CN106336548A - Additive capable of keeping rubber to have lasting elasticity on acidic condition - Google Patents
Additive capable of keeping rubber to have lasting elasticity on acidic condition Download PDFInfo
- Publication number
- CN106336548A CN106336548A CN201610729972.3A CN201610729972A CN106336548A CN 106336548 A CN106336548 A CN 106336548A CN 201610729972 A CN201610729972 A CN 201610729972A CN 106336548 A CN106336548 A CN 106336548A
- Authority
- CN
- China
- Prior art keywords
- rubber
- additive
- parts
- elasticity
- acid condition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an additive capable of keeping rubber to have the lasting elasticity on the acidic condition, and relates to the field of rubber additives. The additive is prepared from, by weight, 0.1 part of europium oxide, 2.3 parts of sodium laurylsulfate, 4.6 parts of argil and 1.5 parts of polyacrylate. When the additive is in use, paroline is adopted as a carrier, the good dispersibility is achieved, the paroline is added into the rubber raw material on the basis of the certain proportion, plastication, mixing and sulfuration molding are performed, and the obtained rubber product can have the lasting elasticity on the acidic condition.
Description
Technical field
The present invention relates to rubber additive field, more particularly, to one kind can keep rubber to have lasting bullet in acid condition
The additive of property.
Background technology
Material is material base and the guide of social production and technological progress, the macromolecular material that eighties of last century grows up
Industry bring huge material progress to human society, rubber as the important component part of macromolecular material, in tire system
Make aspect and there is the irreplaceable specific function of other materials, become indispensable important thing in national economy and daily life
Matter.With the development of modern science and technology, to the elasticity of rubber for tire, abrasion resistance, acid resistance, alkali resistance, the aspect such as anti-aging
Require more and more higher, and traditional rubber additive is limited to its mechanical property raising, present technology can not meet this
Plant and require, be badly in need of the new rubber additive of exploitation, improve the serviceability of rubber.
Content of the invention
It is an object of the invention to provide a kind of additive keeping rubber to have persistently elasticity in acid condition, with
Solve above-mentioned technical problem.
The technical problem to be solved employs the following technical solutions to realize:
A kind of keep rubber have in acid condition persistently elasticity additive it is characterised in that: by following weight
The raw material mixture of part forms:
0.1 part of europium oxide, 2.3 parts of sldium lauryl sulfate, 4.6 parts of potter's clay, 1.5 parts of polyacrylate.
Preferably, also containing 0.23 part of nano aluminium oxide in raw material.
Preferably, the granularity of described potter's clay is 2-15 micron.
Can keep rubber have in acid condition persistently elasticity Rubber modification method it is characterised in that:
Additive is added in paraffin oil, makes additive dispersed in paraffin oil, obtain property-modifying additive, additive
Quality be paraffin oil quality 82.5%;
Property-modifying additive is added in rubber raw materials, the addition of additive is the 1.25% of rubber quality, is moulded
Refining, mixing, sulfidization molding, obtain final product the rubber product can in acid condition with persistently elasticity.
The invention has the beneficial effects as follows:
The additive of the present invention, with paraffin oil as carrier during use, has preferable dispersiveness, adds according to certain ratio
Enter in rubber raw materials, through over-mastication, mixing, sulfidization molding, the rubber product obtaining, can have lasting bullet in acid condition
Property,
Europium oxide, sldium lauryl sulfate, potter's clay, polyacrylate,
Potter's clay is acted synergistically with polyacrylate, makes rubber be very easy to polymerization, and it contributes to playing in acid condition
Sldium lauryl sulfate and the performance of europium oxide, can improve mechanical property, ageing resistace and the acid resistance of rubber, so that rubber
There is lasting elasticity in acid condition.
Specific embodiment
In order that technological means, creation characteristic, reached purpose and effect that the present invention realizes are easy to understand, tie below
Close specific embodiment, the present invention is expanded on further, but following embodiment is only the preferred embodiments of the present invention, and not all.
Based on the embodiment in embodiment, those skilled in the art are obtained other real on the premise of not making creative work
Apply example, broadly fall into protection scope of the present invention.
A kind of additive keeping rubber to have persistently elasticity in acid condition, by the raw material mixture of following weight portion
Form:
0.1 part of europium oxide, 2.3 parts of sldium lauryl sulfate, 4.6 parts of potter's clay (granularity 2-15 micron), polyacrylate 1.5
Part, 0.23 part of nano aluminium oxide,
Rubber can be kept to have the Rubber modification method of persistently elasticity in acid condition,
(1) additive is added in paraffin oil, make additive dispersed in paraffin oil, obtain property-modifying additive, add
Plus the quality of agent is the 82.5% of paraffin oil quality;
(2) property-modifying additive is added in rubber raw materials, the addition of additive is the 1.25% of rubber quality, carries out
Plasticate, knead, sulfidization molding, obtain final product can have in acid condition persistently elasticity rubber product.
According to national standard, performance test is carried out to the rubber product prepared, result is as shown in the table:
General principle, principal character and the advantages of the present invention of the present invention have been shown and described above.The technology of the industry
The only present invention it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and specification for the personnel
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also has various
Changes and improvements, these changes and improvements both fall within scope of the claimed invention.Claimed scope is by institute
Attached claims and its equivalent thereof.
Claims (3)
1. a kind of keep rubber have in acid condition persistently elasticity additive it is characterised in that: by following weight portion
Raw material mixture form:
0.1 part of europium oxide, 2.3 parts of sldium lauryl sulfate, 4.6 parts of potter's clay, 1.5 parts of polyacrylate.
2. the additive keeping rubber to have persistently elasticity in acid condition according to claim 1, its feature exists
In: also contain 0.23 part of nano aluminium oxide in raw material.
3. the additive keeping rubber to have persistently elasticity in acid condition according to claim 1, its feature exists
In: the granularity of described potter's clay is 2-15 micron.