CN107083014A - A kind of heat resistant and wear resistant polymer composite - Google Patents
A kind of heat resistant and wear resistant polymer composite Download PDFInfo
- Publication number
- CN107083014A CN107083014A CN201710359518.8A CN201710359518A CN107083014A CN 107083014 A CN107083014 A CN 107083014A CN 201710359518 A CN201710359518 A CN 201710359518A CN 107083014 A CN107083014 A CN 107083014A
- Authority
- CN
- China
- Prior art keywords
- parts
- polymer composite
- heat resistant
- wear resistant
- resistant polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the raw material composition of a kind of heat resistant and wear resistant polymer composite, including following parts by weight:80 100 parts of phenolic resin;10 20 parts of glass fibre;5 15 parts of haydite;58 parts of graphite powder;6 10 parts of silica flour;0.15 0.25 parts of accelerator;8 12 parts of coupling agent;10 15 parts of Nano filling.Added with the combination such as glass fibre, haydite and silica flour in material component proposed by the present invention, the resistance to elevated temperatures and anti-wear performance of material are significantly improved, in the use environment available for very fast friction and circulation friction, service life is improved, cost input is low, is easy to improve the economic benefit of enterprise.
Description
Technical field
The present invention relates to technical field of polymer composite materials, more particularly to a kind of heat resistant and wear resistant macromolecule composite wood
Material.
Background technology
Composite be by two or more organic material of different nature, by method physically or chemically,
Macroscopically composition has the material of new capability.Various materials make up for each other's deficiencies and learn from each other in performance, produce cooperative effect, make composite wood
The combination property of material is better than former composition material and meets a variety of requirements.Wherein high polymer material is because generally having many gold
Belong to the advantage that can not replace with inorganic material and obtain rapid development, the development of modern project technology, to high polymer material
Propose higher requirement, but existing high polymer material is existed and worn no resistance, the shortcomings of resistance to elevated temperatures is poor, especially in material
Use environment is expected for circulation friction or during very fast friction, and the friction high temperature of generation causes high polymer material denaturation, aging, firmly crisp,
Gradually lose the premium properties that high polymer material possesses in itself.
Therefore, in order to solve above-mentioned technical problem, the invention provides a kind of new technology.
The content of the invention
It is an object of the invention to provide a kind of heat resistant and wear resistant polymer composite.
It is of the invention to be for the technical scheme that above-mentioned technological deficiency is used:
A kind of heat resistant and wear resistant polymer composite, includes the raw material composition of following parts by weight:
Further, a diameter of 5-10mm of the haydite.
Further, the accelerator is methylimidazole.
Further, the coupling agent is titanate coupling agent.
Further, the Nano filling is aluminium hydroxide, titanium dioxide, the mixture of calcium carbonate.
Further, using phenolic resin as main body formulated phenolic resin glue, remaining component is placed in glue and stirred
30-55min is impregnated, batch mixing is placed in into progress granulation in comminutor thereafter produces.
The beneficial effects of the invention are as follows:Glass fibre, haydite and silica flour are added with material component proposed by the present invention
Deng combination, hence it is evident that improve the resistance to elevated temperatures and anti-wear performance of material, the use environment available for very fast friction and circulation friction
In, service life is improved, and cost input is low, is easy to improve the economic benefit of enterprise.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
80 parts of phenolic resin;
10 parts of glass fibre;
5 parts of haydite
Wherein, a diameter of 5mm of haydite;
Preparation method:Using phenolic resin as main body formulated phenolic resin glue, remaining component of said ratio is placed in
Stirring dipping 30min in glue, is placed in progress granulation in comminutor by batch mixing thereafter and produces.
Embodiment 2
90 parts of phenolic resin;
15 parts of glass fibre;
10 parts of haydite
Wherein, a diameter of 5mm of haydite;
Preparation method:Using phenolic resin as main body formulated phenolic resin glue, remaining component of said ratio is placed in
Stirring dipping 45min in glue, is placed in progress granulation in comminutor by batch mixing thereafter and produces.
Embodiment 3
100 parts of phenolic resin;
20 parts of glass fibre;
15 parts of haydite
Wherein, a diameter of 10mm of haydite;
Preparation method:Using phenolic resin as main body formulated phenolic resin glue, remaining component of said ratio is placed in
Stirring dipping 55min in glue, is placed in progress granulation in comminutor by batch mixing thereafter and produces.
The beneficial effects of the invention are as follows:Glass fibre, haydite and silica flour are added with material component proposed by the present invention
Deng combination, hence it is evident that improve the resistance to elevated temperatures and anti-wear performance of material, the use environment available for very fast friction and circulation friction
In, service life is improved, and cost input is low, is easy to improve the economic benefit of enterprise.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should be included in the scope of the protection.
Claims (6)
1. a kind of heat resistant and wear resistant polymer composite, it is characterised in that:Raw material composition including following parts by weight:
2. a kind of heat resistant and wear resistant polymer composite according to claim 1, it is characterised in that:The haydite it is straight
Footpath is 5-10mm.
3. a kind of heat resistant and wear resistant polymer composite according to claim 1, it is characterised in that:The accelerator is
Methylimidazole.
4. a kind of heat resistant and wear resistant polymer composite according to claim 1, it is characterised in that:The coupling agent is
Titanate coupling agent.
5. a kind of heat resistant and wear resistant polymer composite according to claim 1, it is characterised in that:The Nano filling
For aluminium hydroxide, titanium dioxide, calcium carbonate mixture.
6. a kind of preparation method of heat resistant and wear resistant polymer composite according to claim 1, it is characterised in that:With
Remaining component is placed in stirring dipping 30-55min in glue, thereafter will by phenolic resin as main body formulated phenolic resin glue
Batch mixing is placed in progress granulation in comminutor and produced.