CN106337141A - 一种改善adc6铝合金锭性能的方法 - Google Patents

一种改善adc6铝合金锭性能的方法 Download PDF

Info

Publication number
CN106337141A
CN106337141A CN201510409334.9A CN201510409334A CN106337141A CN 106337141 A CN106337141 A CN 106337141A CN 201510409334 A CN201510409334 A CN 201510409334A CN 106337141 A CN106337141 A CN 106337141A
Authority
CN
China
Prior art keywords
refine
aluminium
minute
degasification
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510409334.9A
Other languages
English (en)
Other versions
CN106337141B (zh
Inventor
程帅
陆时忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shuai wing Chi New Material Group Co., Ltd.
Original Assignee
SHANGHAI SHUAIYICHI ALUMINUM ALLOY NEW MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI SHUAIYICHI ALUMINUM ALLOY NEW MATERIAL Co Ltd filed Critical SHANGHAI SHUAIYICHI ALUMINUM ALLOY NEW MATERIAL Co Ltd
Priority to CN201510409334.9A priority Critical patent/CN106337141B/zh
Publication of CN106337141A publication Critical patent/CN106337141A/zh
Application granted granted Critical
Publication of CN106337141B publication Critical patent/CN106337141B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及铝合金技术领域,特别涉及一种改善ADC6铝合金锭性能的方法。将金属元素锌的元素含量控制为0.1%以下,生产步骤如下:熔融;扒渣;熔锰;降温;除渣;精炼;除气;静置;铸锭。本发明方法生产的ADC6铝合金锭氧化着色经多次试验,检测结果均氧化着色得到较大改善,优于现有的生产方法。

Description

一种改善ADC6铝合金锭性能的方法
技术领域
本发明涉及铝合金技术领域,特别涉及一种改善ADC6铝合金锭性能的方法。
背景技术
ADC6铝锭也有较好市场前景,由于该材料镁含量较高,耐腐蚀性较好,可以用于做汽车上的油泵和其它耐腐蚀件。
国家标准的ADC6 成份中部分要控制的有害元素要求较宽,如果不去根据用户的产品特点加以收窄控制,就会对一些有外观要求(比如氧化着色)产品带来严重影响,甚至出现批量报废的问题。这个问题没有得到有效解决之前,ADC6外观件的应用会受到很大限制。
按照现有生产方法进行生产ADC6铝合金锭的作业,其压铸后的产品氧化着色情况严重,无法达到和满足压铸用户进一步的质量要求。
发明内容
本发明的目的是改善ADC6铝合金锭的氧化着色,以解决现有技术中的上述缺陷,提高该系合金的综合性能。
为实现以上目的,本发明提供了一种改善ADC6铝合金锭氧化着色的生产方法,该生产方法包括从铝料投炉熔化至浇铸成锭的整个过程。其主要控制为金属元素锌含量的控制。
本发明的具体技术方案是:
一种改善ADC6铝合金锭氧化着色的生产方法,将金属元素锌的元素含量控制为0.1%以下,具体生产步骤如下:
(1)将质量百分比40%的熟铝、合金,及40%的A00铝锭投入熔炉中,进行助熔,总熔化时长为5-7小时,熔融温度控制为630-740℃;
(2)扒渣:用铁锹在铝合金液表面撒上15-20KG清渣剂,用铁扒轻轻敲打液面5-10分钟后扒渣,并将铝渣清出炉口,不能用铁扒搅动铝液;
(3)熔锰:铝液表面无浮渣时加入金属锰,加入后用铁扒充分搅拌铝液3-5分钟,然后开火加温10-15分钟再搅拌3-5分钟,重复4—6次;
(4)降温:加品管开具的调整料把熔锰的温度降到精炼要求的温度730-740℃,如果温度低应开火升温;加降温料可以是一次也可以是多次,要根据炉内铝液成分来确定,但要保证铝料干净、成分明确;后期如需少量添加锰应以中间合金的形式加入;
(5)除渣:加入调整料后根据铝液表面浮渣的多少来确定清渣剂的投入量,范围在10-15㎏;用铁扒敲打液面5-10分钟后扒渣,并将铝渣清出炉口,不能用铁扒搅动铝液;
(6)精炼:分为两次,第一次精炼:铝液温度控制为740±10℃;精炼时间控制在20分钟;扒渣时间≧15分钟;精炼剂数量控制为1.4-1.7KG/吨。第二次精炼:铝液温度控制为740±10℃;精炼时间控制在20分钟;扒渣时间≧15分钟;精炼剂数量控制为1.1-1.3KG/吨;
(7)除气:除气时间控制为20-30分钟,温度控制为750-770℃;除气过程有浮渣时应在除气结束前把浮渣通过除气集中到炉口用铁扒扒干净;
(8)熔炼工段精炼、除气方法:将精炼管弯头向下伸进铝水中,同时打开氮气阀门,把氮气输出压力调至0.2Mpa,首先由左到右或由右到左纵向精炼、除气,其次由内至外或由外至里横向精炼、除气,以达到在炉内空间搅拌形成“井”字形,不允许在某个部位持续停留;
(9)静置:静置时间15-20分钟,静置温度760±10℃;静置期间不可搅动铝液以保护铝液表面形成的氧化膜;
(10)铸锭。
进一步的,上述步骤(3)熔锰步骤,是在无浮渣时加入金属锰;加入时温度≧720℃;每间隔10-15分钟搅拌铝液3-5分钟;搅拌时停火;加温至760-780℃时停止加温;通常整个熔锰时间控制为60-90分钟;锰的加入量要充足防止后期少量补加;熔锰后加入镁。
进一步的,上述步骤(9)精炼、除气过程要始终将精炼管弯端口与炉底保持一定的距离,通常保持在距离炉底1/4高度;每次纵横精炼、除气时移动速度要匀速;除气时要控制铝液溅起的高度≦15CM。
本发明的有益效果是:
1、本发明方法生产的ADC6铝合金锭氧化着色经多次试验,检测结果均氧化着色得到较大改善,优于现有的生产方法。
2、使得使用本发明方法生产的ADC6铝合金锭,在送至用户处后,反馈良好,该方法生产的铝合金锭压铸件综合性能也优于之前,氧化着色现象得到很好地改善。
具体实施方式
下面结合具体实施例,进一步阐述本发明。应该理解,这些实施例仅用于说明本发明,而不用于限定本发明的保护范围。在实际应用中技术人员根据本发明做出的改进和调整,仍属于本发明的保护范围。
以下列出实施例,以举例说明本发明。
一种ADC6铝合金锭,其组成以质量分数表示为:
Si:0.26%、Fe:0.4%、Cu:0.03%、Mn:0.48%、Mg:3.15%、Cr:0.05%、Ni:0.005%、Zn:0.02%、Ti:0.009%、Pb:0.005%、Sn:0.001%。
4、所述改善ADC6铝合金锭氧化着色的工艺制作方法如下:
该合金成分除铝外,主要含有以下重量百分比的成分:
(1)将质量百分比40%的熟铝、合金,及40%的A00铝锭投入熔炉中,进行助熔,总熔化时长为6小时,熔融温度控制为738℃;
(2)扒渣:用铁锹在铝合金液表面撒上15KG清渣剂(清渣剂由上海虹光金属溶剂厂生产,型号为HGJ-3),用铁扒轻轻敲打液面6分钟后扒渣,并将铝渣清出炉口;
(3)熔锰:铝液表面无浮渣时加入金属锰,加入后用铁扒充分搅拌铝液5分钟,然后开火加温15分钟再搅拌5分钟,重复5次;
(4)降温:加品管开具的调整料把熔锰的温度降到精炼要求的温度741℃;
(5)除渣:加入调整料后根据铝液表面浮渣的多少投入清渣剂10㎏;用铁扒敲打液面6分钟后扒渣,并将铝渣清出炉口;
(6)精炼:分为两次,第一次精炼:铝液温度为741℃;精炼时间为20分钟;扒渣时间为15分钟;精炼剂数量为28KG。第二次精炼:铝液温度为740℃;精炼时间为20分钟;扒渣时间为15分钟;精炼剂数量控制为22KG;(精炼剂由上海虹光金属溶剂厂生产,型号为HGK5-1A)
(7)除气:除气时间控制为20-30分钟,温度控制为743℃;
(8)静置:静置时间20分钟,静置温度758℃;
(9)铸锭
1 清理流槽、模具:①首先用钩子把流槽上的铝料清理干净;其次用毛刷把松动的耐高温材料和其它杂物清理掉。清理后用气管轻轻吹扫干净,用手触摸,确认手上无灰尘;②模具清理:用小铁钎把粘附的铝料清理掉,然后用气管吹扫模具,刷脱模涂料,浇铸前充分烘烤模具。2 刷滑石粉:滑石粉与纯净水按1:4的比例调和均匀后,用毛刷均匀涂在流槽上,等待18分钟,把锰酸纸盖在流槽上方,下方用小火一段一段的烘烤,直到各段水份烘干。3 打磨、清理(针对流槽):烘干后,用砂纸把流槽不平、凸起或松动的地方轻轻磨掉,使之平整;各处打磨完成后,再用毛刷轻轻把打磨掉的滑石粉清理干净,最后用气管轻轻吹扫干净。4 对分配鼓进行清理、吹扫;5 对锭模进行清理、吹扫、刷涂料、烘烤;6 对铸锭线和叠锭机的运行检查(含分配鼓、模具,运行一次);7 对冷却水进行检查;8 浇铸前检查矿灯、塞头、塞套、锰酸纸、铁铲等操作工具的准备情况。9 浇铸工艺:浇铸温度为炉内704℃、分配鼓681℃,放置过滤网,铸锭速度为12m/min。10、①浇铸工段人员在第二次精炼时开始铸锭前准备工作;②铸锭后取检验样品作氧化着色检测,氧化着色检测结果均为良好。
下表所示:
如上表所示,对金属元素锌的元素含量进行控制后,产品压铸件氧化着色问题得到很大改善。

Claims (3)

1.一种改善ADC6铝合金锭氧化着色的生产方法,其中金属元素锌的元素含量控制为0.1%质量百分比以下,生产步骤如下:
(1)将质量百分比40%的熟铝、合金,及40%的A00铝锭投入熔炉中,进行助熔,总熔化时长为5-7小时,熔融温度控制为630-740℃;
(2)扒渣:用铁锹在铝合金液表面撒上15-20KG清渣剂,用铁扒敲打液面5-10分钟后扒渣,并将铝渣清出炉口,不能用铁扒搅动铝液;
(3)熔锰:铝液表面无浮渣时加入金属锰,加入后用铁扒充分搅拌铝液3-5分钟,然后开火加温10-15分钟再搅拌3-5分钟,重复4—6次;
(4)降温:加品管开具的调整料把熔锰的温度降到精炼要求的温度730-740℃;
(5)除渣:加入调整料后根据铝液表面浮渣的多少来确定清渣剂的投入量,范围在10-15㎏;用铁扒敲打液面5-10分钟后扒渣,并将铝渣清出炉口,不能用铁扒搅动铝液;
(6)精炼:分为两次,第一次精炼:铝液温度控制为740±10℃;精炼时间控制在20分钟;扒渣时间≧15分钟;精炼剂数量控制为1.4-1.7KG/吨;
第二次精炼:铝液温度控制为740±10℃;精炼时间控制在20分钟;扒渣时间≧15分钟;精炼剂数量控制为1.1-1.3KG/吨;
(7)除气:除气时间控制为20-30分钟,温度控制为750-770℃;除气过程有浮渣时应在除气结束前把浮渣通过除气集中到炉口用铁扒扒干净;
(8)熔炼工段精炼、除气方法:将精炼管弯头向下伸进铝水中,同时打开氮气阀门,把氮气输出压力调至0.2Mpa,首先由左到右或由右到左纵向精炼、除气,其次由内至外或由外至里横向精炼、除气,以达到在炉内空间搅拌形成“井”字形,不允许在某个部位持续停留;
(9)静置:静置时间15-20分钟,静置温度760±10℃;静置期间不可搅动铝液以保护铝液表面形成的氧化膜;
(10)铸锭。
2.根据权利要求1所述的一种改善ADC6铝合金锭氧化着色的生产方法,其特征在于,所述步骤(3)熔锰步骤,是在无浮渣时加入金属锰;加入时温度≧720℃;每间隔10-15分钟搅拌铝液3-5分钟;搅拌时停火;加温至760-780℃时停止加温;通常整个熔锰时间控制为60-90分钟;锰的加入量要充足防止后期少量补加;熔锰后加入镁。
3.根据权利要求1所述的一种改善ADC6铝合金锭氧化着色的生产方法,其特征在于,所述步骤(8)精炼、除气过程要始终将精炼管弯端口与炉底保持一定的距离,通常保持在距离炉底1/4高度;每次纵横精炼、除气时移动速度要匀速;除气时要控制铝液溅起的高度≦15CM。
CN201510409334.9A 2015-07-14 2015-07-14 一种改善adc6铝合金锭性能的方法 Active CN106337141B (zh)