CN106348738A - Health-maintaining ceramics and preparing method thereof - Google Patents
Health-maintaining ceramics and preparing method thereof Download PDFInfo
- Publication number
- CN106348738A CN106348738A CN201610764801.4A CN201610764801A CN106348738A CN 106348738 A CN106348738 A CN 106348738A CN 201610764801 A CN201610764801 A CN 201610764801A CN 106348738 A CN106348738 A CN 106348738A
- Authority
- CN
- China
- Prior art keywords
- health preserving
- tourmaline
- maifanitum
- health
- preserving pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a ceramic material, and discloses health-maintaining ceramics and a preparing method thereof. The health-maintaining ceramics consist of the following raw materials in weight percentage: 20 -27% of clay, 30 -34% of quartz, 15 - 20% of feldspar, 14 -18% of dolomite, 1 -2% of calcite, 3 -5% of tourmaline and 6 - 8% of medical stone. The preparing process of the health-maintaining ceramics is simple. According to the a new process in which iron content in the tourmaline and the medical stone is reduced, and ceramics are formed via the formula of ceramic foundation blank and glaze, the aims of improving the whiteness and clarity of the health-maintaining ceramics and improving the pyroelectric property are fulfilled.
Description
Technical field
The present invention relates to a kind of ceramic material and preparation method thereof is and in particular to a kind of health preserving pottery and preparation method thereof.
Background technology
Health preserving pottery is in recent years on the basis of the artistry of traditional ceramicses, the suitability, increasingly increases for improving Modern human populations
Long quality of the life and the new porcelain kind researched and developed.Be different from traditional ceramicses is that it such as has health preserving, health care, gets rid of illness at the function.Using
The beneficiating ingredient to human body in natural mineral raw, special physico-chemical effect, implant in traditional ceramicses preparation process above because
Element, is a kind of novel ceramic craft, is also that human development utilizes mineral resources, good for health, life lengthening direction.
But, the dyeing element such as irony in natural mineral raw, whiteness, the transparency of pottery can be affected.And it is most
Crowd is partial to white, saturating or more gorgeous tone, repels the dead color based on ferrum.
" female spy " test shows: the change of iron oxide content in tourmaline, and tourmaline pyroelectric effect is had a direct impact.
Iron oxide content increases, and pyroelectric effect gradually weakens;Conversely, pyroelectric effect strengthens.And pyroelectricity characteristic directly affect negative
Ionic effect and the power of far infrared effect.
Content of the invention
The present invention becomes in porcelain technique, the function raw mineral materials adding only is focused on its granularity, ignorance adjustment for prior art
Its iron-holder, leads to into porcelain whiteness, thoroughly spends poor, the low defect of pyroelectric effect, can strengthen tourmaline, wheat according to reducing iron content
The principle of meal stone pyroelectric effect, provide first by tourmaline, Maifanitum separating-purifying be concentrate, then participate in pottery basis base, glaze
Formula becomes the new technology of porcelain, the high whiteness of output, the high strong health preserving ceramic of degree, health-preserving function thoroughly.
To achieve these goals, a kind of health preserving pottery that the present invention provides, by the percentage by weight group of following raw material
Become: clay 20 ~ 27%;Quartz 30 ~ 34%;Anhydrite 15 ~ 20%;Dolomite 14 ~ 18%;Calcite 1 ~ 2%;Tourmaline 3 ~ 5%;Maifanitum
6~8%.
Further, the raw material composition of described health preserving pottery also includes the lithium porcelain stone that percentage by weight is 2 ~ 6%.
Preferably, described tourmaline and the separated purification of Maifanitum are so as to iron content is less than 0.3%.
The preparation method of described health preserving pottery comprises the following steps:
S1. carried out in small, broken bits to tourmaline and Maifanitum except ferrum by physics, chemical method to 200 mesh, make this two raw mineral materials
Iron content be down to less than 0.3%;
S2. by clay 20 ~ 27%;Quartz 30 ~ 34%;Anhydrite 15 ~ 20%;Dolomite 14 ~ 18%;Calcite 1 ~ 2%;And divide through s1
From tourmaline 3 ~ 5% and the Maifanitum 6 ~ 8% of purification, mix in proportion, fed intake;
S3. press material: ball: the mass ratio of water is 1: 1.5: 0.8, is ground, milling time is 15 ~ 20 hours;
S4. the compound after grinding is carried out process of sieving, then is designed by purposes requirement, extrusion molding, and repair surface,
Reject plug-hole pug;
S5. s4 gained base substrate is sintered in 1300 ~ 1330 DEG C of high temperature reduction flames, firing time is 8 ~ 10 hours, furnace cooling,
Obtain final product described health preserving pottery.
Preferably, 250 eye mesh screens, screen over-size < 0.5% are adopted in described step s4 screening process.
Preferably, the sintering temperature of described step s5 base substrate is 1330 DEG C.
Beneficial effects of the present invention:
(1) in prior art the preparation technology of function ceramics need with 10% about tourmaline and 18% about Maifanitum, this
Invention at most only need to become base, glaze porcelain making with the tourmaline 5% of separated purification and Maifanitum 8% respectively, can at least save tourmaline
5%th, save Maifanitum 10%, the production cost of health preserving pottery is greatly lowered.
(2) preparation process is simple of health preserving pottery of the present invention, is contained by first reducing the ferrum in tourmaline and Maifanitum raw material
Amount, then participate in the new technology that pottery basis base, glaze formula become porcelain, improve health preserving pottery whiteness, thoroughly spend, and lifted its heat to reach
Release the purpose of electrical property.
Specific embodiment
The invention will be further described below.Following examples are only used for the technical side of the present invention is clearly described
Case, and can not be limited the scope of the invention with this.
Embodiment 1
A kind of health preserving pottery, the percentage by weight of its raw material is: clay 25%;Quartz 30%;Anhydrite 17%;Dolomite 14%;Fang Xie
Stone 1%;Tourmaline 5%;Maifanitum 8%.Its product producing process step includes: (1) by small, broken bits to tourmaline and Maifanitum to 200 mesh,
Carry out making the iron content of this two raw mineral materials be down to less than 0.3% except ferrum by physics, chemical method;(2) by raw material press than
Example mix homogeneously, is fed intake;(3) press material: ball: the mass ratio of water is 1: 1.5: 0.8, is ground, milling time is little for 15
When;(4) compound after grinding is carried out process of sieving, adopt 250 eye mesh screens, screen over-size < 0.5% in screening process, then press
Purposes requires to be designed, extrusion molding, and repairs surface, rejects plug-hole pug;(5) by gained base substrate in 1300 DEG C of oxidizing flames
Middle sintering, firing time is 8 hours, and furnace cooling obtains final product described wheat meal porous ceramicss.
Embodiment 2
A kind of health preserving pottery, the percentage by weight of its raw material is: clay 20%;Quartz 34%;Anhydrite 19%;Dolomite 14%;Fang Xie
Stone 2%;Tourmaline 4%;Maifanitum 7%.Its product producing process step includes: (1) by small, broken bits to tourmaline and Maifanitum to 200 mesh,
Carry out making the iron content of this two raw mineral materials be down to less than 0.3% except ferrum by physics, chemical method;(2) by raw material press than
Example mix homogeneously, is fed intake;(3) press material: ball: the mass ratio of water is 1: 1.5: 0.8, is ground, milling time is little for 20
When;(4) compound after grinding is carried out process of sieving, adopt 250 eye mesh screens, screen over-size < 0.5% in screening process, then press
Purposes requires to be designed, extrusion molding, and repairs surface, rejects plug-hole pug;(5) by gained base substrate in 1330 DEG C of oxidizing flames
Middle sintering, firing time is 10 hours, and furnace cooling obtains final product described wheat meal porous ceramicss.
Embodiment 3
A kind of health preserving pottery, the percentage by weight of its raw material is: clay 27%;Quartz 30%;Anhydrite 15%;Dolomite 18%;Fang Xie
Stone 1%;Tourmaline 3%;Maifanitum 6%.Its product producing process step includes: (1) by small, broken bits to tourmaline and Maifanitum to 200 mesh,
Carry out making the iron content of this two raw mineral materials be down to less than 0.3% except ferrum by physics, chemical method;(2) by raw material press than
Example mix homogeneously, is fed intake;(3) press material: ball: the mass ratio of water is 1: 1.5: 0.8, is ground, milling time is little for 18
When;(4) compound after grinding is carried out process of sieving, adopt 250 eye mesh screens, screen over-size < 0.5% in screening process, then press
Purposes requires to be designed, extrusion molding, and repairs surface, rejects plug-hole pug;(5) by gained base substrate in 1300 DEG C of oxidizing flames
Middle sintering, firing time is 9 hours, and furnace cooling obtains final product described wheat meal porous ceramicss.
The health preserving pottery of present invention preparation is by the iron content in first minimizing tourmaline and Maifanitum raw material, then participates in pottery
Basic base, glaze formula become the new technology of porcelain, improve health preserving pottery whiteness, thoroughly spend to reach, and the mesh lifting its pyroelectric property
's.Shown in the following contrast table of its excellent properties.
Unprocessed with the tourmaline after separating-purifying, Maifanitum participates in formula and becomes the whiteness after porcelain to compare:
Unprocessed with the tourmaline after separating-purifying, Maifanitum participates in formula and becomes anion releasing number after porcelain to compare
Finally it is noted that obviously, above-described embodiment is only intended to clearly illustrate example of the present invention, and not right
The restriction of embodiment.For those of ordinary skill in the field, can also be made it on the basis of the above description
The change of its multi-form or variation.There is no need to be exhaustive to all of embodiment.And thus amplified out
Obvious change or change still in protection scope of the present invention among.
Claims (6)
1. a kind of health preserving pottery is it is characterised in that be made up of the percentage by weight of following raw material: clay 20 ~ 27%;Quartzy 30 ~
34%;Anhydrite 15 ~ 20%;Dolomite 14 ~ 18%;Calcite 1 ~ 2%;Tourmaline 3 ~ 5%;Maifanitum 6 ~ 8%.
2. a kind of health preserving pottery according to claim 1 is it is characterised in that the raw material composition of described health preserving pottery also includes
Percentage by weight is 2 ~ 6% lithium porcelain stone.
3. a kind of health preserving pottery according to claim 1 is it is characterised in that described tourmaline and Maifanitum is separated carries
Pure so as to iron content be less than 0.3%.
4. a kind of preparation method of the health preserving pottery described in claim 1 is it is characterised in that the method comprising the steps of:
S1. carried out in small, broken bits to tourmaline and Maifanitum except ferrum by physics, chemical method to 200 mesh, make this two raw mineral materials
Iron content be down to less than 0.3%;
S2. by clay 20 ~ 27%;Quartz 30 ~ 34%;Anhydrite 15 ~ 20%;Dolomite 14 ~ 18%;Calcite 1 ~ 2%;And divide through s1
From tourmaline 3 ~ 5% and the Maifanitum 6 ~ 8% of purification, mix in proportion, fed intake;
S3. press material: ball: the mass ratio of water is 1: 1.5: 0.8, is ground, milling time is 15 ~ 20 hours;
S4. the compound after grinding is carried out process of sieving, then is designed by purposes requirement, extrusion molding, and repair surface,
Reject plug-hole pug;
S5. s4 gained base substrate is sintered in 1300 ~ 1330 DEG C of high temperature reduction flames, firing time is 8 ~ 10 hours, furnace cooling,
Obtain final product described health preserving pottery.
5. a kind of preparation method of health preserving pottery according to claim 4 is it is characterised in that described step s4 screening process
In adopt 250 eye mesh screens, screen over-size < 0.5%.
6. a kind of preparation method of health preserving pottery according to claim 4 is it is characterised in that the burning of described step s5 base substrate
Junction temperature is 1330 DEG C.