CN106315041A - Acid-alkali-corrosion-resistant and impact-resistant sine-wave foam-wall vitreous enamel petroleum tank with service life of thousand years - Google Patents
Acid-alkali-corrosion-resistant and impact-resistant sine-wave foam-wall vitreous enamel petroleum tank with service life of thousand years Download PDFInfo
- Publication number
- CN106315041A CN106315041A CN201510359078.7A CN201510359078A CN106315041A CN 106315041 A CN106315041 A CN 106315041A CN 201510359078 A CN201510359078 A CN 201510359078A CN 106315041 A CN106315041 A CN 106315041A
- Authority
- CN
- China
- Prior art keywords
- resistant
- vitreous enamel
- glaze slip
- oil tank
- alkali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Current petroleum tanks are made of steel; the technique is complicated; manufacture cost is high; corrosion resistance is performed, but acid-alkali-resistance is still poor; and the current petroleum tanks are scraped in only several years. The invention discloses an acid-alkali-corrosion-resistant and impact-resistant sine-wave foam-wall vitreous enamel petroleum tank with a service life of a thousand years. The acid-alkali-corrosion-resistant and impact-resistant sine-wave foam-wall vitreous enamel petroleum tank is manufactured by sintering argil bonding high-temperature-resistant ceramic mesh fabric; metal is replaced by the acid-alkali-corrosion-resistant and impact-resistant sine-wave foam-wall vitreous enamel petroleum tank; the acid-alkali-corrosion-resistant and impact-resistant sine-wave foam-wall vitreous enamel petroleum tank is acid-alkali-corrosion-resistant; the service life can reach a thousand years; the technique is simple; and cost is low. The high-temperature-resistant ceramic mesh fabric can resist a high temperature of 1250 DEG C, and argil formed by sintering glaze slurry can resist a high temperature of 1000 DEG C, so that the tensile property of the high-temperature-resistant ceramic mesh fabric cannot be damaged after vitreous enamel is formed through sintering. The petroleum tank is made of sine wave foam plates; when the foam plates are impacted, foam plate surfaces generate curve and absorb impact force, and remaining impact force is distributed to the sine wave plates, so that the impact force is totally absorbed by the multi-layer sine wave foam plates; and therefore the petroleum tank is impact-resistant. Cold working is adopted for manufacturing the vitreous enamel petroleum tank, and welding is not needed, so that labor intensity is lowered. The vitreous enamel ceramic mesh fabric is acid-alkali-corrosion-resistant, and the service life can reach a thousand years. The cost of the high-temperature-resistant ceramic mesh fabric is lower than that of steel.
Description
Current Oil Tank iron and steel is made, complex process, and cost is expensive, although carry out anticorrosion, but anti acid alkali performance energy or very poor, use
Within several years, just do not scrap.Market is without seeing the vitreous enamel Oil Tank of the complete antiacid caustic corrosion made with vitreous enamel bonding pottery screen cloth.
The string ripple foam wall vitreous enamel Oil Tank in antiacid thousand caustic corrosion impact resistant life-spans that this technology proposes, is called for short string ripple foam wall vitreous enamel oil
Tank, belongs to vitreous enamel container scope, can help the shortcoming overcoming above-mentioned existence.
String ripple foam wall vitreous enamel Oil Tank, it provides the benefit that, replaces iron and steel, antiacid caustic corrosion, thousand life-spans, and technique is simple, fall
Low cost.
The string ripple foam wall vitreous enamel Oil Tank in antiacid thousand caustic corrosion impact resistant life-spans, it solves the technical scheme that technical problem is used
It is to be made up of vitreous enamel bonding refractory ceramics screen cloth；Its technique is: making refractory ceramics screen cloth by glaze slip, glaze slip can add
Binding agent, makes glaze slip through pottery screen cloth hole, scrapes off unnecessary glaze slip, makes glaze slip parcel pottery screen cloth, becomes glaze slip ceramic network
Cloth；By each part requirement of Oil Tank, such as can body, cover etc., by polylith glaze slip ceramic network cloth overlap, stick into the straight or glaze slip of bending
Ceramic network fabric swatch (1)；By each part requirement of Oil Tank, by straight or curved glaze slip ceramic network fabric swatch, it is split into straight or curved glaze
Slip ceramic network cloth lath, is pressed into sinusoidal wave lath (2) by straight or curved glaze slip ceramic network cloth lath；Want by each parts of Oil Tank
Ask, on straight or bending glaze slip ceramic network fabric swatch, by lath with sinusoidal wave lath is alternate piles, then put on lath and sinusoidal wave lath
Ceramic network fabric swatch bonds, sinusoidal wave lath and ceramic network fabric swatch can alternate overlap, make the sinusoidal wave cystosepiment of each parts of Oil Tank, sinusoidal
Ripple cystosepiment glaze slip ceramic network cloth edge sealing, it is thus achieved that the sinusoidal wave cystosepiment (3) of each parts of Oil Tank；The stone of relevant hole position will be held successfully
Oil tank each parts sine wave cystosepiment is put into stove and is fired, and makes glaze slip become vitreous enamel, obtains vitreous enamel bonding refractory ceramics screen cloth after cooling
The sinusoidal wave each parts of foam wall Oil Tank；If can body volume is excessive, can body can be divided into a few part；By each for sine wave foam wall Oil Tank
Parts are mounted to sinusoidal wave foam wall vitreous enamel Oil Tank (4), so that the string ripple foam wall glaze porcelain stone in antiacid thousand caustic corrosion impact resistant life-spans
Oil tank is run.Such as Fig. 1
In conjunction with principles and methods vitreous enamel Oil Tank:
Take glaze slip to reduce the use temperature of refractory ceramics screen cloth and reduce cost；Sinusoidal wave cystosepiment can make technique simple and drop
Low cost.
Resistance to 1,000 degree of refractory ceramics screen cloth, glaze slip burns till vitreous enamel 800 degree, so will not destroy refractory ceramics net after burning till vitreous enamel
The performances such as the tension of cloth.
Binding agent can be gelatinized corn starch, adds binding agent, and glaze slip can be made without departing from pottery screen cloth.
When vitreous enamel Oil Tank is impacted, impulsive force can all be absorbed by sinusoidal wave cystosepiment, makes Oil Tank intact；The each parts of Oil Tank
Inside is sinusoidal wave plate, and ceramic network fabric swatch constitutes the most sinusoidal wave cystosepiment, and when cystosepiment is hit, cystosepiment face produces bending,
Impulsive force being absorbed, and remainder impulsive force is diverted to sinusoidal wave plate, if there being multilamellar sine wave plate, just impulsive force all being absorbed；Vitreous enamel
Because of thin and flexible, after impulsive force, foam face recovers straight, so sinusoidal wave cystosepiment has good impact resistance performance.
Current Oil Tank, is to be made by Plate Welding, and complex process, cost is expensive.
Vitreous enamel, the pottery antiacid caustic corrosion of screen cloth, thousand life-spans.
Vitreous enamel Oil Tank is cold working, need not weld, and reduces labor intensity.
Refractory ceramics screen cloth price is lower than iron and steel.
Figure of description
The string ripple foam wall vitreous enamel Oil Tank in Fig. 1: antiacid thousand caustic corrosion impact resistant life-spans
1 glaze slip ceramic network fabric swatch, 2 sinusoidal wave laths, 3 sinusoidal wave cystosepiments, 4 string ripple foam wall vitreous enamel Oil Tank.
Claims (1)
- The string ripple foam wall vitreous enamel Oil Tank in the most antiacid thousand caustic corrosion impact resistant life-spans, is characterized in that, vitreous enamel bond refractory ceramics Screen cloth forms；Its technique is: making refractory ceramics screen cloth by glaze slip, glaze slip can add binding agent, makes glaze slip through ceramic network Cloth hole, scrapes off unnecessary glaze slip, makes glaze slip bag assist pottery screen cloth, becomes glaze slip ceramic network cloth；By each part requirement of Oil Tank, as Can body, cover etc., polylith glaze slip ceramic network cloth is overlapping, stick into the straight or glaze slip ceramic network fabric swatch of bending；By each parts of Oil Tank Requirement, by straight or curved glaze slip ceramic network fabric swatch, is split into straight or curved glaze slip ceramic network cloth lath, by straight or curved Glaze slip ceramic network cloth lath be pressed into sinusoidal wave lath；By each part requirement of Oil Tank, on straight or bending glaze slip ceramic network fabric swatch, By lath with sinusoidal wave lath is alternate piles, then on lath and sinusoidal wave lath, put the bonding of ceramic network fabric swatch, sinusoidal wave lath and ceramic network Fabric swatch can alternate overlap, make the sinusoidal wave cystosepiment of each parts of Oil Tank, sinusoidal wave cystosepiment glaze slip ceramic network cloth edge sealing, obtain Obtain the sinusoidal wave cystosepiment of each parts of Oil Tank；Each for the Oil Tank holding relevant hole position successfully parts sine wave cystosepiment is put into stove fire, make glaze Slip becomes vitreous enamel, obtains the sinusoidal wave each parts of foam wall Oil Tank of vitreous enamel bonding refractory ceramics screen cloth after cooling；If can body volume Excessive, can body can be divided into a few part；The sine wave each parts of foam wall Oil Tank are mounted to sinusoidal wave foam wall vitreous enamel Oil Tank, thus The string ripple foam wall vitreous enamel Oil Tank making antiacid thousand caustic corrosion impact resistant life-spans is run.