CN101880803A - 汽车车身板用Al-Mg系铝合金及其制造方法 - Google Patents

汽车车身板用Al-Mg系铝合金及其制造方法 Download PDF

Info

Publication number
CN101880803A
CN101880803A CN 201010241214 CN201010241214A CN101880803A CN 101880803 A CN101880803 A CN 101880803A CN 201010241214 CN201010241214 CN 201010241214 CN 201010241214 A CN201010241214 A CN 201010241214A CN 101880803 A CN101880803 A CN 101880803A
Authority
CN
China
Prior art keywords
temperature
alloys
automobile
sheets
aluminium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010241214
Other languages
English (en)
Other versions
CN101880803B (zh
Inventor
丁荣辉
曲明洋
黄文辉
曾凡清
张超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Ju Ke Industrial Co., Ltd.
Original Assignee
ZHEJIANG GKO ALUMINUM CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG GKO ALUMINUM CO Ltd filed Critical ZHEJIANG GKO ALUMINUM CO Ltd
Priority to CN201010241214A priority Critical patent/CN101880803B/zh
Publication of CN101880803A publication Critical patent/CN101880803A/zh
Application granted granted Critical
Publication of CN101880803B publication Critical patent/CN101880803B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种汽车车身板用Al-Mg系铝合金及其制造方法,属于合金材料技术领域。它解决了现有的5754系铝合金强度以及抗冲击性差的问题。本汽车车身板用Al-Mg系铝合金,该铝合金的成分及其质量百分比为:Cu:0.001-0.25wt%;Mn:0.05-0.35wt%;Mg:2.5-3.5wt%;Cr:0.005%-0.25wt%;Zn:0.008-0.8wt%;Ti:0.01-0.15wt%;Zr:0.001-0.2wt%;Si≤0.2wt%;Fe≤0.3wt%;余量为Al。本汽车车身板用Al-Mg系铝合金及其制造方法具有抗冲击性能好、塑性好、可行性强以及加工过程中能实现节能减排目的的优点。

Description

汽车车身板用A卜Mg系铝合金及其制造方法
技术领域
[0001] 本发明涉及一种铝合金及其制造方法,尤其涉及一种汽车车身板用Al-Mg系铝合 金及其制造方法,属于合金材料技术领域。
背景技术
[0002] 世界汽车工业正面临越来越严峻的三大课题:能源、环保、安全。减轻汽车自重以 降低能耗,减少环境污染,提高汽车的燃料经济性,节约有限资源已成为各大汽车厂关注的 焦点。铝合金作为汽车轻量化的首选材料,具有其它合金材料无法比拟的优良性能。主要 体现在比强度高、耐蚀性好、抗冲击性良好,易表面着色,良好的加工成形性,以及较高的再 回收、再生性等一系列优良特性。
[0003] 由于轿车车身约占总车重量30%,近年来铝合金车身板倍受关注。非可热处理的 5xxx系铝合金被认为是用作汽车车身板非常理想的合金,其在汽车制造过程中有良好的深 拉延性能和冲型性能,易于制造内板等形状复杂的部位。
[0004] 5xxx系铝合金中的5754铝合金具有中等强度、良好的耐蚀性、焊接性及易于加工 成形等特点,是Al-Mg系合金中的典型合金,不同热处理状态的5754铝合金板材是汽车制 造业(轿车车门、模具、密封件)、制罐工业所用的主要材料。
[0005] 现有技术中5754系铝合金属于不可热处理强化合金,如果将其应用于汽车车身 板其强度略显不够,抗冲击性较差,现有生产5754铝合金强度和抗凹陷性不能满足汽车车 身板的要求。同时5754铝合金在深冲过程中通常产生产品表面出现一系列新台阶或锯齿 状变形带,严重影响表面质量,而且烤漆后出现软化现象,使其不利于作为铝合金汽车车身 板的应用。
发明内容
[0006] 本发明的目的是针对现有的5754铝合金所存在的缺陷,提供一种以5754铝合金 为研究对象,强度高、拉伸性能好,烤漆后强度不会降低,满足成形性和对抗冲击性的汽车 车身板用Al-Mg系铝合金。
[0007] 本发明的目的可通过下列技术方案来实现:一种汽车车身板用Al-Mg系铝合金, 该铝合金的成分及其质量百分比为:
[0008] Cu :0. 001-0. 25wt% ;Mn :0. 05-0. 35wt% ;Mg :2. 5-3. 5wt% ;
[0009] Cr :0. 005% -0. 25wt% ;Zn :0. 008-0· 8wt% ;Ti :0. 01-0. 15wt% ;
[0010] Zr :0. 001-0. 2wt% ;Si 彡 0. 2wt% ;Fe 彡 0. 3wt% ;
[0011] 余量为Al。
[0012] 现有技术中的5754铝板的化学成份及其质量百分比为:娃Si :0. 40 ;铜Cu :0. 10 ; 镁 Mg :2. 6 〜3. 6 ;锌 Zn :0. 2 ;锰 Mn :0. 50 ;铬 Cr :0. 30 ;铁 Fe :0. 40 ;铝 Al :余量。
[0013] 本发明以5754铝合金为研究对象,在基体合金基础上添加0. 001-0. 2衬%的Zr。 在铝镁合金中,析出了弥散、细小的共格第二相质点Al3Zr,其强化机理是在合金中产生了
3极其强烈的细晶强化、亚结构强化、弥散强化及共格强化等强化作用,避免形成粗大的第二 相化合物,细化材料的组织,改善材料的性能。
[0014] 在合金中加入一定的Zn和Cu,可以通过形成η-MgZn2、CuMgAl2与Al2Cu化合物的 弥散分布提高合金强度,还可以产生一定的时效强化,在5754铝合金中添加锌较好的防止 了拉伸滑移带的产生,有利于冲压成形,烤漆后屈服强度不会下降,较好的满足汽车车身板 抗冲击的性能。
[0015] 在合金中加入其质量百分比为0.01-0. 15衬%的Ti,可以提高汽车车身板用 Al-Mg系铝合金的抗腐蚀性能和在铸造过程中热裂纹倾向,同事又避免降低铝合金的加工 性能。
[0016] 本发明还有效的控制了有害杂质Si和Fe的含量,提高了铝合金的抗腐蚀性能和 塑性。
[0017] 在上述的汽车车身板用Al-Mg系铝合金中,该铝合金的成分及其质量百分比为:
[0018] Cu :0. 1-0. 2wt% ;Mn :0. 1-0. 2wt% ;Mg :2. 8-3. 4wt% ;
[0019] Cr :0. 01% —0. 2wt% ;Zn :0. 2-0. 5wt% ;Ti :0. 05-0. Iwt% ;
[0020] Zr :0. 005-0. 15wt% ;Si 彡 0. Iwt% ;Fe 彡 0. 2wt% ;
[0021] 余量为Al。
[0022] 本发明的另一个目的在于提供上述汽车车身板用Al-Mg系铝合金的制造方法,该 方法包括以下步骤:
[0023] A、浇注成型:先将铝锭加入坩埚电阻炉中,待铝锭熔化且熔体温度为750-800°C 时,加入AlCu50、AlMnl0、AlCr4、Al&4中间合金并搅拌;待熔体温度至700-750°C,加入Mg 和Zn,打渣、精炼;待温度在700-730°C,加入Α1-5ΊΊ-Β中间合金,搅拌并静置10-30分钟, 在铸铁模中浇注成型;
[0024] B、均勻化处理:将上述浇注成型的铝合金铸锭均勻化处理,轧制成薄板;
[0025] C、退火:将上述制得的薄板进行退火处理,退火处理的温度为320_420°C,处理的 时间为0. 5-3h,退火处理后制得成品。
[0026] 在上述汽车车身板用Al-Mg系铝合金的制造方法中,作为优选,步骤A中在铸铁模 中浇注成型的温度为700-730°C。本发明以5754铝合金为研究对象,5754铝合金中Mg含 量较高,质量分数为2. 8-3.4%,熔体表面的MgO膜不致密(MgO/Mg为0. 78,< 1),氧化膜 容易破裂或呈疏松多孔状,气体可通过氧化膜的裂缝或空缝进入熔体,吸气率随时间增长 呈直线增加。吸气率还与熔体温度有关,熔体温度越高,吸气性越强,铝中吸收的气体主要 是氢。氢是熔融铝和水反应生成的,在一定的大气压下,温度越高,氢在铝中的溶解度就越 大。在固态时,氢几乎不溶于铝。而从固态到液态时,氢在铝中的溶解度出现一个突变,这 种溶解度急剧变化的特点,决定了铝在凝固时,使氢原子从金属中析出成为分子氢,最后以 疏松、气孔的形式存在于铸锭中,造成疏松、气孔等缺陷,同时,浇铸温度过高,5系铝合金中 Mg烧损严重,最终影响成品的强度与延伸率。浇铸温度过低,高熔点的第二相凝固沉淀,造 成铸锭成分组织部均勻。待温度在700-730°C浇铸时,吸气少,Mg烧损不大,中间合金元素 均勻扩散。
[0027] 在上述汽车车身板用Al-Mg系铝合金的制造方法中,作为优选,步骤A中加入Mg 和Zn时熔体温度为710-740°C。Zn和Mg熔点都很低,并且均容易被氧化,熔炼时烧损严
4重,710-740°C加入Zn和Mg可以减少Zn和Mg的烧损量,从而保证成品的力学性能和成形 性能。
[0028] 在上述汽车车身板用Al-Mg系铝合金的制造方法中,步骤B中均勻化处理的温度 为450-480°C,处理时间为10-24小时。均勻化退火的目的是为后续加工做组织准备。均 勻化退火中的主要组织变化是枝晶偏析消除、非平衡相溶解和过饱和的过渡元素相沉淀, 溶质的浓度逐渐均勻化。在均勻化退火过程中,不溶的过剩相也会发生聚集、球化。均勻化 退火保温后慢冷时,高温下溶入固溶体的溶质,将按溶解度随温度降低而减小的规律,在晶 粒内部较均勻地沉淀析出。温度升高将使扩散过程大大加速,为加速均勻化过程,应尽可能 提高均勻化退火温度。通常采用的均勻化退火温度为0.9-0. 95Tm。Tm表示铸锭实际开始 熔化温度,它低于平衡相图上的固相线。但5系合金均勻化温度过高Mg烧损氧化严重,粗 晶,造成成品强度不够。所以,铝-镁合金均勻化温度一般选为440-495°C,Mg含量较高时, 温度控制在下限。同时,应确保均勻化退火炉炉膛温度均勻,最好是偏差不要超过士 10°C。 铝-镁合金铸锭均勻化保温时间一般控制在13_36h,Mg含量高时控制在上限,否则偏析难 以消除,导致成品延伸率较低。本发明以5754铝合金为研究对象,Mg含量中高,450-480°C, 处理时间为10-24小时较为合理。
[0029] 在汽车车身板用Al-Mg系铝合金的制造方法中,作为优选,步骤C中退火处理的温 度为350-400°C,处理的时间为l_2h,退火处理后空冷。进一步的优选,步骤C中退火处理 的温度为350°C,处理的时间为2h。本发明以5754铝合金为研究对象,5754充分再结晶温 度范围为320-400°C,加热温度过高、保温时间过长会导致晶粒长大,造成粗晶,从而影响成 品的力学性能和成形性能,所以退火处理的温度为350-400°C,处理的时间为l_2h较为合 理。
[0030] 综上所述,本发明具有以下优点:
[0031] 1、本发明的汽车车身板用Al-Mg系铝合金在5754铝合金基础上通过对成分的适 当配比,添加少量的Zr、Ti、Zn和Cu后的合金薄板冲压前的屈服强度较低,有利于冲压成 形,而烤漆后强度没有降低,而且有所升高,该铝合金用作车身板具有良好的抗冲击性能。
[0032] 2、本发明的Al-Mg系铝合金用作汽车车身板能有效防止烤漆后的强度降低,同时 具有良好的塑性,更好的促进汽车行业广泛采用铝合金板材来替代钢板生产汽车车身冲压 件,满足实现节能减排的目的,带来了极为良好的经济效益,应用前景十分看好。
[0033] 3、本发明汽车车身板用Al-Mg系铝合金的制造方法工艺流程简单,可行性强,能 实现大规模工业化生产。
具体实施方式
[0034] 下面通过具体实施例,对本发明的技术方案作进一步具体的说明;但是本发明并 不限于这些实施例。
[0035] 本发明以5754铝合金为研究对象,材料的成分及其质量百分比为:Cu : 0. 001-0. 25wt % ;Mn :0. 05-0. 35wt % ;Mg :2. 5-3. 5wt % ;Cr :0. 005 % -0. 25wt % ;Zn : 0. 008-0. 8wt% ;Ti :0. 01-0. 15wt% ;Zr :0. 001-0. 2wt% ;Si 彡 0. 2wt% ;Fe 彡 0. 3wt% ;余 量为Al。
[0036]优选为:Cu :0. 1-0. 2wt % ;Mn :0. 1-0. 2wt % ;Mg :2. 8-3. 4wt % ;Cr :0. 01% -0. 2wt% ;Zn :0. 2-0. 5wt% ;Ti :0. 05-0. lwt%;Zr :0. 005-0. 15wt%;Si ( 0. Iwt% ; Fe≤0. 2wt% ;余量为 Al。
[0037] 具体制造时,合金原料采用电解纯铝,99. 99% Mg,99. 99% Zn和AlCu50、AlMnlO, AlCr4、AlZr4、Al-5Ti-B 中间合金。
[0038] 表1 :实施例1-4铝合金成分的质量百分数)
[0039]
[0040] 实施例1
[0041] 按照表1中实施例1质量百分比进行配料,制成铝锭,中间合金AlCu50、AlMnlO, AlCr4、AlZr4、Al-5Ti-B。
[0042] 先将铝锭加入坩埚电阻炉中,待铝锭熔化且熔体温度为750°C时,加入A1CU50、 AlMnlO, AlCr4,AlZr4中间合金并搅拌;待熔体温度至650°C,加入Mg和Zn,打渣、精炼;待 温度在700°C,加入Α1-5ΊΊ-Β中间合金,搅拌并静置30分钟,在温度为700°C的铸铁模中浇
注成型。
[0043] 将上述浇注成型的铝合金铸锭均勻化处理,均勻化处理的温度为450°C,处理时间 为24小时,在温度为450°C条件下热轧,中间退火,中间退火的温度为400°C,中间退火的时 间为40min,中间退火后采用水淬快速冷却。冷轧2次轧成薄板。
[0044] 将上述制得的薄板进行退火处理,退火处理的温度为320°C,处理的时间为3h,退 火处理后出炉空冷制得汽车车身板用Al-Mg系铝合金成品。
[0045] 实施例2
[0046] 按照表1中实施例2质量百分比进行配料,制成铝锭,中间合金AlCu50、AlMnlO, AlCr4、AlZr4、Al-5Ti-B。
[0047] 先将铝锭加入坩埚电阻炉中,待铝锭熔化且熔体温度为780°C时,加入A1CU50、 AlMnlO、AlCr4、AlBe3、AlZr4中间合金并搅拌;待熔体温度至700°C,加入Mg和Zn,打渣、精 炼;待温度在710°C,加入Α1-5ΊΊ-Β中间合金,搅拌并静置20分钟,在温度为710°C的铸铁 模中浇注成型。[0048] 将上述浇注成型的铝合金铸锭均勻化处理,均勻化处理的温度为460°C,处理时间 为20小时,在温度为460°C条件下热轧,中间退火,中间退火的温度为420°C,中间退火的时 间为30min,中间退火后采用强风快速冷却。冷轧2次轧成薄板。
[0049] 将上述制得的薄板进行退火处理,退火处理的温度为350°C,处理的时间为2h,退 火处理后出炉空冷制得汽车车身板用Al-Mg系铝合金成品。
[0050] 实施例3
[0051] 按照表1中实施例3质量百分比进行配料,制成铝锭,中间合金AlCu50、AlMnlO, AlCr4、AlZr4、Al-5Ti-B。
[0052] 先将铝锭加入坩埚电阻炉中,待铝锭熔化且熔体温度为780°C时,加入A1CU50、 AlMnlO, AlCr4,AlZr4中间合金并搅拌;待熔体温度至720°C,加入Mg和Zn,打渣、精炼;待 温度在720V,加入Α1-5ΊΊ-Β中间合金,搅拌并静置20分钟,在温度为720V的铸铁模中浇
注成型。
[0053] 将上述浇注成型的铝合金铸锭均勻化处理,均勻化处理的温度为470°C,处理时间 为15小时,在温度为470°C条件下热轧,中间退火,中间退火的温度为400°C,中间退火的时 间为30min,中间退火后采用水淬快速冷却。冷轧2次轧成薄板。
[0054] 将上述制得的薄板进行退火处理,退火处理的温度为380°C,处理的时间为lh,退 火处理后出炉空冷制得汽车车身板用Al-Mg系铝合金成品。
[0055] 实施例4
[0056] 按照表1中实施例4质量百分比配料,制成铝锭,中间合金AlCu50、AlMnl0、AlCr4、 AlZr4、Al-5Ti-B。
[0057] 先将铝锭加入坩埚电阻炉中,待铝锭熔化且熔体温度为800°C时,加入A1CU50、 AlMnlO, AlCr4,AlZr4中间合金并搅拌;待熔体温度至730°C,加入Mg和Zn,打渣、精炼;待 温度在720V,加入Α1-5ΊΊ-Β中间合金,搅拌并静置20分钟,在温度为730°C的铸铁模中浇 注成型。
[0058] 将上述浇注成型的铝合金铸锭均勻化处理,均勻化处理的温度为480,处理时间为 10小时,在温度为480条件下热轧,中间退火,中间退火的温度为420°C,中间退火的时间为 20min,中间退火后采用水淬快速冷却。冷轧2次轧成薄板。
[0059] 将上述制得的薄板进行退火处理,退火处理的温度为420°C,处理的时间为0. 5h, 退火处理后出炉空冷制得汽车车身板用Al-Mg系铝合金成品。
[0060] 随机抽取上述实施例1-4制得铝合金成品在室温下停放3天后进行拉伸试验。模 拟170°C X30min烤漆处理是在电阻炉中进行。
[0061] 随机抽取实施例1-4制得含一定量的Ti和ττ的铝合金薄板固溶后室温放置3天 以及烤漆后的性能指标同未添加上述成分的5754铝合金薄板烤漆前后性能进行比较,详 细见表2。
[0062]表 2
[0063]
7
[0064] 由表2可见,本发明的汽车车身板用Al-Mg系铝合金在5754铝合金基础上通过对 成分的适当配比,添加少量的&、Ti、Zn和Cu后的合金薄板冲压前的屈服强度较低,有利于 冲压成形,而烤漆后强度没有降低,而且有所升高,该铝合金用作车身板具有良好的抗冲击 性能。
[0065] 本发明中所描述的具体实施例仅是对本发明精神作举例说明。本发明所属技术领 域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替 代,但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。
[0066] 尽管对本发明已作出了详细的说明并引证了一些具体实施例,但是对本领域熟练 技术人员来说,只要不离开本发明的精神和范围可作各种变化或修正是显然的。

Claims (7)

  1. 一种汽车车身板用Al-Mg系铝合金,该铝合金的成分及其质量百分比为:Cu:0.001-0.25wt%;Mn:0.05-0.35wt%;Mg:2.5-3.5wt%;Cr:0.005%-0.25wt%;Zn:0.008-0.8wt%;Ti:0.01-0.15wt%;Zr:0.001-0.2wt%;Si≤0.2wt%;Fe≤0.3wt%;余量为Al。
  2. 2.根据权利要求1所述的汽车车身板用Al-Mg系铝合金,该铝合金的成分及其质量百 分比为:Cu :0. 1-0. 2wt% ;Mn :0. 1-0. 2wt% ;Mg :2. 8-3. 4wt% ;Cr :0. 01% -0. 2wt% ;Zn :0. 2-0. 5wt% ;Ti :0. 05-0. Iwt% ;Zr :0. 005-0. 15wt% ;Si 彡 0. Iwt % ;Fe 彡 0. 2wt% ;余量为Al。
  3. 3. —种如权利要求1所述的汽车车身板用Al-Mg系铝合金的制造方法,该方法包括以 下步骤:A、浇注成型:先将铝锭加入坩埚电阻炉中,待铝锭熔化且熔体温度为750-800°C时,加 入AlCu50、A IMnlO, AlCr4、AlZr4中间合金并搅拌;待熔体温度至600_750°C,加入Mg和 Zn,打渣、精炼;待温度在700-730°C,加入Al_5Ti_B中间合金,搅拌并静置10-30分钟,在 铸铁模中浇注成型;B、均勻化处理:将上述浇注成型的铝合金铸锭均勻化处理,轧制成薄板;C、退火:将上述制得的薄板进行退火处理,退火处理的温度为320-420°C,处理的时间 为0. 5-3h,退火处理后制得成品。
  4. 4.根据权利要求3所述的汽车车身板用Al-Mg系铝合金的制造方法,其特征在于:步 骤A中在铸铁模中浇注成型的温度为700-730°C。
  5. 5.根据权利要求3或4所述的汽车车身板用Al-Mg系铝合金的制造方法,其特征在于: 步骤A中加入Mg和Zn时熔体温度为710-740°C。
  6. 6.根据权利要求3所述的汽车车身板用Al-Mg系铝合金的制造方法,其特征在于:步 骤B中均勻化处理的温度为450-480°C,处理时间为10-24小时。
  7. 7.根据权利要求3所述的汽车车身板用Al-Mg系铝合金的制造方法,其特征在于:步 骤C中退火处理的温度为350-400°C,处理的时间为l_2h,退火处理后空冷。
CN201010241214A 2010-07-30 2010-07-30 汽车车身板用Al-Mg系铝合金及其制造方法 Active CN101880803B (zh)