CN106317849A - Adiabatic bodywork protective film - Google Patents
Adiabatic bodywork protective film Download PDFInfo
- Publication number
- CN106317849A CN106317849A CN201610719408.3A CN201610719408A CN106317849A CN 106317849 A CN106317849 A CN 106317849A CN 201610719408 A CN201610719408 A CN 201610719408A CN 106317849 A CN106317849 A CN 106317849A
- Authority
- CN
- China
- Prior art keywords
- vehicle body
- protecting film
- body protecting
- protective film
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an adiabatic bodywork protective film, wherein the nanometer metal powder is evenly mixed with polyurethane adhesive, pressure-sensitive adhesive or acrylate adhesive through dispersing agent, and nanometer metal powder thereof holds a total mass ratio of 0.1%- 50%, and then stretch the mixture into film and put on the PVC surface to form bodywork protective film. The resin has the following technical effects: there is a significant leat insulation function when using the protective film of the vehicle body surface, therefore, in the hot summer, too high temperature inside the vehicle will not be caused under outdoor exposure.
Description
Technical field
The present invention relates to a kind of vehicle body protecting film, particularly relate to a kind of vehicle body protecting film with heat insulating function.
Background technology
Along with China's expanding economy, automobile has become ordinary walking-replacing tool, and its automobile when not in use, is generally positioned at
Outdoor, owing to outdoor temperature in summer is high, in vapour, temperature is high, must turn on the aircondition in advance into the car, wastes the energy;In order to avoid
Automobile is quick-fried, and some car owners can put on anti-fluffy to automobile, but drapes over one's shoulders anti-fluffy not only bother, and is placed on boot and takies sky
Between, in-convenience in use.
Summary of the invention
It is an object of the invention to provide a kind of vehicle body protecting film with heat insulating function, solve current automobile at high temperature
Under quick-fried, problem that vehicle interior temperature is high.
The present invention is achieved in that and it is characterized in that: Nano metal powder by dispersant and polyurethane adhesive, pressure sensitive adhesive or
SGA mix homogeneously, it is 0.1%-50% that its Nano metal powder accounts for total mass ratio, then mixture is stretched film forming and is distributed in
PVC surface forms vehicle body protecting film.
Described Nano metal powder is silver, copper, titanium, gold, silver oxide, copper oxide or titanium oxide.
Described PVC is replaced by PVB, PET, EVA or TPU.
It is 1%-30% that described Nano metal powder accounts for total mass ratio.
It is 5%-10% that described Nano metal powder accounts for total mass ratio.
The solution have the advantages that: this protecting film is used on car body surface, there is significant heat insulating function, from
And in hot summer, automobile is quick-fried in outdoor, and also not result in vehicle interior temperature the highest.
Detailed description of the invention
Embodiment 1
The present invention is achieved in that nanometer silver powder passes through dispersant and mixs homogeneously with polyurethane adhesive, and its nanometer silver powder accounts for total matter
Amount ratio is 0.1%, then mixture stretches film forming and is distributed in PVC surface formation vehicle body protecting film.
Embodiment 2
The present invention is achieved in that copper nanoparticle passes through dispersant and mixs homogeneously with pressure sensitive adhesive, and its copper nanoparticle accounts for gross mass
Ratio is 50%, then mixture stretches film forming and is distributed in PVB surface formation vehicle body protecting film.
Embodiment 3
The present invention is achieved in that nano titanium powder passes through dispersant and mixs homogeneously with SGA, and its nano titanium powder accounts for always
Mass ratio is 10%, then mixture stretches film forming and is distributed in pet sheet face formation vehicle body protecting film.
Embodiment 4
The present invention is achieved in that nano oxidized argentum powder is mixed homogeneously with polyurethane adhesive by dispersant, its nano phase ag_2 o
It is 30% that powder accounts for total mass ratio, then mixture stretches film forming and is distributed in EVA surface formation vehicle body protecting film.
Embodiment 5
The present invention is achieved in that nano oxidized titanium valve is mixed homogeneously with pressure sensitive adhesive by dispersant, its nano oxidized titanium valve
Accounting for total mass ratio is 40%, then mixture stretches film forming and is distributed in PVC surface formation vehicle body protecting film.
Embodiment 6
The present invention is achieved in that nano oxidized copper powder is mixed homogeneously with SGA by dispersant, and it is nano oxidized
It is 5% that copper powder accounts for total mass ratio, then mixture stretches film forming and is distributed in PVC surface formation vehicle body protecting film.
The car body that above-mentioned film is used for car body surface and unused protecting film is Experimental comparison, finds outdoor temperature 40 degree
Time, the vehicle interior temperature of unused protecting film is 64-70 degree, and uses the car inner question 35-45 degree of protecting film, and its effect is substantially better than
Do not use the car body of protecting film.
Claims (5)
1. a vehicle body protecting film with heat insulating function, it is characterised in that: Nano metal powder by dispersant and polyurethane adhesive,
Pressure sensitive adhesive or SGA mix homogeneously, it is 0.1%-50% that its Nano metal powder accounts for total mass ratio, is then stretched by mixture
Film forming is distributed in PVC surface and forms vehicle body protecting film.
A kind of vehicle body protecting film with heat insulating function the most according to claim 1, it is characterised in that: described nano metal
Powder is silver, copper, titanium, gold, silver oxide, copper oxide or titanium oxide.
A kind of vehicle body protecting film with heat insulating function the most according to claim 1, it is characterised in that: described PVC by
PVB, PET, EVA or TPU replace.
A kind of vehicle body protecting film with heat insulating function the most according to claim 1, it is characterised in that: described nano metal
It is 1%-30% that powder accounts for total mass ratio.
A kind of vehicle body protecting film with heat insulating function the most according to claim 1, it is characterised in that: described nano metal
It is 5%-10% that powder accounts for total mass ratio.