CN106380937A - Milk-white environment-friendly type synthesis polymer steel roofing paint - Google Patents
Milk-white environment-friendly type synthesis polymer steel roofing paint Download PDFInfo
- Publication number
- CN106380937A CN106380937A CN201610774359.3A CN201610774359A CN106380937A CN 106380937 A CN106380937 A CN 106380937A CN 201610774359 A CN201610774359 A CN 201610774359A CN 106380937 A CN106380937 A CN 106380937A
- Authority
- CN
- China
- Prior art keywords
- parts
- solvent naphtha
- steel roofing
- paint
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly type synthesis polymer steel roofing paint, which belongs to the field of waterproof construction. The paint comprises the following components: 8-20 parts of a polyolefin thermoplastic elastomer, 4-8 parts of aldehyde ketone resin, 2-12 parts of styrene resin, 1-5 parts of silicon powder, 1-10 parts of mica powder, 1-5 parts of rutile titanium dioxide, 0.3-1 part of an antioxidant 1010, 0.3-1 part of an antioxidant 1076, 0.3-1 part of an anti-oxidant 531, 0.5-2.5 parts of an antifoaming agent, 0.3-1 part of an ultraviolet ray absorber, 5-30 parts of D40 solvent naphtha, and 5-30 parts of butyiate solvent naphtha. The milk-white steel roofing waterproof paint has the characteristics of no toxicity, no harm, no pollution, no containing of noxious materials and harmful components such as pitch and benzene, and realization of free toning. The product performance is stable, the material service life can reach 30 years or more, and has the characteristics of strong adhesion stress, good penetration performance and good elongation percentage.
Description
Technical field
The present invention relates to a kind of architectural waterproof material is and in particular to a kind of milky environment-friendly synthetic macromolecular steel roofing is special
Use coating.
Background technology
Buildings waterproof is by preventing water from the infiltration at some positions of building is taken from construction material and on construction
Measure.Using in roofing, hypogee, the under ground portion of building and the interior room needing waterproof and water storage structures more than waterproof
Deng.The measure taken by it and the difference of means, are divided into material waterproofing and constructional waterproofing two big class.Involved in the present invention is main
It is a kind of material waterproofing, the problem of the always one waterproof headache of protruding parts of steel structural roof, waterproof on the market at present
The material such as coating such as silica gel, APP, construction is complicated, is difficult that toning, decorative effect are poor, and permeability, cohesive force are poor, and properties of product are not
Stable, service life is short, containing multiple harmful chemicals preparations, and all can not solve the leakage problems of roofing well.And apply for
Artificially solve the above problems, applied for that in 2006 patent name is " green waterproof milk white polymer paint ", specially
Profit number for " 200610099088.2 " patent of invention although possess nontoxic, pollution-free, UV resistant irradiate, heat-insulated, anti-ageing
Change, direct brushing, construction are simple, and the features such as color-adjustable, but, after years of research and found that, this coating is permissible for interior,
For during outdoor steel roof waterproof, because outdoor environment is changeable, use environment is poor：Wind scrape drench with rain, the extraneous dirty spies such as many
Point, in outdoor UV resistant, loss of properties on aging, properties of product are not very stable to this coating, have more than is needed several years, properties of product
It is easily broken and water leakage situation occurs again, therefore be badly in need of improving.
Content of the invention
It is an object of the invention to overcoming the technology that in prior art, water-repellent paint exists in outdoor steel roof waterproof to ask
Topic, provides a kind of environment-friendly synthetic macromolecular steel roofing special coating, and this coating is steel roofing waterproof paint specially, ageing-resistant,
UV resistant performance is good, and properties of product are stable, and service life was up to 30 years as long as.
Technical scheme：A kind of environment-friendly synthetic macromolecular steel roofing special coating, this coating is made up of following components：Polyene
Hydrocarbon thermoplastic elastomer (TPE) 8-20 part, aldehyde ketone resin 4-8 part, styrene resin 2-12 part, silica flour 1-5 part, mica powder 1-10 part, gold
Red stone-type titanium dioxide 1-5 part, age resistor 1010 0.3-1 part, age resistor 1076 0.3-1 part, antioxidant 531 0.3-1 part, disappear
Infusion 0.5-2.5 part, UV absorbent 327 0.3-1 part, D40 solvent naphtha 5-30 part, butyl ester solvent naphtha 5-30 part.
Based on technique scheme, the steel roofing special coating of the present invention is made up of following components：Polylefin thermoplatic bullet
15 parts of gonosome, 6 parts of aldehyde ketone resin, 8 parts of styrene resin, 3 parts of silica flour, 5 parts of mica powder, 3 parts of Rutile type titanium dioxide, age resistor
1010 0.7 parts, 1,076 0.6 parts of age resistor, 531 0.8 parts of antioxidant, 1 part of defoamer, 327 0.8 parts of UV absorbent,
20 parts of D40 solvent naphtha, 15 parts of butyl ester solvent naphtha.
Main component in technique scheme is：TPO, aldehyde ketone resin and styrene resin, its
Middle TPO is a kind of High performance polyolefin product, at normal temperatures become caoutchouc elasticity, have density little, bending
Greatly, low-temperature impact resistance height, easy processing, reusable the features such as.Aldehyde ketone resin refers to by ketone and aldehydes through polycondensation reaction
Polymer, also referred to as aldehyde ketone resin or polyketone resin.The chemical constitution of aldehyde ketone resin gives its very special quality and spy
Property, resin defines the circulus of saturation so as to have high glaze, hardness, anti-degraded and weatherability feature in the condensation phase.By
Do not contain ester bond in the structure in this resin, thus have preferable resistance to water, major key contains a lot of cyclohexyls so as to have
Thermostability.In addition, the polarity of ketone groups and hydroxyl groups makes it have extensive dissolubility intermiscibility, therefore, polyketone resin both may be used
The compound larger with polarity is compatible, again can be compatible with the less compound of polarity, is suitable for most of ink, coating and adhesive
System.Styrene resin is engineering thermoplasties, has very high impact strength and toughness, can improve as coating additive
UV resistant performance and heat stability, anti-flammability and antistatic property.After triplicity, product genus paint property of the present invention is polynary poly-
Compound, becomes a kind of continuous closing rubber-like elastic body, has superpower cohesive force, may penetrate into cement after product curing of coating
2-3 millimeter, is integrated with cement basic layer completely, has high tensile, can effectively resist because of building basic unit uneven settlement,
The face coat crack performance that structural cracking caused by four seasons difference variation causes occurs.
The present invention has the advantages that：1. the present invention is milky steel roofing waterproof paint specially, the product five poisonous creatures: scorpion, viper, centipede, house lizard, toad,
Harmless, pollution-free, the not noxious substance harmful components such as bituminous, benzene, the health of environment and personnel is all had no adverse effects, product
For milky, can achieve and freely mix colours, color and luster is attractive in appearance, product can need to match colors according to design requirement and user, has splendid
Heat-insulation and heat-preservation and decoration effect.
2. stable performance, stable performance in the presence of ultraviolet, light, heat and oxygen, the materials'use life-span reaches in external enwergy
More than 30 years, under protective layer, service life was identical with cement.
3. cohesive force is extremely strong, adhesion strength 1.8MPa, does not peel off under external force, not stratified, can form stable preventing
Water is overall, because cohesive force is excellent, filled up China can only downstream waterproof it is impossible to the technological gap of waterproof against the current.
4th, permeance property is good, because the permeance property of material is good, applies brush material and can penetrate into cement basic layer basic material
Space in, plug penetrating passage, good water-proof effect, permeable cement basic unit 2-3mm, combine together with cement basic layer completely
5. elongation percentage is high, product waterproof, antistatic, anti-fracture, elongation percentage height after solidification, because elongation percentage is high, after basic unit's deformation, prevents
Water layer and basic unit are without departing from the blank of waterproof material no fracture when solving basic unit's differential settlement.
6. high and low temperature resistance is good, and product is high temperature resistant to trickle up to 130 degree of portions, low temperature 40 degrees below zero not embrittlement, and subzero 35
Degree more than can normal construction, product by roof coated with high reflectance white material, can by sunlight reflectance bring up to 60% with
On, and roof painted white can make a building energy conservation 20%.
Specific embodiment
With reference to specific embodiment, the present invention will be further described, to be better understood from technical solution of the present invention.
Embodiment 1：Environment-friendly synthetic macromolecular steel roofing special coating, this coating is weighed by following parts by weight when making
Raw material：8 parts of TPO, 4 parts of aldehyde ketone resin, 2 parts of styrene resin, 1 part of silica flour, 1 part of mica powder, rutile
5 parts of type titanium dioxide, 1,010 1 parts of age resistor, 1,076 0.3 parts of age resistor, 531 1 parts of antioxidant, 0.5 part of defoamer, ultraviolet
327 1 parts of absorbent, 5 parts of D40 solvent naphtha, 30 parts of butyl ester solvent naphtha.
Embodiment 2：Environment-friendly synthetic macromolecular steel roofing special coating, this coating is weighed by following parts by weight when making
Raw material：15 parts of TPO, 6 parts of aldehyde ketone resin, 8 parts of styrene resin, 3 parts of silica flour, 5 parts of mica powder, golden red
3 parts of stone-type titanium dioxide, 1,010 0.7 parts of age resistor, 1,076 0.6 parts of age resistor, 531 0.8 parts of antioxidant, 1 part of defoamer is purple
327 0.8 parts of ultraviolet absorbers, 20 parts of D40 solvent naphtha, 15 parts of butyl ester solvent naphtha.
Embodiment 3：Environment-friendly synthetic macromolecular steel roofing special coating, this coating is weighed by following parts by weight when making
Raw material：
20 parts of TPO, 8 parts of aldehyde ketone resin, 12 parts of styrene resin, 5 parts of silica flour, 10 parts of mica powder,
1 part of Rutile type titanium dioxide, 1,010 0.3 parts of age resistor, 1,076 1 parts of age resistor, 531 0.3 parts of antioxidant, defoamer 2.5
Part, 327 0.3 parts of UV absorbent, D40 solvent naphtha 5-30 part, butyl ester solvent naphtha 5-30 part.
Environment-friendly synthetic macromolecular steel roofing special coating in above-described embodiment, for the use characteristic of steel roof waterproof,
Steel construction color steel roof causes drainage especially severe due to reasons such as installation, roofing elastic deformation, roofing vibrations, and
And, water-repellent paint exposed for a long time outside it is easy to being aging, corroding, and then reduce water resistance, cause water-repellent paint ftracture,
Drainage occurs.Therefore steel roofing waterproof paint need to have superpower tensile strength, uvioresistant, aging resistance, resisting fatigue,
Low temperature flexibility, corrosion-free, stay in grade feature, above-described embodiment is in the documents of Patent No. " 200610099088.2 "
On the basis of, component is improved, TPO and aldehyde ketone resin, styrene resin is effectively combined,
Instead of SEBS, the SBS in documents, and eliminate the fractions in documents, from specific antioxidant, prevent always
Agent, UV absorbent and solvent naphtha, and a kind of milky steel roofing waterproof paint specially made, have superpower gluing
Knot power, may penetrate into cement 2-3 millimeter, is integrated with cement basic layer completely, can effectively resist and sink not because of building basic unit
Even, the face coat crack performance that the structural cracking caused by four seasons difference variation causes occurs.High-low temperature resistant, corrosion-resistant,
Antioxygenic property is extremely strong, and properties of product are stable, service life up to 30 years, highly promotion and implementation.
Claims (2)
1. a kind of environment-friendly synthetic macromolecular steel roofing special coating, is characterized in that：This coating is made up of following components：Polyolefin
Thermoplastic elastomer (TPE) 8-20 part, aldehyde ketone resin 4-8 part, styrene resin 2-12 part, silica flour 1-5 part, mica powder 1-10 part, golden red
Stone-type titanium dioxide 1-5 part, age resistor 1010 0.3-1 part, age resistor 1076 0.3-1 part, antioxidant 531 0.3-1 part, froth breaking
Agent 0.5-2.5 part, UV absorbent 327 0.3-1 part, D40 solvent naphtha 5-30 part, butyl ester solvent naphtha 5-30 part.
2. environment-friendly synthetic macromolecular steel roofing special coating according to claim 1, is characterized in that：This coating is by following
Component is made：15 parts of TPO, 6 parts of aldehyde ketone resin, 8 parts of styrene resin, 3 parts of silica flour, 5 parts of mica powder,
3 parts of Rutile type titanium dioxide, 1,010 0.7 parts of age resistor, 1,076 0.6 parts of age resistor, 531 0.8 parts of antioxidant, defoamer 1
Part, 327 0.8 parts of UV absorbent, 20 parts of D40 solvent naphtha, 15 parts of butyl ester solvent naphtha.