CN106349612A - Pvdf flange - Google Patents
Pvdf flange Download PDFInfo
- Publication number
- CN106349612A CN106349612A CN201610764654.0A CN201610764654A CN106349612A CN 106349612 A CN106349612 A CN 106349612A CN 201610764654 A CN201610764654 A CN 201610764654A CN 106349612 A CN106349612 A CN 106349612A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvdf
- flange
- sulfonate
- polybutylene terephthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVDF flange. The PVDF is prepared from, by weight, 1-2 parts of maleic acid isooctyl ester sulfate, 0.7 part of hydroxy propyl methyl cellulose, 1.3 parts of polybutylene terephthalate, 0.3 part of zinc dialkyl dithiophosphate, 0.8 part of ethylenediamine tetraacetic acid, 1.5 parts of polyoxyethylene glycol bisstearate, 0.9 part of sodium xylene sulfonate, 0.7 part of dinitroso e tetramine, 2.6 parts of propylene glycol methyl ether acetate, and 31 parts of polyvinylidene fluoride. The PVDF flange has excellent properties of flame retardance, friction resistance, corrosion resistance, high temperature resistance, oxidation resistance, antistatic performance and weather resistance.
Description
Technical field
The present invention relates to pvdf flange.
Background technology
Existing pvdf flange, it is fire-retardant, abrasion-resistant, corrosion-resistant, high temperature resistant, resistance to oxidation, antistatic, weatherability all need to be carried
High.
Content of the invention
It is an object of the invention to provide a kind of pvdf flange, it has excellent fire-retardant, abrasion-resistant, corrosion-resistant, resistance to height
Temperature, resistance to oxidation, antistatic, weatherability performance.
For achieving the above object, the technical scheme is that a kind of pvdf flange of design, by weight by with the following group
Divide and make:
1~2 part of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Preferably, pvdf flange, is made up of following components by weight:
1 part of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Preferably, pvdf flange, is made up of following components by weight:
2 parts of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Preferably, pvdf flange, is made up of following components by weight:
1.2 parts of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Advantages of the present invention and having the beneficial effects that: a kind of pvdf flange is provided, its have excellent fire-retardant, abrasion-resistant,
Corrosion-resistant, high temperature resistant, resistance to oxidation, antistatic, weatherability performance.
The performance of " pvdf flange " and purposes are determined by its component and proportioning, and different groups in " pvdf flange "
Branch influences each other, and component and its proportioning can determine the final performance of " pvdf flange ", and such as fruit component and its proportioning is not mutually assisted
Adjust, the beneficial effect that single component is brought, even can be eliminated by other components abatement, when serious, different component is mutual
Conflict, do not have whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains
To " pvdf flange " optimal component and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect
Should.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Pvdf flange, is made up of following components by weight:
1~2 part of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Embodiment 2
Pvdf flange, is made up of following components by weight:
1 part of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Embodiment 3
Pvdf flange, is made up of following components by weight:
2 parts of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
Embodiment 4
Pvdf flange, is made up of following components by weight:
1.2 parts of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
The pvdf flange of the various embodiments described above, has excellent fire-retardant, abrasion-resistant, corrosion-resistant, high temperature resistant, resistance to oxidation, anti-
Electrostatic, weatherability performance.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1.pvdf flange is it is characterised in that be made up of following components by weight:
1~2 part of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
2. pvdf flange according to claim 1 is it is characterised in that be made up of following components by weight:
1 part of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
3. pvdf flange according to claim 1 is it is characterised in that be made up of following components by weight:
2 parts of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.
4. pvdf flange according to claim 1 is it is characterised in that be made up of following components by weight:
1.2 parts of diisooctyl maleate sulfonate,
0.7 part of HYDROXY PROPYL METHYLCELLULOSE,
1.3 parts of polybutylene terephthalate (PBT)s,
0.3 part of zinc dialkyl dithiophosphate,
0.8 part of disodiumedetate,
1.5 parts of polyethylene glycol stearate diesters,
0.9 part of sodium xylene sulfonate,
0.7 part of dinitroso penta tetramine,
2.6 parts of propylene glycol methyl ether acetates,
31 parts of Kynoar.