CN106366558A - 一种工程塑料材料及制备方法 - Google Patents

一种工程塑料材料及制备方法 Download PDF

Info

Publication number
CN106366558A
CN106366558A CN201610878161.XA CN201610878161A CN106366558A CN 106366558 A CN106366558 A CN 106366558A CN 201610878161 A CN201610878161 A CN 201610878161A CN 106366558 A CN106366558 A CN 106366558A
Authority
CN
China
Prior art keywords
engineering plastic
plastic materials
antioxidant
materials according
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610878161.XA
Other languages
English (en)
Inventor
张达明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Mingsheng Strong Blower Co Ltd
Original Assignee
Wuxi Mingsheng Strong Blower Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Mingsheng Strong Blower Co Ltd filed Critical Wuxi Mingsheng Strong Blower Co Ltd
Priority to CN201610878161.XA priority Critical patent/CN106366558A/zh
Publication of CN106366558A publication Critical patent/CN106366558A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种工程塑料材料，其按重量份数包括如下组成：POM树脂66～89、苯乙烯‑马来酸酐共聚物3～5、木纤维粉5～30、芥酸酰胺0.5～1、抗氧剂0.5～1。本发明通过配合特定分子量的均聚甲醛POM树脂，与特定分子量的苯乙烯‑马来酸酐共聚物，与纤维素粉和芥酸酰胺混合，得到了一种具有优异的机械强度和韧性的工程塑料。

Description

一种工程塑料材料及制备方法
技术领域
本发明属于材料领域，具体涉及一种工程塑料材料及制备方法。
背景技术
POM(聚甲醛树脂)，聚甲醛是一种没有侧链、高密度、高结晶性的线型聚合物。按其分子链中化学结构的不同，可分为均聚甲醛和共聚甲醛两种。两者的重要区别是：均聚甲醛密度、结晶度、熔点都高，但热稳定性差，加工温度范围窄(约10℃)，对酸碱稳定性略低；而共聚甲醛密度、结晶度、熔点、强度都较低，但热稳定性好，不易分解，加工温度范围宽(约50℃)，对酸碱稳定性较好。是具有优异的综合性能的工程塑料。
本领域需要开发一种韧性高、机械强度大的工程塑料。
发明内容
本发明的目的之一在于提供一种工程塑料材料，其按重量份数包括如下组成：
POM树脂66～89
苯乙烯-马来酸酐共聚物3～5
木纤维粉 5～30
芥酸酰胺 0.5～1
抗氧剂 0.5～1
优选地，所述苯乙烯-马来酸酐共聚物的数均分子量为2500～3000g/mol。
优选地，所述POM树脂为均聚甲醛。
优选地，所述POM树脂的重均分子量为1.5～3万。
优选地，木纤维粉为树木树干磨成的粉和/或秸秆磨成的粉。
优选地，所述抗氧剂为方案类抗氧剂、酚类抗氧剂或亚磷酸酯抗氧剂中的任意1种或至少2种的组合。
本发明的目的之二是提供一种如目的之一所述的工程塑料材料的方法，所述方法包括如下步骤：
(1)按权利要求1～6任意一项所述的工程塑料的配方配制原料，并在高速混合机中混合干燥；
(2)将混合后的原料降温，投入双螺杆挤出机进行基础，得到POM工程塑料母粒。
优选地，所述混合干燥的温度为150～180℃。
与现有技术相比，本发明具有以下有益效果：
本发明通过配合特定分子量的均聚甲醛POM树脂，与特定分子量的苯乙烯-马来酸酐共聚物，与纤维素粉和芥酸酰胺混合，得到了一种具有优异的机械强度和韧性的工程塑料。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
本领域技术人员应该明了，所述实施例仅仅是帮助理解本发明，不应视为对本发明的具体限制。
实施例1
一种工程塑料材料，其按重量份数包括如下组成：
POM树脂(分子量为2万)70
苯乙烯-马来酸酐共聚物(分子量为2500～3000g/mol)4
树木树干磨成的粉20
芥酸酰胺0.7
抗氧剂0.7
制备方法包括如下步骤：
(1)按配方配制原料，并在高速混合机中混合干燥，混合温度为170℃；
(2)将混合后的原料降温，投入双螺杆挤出机进行基础，得到POM工程塑料母粒。
实施例2
一种工程塑料材料，其按重量份数包括如下组成：
POM树脂(分子量为1.5万)66
苯乙烯-马来酸酐共聚物(分子量为3000g/mol)3
树木树干磨成的粉30
芥酸酰胺0.5
抗氧剂1
制备方法包括如下步骤：
(1)按配方配制原料，并在高速混合机中混合干燥，混合温度为150℃；
(2)将混合后的原料降温，投入双螺杆挤出机进行基础，得到POM工程塑料母粒。
实施例3
一种工程塑料材料，其按重量份数包括如下组成：
POM树脂(分子量为3万) 89
苯乙烯-马来酸酐共聚物(分子量为2500g/mol) 5
树木树干磨成的粉 5
芥酸酰胺 1
抗氧剂 0.5
制备方法包括如下步骤：
(1)按配方配制原料，并在高速混合机中混合干燥，混合温度为180℃；
(2)将混合后的原料降温，投入双螺杆挤出机进行基础，得到POM工程塑料母粒。
性能测试
申请人声明，本发明通过上述实施例来说明本发明的工艺方法，但本发明并不局限于上述工艺步骤，即不意味着本发明必须依赖上述工艺步骤才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明所选用原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。

Claims (8)

1.一种工程塑料材料，其特征在于，其按重量份数包括如下组成：
POM树脂66～89
苯乙烯-马来酸酐共聚物3～5
木纤维粉5～30
芥酸酰胺0.5～1
抗氧剂0.5～1。
2.根据权利要求1所述的工程塑料材料，其特征在于，所述苯乙烯-马来酸酐共聚物的数均分子量为2500～3000g/mol。
3.根据权利要求1所述的工程塑料材料，其特征在于，所述POM树脂为均聚甲醛。
4.根据权利要求1所述的工程塑料材料，其特征在于，所述POM树脂的重均分子量为1.5～3万。
5.根据权利要求1所述的工程塑料材料，其特征在于，木纤维粉为树木树干磨成的粉和/或秸秆磨成的粉。
6.根据权利要求1所述的工程塑料材料，其特征在于，所述抗氧剂为方案类抗氧剂、酚类抗氧剂或亚磷酸酯抗氧剂中的任意1种或至少2种的组合。
7.一种制备如权利要求1-6任意一项所述的工程塑料材料的方法，其特征在于，所述方法包括如下步骤：
(1)按权利要求1～6任意一项所述的工程塑料的配方配制原料，并在高速混合机中混合干燥；
(2)将混合后的原料降温，投入双螺杆挤出机进行基础，得到POM工程塑料母粒。
8.根据权利要求7所述的方法，其特征在于，所述混合干燥的温度为150～180℃。
CN201610878161.XA 2016-09-30 2016-09-30 一种工程塑料材料及制备方法 Pending CN106366558A (zh)