CN106366520A - Pvdf elbow - Google Patents
Pvdf elbow Download PDFInfo
- Publication number
- CN106366520A CN106366520A CN201610761702.0A CN201610761702A CN106366520A CN 106366520 A CN106366520 A CN 106366520A CN 201610761702 A CN201610761702 A CN 201610761702A CN 106366520 A CN106366520 A CN 106366520A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvdf
- elbow
- resistance
- diisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVDF elbow which is prepared from the following components in parts by weight: 1-2 parts of alpha-alkenyl sodium sulfonate, 0.7 part of hydroxyethyl cellulose, 0.4 part of lauryl sodium sulfate, 0.3 part of 2-aminoethyl heptadecenyl imidazoline, 1.1 part of alkylphenol polyoxyethylene, 1.9 parts of polyoxyethylene sorbitan fatty acid ester, 0.5 part of polyalkyl trialkyl ammonium chloride, 1.6 parts of diisocyanate, 2.3 parts of butyl ether acetate and 33 parts of polyvinylidene fluoride. The PVDF elbow has excellent flame retardance, abrasion resistance, corrosion resistance, high temperature resistance, oxidation resistance, static resistance and weather resistance.
Description
Technical field
The present invention relates to pvdf elbow.
Background technology
Existing pvdf elbow, it is fire-retardant, abrasion-resistant, corrosion-resistant, high temperature resistant, resistance to oxidation, antistatic, weatherability all need to be carried
High.
Content of the invention
It is an object of the invention to provide a kind of pvdf elbow, it has excellent fire-retardant, abrasion-resistant, corrosion-resistant, resistance to height
Temperature, resistance to oxidation, antistatic, weatherability performance.
For achieving the above object, the technical scheme is that a kind of pvdf elbow of design, by weight by with the following group
Divide and make:
1～2 part of α-sodium olefin sulfonate,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Preferably, pvdf elbow, is made up of following components by weight:
1 part of α-sodium olefin sulfonate,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Preferably, pvdf elbow, is made up of following components by weight:
2 parts of α-sodium olefin sulfonates,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Preferably, pvdf elbow, is made up of following components by weight:
1.2 parts of α-sodium olefin sulfonates,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Advantages of the present invention and having the beneficial effects that: a kind of pvdf elbow is provided, its have excellent fire-retardant, abrasion-resistant,
Corrosion-resistant, high temperature resistant, resistance to oxidation, antistatic, weatherability performance.
The performance of " pvdf elbow " and purposes are determined by its component and proportioning, and different groups in " pvdf elbow "
Branch influences each other, and component and its proportioning can determine the final performance of " pvdf elbow ", and such as fruit component and its proportioning is not mutually assisted
Adjust, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different component is mutual
Conflict, do not have whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains
To " pvdf elbow " optimal component and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect
Should.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Pvdf elbow, is made up of following components by weight:
1～2 part of α-sodium olefin sulfonate,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Embodiment 2
Pvdf elbow, is made up of following components by weight:
1 part of α-sodium olefin sulfonate,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Embodiment 3
Pvdf elbow, is made up of following components by weight:
2 parts of α-sodium olefin sulfonates,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
Embodiment 4
Pvdf elbow, is made up of following components by weight:
1.2 parts of α-sodium olefin sulfonates,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
The pvdf elbow of the various embodiments described above, has excellent fire-retardant, abrasion-resistant, corrosion-resistant, high temperature resistant, resistance to oxidation, anti-
Electrostatic, weatherability performance.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1.pvdf elbow is it is characterised in that be made up of following components by weight:
1～2 part of α-sodium olefin sulfonate,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
2. pvdf elbow according to claim 1 is it is characterised in that be made up of following components by weight:
1 part of α-sodium olefin sulfonate,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
3. pvdf elbow according to claim 1 is it is characterised in that be made up of following components by weight:
2 parts of α-sodium olefin sulfonates,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.
4. pvdf elbow according to claim 1 is it is characterised in that be made up of following components by weight:
1.2 parts of α-sodium olefin sulfonates,
0.7 part of hydroxyethyl cellulose,
0.4 part of sodium lauryl sulphate,
0.3 part of 2- aminoethyl 17 alkenyl imidazoline,
1.1 parts of alkylphenol polyoxyethylene,
1.9 parts of polyoxyethylene sorbitan fatty acid esters,
0.5 part of poly- alkyl tri alkyl ammomium chloride,
1.6 parts of diisocyanate,
2.3 parts of monobutyl ether acetates,
33 parts of Kynoar.