CN106318121A - Wrinkle paint for mechanical casing - Google Patents
Wrinkle paint for mechanical casing Download PDFInfo
- Publication number
- CN106318121A CN106318121A CN201610778836.3A CN201610778836A CN106318121A CN 106318121 A CN106318121 A CN 106318121A CN 201610778836 A CN201610778836 A CN 201610778836A CN 106318121 A CN106318121 A CN 106318121A
- Authority
- CN
- China
- Prior art keywords
- polyester
- pigment
- mechanical cover
- wrinkle coating
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses wrinkle paint for a mechanical casing. The wrinkle paint is prepared from raw materials by weight as follows: 20-30 kg of epoxy resin, 16-20 kg of polyester A, 14-18 kg of polyester B, 0.2-0.5 kg of wax powder, 25-30 kg of barium sulfate, 20-30 kg of titanium dioxide, 0.001-0.005 kg of carbon black, 0.0011-0.0015 kg of a texturizing agent and 0.002-0.008 kg of pigments. Through reasonable compounding of components as well as selection and dosage control of the pigments, the wrinkle paint has better luster and permeability and excellent performance, can be widely used in the field of appearance decoration, is low in industrial production and facilitates improvement of economic benefits.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of mechanical cover wrinkle coating.
Background technology
Along with people to life pursuit, the decoration of product appearance increasingly become attract consumer important means it
One, the vast fields, especially alloy material such as household electrical appliance, mechanical cover, office appliance, electronic device, auto industry, people
The aesthetics of product appearance, color and luster, hardness, scratch resistance are had higher requirement.China's electrical equipment outward appearance mostly is at present
Alloy material, thus face appearance looks elegant degree not, ornament materials high in cost of production problem.
Summary of the invention
It is an object of the invention to provide a kind of mechanical cover wrinkle coating, decorated for product appearance, industry is melted into
This is low.
The present invention is directed to the technical scheme that above-mentioned technological deficiency proposed is:
A kind of mechanical cover wrinkle coating, the raw material including following weight forms:
Epoxy resin 20-30kg；
Polyester A 16-20kg；
Polyester B 14-18kg；
Wax powder 0.2-0.5kg；
Barium sulfate 25-30kg；
Titanium dioxide 20-30kg；
White carbon black 0.001-0.005kg；
Sand streak agent 0.0011-0.0015kg；
Pigment 0.002-0.008kg.
Further, the raw material including following weight forms:
Epoxy resin 26.1kg；
Polyester A 18.5kg；
Polyester B 16kg；
Wax powder 0.4kg；
Barium sulfate 28.1kg；
Titanium dioxide 27.3kg；
White carbon black 0.0036kg；
Sand streak agent 0.0013kg；
Pigment 0.0054kg.
Further, described polyester A and polyester B is two different kinds of polyester.
Further, described pigment is the mixture of iron oxide yellow and naphthol green.
Further, in described pigment, the part by weight of iron oxide yellow and naphthol green is 1:0.035-0.04.
The invention has the beneficial effects as follows: the present invention rationally compounding by component, and the selection of pigment and consumption control
Make the wrinkle coating prepared have preferable color and luster and permeability, excellent performance, can be widely used for decorative appearance field, industry
Change low cost, be beneficial to increase economic efficiency.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in further detail.
Embodiment 1
A kind of mechanical cover wrinkle coating, the raw material including following weight forms:
Epoxy resin 26.1kg；
Polyester A 18.5kg；
Polyester B 16kg；
Wax powder 0.4kg；
Barium sulfate 28.1kg；
Titanium dioxide 27.3kg；
White carbon black 0.0036kg；
Sand streak agent 0.0013kg；
Pigment 0.0054kg,
Wherein, pigment includes the material of following weight: iron oxide yellow 0.063kg, naphthol green 0.0024kg.
Embodiment 2
A kind of mechanical cover wrinkle coating, the raw material including following weight forms:
Epoxy resin 22.2kg；
Polyester A 16.4kg；
Polyester B 14kg；
Wax powder 0.2kg；
Barium sulfate 25.2kg；
Titanium dioxide 24.6kg；
White carbon black 0.0016kg；
Sand streak agent 0.0011kg；
Pigment 0.0032kg,
Wherein, pigment includes the material of following weight: iron oxide yellow 0.0031kg, naphthol green 0.0001kg.
Embodiment 3
A kind of mechanical cover wrinkle coating, the raw material including following weight forms:
Epoxy resin 28.6kg；
Polyester A 19.8kg；
Polyester B 18kg；
Wax powder 0.5kg；
Barium sulfate 30kg；
Titanium dioxide 28.8kg；
White carbon black 0.0046kg；
Sand streak agent 0.0015kg；
Pigment 0.0068kg,
Wherein, pigment includes the material of following weight: iron oxide yellow 0.0065kg, naphthol green 0.0003kg.
The invention has the beneficial effects as follows: the present invention rationally compounding by component, and the selection of pigment and consumption control
Make the wrinkle coating prepared have preferable color and luster and permeability, excellent performance, can be widely used for decorative appearance field, industry
Change low cost, be beneficial to increase economic efficiency.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, that is made any repaiies
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (5)
1. a mechanical cover wrinkle coating, it is characterised in that: include that the raw material of following weight forms:
Epoxy resin 20-30kg；
Polyester A 16-20kg；
Polyester B 14-18kg；
Wax powder 0.2-0.5kg；
Barium sulfate 25-30kg；
Titanium dioxide 20-30kg；
White carbon black 0.001-0.005kg；
Sand streak agent 0.0011-0.0015kg；
Pigment 0.002-0.008kg.
A kind of mechanical cover wrinkle coating the most according to claim 1, it is characterised in that: include the raw material of following weight
Composition:
Epoxy resin 26.1kg；
Polyester A 18.5kg；
Polyester B 16kg；
Wax powder 0.4kg；
Barium sulfate 28.1kg；
Titanium dioxide 27.3kg；
White carbon black 0.0036kg；
Sand streak agent 0.0013kg；
Pigment 0.0054kg.
A kind of mechanical cover wrinkle coating the most according to claim 1, it is characterised in that: described polyester A and polyester B is
Two different kinds of polyester.
A kind of mechanical cover wrinkle coating the most according to claim 1, it is characterised in that: described pigment is iron oxide yellow and face
Expect green mixture.
A kind of mechanical cover wrinkle coating the most according to claim 4, it is characterised in that: iron oxide yellow and face in described pigment
Expect that green part by weight is 1:0.035-0.04.