CN106313729B - The work top of glass cutting machine - Google Patents

The work top of glass cutting machine Download PDF

Info

Publication number
CN106313729B
CN106313729B CN201610671509.8A CN201610671509A CN106313729B CN 106313729 B CN106313729 B CN 106313729B CN 201610671509 A CN201610671509 A CN 201610671509A CN 106313729 B CN106313729 B CN 106313729B
Authority
CN
China
Prior art keywords
flannelette
composite
cutting machine
substrate
work top
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610671509.8A
Other languages
Chinese (zh)
Other versions
CN106313729A (en
Inventor
朱晓玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI YINRUI GLASS MACHINERY Co Ltd
Original Assignee
ANHUI YINRUI GLASS MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI YINRUI GLASS MACHINERY Co Ltd filed Critical ANHUI YINRUI GLASS MACHINERY Co Ltd
Priority to CN201610671509.8A priority Critical patent/CN106313729B/en
Publication of CN106313729A publication Critical patent/CN106313729A/en
Application granted granted Critical
Publication of CN106313729B publication Critical patent/CN106313729B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention provides a kind of work top of glass cutting machine, is related to glass machinery field, is made up of substrate and the flannelette composite for being coated on substrate surface, the thickness of flannelette composite is 1.5 2mm, and substrate is bonded with flannelette composite by elastic gel.Flannelette composite provided by the invention has good elasticity, and compared to more traditional flannelette, flannelette composite material surface frictional force of the invention is small, and has more preferable ductility and wear resistance, and elastic resilience is strong；It is not only wear-resistant using the work top of glass cutting machine made of flannelette composite parcel, more preferable protective effect can be played to plate glass, and the levelness under can ensureing plate glass in the raw.

Description

The work top of glass cutting machine
Technical field
The present invention relates to glass machinery field, more particularly to a kind of work top of glass cutting machine.
Background technology
Glass cutting machine refers to a kind of processing equipment for being exclusively used in glass processing and blanking, and glass cutting machine includes head and the tail and arranged The air-flotation type sheet feeding table of row, double bridge grade separation type cutter's table.The table top of air-flotation type sheet feeding table and the table top of double bridge grade separation type cutter's table are common The work top of glass cutting machine is constituted, work top generally one layer of flannelette of cladding of glass cutting machine, flannelette is directly with treating The plate glass contact of cutting, plays buffering and the purpose of protection plate glass, but the flannelette used in the prior art will ensure It has preferable cushioning and protection, must just have certain thickness, and the fine hair on flannelette surface has certain length. But flannelette is thicker, the fine hair on flannelette surface is longer, larger to the frictional force of plate glass, can hinder the movement of plate glass, no It is easy to process operation.And plate glass in the vertical direction unbalance stress, easily causes plate glass to lose horizontality, shadow Ring cutting accuracy.
The content of the invention
Suede it is an object of the invention to provide a kind of work top of glass cutting machine and for coating the workbench Cloth composite, to solve above-mentioned technical problem.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of work top of glass cutting machine, it is characterised in that：It is compound by substrate and the flannelette for being coated on substrate surface Material is formed, and the thickness of flannelette composite is 1.5-2mm, and substrate is bonded with flannelette composite by elastic gel,
Flannelette composite is made up of flannelette, graphite powder, paraffin, silicone oil, the material based on flannelette, in flannelette The mixture that surface spraying is made up of graphite powder, paraffin and silicone oil, every square metre of flannelette surface spraying mixture 25g, wherein Comprising ink powder 4.5g, paraffin 8.5g, silicone oil 12g, mixture is to be sprayed on using the nitrogen of HTHP as carrier on flannelette, nitrogen Temperature be 85-90 DEG C, nitrogen spray flow velocity be 3m/s；
Elastic gel is made up of the raw material of following quality proportioning：
Dimethyl sulfoxide (DMSO)：Sodium carboxymethylcellulose：Toluene：Water：Glycerine：Titanium dioxide=3,0.15,0.5,8,0.6, 0.5；
Dimethyl sulfoxide (DMSO), sodium carboxymethylcellulose, toluene, water are proportionally added into reactor and are stirred, Ran Houjin Row heating, heating-up temperature are 85 DEG C, are kept for 2 hours, are then cooled to 45 DEG C, kept for 0.5 hour, be cooled to normal temperature, discharge Material A；
Glycerine, titanium dioxide are proportionally added into reactor, discharged after being uniformly mixed, obtains material B；
Material A and material B are added in reactor, are warming up to 62 DEG C, 25mi n is stirred, is cooled to 45 DEG C, you can is used.
Opened preferably, the flannelette is longitudinally open and flat, mixture even application is carried by carrier of the nitrogen of HTHP On flannelette, flannelette is vacantly set, and nitrogen stream passes through flannelette, and the mixture that nitrogen stream carries is adhered to flannelette surface and flannelette is empty In gap, it then will solidify in flannelette feeding refrigerating chamber and produce, the temperature of refrigerating chamber is maintained at 2-5 DEG C, and hardening time is 3 hours.
Preferably, after the elastic gel uniformly coats, substrate and flannelette composite are bonded, are then fed into temperature In the environment of -2 DEG C of degree, refrigerate 1.5 hours.By chilling treatment, elastic gel can be firm by substrate and flannelette composite Bonding, and make elastic gel that there is good elasticity.
Elastic gel has preferable elastic resilience, and high-low temperature resistant is anti-aging, and adhesion is strong, can be compound by flannelette Material is firmly adhered on the substrate of glass cutting machine work top.
The beneficial effects of the invention are as follows：
Flannelette composite provided by the invention has good elasticity, and compared to more traditional flannelette, flannelette of the invention is answered Condensation material skin-friction force is small, and has more preferable ductility and wear resistance, and elastic resilience is strong；Answered using the flannelette The work top of glass cutting machine, not only wear-resistant made of condensation material parcel, and more preferable protection can be played to plate glass Effect, and the levelness under can ensureing plate glass in the raw.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below Specific embodiment is closed, the present invention is expanded on further, but following embodiments are only the preferred embodiments of the present invention, and it is not all. Based on the embodiment in embodiment, those skilled in the art obtain other realities on the premise of creative work is not made Example is applied, belongs to protection scope of the present invention.
Elastic gel is prepared, is made up of the raw material of following quality proportioning：
Dimethyl sulfoxide (DMSO)：Sodium carboxymethylcellulose：Toluene：Water：Glycerine：Titanium dioxide=3,0.15,0.5,8,0.6, 0.5；
Step is：
(1) dimethyl sulfoxide (DMSO), sodium carboxymethylcellulose, toluene, water are proportionally added into reactor and are stirred, then Heated, heating-up temperature is 85 DEG C, is kept for 2 hours, is then cooled to 45 DEG C, is kept for 0.5 hour, is cooled to normal temperature, is discharged Obtain material A；
(2) glycerine, titanium dioxide are proportionally added into reactor, discharged after being uniformly mixed, obtain material B；
(3) material A and material B are added in reactor, is warming up to 62 DEG C, stirred 25mi n, be cooled to 45 DEG C, you can make With.
Prepare flannelette composite, the material based on flannelette, flannelette surface spraying by graphite powder, paraffin and silicon The mixture of oil composition, every square metre of flannelette surface spraying mixture 25g, wherein including ink powder 4.5g, paraffin 8.5g, silicone oil 12g, mixture are to be sprayed on using the nitrogen of HTHP as carrier on flannelette, and the temperature of nitrogen is 85-90 DEG C, what nitrogen sprayed Flow velocity is 3m/s；Flannelette is longitudinally open and flat to be opened, and carries mixture even application on flannelette by carrier of the nitrogen of HTHP, suede Cloth is vacantly set, and nitrogen stream passes through flannelette, and the mixture that nitrogen stream carries is adhered in flannelette surface and flannelette space, then will Flannelette is sent into refrigerating chamber to solidify and produced, and the temperature of refrigerating chamber is maintained at 2-5 DEG C, and hardening time is 3 hours.
The work top of glass cutting machine, it is made up of substrate and the flannelette composite for being coated on substrate surface, flannelette is multiple The thickness of condensation material is 1.5-2mm, and substrate is bonded with flannelette composite by elastic gel, and elastic gel is coated uniformly on base After plate surface, flannelette composite is bonded on substrate, substrate is then sent into temperature -2 together with flannelette composite DEG C environment in, refrigerate 1.5 hours.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is only the present invention Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also have it is various Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute Attached claims and its equivalent thereof.

Claims (3)

  1. A kind of 1. work top of glass cutting machine, it is characterised in that：By substrate and the flannelette composite wood for being coated on substrate surface Material is formed, and the thickness of flannelette composite is 1.5-2mm, and substrate is bonded with flannelette composite by elastic gel,
    Flannelette composite is made up of flannelette, graphite powder, paraffin, silicone oil, the material based on flannelette, on the surface of flannelette Spray the mixture being made up of graphite powder, paraffin and silicone oil, every square metre of flannelette surface spraying mixture 25g, wherein including Ink powder 4.5g, paraffin 8.5g, silicone oil 12g, mixture are to be sprayed on using the nitrogen of HTHP as carrier on flannelette, the temperature of nitrogen Spend for 85-90 DEG C, the flow velocity that nitrogen sprays is 3m/s；
    Elastic gel is made up of the raw material of following quality proportioning：
    Dimethyl sulfoxide (DMSO)：Sodium carboxymethylcellulose：Toluene：Water：Glycerine：Titanium dioxide=3,0.15,0.5,8,0.6,0.5；
    Dimethyl sulfoxide (DMSO), sodium carboxymethylcellulose, toluene, water are proportionally added into reactor and are stirred, and are then added Heat, heating-up temperature are 85 DEG C, are kept for 2 hours, are then cooled to 45 DEG C, kept for 0.5 hour, be cooled to normal temperature, discharge to obtain material A；
    Glycerine, titanium dioxide are proportionally added into reactor, discharged after being uniformly mixed, obtains material B；
    Material A and material B are added in reactor, are warming up to 62 DEG C, 25min is stirred, is cooled to 45 DEG C, you can is used.
  2. 2. the work top of glass cutting machine according to claim 1, it is characterised in that：The flannelette is longitudinally open and flat to be opened, Mixture even application is carried on flannelette by carrier of the nitrogen of HTHP, flannelette is vacantly set, and nitrogen stream passes through flannelette, The mixture that nitrogen stream carries is adhered in flannelette surface and flannelette space, then will be solidified in flannelette feeding refrigerating chamber and is produced, The temperature of refrigerating chamber is maintained at 2-5 DEG C, and hardening time is 3 hours.
  3. 3. the work top of glass cutting machine according to claim 1, it is characterised in that：The elastic gel uniformly coats Afterwards, substrate and flannelette composite are bonded, are then fed into the environment of -2 DEG C of temperature, refrigerated 1.5 hours.
CN201610671509.8A 2016-08-15 2016-08-15 The work top of glass cutting machine Active CN106313729B (en)