CN106349509A - Fiber-base wood-plastic composite material - Google Patents
Fiber-base wood-plastic composite material Download PDFInfo
- Publication number
- CN106349509A CN106349509A CN201610725112.2A CN201610725112A CN106349509A CN 106349509 A CN106349509 A CN 106349509A CN 201610725112 A CN201610725112 A CN 201610725112A CN 106349509 A CN106349509 A CN 106349509A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- base
- wood
- plastic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fiber-base wood-plastic composite material which comprises the following components in parts by weight: 40-65 parts of pineapple leaf fiber base, 35-45 parts of basalt fiber, 5-8 parts of polyethylene, 3.5-4.5 parts of methyl isothiazolinone, 2-3 parts of benzoin, 4-6 parts of methylphenyl polyborosiloxane, 2.0-2.5 parts of polysebacic anhydride, 5.5-7.5 parts of asbestos, 5-7 parts of hexamethoxymethyl melamine resin, 8-10 parts of camphor powder, 6-8 parts of ginkgo leaf, 6-8 parts of Aralia echinocaulis powder, 0.1-0.2 part of agalloch powder, 4-6 parts of 3-hydroxybenzoic acid, 1-2 parts of laurinol sulfate, 4-6 parts of plant saponin, 0.1-0.2 part of polyamide wax micropowder and 1-3 parts of white latex. The wood-plastic composite material disclosed by the invention continuously emits a faint fragrance; the board has the characteristics of antimicrobial property, corrosion resistance and mildew resistance, can be used indoors and outdoors, can resist aging, and can not generate cracking or deformation.
Description
Technical field
The invention belongs to plastic-wood material production technical field, specifically a kind of fibre base wood-plastic composite material.
Background technology
Construction material refers to the general name of the various materials for building and field of civil engineering, referred to as " building materials ".In the narrow sense
The building materials material that refers to for civil engineering, such as steel, timber, glass, cement, coating etc., generally by cement, steel and timber
It is referred to as three big materials of common buildings engineering.Sensu lato building materials also include the material for Architectural Equipment, such as electric wire, water pipe
Deng." construction material " of discipline of architecture refers to the subject that physics and the chemical characteristic of different construction materials are studied.
Floor, i.e. the surface layer of house earth surface or flooring, is one kind of construction material.Made by timber or other materials.
The classification on floor has a lot, has by textural classification: solid wooden floor board, reinforced composite wooden floor, solid wooden compound floor, bamboo-wood floor,
Cork flooring and at present most popular multi-layer solid wood composite floor etc.；Classification by use has: domestic, commercially use, antistatic ground
Special floor, the special floor of track and field etc. in the special floor of plate, outdoor flooring, choreography, Stadium field；By environmental protection grade classification
Have: e0 level floor, the f4 star floor of jas star criteria etc..
At present plastic-wood composite floor is mainly with plastics, bamboo/wood fiber as raw material, it be by plastics and bamboo (wooden) consider to be worth doing according to
It is similar to what the ratio of 3:5 was made.Mould wood and have the Waterproof corrosion of plastics and two kinds of characteristics of texture of timber concurrently so that it becomes one
Plant function admirable and very durable outdoor building materials purposes is extremely wide.Existing wood products performance of moulding is still not ideal enough, also exists
The parameters such as the homogeneous degree of some defects, such as plastic wood sheet, density, water absorption still need to improve further.And existing mould
Wood material kind is more single, user according to oneself like selection space too little.
Content of the invention
It is an object of the invention to overcoming prior art defect, provide a kind of fibre base wood-plastic composite material.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of fibre base wood-plastic composite material, includes following component: arghan base 40-65 part, the Black Warrior by weight
Rock fiber 35-45 part, polyethylene 5-8 part, Methylisothiazolinone 3.5-4.5 part, Benzoinum 2-3 part, the poly- borosilicate of aminomethyl phenyl
Oxygen alkane 4-6 part, poly sebacic polyanhydride 2.0-2.5 part, asbestos 5.5-7.5 part, hexamethoxymethyl melamine resin 5-7 part, Lignum cinnamomi camphorae
Powder 8-10 part, Folium Ginkgo 6-8 part, spine stem wood powder 6-8 part, eaglewood powder 0.1-0.2 part, 3- hydroxy benzoic acid 4-6 part, Laurel
Alcohol sulfate 1-2 part, plant saponin 4-6 part, polyamide wax micropowder 0.1-0.2 part, white glue with vinyl 1-3 part.
A kind of described fibre base wood-plastic composite material, includes following component: 55 parts of arghan base, the Black Warrior by weight
40 parts of rock fiber, 6 parts of polyethylene, 4 parts of Methylisothiazolinone, 2 parts of Benzoinum, 5 parts of aminomethyl phenyl polyborosiloxane, the poly- last of the ten Heavenly stems two
2 parts of anhydride, 6 parts of asbestos, 6 parts of hexamethoxymethyl melamine resin, 9 parts of camphorwood powder, 7 parts of Folium Ginkgo, 7 parts of spine stem wood powder,
0.2 part of eaglewood powder, 4 parts of 3- hydroxy benzoic acid, 1 part of sulfated lauryl alcohol, 6 parts of plant saponin, polyamide wax micropowder 0.1
Part, 1 part of white glue with vinyl.
A kind of described fibre base wood-plastic composite material, its preparation method comprises the following steps:
(1) successively by arghan base, basalt fibre, polyethylene, Methylisothiazolinone, Benzoinum, methylbenzene
Base polyborosiloxane, poly sebacic polyanhydride, asbestos, hexamethoxymethyl melamine resin, camphorwood powder, Folium Ginkgo, spine stem wood powder,
Eaglewood powder, 3- hydroxy benzoic acid, sulfated lauryl alcohol, plant saponin, polyamide wax micropowder, white glue with vinyl add mixed at high speed
Machine is sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the time in comminutor for the material is 20-30 minute, is finally obtained
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.
Beneficial effects of the present invention: the wood plastic composite that the present invention provides, can persistently give out delicate fragrance, sheet material has
Preferably intensity, with more antibacterial, anti-corrosion, mould proof feature, indoor, open air all can use, and aging resistance will not craze and transfiguration.
Specific embodiment
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated with reference to specific embodiment.
Embodiment 1
A kind of fibre base wood-plastic composite material, includes following component: arghan base 40, basalt fibre by weight
35th, polyethylene 5, Methylisothiazolinone 3.5, Benzoinum 2, aminomethyl phenyl polyborosiloxane 4, poly sebacic polyanhydride
2nd, asbestos 5.5, hexamethoxymethyl melamine resin 5, camphorwood powder 8, Folium Ginkgo 6 is spine stem wood powder 6, heavy
Incense wood powder 0.1,3- hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 4, polyamide wax micropowder 0.1,
White glue with vinyl 1.
Its preparation method comprises the following steps:
(1) successively by arghan base 40, basalt fibre 35, polyethylene 5, Methylisothiazolinone 3.5
, Benzoinum 2, aminomethyl phenyl polyborosiloxane 4, poly sebacic polyanhydride 2, asbestos 5.5, hexamethoxymethyl melamine
Resin 5, camphorwood powder 8, Folium Ginkgo 6, spine stem wood powder 6, eaglewood powder 0.1,3- hydroxy benzoic acid 4, Laurel
Alcohol sulfate 1, plant saponin 4, polyamide wax micropowder 0.1, white glue with vinyl 1 add high-speed mixer to be sufficiently mixed all
Even；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the time in comminutor for the material is 20-30 minute, is finally obtained
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.
Embodiment 2
A kind of fibre base wood-plastic composite material, includes following component: arghan base 65, basalt fibre by weight
45th, polyethylene 8, Methylisothiazolinone 4.5, Benzoinum 3, aminomethyl phenyl polyborosiloxane 6, poly sebacic polyanhydride
2.5th, asbestos 7.5, hexamethoxymethyl melamine resin 7, camphorwood powder 10, Folium Ginkgo 8, spine stem wood powder 8,
Eaglewood powder 0.2,3- hydroxy benzoic acid 6, sulfated lauryl alcohol 2, plant saponin 6, polyamide wax micropowder 0.2
, white glue with vinyl 3.
Its preparation method comprises the following steps:
(1) successively by arghan base 65, basalt fibre 45, polyethylene 8, Methylisothiazolinone 4.5
, Benzoinum 3, aminomethyl phenyl polyborosiloxane 6, poly sebacic polyanhydride 2.5, asbestos 7.5, hexakis-methoxy methyl melamine
Polyimide resin 7, camphorwood powder 10, Folium Ginkgo 8, spine stem wood powder 8, eaglewood powder 0.2,3- hydroxy benzoic acid 6, the moon
Cinnamic alcohol sulfate 2, plant saponin 6, polyamide wax micropowder 0.2, white glue with vinyl 3 add high-speed mixer to be sufficiently mixed
Uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the time in comminutor for the material is 20-30 minute, is finally obtained
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.
Embodiment 3
A kind of fibre base wood-plastic composite material, includes following component: arghan base 50, basalt fibre by weight
40th, polyethylene 6, Methylisothiazolinone 4, Benzoinum 3, aminomethyl phenyl polyborosiloxane 5, poly sebacic polyanhydride 2
, asbestos 6, hexamethoxymethyl melamine resin 6, camphorwood powder 9, Folium Ginkgo 6, spine stem wood powder 6, Lignum Aquilariae Resinatum
Powder 0.1,3- hydroxy benzoic acid 6, sulfated lauryl alcohol 1, plant saponin 6, polyamide wax micropowder 0.2, Virgin's milk
Glue 1.
Its preparation method comprises the following steps:
(1) successively by arghan base 50, basalt fibre 40, polyethylene 6, Methylisothiazolinone 4,
Benzoinum 3, aminomethyl phenyl polyborosiloxane 5, poly sebacic polyanhydride 2, asbestos 6, hexamethoxymethyl melamine resin 6
, camphorwood powder 9, Folium Ginkgo 6, spine stem wood powder 6, eaglewood powder 0.1,3- hydroxy benzoic acid 6, lauryl alcohol sulphuric acid
Salt 1, plant saponin 6, polyamide wax micropowder 0.2, white glue with vinyl 1 add high-speed mixer to be sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the time in comminutor for the material is 20-30 minute, is finally obtained
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.
Embodiment 4
A kind of fibre base wood-plastic composite material, includes following component: arghan base 60, basalt fibre by weight
40th, polyethylene 8, Methylisothiazolinone 4.5, Benzoinum 2, aminomethyl phenyl polyborosiloxane 4, poly sebacic polyanhydride
2nd, asbestos 7.5, hexamethoxymethyl melamine resin 6, camphorwood powder 9, Folium Ginkgo 7 is spine stem wood powder 7, heavy
Incense wood powder 0.2,3- hydroxy benzoic acid 5, sulfated lauryl alcohol 1, plant saponin 5, polyamide wax micropowder 0.2,
White glue with vinyl 2.
Its preparation method comprises the following steps:
(1) successively by arghan base 60, basalt fibre 40, polyethylene 8, Methylisothiazolinone 4.5
, Benzoinum 2, aminomethyl phenyl polyborosiloxane 4, poly sebacic polyanhydride 2, asbestos 7.5, hexamethoxymethyl melamine
Resin 6, camphorwood powder 9, Folium Ginkgo 7, spine stem wood powder 7, eaglewood powder 0.2,3- hydroxy benzoic acid 5, Laurel
Alcohol sulfate 1, plant saponin 5, polyamide wax micropowder 0.2, white glue with vinyl 2 add high-speed mixer to be sufficiently mixed all
Even；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the time in comminutor for the material is 20-30 minute, is finally obtained
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.
Embodiment 5
A kind of fibre base wood-plastic composite material, includes following component: arghan base 60, basalt fibre by weight
40th, polyethylene 6, Methylisothiazolinone 4, Benzoinum 2, aminomethyl phenyl polyborosiloxane 5, poly sebacic polyanhydride 2
, asbestos 7, hexamethoxymethyl melamine resin 6, camphorwood powder 8, Folium Ginkgo 8, spine stem wood powder 6, Lignum Aquilariae Resinatum
Powder 0.2,3- hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 6, polyamide wax micropowder 0.2, Virgin's milk
Glue 2.
Its preparation method comprises the following steps:
(1) successively by arghan base 60, basalt fibre 40, polyethylene 6, Methylisothiazolinone 4,
Benzoinum 2, aminomethyl phenyl polyborosiloxane 5, poly sebacic polyanhydride 2, asbestos 7, hexamethoxymethyl melamine resin 6
, camphorwood powder 8, Folium Ginkgo 8, spine stem wood powder 6, eaglewood powder 0.2,3- hydroxy benzoic acid 4, lauryl alcohol sulphuric acid
Salt 1, plant saponin 6, polyamide wax micropowder 0.2, white glue with vinyl 2 add high-speed mixer to be sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the time in comminutor for the material is 20-30 minute, is finally obtained
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.
Above content is only citing made for the present invention and illustrates, affiliated those skilled in the art are to being retouched
The specific embodiment stated is made various modifications or supplements or substituted using similar mode, without departing from invention or super
More scope defined in the claims, all should belong to protection scope of the present invention.
Claims (3)
1. a kind of fibre base wood-plastic composite material is it is characterised in that include following component by weight: arghan base 40-
65 parts, basalt fibre 35-45 part, polyethylene 5-8 part, Methylisothiazolinone 3.5-4.5 part, Benzoinum 2-3 part, methylbenzene
Base polyborosiloxane 4-6 part, poly sebacic polyanhydride 2.0-2.5 part, asbestos 5.5-7.5 part, hexamethoxymethyl melamine resin 5-7
Part, camphorwood powder 8-10 part, Folium Ginkgo 6-8 part, spine stem wood powder 6-8 part, eaglewood powder 0.1-0.2 part, 3- hydroxy benzoic acid 4-6
Part, sulfated lauryl alcohol 1-2 part, plant saponin 4-6 part, polyamide wax micropowder 0.1-0.2 part, white glue with vinyl 1-3 part.
2. as claimed in claim 1 a kind of fibre base wood-plastic composite material it is characterised in that including following component by weight:
55 parts of arghan base, 40 parts of basalt fibre, 6 parts of polyethylene, 4 parts of Methylisothiazolinone, 2 parts of Benzoinum, methylbenzene
5 parts of base polyborosiloxane, 2 parts of poly sebacic polyanhydride, 6 parts of asbestos, 6 parts of hexamethoxymethyl melamine resin, 9 parts of camphorwood powder, silver
7 parts of Folium Pruni, 7 parts of spine stem wood powder, 0.2 part of eaglewood powder, 4 parts of 3- hydroxy benzoic acid, 1 part of sulfated lauryl alcohol, plant Fructus Gleditsia
6 parts of glycosides, 0.1 part of polyamide wax micropowder, 1 part of white glue with vinyl.
3. as claimed in claim 1 a kind of fibre base wood-plastic composite material it is characterised in that its preparation method includes following step
Rapid:
(1) successively arghan base, basalt fibre, polyethylene, Methylisothiazolinone, Benzoinum, aminomethyl phenyl are gathered
Borosiloxane, poly sebacic polyanhydride, asbestos, hexamethoxymethyl melamine resin, camphorwood powder, Folium Ginkgo, spine stem wood powder, Lignum Aquilariae Resinatum
Wood powder, 3- hydroxy benzoic acid, sulfated lauryl alcohol, plant saponin, polyamide wax micropowder, white glue with vinyl add high-speed mixer to fill
Divide mix homogeneously；
(2) step of pelletize, is carried out in comminutor, through the process heating, mediate, bonding, by the material after high pressure batch mixing
Add in comminutor, prilling temperature is 180-300 DEG C, the time in comminutor for the material is 20-30 minute, be finally obtained compound
Material grain；
(3) extrusion molding, the compound material grain stirring mixing obtaining in granulation step is subsequently adding extruder and is extruded into plate
Material, the machine barrel of extruder includes five warm areas, from feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05mpa.