CN109988585A - A kind of environmental protection fire retarding agent - Google Patents
A kind of environmental protection fire retarding agent Download PDFInfo
- Publication number
- CN109988585A CN109988585A CN201711488259.5A CN201711488259A CN109988585A CN 109988585 A CN109988585 A CN 109988585A CN 201711488259 A CN201711488259 A CN 201711488259A CN 109988585 A CN109988585 A CN 109988585A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- fire retarding
- protection fire
- retarding agent
- hydrotalcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental protection fire retarding agents, belong to chemical field.Environmental protection fire retarding agent is made of according to the following number of weight ratio following component: vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=2-5: 3-10: 12-25: 15-35: 22-45.Advantage for present invention is with effect: environmental protection fire retarding agent of the present invention be using vinyltriethoxysilane, diethylene triamine, hydrotalcite, ammonium dihydrogen phosphate and water as halogen-free flame retardants made of raw material, have thermal stability it is high, to substrate inertia, nontoxic, environmentally friendly.Thorough trap heat and starvation reach flame retardant effect during high-temp combustion, and smoke amount it is extremely low, it is nontoxic, without molten drop, especially suitable for the demanding fire-retardant place of oxygen index (OI).
Description
Technical field
The present invention relates to a kind of environmental protection fire retarding agents, belong to chemical field.
Background technique
With the development of China's synthetic material industry and the continuous expansion of application field, fire retardant is widely used in chemistry
In the every field such as building materials, electronic apparatus, communications and transportation, space flight and aviation, household furniture, interior decoration, clothing, food, lodging and transportion -- basic necessities of life.China's resistance
Combustion agent has evolved into the second largest polymer modification additive for being only second to plasticizer, current 200,000 t/a of production capacity
Left and right, year output is between 150,000-17 ten thousand tons, and 200,000 tons of annual consumption or so.Most common halogenated flame retardant in fire retardant
Although having the unrivaled high efficiency of other fire retardants series, it is very important to the harm of environment and people.Ring
Guarantor's problem is auxiliary agent development and application quotient's focus of attention, therefore the exploitation of environmental protection fire retarding agent is the task of top priority.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of environmental protection fire retarding agents, and the fire retardant fire protecting performance is excellent, nontoxic,
It is free from environmental pollution.
It is of the existing technology in order to solve the problems, such as, the technical solution adopted by the present invention is that:
Environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=2-5: 3-10: 12-25: 15-
35∶22-45。
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3-4: 5-8: 15-21: 18-25
∶30-40。
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3.5: 7: 19: 20: 35.
Advantage for present invention is with effect: environmental protection fire retarding agent of the present invention is with vinyltriethoxysilane, two
Vinyl triamine, hydrotalcite, ammonium dihydrogen phosphate and water are halogen-free flame retardants made of raw material, have thermal stability height, to substrate
It is inertia, nontoxic, environmentally friendly.Thorough trap heat and starvation reach flame retardant effect, and smoke amount during high-temp combustion
It is extremely low, nontoxic, without molten drop, especially suitable for the demanding fire-retardant place of oxygen index (OI).
Specific embodiment
Embodiment 1:
Environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=5: 3: 12: 15: 22.
Embodiment 2:
Environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=2: 10: 25: 35: 45.
Embodiment 3:
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component: vinyltriethoxysilane: two
Vinyl triamine: hydrotalcite: ammonium dihydrogen phosphate: water=4: 5: 15: 18: 30.
Embodiment 4:
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3: 8: 21: 25: 40.
Embodiment 5:
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=
3.5∶7∶19∶20∶35。
Embodiment 6:
Environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=4: 6: 20: 18: 25.
Embodiment 7:
Environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3: 4: 21: 18: 41.
Embodiment 8:
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3: 6: 20: 19: 31.
Embodiment 9:
The environmental protection fire retarding agent is made of according to the following number of weight ratio following component:
Vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=4: 7: 16: 20: 39.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
It is merely illustrated the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also has
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
It is defined by the appending claims and its equivalent thereof.
Claims (3)
1. environmental protection fire retarding agent, it is characterised in that be made of according to the following number of weight ratio following component: vinyl triethoxyl
Silane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water 2-5: 3-10: 12-25: 15-35: 22-45.
2. environmental protection fire retarding agent according to claim 1, it is characterised in that be by following component group according to the following number of weight ratio
At: vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3-4: 5-8: 15-21: 18-
25∶30-40。
3. environmental protection fire retarding agent according to claim 1, it is characterised in that be by following component group according to the following number of weight ratio
At: vinyltriethoxysilane: diethylene triamine: hydrotalcite: ammonium dihydrogen phosphate: water=3.5: 7: 19: 20: 35.