, 5 parts of SILICA FUME, powder
30 parts of coal ash, 40 parts of black sand, 60 parts of white sand, 1 part of iron oxide red, iron black 5 parts, golden 0.5 part of master slice, 2 parts of silver-colored master slice and 5 parts of additive.
Described additive is mainly made up by weight of following component：1 part of polycarboxylate water-reducer, 0.1 part of boric acid, fiber
0.1 part of plain ether, 0.1 part of defoamer.
Described defoamer is mainly made up by weight of following component：20 parts of epoxychloropropane, 1 part of Tissuemat E, poly-
10 parts of oxygen ethylene polypropylene glycerol aether and 5 parts of polyacrylamide.
Described cellulose ether is ethyl cellulose.
It is equipped with fiberglass gridding cloth in described initial bed and the described middle bed of material.
A kind of preparation method of artificial granite Side fascia, comprises the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added blender according to respective material rate and water
Middle stirring 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance, maintenance is to be in temperature 30-40 DEG C, relative humidity
Under 70-80% environment, carry out maintenance 3 days, obtain product, according to construction requirement, size of all sizes can be cut into.
The wallboard that detection above-described embodiment is made, wallboard strength=14.7MPa, comprcssive strength=12.5MPa, tensile strength
=6.7MPa.
Embodiment 3
A kind of artificial granite Side fascia, described artificial granite Side fascia includes initial bed, the middle bed of material and precoat, described in
Between bed of material setting and described initial bed and precoat.
Described initial bed is mainly prepared from the following materials, and counts by weight, 150 parts of cement, 5 parts of SILICA FUME, powder
30 parts of coal ash, 30 parts of quartz sand, 1 part of polypropylene fibre and 10 parts of additive；
The described middle bed of material is mainly prepared from the following materials, and counts by weight, cement 100-150 part, SILICA FUME 4-
26 parts, flyash 15-30 part, building waste powder 30-50 part, polypropylene fibre 2-8 part, magnesium oxide 1-10 part, Pulvis Talci 15-
30 parts, bamboo fibre 15-30 part, kieselguhr 15-30 part, gangue 10-15 part, calcined kaolin 5-20 part, Gypsum Fibrosum 13-28 part and
Additive 5-10 part.
Described precoat is mainly prepared from the following materials, and counts by weight, 150 parts of cement, 20 parts of SILICA FUME, powder
15 parts of coal ash, 60 parts of black sand, 40 parts of white sand, 5 parts of iron oxide red, iron black 1 part, golden 2 parts of master slice, 0.5 part of silver-colored master slice and 10 parts of additive.
Described additive is mainly made up by weight of following component：0.1 part of polycarboxylate water-reducer, 1 part of boric acid, fiber
0.1 part of plain ether, 1 part of defoamer.
Described defoamer is mainly made up by weight of following component：10 parts of epoxychloropropane, 5 parts of Tissuemat E, poly-
5 parts of oxygen ethylene polypropylene glycerol aether and 10 parts of polyacrylamide.
Described cellulose ether is hydroxyethylmethyl-cellulose.
It is equipped with fiberglass gridding cloth in described initial bed and the described middle bed of material.
A kind of preparation method of artificial granite Side fascia, comprises the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added blender according to respective material rate and water
Middle stirring 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance, maintenance is to be in temperature 70-80 DEG C, relative humidity
Under 80-90% environment, carry out maintenance 3 days, obtain product, according to construction requirement, size of all sizes can be cut into.
The wallboard that detection above-described embodiment is made, wallboard strength=14.9MPa, comprcssive strength=13.3MPa, tensile strength
=6.8MPa.
Embodiment 4
A kind of artificial granite Side fascia, described artificial granite Side fascia includes initial bed, the middle bed of material and precoat, described in
Between bed of material setting and described initial bed and precoat.
Described initial bed is mainly prepared from the following materials, and counts by weight, 130 parts of cement, 11 parts of SILICA FUME, powder
23 parts of coal ash, 43 parts of quartz sand and 3 parts of polypropylene fibre；
The described middle bed of material is mainly prepared from the following materials, and counts by weight, 120 parts of cement, 21 parts of SILICA FUME, powder
17 parts of coal ash, 40 parts of building waste powder, 6 parts of polypropylene fibre, 7 parts of magnesium oxide, 22 parts of Pulvis Talci, 26 parts of bamboo fibre, diatom
21 parts of soil, 12 parts of gangue, 11 parts of calcined kaolin and 18 parts of Gypsum Fibrosum.
Described precoat is mainly prepared from the following materials, and counts by weight, 130 parts of cement, 13 parts of SILICA FUME, powder
22 parts of coal ash, 50 parts of black sand, 54 parts of white sand, 3 parts of iron oxide red, iron black 3 parts, 1 part of golden master slice and silver-colored 1.5 parts of master slice.
It is equipped with fiberglass gridding cloth in described initial bed and the described middle bed of material.
A kind of preparation method of artificial granite Side fascia, comprises the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added blender according to respective material rate and water
Middle stirring 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance, maintenance is to be in temperature 50-60 DEG C, relative humidity
Under 75-80% environment, carry out maintenance 3 days, obtain product, according to construction requirement, size of all sizes can be cut into.
The wallboard that detection above-described embodiment is made, wallboard strength=9.5MPa, comprcssive strength=6.4MPa, tensile strength=
3.6MPa.
Embodiment 5
A kind of artificial granite Side fascia, described artificial granite Side fascia includes initial bed, the middle bed of material and precoat, described in
Between bed of material setting and described initial bed and precoat.
Described initial bed is mainly prepared from the following materials, and counts by weight, 130 parts of cement, 11 parts of SILICA FUME, powder
23 parts of coal ash, 43 parts of quartz sand, 3 parts of polypropylene fibre and 7 parts of additive；
The described middle bed of material is mainly prepared from the following materials, and counts by weight, 120 parts of cement, 21 parts of SILICA FUME, powder
17 parts of coal ash, 40 parts of building waste powder, 6 parts of polypropylene fibre, 7 parts of magnesium oxide, 18 parts of Gypsum Fibrosum and 8 parts of additive.
Described precoat is mainly prepared from the following materials, and counts by weight, 130 parts of cement, 13 parts of SILICA FUME, powder
22 parts of coal ash, 50 parts of black sand, 54 parts of white sand, 3 parts of iron oxide red, iron black 3 parts, golden 1 part of master slice, 1.5 parts of silver-colored master slice and 7 parts of additive.
Described additive is mainly made up by weight of following component：0.5 part of polycarboxylate water-reducer, 0.5 part of boric acid, fibre
Plain 0.4 part of the ether of dimension, 0.7 part of defoamer.
Described defoamer is mainly made up by weight of following component：13 parts of epoxychloropropane, 3 parts of Tissuemat E, poly-
7 parts of oxygen ethylene polypropylene glycerol aether and 7 parts of polyacrylamide.
Described cellulose ether is methylcellulose.
It is equipped with fiberglass gridding cloth in described initial bed and the described middle bed of material.
A kind of preparation method of artificial granite Side fascia, comprises the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added blender according to respective material rate and water
Middle stirring 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance, maintenance is to be in temperature 50-60 DEG C, relative humidity
Under 75-80% environment, carry out maintenance 3 days, obtain product, according to construction requirement, size of all sizes can be cut into.
The wallboard that detection above-described embodiment is made, wallboard strength=12.1MPa, comprcssive strength=11.1MPa, tensile strength
=5.9MPa.
The description of the aforementioned specific illustrative embodiment to the present invention illustrate that and illustration purpose.These descriptions
It is not wishing to limit the invention to disclosed precise forms, and it will be apparent that according to above-mentioned teaching, can much be changed
And change.The purpose of selecting and describing the exemplary embodiment is that explaining that the certain principles of the present invention and its reality should
With so that those skilled in the art be capable of and utilize the present invention various different exemplary and
Various different selections and change.The scope of the present invention is intended to be limited by claims and its equivalents.
Claims (10)
1. a kind of artificial granite Side fascia is it is characterised in that described artificial granite Side fascia includes initial bed, the middle bed of material and fabric
Layer, between described middle bed of material setting and described initial bed and precoat；
Described initial bed is mainly prepared from the following materials：Cement, SILICA FUME, flyash, quartz sand, polypropylene fibre and outer
Plus agent；
The described middle bed of material is mainly prepared from the following materials：Cement, SILICA FUME, flyash, building waste powder, polypropylene are fine
Dimension, magnesium oxide, Pulvis Talci, bamboo fibre, kieselguhr, gangue, calcined kaolin, Gypsum Fibrosum and additive；
Described precoat is mainly prepared from the following materials：Cement, SILICA FUME, flyash, black sand, white sand, iron oxide red, iron oxide black,
Golden master slice, silver-colored master slice and additive.
2. artificial granite Side fascia according to claim 1 is it is characterised in that described initial bed is mainly by following raw material system
Standby form, count by weight, cement 100-150 part, SILICA FUME 5-20 part, flyash 15-30 part, quartz sand 30-50 part, poly-
Tacryl 1-5 part and additive 5-10 part.
3. artificial granite Side fascia according to claim 1 is it is characterised in that the described middle bed of material is mainly by following raw material system
For forming, count by weight, cement 100-150 part, SILICA FUME 4-26 part, flyash 15-30 part, building waste powder 30-
50 parts, polypropylene fibre 2-8 part, magnesium oxide 1-10 part, Pulvis Talci 15-30 part, bamboo fibre 15-30 part, kieselguhr 15-30 part,
Gangue 10-15 part, calcined kaolin 5-20 part, Gypsum Fibrosum 13-28 part and additive 5-10 part.
4. artificial granite Side fascia according to claim 1 is it is characterised in that described precoat is mainly by following raw material system
For forming, count by weight, cement 100-150 part, SILICA FUME 5-20 part, flyash 15-30 part, black sand 40-60 part, white sand
40-60 part, iron oxide red 1-5 part, iron black 1-5 part, golden master slice 0.5-2 part, silver-colored master slice 0.5-2 part and additive 5-10 part.
5. artificial granite Side fascia according to claim 1 is it is characterised in that described additive is mainly pressed by following component
Parts by weight are made：Polycarboxylate water-reducer 0.1-1 part, boric acid 0.1-1 part, cellulose ether 0.1-0.5 part, defoamer 0.1-1
Part.
6. artificial granite Side fascia according to claim 5 it is characterised in that described cellulose ether be methylcellulose,
One of hydroxyethylmethyl-cellulose, carboxymethyl cellulose or ethyl cellulose.
7. artificial granite Side fascia according to claim 6 is it is characterised in that described defoamer is mainly pressed by following component
Parts by weight are made：Epoxychloropropane 10-20 part, Tissuemat E 1-5 part, polyoxyethylene polyoxypropylene glycerin ether 5-10 part and poly-
Acrylamide 5-10 part.
8. artificial granite Side fascia according to claim 1 is it is characterised in that spread in described initial bed and the described middle bed of material
It is provided with fiberglass gridding cloth.
9. a kind of preparation method of artificial granite Side fascia as claimed in claim 1 is it is characterised in that comprise the following steps：
(1) prepare to produce required raw material；
(2) material of initial bed, the middle bed of material and precoat is sequentially added in blender according to respective material rate and water and stir
Mix 5-10 minute；
(3) bed material layer material is mated formation in template respectively, and lay fiberglass gridding cloth above；
(4) bed of material in laying above initial bed, and lay fiberglass gridding cloth on the middle bed of material；
(5) lay precoat on the middle bed of material, then carry out maintenance and obtain product.
10. according to claim 9 the preparation method of artificial granite Side fascia it is characterised in that described maintenance is in temperature
30-80 DEG C, relative humidity be 70-90% environment under, carry out maintenance 2-5 days.