CN106367871A - High-grade yoga clothes fabric and preparation method thereof - Google Patents
High-grade yoga clothes fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106367871A CN106367871A CN201610764502.0A CN201610764502A CN106367871A CN 106367871 A CN106367871 A CN 106367871A CN 201610764502 A CN201610764502 A CN 201610764502A CN 106367871 A CN106367871 A CN 106367871A
- Authority
- CN
- China
- Prior art keywords
- fabric
- yoga
- calcium carbonate
- pearl
- pearl fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-grade yoga clothes fabric and a preparation method thereof. The high-grade yoga clothes fabric is prepared from pearl fibers and polyamide fibers through blending and has very good anti-bacterial function, moisture absorption and sweat releasing functions and health function as well as good wearability; by adding calcium carbonate in the preparation process of the pearl fibers, the cost is lowered; added calcium carbonate is light calcium carbonate with few impurities, so that the uniformity of far infrared ray emission of the prepared fabric is improved; and by virtue of mutual cooperation between the bamboo pulp added into the pearl fibers and milk fibers, the anti-bacterial property of the fabric is remarkably improved.
Description
Technical field
The present invention relates to textile fabric field, a kind of more particularly, to top grade Yoga takes fabric and preparation method thereof.
Background technology
Pearl fiber is to be added in fiber nanometer pearl powder in viscose rayon spinning using high-tech means, makes fibre
Dimension is internal and appearance is uniform-distribution with nano-pearl microgranule.It is specially pearl protein function master batch and fibre resin section structure
Become, make the inner and outer table of corpus fibrosum be uniform-distribution with nano-pearl microgranule, individual fibers are just as a string pearl necklace, abnormal light
Bright smooth.It is that a kind of common tencel researched and developed is cooperated with Shanghai novel spinning center by Donghua University, belong to and initiating both at home and abroad
High-grade functional fiber.
Pearl fiber existing pearl face skin-care effect, have again viscose rayon moisture absorption breathe freely, characteristic comfortable and easy to wear.Margarita
Fiber surface is uniform-distribution with pearl micro-particle, for a long time in skin contact, have pearl face skin protection, relieve inflammation or internal heat relieve internal heat, tender white muscle skin,
Anti-ultraviolet effect.Pearl fiber contains several amino acids and trace element, and fiber surface is smooth nice and cool, has light as Margarita
Pool.
After Margarita powder is absorbed by the body, by participating in body metabolism, reach the entirety conditioning of whole body skin and maintain.Its energy
Promote regenerative cell synthesis, and constantly add to skin surface, make skin smooth, exquisiteness, flexible.Scientifically take Margarita powder
Play the role of significantly to mitigate serum lipid peroxidation, and this lipid and protein are combined into and can generate lipofuscin (senile plaque), this
Exactly the Empress Dowager is apt to, with Margarita, the secret place that skin care is held.
The activity of human skin superoxide dismutase (sod) behind Margarita powder painting face, can be promoted, suppression is melanic
Synthesis, keeps whitening skin.Further, since sod has the effect removing free radical, skin aging, wrinkling can be prevented.
(1) beauty care, tender pale skin
Human body wears pearl fiber underwear, the pearl nano particle on fiber and skin intimate contact, and the lactic acid in perspiration can be molten
Go out fiber middles and divide pearl nutritional composition, absorbed by skin, promote the work of human skin superoxide dismutase (sod)
Property, the melanic synthesis of suppression keeps whitening skin.Further, since sod has the effect removing free radical, can prevent skin from declining
Always wrinkling.The traditional Chinese medical science thinks: Margarita sweet-salty cold in nature, GUIXIN Liver Channel, function appearance skin Caring, skin moistening granulation promoting, and clear speckle subtracts wrinkle, delays to decline
Always；Be mainly used in facial freckle, chloasma, senile plaguess, wrinkle, the weary pool of of flaccid muscles, pachylosiies, have an old and weathered face and acne,
Burn and scald, skin infection, wound are not received, dermatitis etc..Pearl growth is in water, cold in nature, has the effect that relieves internal heat of relieving inflammation or internal heat, and wears Margarita for a long time
Fiber underwear can remove skin surface hot pox poison, have functions that speckle dispelling, remove pox, maintenance skin.
(2) uvioresistant
The main component of Margarita is Calcium Carbonate, and itself has anti-ultraviolet function, adds fiber when it is ground into nm regime
When, its function greatly reinforces.Pearl fiber has the effect of anti-ultraviolet anti-skin aging.According to recent studies have shown that: nano-pearl
Powder also has the function of transmitting infrared waves, and it can improve microcirculation in human body, have health-care effect to human body.
Moisture absorption breathe freely, take comfortable
The carrier of nano-pearl fiber is viscose rayon, its moisture absorption air permeable dress with comfortable, add after resistance to Margarita powder fibrous inside and
Surface is uniform-distribution with pearl nano particle, and fabric hand is smooth nice and cool, and outward appearance is beautiful.
(4) All Pure Nature
Nanometer Margarita powder is to be processed through pure physical method by high-quality mussel pearl, and prezenta is extracted by cotton linter, because
This pearl fiber does not contain the harmful substance of any chemical product, has natural affinity with skin.
(5) durable in use
In pearl fiber, pearl nano particle is intimately combined with fiber, has permanent, and long-term washing dress will not fall off.Margarita
Alkaline-resisting not acidproof, alkaline washing does not hinder the slightest, and only under acidic sweat effect, pearl nano particle just can generating unit analyze,
Margarita underwear is the perfect adaptation turning with washing in fact.
In recent years the raising with people's living standard and the transformation of consumption fashion, people pursue comfortable in terms of dressing dress ornament
With attractive in appearance, it is superior further to wear grade, especially man's Yoga clothes, not only requires hygroscopicity strong, good permeability, and dress is relaxed
Suitable, and after requiring dress, preferably also there is the effects such as antibacterial, health care.
Content of the invention
Present invention aim at provide a kind of comfortable and easy to wear, take into account antibacterial simultaneously, the high-grade Yoga of health-care effect takes fabric
And preparation method thereof, to solve technical problem.
A kind of Yoga of top grade takes fabric, is formed by pearl fiber and nylon fibre hybrid woven, described Yoga takes fabric
Composition including following percentage by weight:
Pearl fiber: 95-98%
Nylon fibre: surplus.
Preferably, described pearl fiber, including the composition of following percentage by weight:
Viscose rayon 85-90%
Calcium Carbonate 5-8%
Bamboo pulp 0.2-0.5%
Dispersant 0.5-0.8%
Margarita powder surplus.
Preferably, described dispersant is carboxymethyl cellulose.
A kind of Yoga of top grade takes the preparation method of fabric, comprises the following steps:
A, by the lime slurry containing 5-12% under conditions of 8-15 DEG C, add nucleating additive, stir, in constant temperature
Under, it is passed through the carbonated gas that volume content is 20-40%, when ph value is for 7.5-8, terminate carburizing reagent, will be anti-
The calcium carbonate suspension answering gained filters, dries；
B, Margarita powder is carried out wet grinding, particle diameter is ground to less than 200 microns；
The Calcium Carbonate that c, addition dispersant and step a obtain, after stirring, carries out ball milling, makes slurry, so that diameter of particle is reached
To 200-500nm；
D, by bamboo pulp add slurry and be diluted to concentration be 15-25%, filter；
E, the slurry after filtering press formula ratio addition viscose rayon spinning slurry, blended, filtration, spray webbing, drawing-off, be shaped into
Pearl fiber；
F, pearl fiber and nylon fibre are carried out blending, obtain high-grade Yoga and take fabric.
The method have the advantages that
1st, fabric is formed by pearl fiber and nylon fibre blending, possesses extraordinary antibacterial functions and wearability；
2nd, Margarita antibacterial adds Calcium Carbonate in preparation process, not only reduces cost, and the Calcium Carbonate due to adding is
Precipitated calcium carbonate, impurity is few, therefore improves the uniformity of the fabric far infrared transmitting of preparation；
3rd, add the bamboo pulp in pearl fiber, fabric possesses good anti-microbial property.
In addition to objects, features and advantages described above, the present invention also has other objects, features and advantages.
The present invention is further detailed explanation below.
Specific embodiment
Hereinafter embodiments of the invention are described in detail, but the present invention can limit according to claim and cover
Multitude of different ways implement.
Embodiment 1
A kind of Yoga of top grade takes fabric, is formed by pearl fiber and nylon fibre hybrid woven, described Yoga takes fabric and includes
The composition of following percentage by weight:
Pearl fiber: 97%
Nylon fibre: 3%.
Described pearl fiber, including the composition of following percentage by weight:
Viscose rayon 88%
Calcium Carbonate 7%
Bamboo pulp 0.3%
Carboxymethyl cellulose 0.6%
Margarita powder surplus.
A kind of Yoga of top grade takes the preparation method of fabric, comprises the following steps:
A, by the lime slurry containing 10% under conditions of 9 DEG C, add nucleating additive, stir, under constant temperature, lead to
Enter the carbonated gas that volume content is 25%, when ph value is for 7.5-8, terminate carburizing reagent, by reaction gained
Calcium carbonate suspension filters, dries；
B, Margarita powder is carried out wet grinding, particle diameter is ground to less than 200 microns；
The Calcium Carbonate that c, addition dispersant and step a obtain, after stirring, carries out ball milling, makes slurry, so that diameter of particle is reached
To 200-500nm；
D, by bamboo pulp add slurry and be diluted to concentration be 20%, filter；
E, the slurry after filtering press formula ratio addition viscose rayon spinning slurry, blended, filtration, spray webbing, drawing-off, be shaped into
Pearl fiber；
F, pearl fiber and nylon fibre are carried out blending, obtain high-grade Yoga and take fabric.
Embodiment 2
A kind of Yoga of top grade takes fabric, is formed by pearl fiber and nylon fibre hybrid woven, described Yoga takes fabric and includes
The composition of following percentage by weight:
Pearl fiber: 95%
Nylon fibre: 5%.
Described pearl fiber, including the composition of following percentage by weight:
Viscose rayon 90%
Calcium Carbonate 5%
Bamboo pulp 0.5%
Carboxymethyl cellulose 0.5%
Margarita powder surplus.
A kind of Yoga of top grade takes the preparation method of fabric, comprises the following steps:
A, by the lime slurry containing 12% under conditions of 8 DEG C, add nucleating additive, stir, under constant temperature, lead to
Enter the carbonated gas that volume content is 40%, when ph value is for 7.5-8, terminate carburizing reagent, by reaction gained
Calcium carbonate suspension filters, dries；
B, Margarita powder is carried out wet grinding, particle diameter is ground to less than 200 microns；
The Calcium Carbonate that c, addition dispersant and step a obtain, after stirring, carries out ball milling, makes slurry, so that diameter of particle is reached
To 200-500nm；
D, by bamboo pulp add slurry and be diluted to concentration be 15%, filter；
E, the slurry after filtering press formula ratio addition viscose rayon spinning slurry, blended, filtration, spray webbing, drawing-off, be shaped into
Pearl fiber；
F, pearl fiber and nylon fibre are carried out blending, obtain high-grade Yoga and take fabric.
Embodiment 3
A kind of Yoga of top grade takes fabric, is formed by pearl fiber and nylon fibre hybrid woven, described Yoga takes fabric and includes
The composition of following percentage by weight:
Pearl fiber: 98%
Nylon fibre: 2%.
Described pearl fiber, including the composition of following percentage by weight:
Viscose rayon 85%
Calcium Carbonate 8%
Bamboo pulp 0.2%
Carboxymethyl cellulose 0.8%
Margarita powder surplus.
A kind of Yoga of top grade takes the preparation method of fabric, comprises the following steps:
A, by the lime slurry containing 5% under conditions of 15 DEG C, add nucleating additive, stir, under constant temperature, lead to
Enter the carbonated gas that volume content is 20%, when ph value is for 7.5-8, terminate carburizing reagent, by reaction gained
Calcium carbonate suspension filters, dries；
B, Margarita powder is carried out wet grinding, particle diameter is ground to less than 200 microns；
The Calcium Carbonate that c, addition dispersant and step a obtain, after stirring, carries out ball milling, makes slurry, so that diameter of particle is reached
To 200-500nm；
D, by bamboo pulp add slurry and be diluted to concentration be 25%, filter；
E, the slurry after filtering press formula ratio addition viscose rayon spinning slurry, blended, filtration, spray webbing, drawing-off, be shaped into
Pearl fiber；
F, pearl fiber and nylon fibre are carried out blending, obtain high-grade Yoga and take fabric.
Comparative example 1
Calcium Carbonate in embodiment 1 is replaced with Margarita powder, other conditions are constant.
Comparative example 2
Bamboo pulp in embodiment 1 is removed, other conditions are constant.
Table one: far infrared transmission test result
F1: all-wave length integrated emissivity；
F2:8-25 micron integrated emissivity
Wavelength integrated emission rate (1 micron of bandwidth) centered on f3-f7
F3:8.45 micron
F4:9.50 micron
F5:10.60 micron
F6:12.00 micron
F7:13.50 micron
F8:14-25 micron integrated emissivity
Table two: the impact test to human body for the fabric:
The impact test condition to human body for the described fabric is: is 19-21 DEG C in temperature, humidity is the interior of 48-52%r.h.
Under the conditions of, randomly select 20-40 year Ms tested, first adapt to environment 10 minutes, then put on test fabric and carry out the fine jade
Gal is taken exercise 30 minutes, tests in the middle part of the forearm of human body to before wearing the clothes and after wearing the clothes.
Table three: after fabric washs 20 times, anti-microbial property test:
From above detection data, the Yoga of present invention preparation take fabric possess compared to traditional pearl fiber fabric more preferably remote
Infrared emitting uniformity, more efficiently improves human body skin microcirculation；Bamboo pulp is added to prepare pearl fiber, the antibacterial of fabric
Performance significantly improves.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, made any repair
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (4)
1. a kind of top grade Yoga takes fabric it is characterised in that being formed by pearl fiber and nylon fibre hybrid woven, the described fine jade
Gal takes the composition that fabric includes following percentage by weight:
Pearl fiber: 95-98%
Nylon fibre: surplus.
2. top grade according to claim 1 Yoga takes fabric it is characterised in that described pearl fiber, includes following weight
The composition of amount percentage ratio:
Viscose rayon 85-90%
Calcium Carbonate 5-8%
Bamboo pulp 0.2-0.5%
Dispersant 0.5-0.8%
Margarita powder surplus.
3. top grade according to claim 1 Yoga takes fabric it is characterised in that described dispersant is carboxymethyl cellulose
Element.
4. a kind of top grade Yoga takes the preparation method of fabric it is characterised in that comprising the following steps:
A, by the lime slurry containing 5-12% under conditions of 8-15 DEG C, add nucleating additive, stir, in constant temperature
Under, it is passed through the carbonated gas that volume content is 20-40%, when ph value is for 7.5-8, terminate carburizing reagent, will be anti-
The calcium carbonate suspension answering gained filters, dries；
B, Margarita powder is carried out wet grinding, particle diameter is ground to less than 200 microns；
The Calcium Carbonate that c, addition dispersant and step a obtain, after stirring, carries out ball milling, makes slurry, so that diameter of particle is reached
To 200-500nm；
D, by bamboo pulp add slurry and be diluted to concentration be 15-25%, filter；
E, the slurry after filtering press formula ratio addition viscose rayon spinning slurry, blended, filtration, spray webbing, drawing-off, be shaped into
Pearl fiber；
F, pearl fiber and nylon fibre are carried out blending, obtain high-grade Yoga and take fabric.