CN106280119A - A kind of environmental protection Wood-plastic floor material - Google Patents
A kind of environmental protection Wood-plastic floor material Download PDFInfo
- Publication number
- CN106280119A CN106280119A CN201610725239.4A CN201610725239A CN106280119A CN 106280119 A CN106280119 A CN 106280119A CN 201610725239 A CN201610725239 A CN 201610725239A CN 106280119 A CN106280119 A CN 106280119A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- environmental protection
- asbestos
- plastic floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of environmental protection Wood-plastic floor material of the present invention, include following component by weight: PVC resin powder 40 65 parts, straw 35 45 parts, polyethylene 58 parts, polyphenylene oxide 3.5 4.5 parts, Benzoinum 23 parts, mica powder 46 parts, Firebrake ZB 2.0 2.5 parts, 5.5 7.5 parts of asbestos, 57 parts of Firmiana platanifolia (Linn. f.) Marsili bark, 8 10 parts of bamboo powder, Folium Ginkgo 68 parts, expanded perlite 68 parts, wintergreen oil 0.1 0.2 parts, 3 hydroxy benzoic acid 46 parts, sulfated lauryl alcohol 12 parts, plant saponin 46 parts, terpineol 0.1 0.2 parts, white glue with vinyl 13 parts.This kind of flooring material has carried out sufficient utilization to refuse, has saved the energy, has reduced production cost, easily manufactured, the employing of asbestos, makes floor have the effect of sound insulation, when people are trampling when, will not there is the appearance of sound, having more waterproof, anticorrosion, the feature of mildew-resistant, indoor, open air all can use, aging resistance, will not craze and transfiguration, meet the demand of people.
Description
Technical field
The invention belongs to technical field of buildings, specifically a kind of environmental protection Wood-plastic floor material.
Background technology
Construction material refers to, for building and the general name of the various materials of field of civil engineering, be called for short " building materials ".In the narrow sense
Building materials refer to the material for civil engineering, such as steel, timber, glass, cement, coating etc., generally by cement, steel and timber
It is referred to as three big materials of common buildings engineering.Sensu lato building materials also include the material for Architectural Equipment, such as electric wire, water pipe
Deng." construction material " of discipline of architecture refers to the subject that the physics to different construction materials and chemical characteristic are studied.
The surface layer on floor, i.e. house earth surface or flooring, is the one of construction material.Made by timber or other materials.
The classification on floor has a lot, has by textural classification: solid wooden floor board, reinforced composite wooden floor, solid wooden compound floor, bamboo-wood floor,
Cork flooring and current most popular multi-layer solid wood composite floor etc.；Classification by use has: domestic, business are used, antistatic ground
Special floor, the special floor of track and field etc. in the special floor of plate, outdoor flooring, choreography, Stadium field；By environmental protection grade separation
Have: E0 level floor, the F4 star floor etc. of JAS star criteria.
At present, become better and better, for furniture or the environmental quality of public place along with the development people living condition of society
Pursue and improve constantly the most accordingly, especially ground decoration, current commonly used floor tile or wood floors or marble ground
Plate.The radiation relatively greatly and containing trace element of floor tile and marble floor weight, floor is more sliding, installs time-intensive, expensive, wood
Floor is not only faced with the water funk problem such as inflammable and the forest reserves causes waste greatly and destroys.
It addition, in order to prevent flooring material surface from out-of-flatness occurring or has the generation of the situations such as piebaldism, existing flooring board
Expect that its thickness general control is at below 0.7mm, it is impossible to meet the greater demand of more and more user.
Summary of the invention
It is an object of the invention to overcome prior art defect, it is provided that a kind of environmental protection Wood-plastic floor material.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 40-65 part, straw 35-45
Part, polyethylene 5-8 part, polyphenylene oxide 3.5-4.5 part, Benzoinum 2-3 part, mica powder 4-6 part, Firebrake ZB 2.0-2.5 part, asbestos
5.5-7.5 part, Firmiana platanifolia (Linn. f.) Marsili bark 5-7 part, bamboo powder 8-10 part, Folium Ginkgo 6-8 part, expanded perlite 6-8 part, wintergreen oil 0.1-
0.2 part, 3-hydroxy benzoic acid 4-6 part, sulfated lauryl alcohol 1-2 part, plant saponin 4-6 part, terpineol 0.1-0.2 part, white
Latex 1-3 part.
Described a kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 55 parts, straw 40 parts,
Polyethylene 6 parts, polyphenylene oxide 4 parts, Benzoinum 2 parts, mica powder 5 parts, Firebrake ZB 2 parts, 6 parts of asbestos, 6 parts of Firmiana platanifolia (Linn. f.) Marsili bark, bamboo powder 9
Part, Folium Ginkgo 7 parts, expanded perlite 7 parts, wintergreen oil 0.2 part, 3-hydroxy benzoic acid 4 parts, sulfated lauryl alcohol 1 part, plant soap
Angle glycosides 6 parts, terpineol 0.1 part, white glue with vinyl 1 part.
Described a kind of environmental protection Wood-plastic floor material, its preparation method comprises the following steps:
(1) successively by PVC resin powder, straw, polyethylene, polyphenylene oxide, Benzoinum, mica powder, Firebrake ZB, asbestos, Firmiana platanifolia (Linn. f.) Marsili
Bark, bamboo powder, Folium Ginkgo, expanded perlite, wintergreen oil, 3-hydroxy benzoic acid, sulfated lauryl alcohol, plant saponin, pine
Oleyl alcohol, white glue with vinyl add high-speed mixer and are sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, finally prepares
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
Described mica powder granularity is 100-260 mesh.
Beneficial effects of the present invention: this kind of flooring material has carried out sufficient utilization to refuse, has saved the energy, has reduced
Production cost, easily manufactured, the employing of asbestos, make floor have the effect of sound insulation, when people are trampling when, will not be sound
The appearance of sound, has more waterproof, anticorrosion, the feature of mildew-resistant, and indoor, open air all can use, aging resistance, will not craze and transfiguration, full
The foot demand of people.
Detailed description of the invention
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 40, straw 35, polyethylene
5, polyphenylene oxide 3.5, Benzoinum 2, mica powder 4, Firebrake ZB 2, asbestos 5.5, Firmiana platanifolia (Linn. f.) Marsili bark 5, bamboo powder 8
, Folium Ginkgo 6, expanded perlite 6, wintergreen oil 0.1,3-hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant soap
Angle glycosides 4, terpineol 0.1, white glue with vinyl 1.
Its preparation method comprises the following steps:
(1) successively by PVC resin powder 40, straw 35, polyethylene 5, polyphenylene oxide 3.5, Benzoinum 2, Muscovitum
Powder 4, Firebrake ZB 2, asbestos 5.5, Firmiana platanifolia (Linn. f.) Marsili bark 5, bamboo powder 8, Folium Ginkgo 6, expanded perlite 6, Ilicis Purpureae
Oil 0.1,3-hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 4, terpineol 0.1, white glue with vinyl 1 add
Enter high-speed mixer to be sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, finally prepares
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
Embodiment 2
A kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 65, straw 45, polyethylene
8, polyphenylene oxide 4.5, Benzoinum 3, mica powder 6, Firebrake ZB 2.5, asbestos 7.5, Firmiana platanifolia (Linn. f.) Marsili bark 7, bamboo powder
10, Folium Ginkgo 8, expanded perlite 8, wintergreen oil 0.2,3-hydroxy benzoic acid 6, sulfated lauryl alcohol 2, plant
Saponin 6, terpineol 0.2, white glue with vinyl 3.
Its preparation method comprises the following steps:
(1) successively by PVC resin powder 65, straw 45, polyethylene 8, polyphenylene oxide 4.5, Benzoinum 3, Muscovitum
Powder 6, Firebrake ZB 2.5, asbestos 7.5, Firmiana platanifolia (Linn. f.) Marsili bark 7, bamboo powder 10, Folium Ginkgo 8, expanded perlite 8, winter
Blue or green oil 0.2,3-hydroxy benzoic acid 6, sulfated lauryl alcohol 2, plant saponin 6, terpineol 0.2, white glue with vinyl 3
Add high-speed mixer to be sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, finally prepares
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
Embodiment 3
A kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 50, straw 40, polyethylene
6, polyphenylene oxide 4, Benzoinum 3, mica powder 5, Firebrake ZB 2, asbestos 6, Firmiana platanifolia (Linn. f.) Marsili bark 6, bamboo powder 9, silver
Folium Pruni 6, expanded perlite 6, wintergreen oil 0.1,3-hydroxy benzoic acid 6, sulfated lauryl alcohol 1, plant saponin 6
, terpineol 0.2, white glue with vinyl 1.
Its preparation method comprises the following steps:
(1) successively by PVC resin powder 50, straw 40, polyethylene 6, polyphenylene oxide 4, Benzoinum 3, mica powder 5
, Firebrake ZB 2, asbestos 6, Firmiana platanifolia (Linn. f.) Marsili bark 6, bamboo powder 9, Folium Ginkgo 6, expanded perlite 6, wintergreen oil 0.1
, 3-hydroxy benzoic acid 6, sulfated lauryl alcohol 1, plant saponin 6, terpineol 0.2, white glue with vinyl 1 add height
Speed mixer is sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, finally prepares
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
Embodiment 4
A kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 60, straw 40, polyethylene
8, polyphenylene oxide 4.5, Benzoinum 2, mica powder 4, Firebrake ZB 2, asbestos 7.5, Firmiana platanifolia (Linn. f.) Marsili bark 6, bamboo powder 9
, Folium Ginkgo 7, expanded perlite 7, wintergreen oil 0.2,3-hydroxy benzoic acid 5, sulfated lauryl alcohol 1, plant soap
Angle glycosides 5, terpineol 0.2, white glue with vinyl 2.
Its preparation method comprises the following steps:
(1) PVC resin powder 60, straw 40, polyethylene 8, polyphenylene oxide 4.5, Benzoinum 2, mica powder 4 successively
, Firebrake ZB 2, asbestos 7.5, Firmiana platanifolia (Linn. f.) Marsili bark 6, bamboo powder 9, Folium Ginkgo 7, expanded perlite 7, wintergreen oil
0.2,3-hydroxy benzoic acid 5, sulfated lauryl alcohol 1, plant saponin 5, terpineol 0.2, white glue with vinyl 2 add
High-speed mixer is sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, finally prepares
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
Embodiment 5
A kind of environmental protection Wood-plastic floor material, includes following component by weight: PVC resin powder 60, straw 40, polyethylene
6, polyphenylene oxide 4, Benzoinum 2, mica powder 5, Firebrake ZB 2, asbestos 7, Firmiana platanifolia (Linn. f.) Marsili bark 6, bamboo powder 8, silver
Folium Pruni 8, expanded perlite 6, wintergreen oil 0.2,3-hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 6
, terpineol 0.2, white glue with vinyl 2.
Its preparation method comprises the following steps:
(1) successively by PVC resin powder 60, straw 40, polyethylene 6, polyphenylene oxide 4, Benzoinum 2, mica powder 5
, Firebrake ZB 2, asbestos 7, Firmiana platanifolia (Linn. f.) Marsili bark 6, bamboo powder 8, Folium Ginkgo 8, expanded perlite 6, wintergreen oil 0.2
, 3-hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 6, terpineol 0.2, white glue with vinyl 2 add height
Speed mixer is sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, after high pressure batch mixing
Material adds in comminutor, and prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, finally prepares
Compound material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into
Sheet material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
Above content is only citing made for the present invention and explanation, and affiliated those skilled in the art are to being retouched
The specific embodiment stated makes various amendment or supplements or use similar mode to substitute, without departing from inventing or super
More scope defined in the claims, all should belong to protection scope of the present invention.
Claims (4)
1. an environmental protection Wood-plastic floor material, it is characterised in that include following component by weight: PVC resin powder 40-65 part,
Straw 35-45 part, polyethylene 5-8 part, polyphenylene oxide 3.5-4.5 part, Benzoinum 2-3 part, mica powder 4-6 part, Firebrake ZB 2.0-2.5
Part, asbestos 5.5-7.5 part, Firmiana platanifolia (Linn. f.) Marsili bark 5-7 part, bamboo powder 8-10 part, Folium Ginkgo 6-8 part, expanded perlite 6-8 part, Ilicis Purpureae
Oil 0.1-0.2 part, 3-hydroxy benzoic acid 4-6 part, sulfated lauryl alcohol 1-2 part, plant saponin 4-6 part, terpineol 0.1-0.2
Part, white glue with vinyl 1-3 part.
2. a kind of environmental protection Wood-plastic floor material, it is characterised in that include following component: PVC by weight
Resin-oatmeal 55 parts, straw 40 parts, polyethylene 6 parts, polyphenylene oxide 4 parts, Benzoinum 2 parts, mica powder 5 parts, Firebrake ZB 2 parts, asbestos 6
Part, 6 parts of Firmiana platanifolia (Linn. f.) Marsili bark, 9 parts of bamboo powder, Folium Ginkgo 7 parts, expanded perlite 7 parts, wintergreen oil 0.2 part, 3-hydroxy benzoic acid 4 parts,
Sulfated lauryl alcohol 1 part, plant saponin 6 parts, terpineol 0.1 part, white glue with vinyl 1 part.
3. a kind of environmental protection Wood-plastic floor material, it is characterised in that its preparation method comprises the following steps:
(1) successively by PVC resin powder, straw, polyethylene, polyphenylene oxide, Benzoinum, mica powder, Firebrake ZB, asbestos, Firmiana platanifolia (Linn. f.) Marsili bark,
Bamboo powder, Folium Ginkgo, expanded perlite, wintergreen oil, 3-hydroxy benzoic acid, sulfated lauryl alcohol, plant saponin, terpineol,
White glue with vinyl adds high-speed mixer and is sufficiently mixed uniformly；
(2) step of pelletize, is carried out in comminutor, through the process heated, mediate, bond, by the material after high pressure batch mixing
Adding in comminutor, prilling temperature is 180-300 DEG C, and the material time in comminutor is 20-30 minute, and final preparing is combined
Material grain；
(3) extrusion molding, the compound material grain stirring mixing that will obtain in granulation step, it is subsequently adding extruder and is extruded into plate
Material, the machine barrel of extruder includes five warm areas, by feed end to extruding end, the temperature of five warm areas be set as successively 150 DEG C,
260 DEG C, 200 DEG C, 220 DEG C, 185 DEG C, the machine barrel of extruder connects vaccum-pumping equipment, and the pressure in machine barrel is 0.05MPa.
A kind of environmental protection Wood-plastic floor material the most according to claim 1, it is characterised in that described mica powder granularity is 100-
260 mesh.