CN106283339B - 一种具有抗菌保健功能的衬衫用混纺面料及其制备方法 - Google Patents
一种具有抗菌保健功能的衬衫用混纺面料及其制备方法 Download PDFInfo
- Publication number
- CN106283339B CN106283339B CN201610670849.9A CN201610670849A CN106283339B CN 106283339 B CN106283339 B CN 106283339B CN 201610670849 A CN201610670849 A CN 201610670849A CN 106283339 B CN106283339 B CN 106283339B
- Authority
- CN
- China
- Prior art keywords
- fiber
- fleece
- pearl
- fabric
- flower root
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种具有抗菌保健功能的衬衫用混纺面料及其制备方法，不但具有抗菌保健功效，而且采用植物染色剂，健康、环保；使用的何首乌藤纤维是将废弃物的何首乌藤再利用，符合国家循环经济的要求；将何首乌藤纤维作为外包层，珍珠纤维作为芯丝，纺织成包芯纱，不但克服了何首乌藤纤维离散性较大，单纤维成纱较困难的缺点，而且延长了珍珠纤维发射远红外线的时间和效果，还提升了面料的抗菌性能；将何首乌藤纤维作为外包层，涤纶纤维作为芯丝，纺织成包芯纱，不但可以保留涤纶纤维的硬挺度，而且可以显著改性纤维的着色性能，综上所述，本发明的面料的制备方法是一种新型天然纤维的优化利用工艺。
Description
技术领域
本发明涉及纺织面料领域，特别地，涉及一种具有抗菌保健功能的衬衫用混纺面料及其制备方法。
背景技术
珍珠纤维是采用高科技手段将纳米级珍珠粉在粘胶纤维纺丝时加入纤维内，使纤维体内和外表均匀分布着纳米珍珠微粒。具体为珍珠蛋白功能母粒和纤维级树脂切片构成，使纤维体内和外表均匀分布着纳米珍珠微粒，一根根纤维犹如一串串珍珠项链，异常光亮滑爽。是由东华大学和上海新型纺纱中心合作共同研发的一种新型纤维，属国内外首创的高档功能性纤维。
珍珠纤维既有珍珠养颜护肤功效，又有粘胶纤维吸湿透气、穿着舒适的特性。珍珠纤维表面均匀分布着珍珠微粒，长期于皮肤接触，具有珍珠养颜护肤、清火败毒、嫩白肌肤、抗紫外线的功效。珍珠纤维含有多种氨基酸和微量元素，纤维表面光滑凉爽，有珍珠般光泽。
珍珠粉被人体吸收后，通过参与肌体代谢，达到全身肌肤的整体调理和保养。它能促进新生细胞合成，并不断补充到皮肤表层，使皮肤光滑、细腻、有弹性。科学地服用珍珠粉有明显地减轻血清过氧化脂的作用，而此脂质与蛋白质结合成能生成脂褐素（老人斑），这正是慈禧太后用珍珠善养颜容的秘密所在。
用珍珠粉涂面后，可以促进人体肌肤超氧化物歧化酶（SOD）的活性，抑制黑色素的合成，保持皮肤白皙。此外，由于SOD具有清除自由基的作用，可防止皮肤衰老、起皱。
⑴养颜护肤、嫩白皮肤
人体穿着珍珠纤维衬衫，纤维上的珍珠纳米微粒与肌肤亲密接触，汗液中的乳酸会溶出纤维中部分珍珠营养成分，通过皮肤被吸收，促进人体肌肤超氧化物歧化酶（SOD）的活性，抑制黑色素的合成保持皮肤白皙。此外，由于SOD具有清除自由基的作用，可防止皮肤衰老起皱。中医认为：珍珠性寒味甘咸，归心肝经，功能容颜美肤，润肤生肌，清斑减皱，延缓衰老；主要用于面部雀斑、黄褐斑、寿斑、皱纹、肌肉松弛、皮肤粗糙乏泽、面色苍老以及痤疮、烧烫伤、疮疡、伤口不收、皮炎等。珍珠生长在水中，性寒，具有清火败毒功效，长期穿着珍珠纤维衬衫可清除皮肤表面热痘毒，具有祛斑、除痘、养护肌肤的功效。
⑵抗紫外线
珍珠的主要成分为碳酸钙，其本身具有防紫外线功能，当其粉碎成纳米状态加入纤维时，其功能大大加强。珍珠纤维具有防紫外线防皮肤老化作用。据最新研究表明：纳米珍珠粉还具有发射红外波的功能，它可改善人体微循环，对人体有保健作用。
⑶吸湿透气、服用舒适
纳米珍珠纤维的载体是粘胶纤维，它吸湿透气服用舒适，加入耐珍珠粉后纤维内部及表面均匀分布着珍珠纳米微粒，纤维手感光滑凉爽，外观亮丽。
⑷全天然
纳米珍珠粉是由优质淡水珍珠经纯物理方法加工而成，粘胶纤维素由棉短绒提取，因此珍珠纤维不含任何化学性产品之有害物质，与肌肤有天然的亲和性。
⑸经久耐用
珍珠纤维中珍珠纳米微粒与纤维亲密结合，具有永久性，长期洗涤穿着不会脱落。珍珠耐碱不耐酸，碱性洗涤不伤毫发，只有在酸性汗液作用下珍珠纳米微粒才会产生部分析出，珍珠衬衫实乃转着与洗涤之完美结合。
现有的珍珠纤维具有非常好的保健功效，但是现在的消费者，对面料的要求越来越高，具备抗菌性能的衬衫产品，具有更好的市场前景，故有必要研发一种具有抗菌保健功能的衬衫用混纺面料。
发明内容
本发明目的在于提供一种具有抗菌保健功能的衬衫用混纺面料及其制备方法，以解决技术问题。
为实现上述目的，本发明提供了一种具有抗菌保健功能的衬衫用混纺面料及其制备方法。
一种具有抗菌保健功能的衬衫用混纺面料，包括以下重量百分比的成分：
珍珠纤维 10-20%
何首乌藤纤维 40-60%
涤纶纤维 余量。
一种具有抗菌保健功能的衬衫用混纺面料的制备方法，包括以下步骤：
A、以珍珠纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成珍珠纤维包芯纱，以涤纶纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成涤纶纤维包芯纱；
B、将珍珠纤维包芯纱和涤纶纤维包芯纱进行混纺织成坯布；
C、将坯布进行上浆和上油处理；
D、采用低浴比高压喷射溢流机进行退浆精炼处理，具体条件如下：退浆浴pH值7.5-8，精炼剂：1-2g/L，氢氧化钠：1-3g/L，浴比：1：（10-15），温度：80-90℃，时间：10-15min；
E、采用浸压法对面料进行染色，具体条件如下：浸轧温度控制在60-75℃，浸轧率80-85%，浸轧处理液中含有2-8%的天然植物染色剂，浴比：1：（15-25），pH值6.5-7.5；
F、进行高温定型，温度：120-130℃，时间：20-30s；
G、印花并进行后定型烘干处理，先进行清水浸轧，再在160-170℃条件下烘干定型。
优选的，所述的何首乌藤纤维的单纤维长度为10-20mm，单纤维细度为15-25μm。
优选的，所述的珍珠纤维包芯纱中，珍珠纤维和何首乌藤纤维的重量比为（2-4）：1。
优选的，所述的涤纶纤维包芯纱中，涤纶纤维和何首乌藤纤维的重量比为1：（1-2）。
何首乌藤纤维是一种新型天然纤维，其单纤维的横截面为不规则的椭圆形，内有中腔，中腔较小，不同纤维的中腔形态存在差异；单纤维整体上呈现为不规则的管状，有凹槽，纤维末端较细，中间较粗。总体来说，该纤维既有棉纤维的天然转曲形态，又具有麻类纤维的结节的特征。
由于何首乌藤纤维离散性较大，单纤维成纱较困难，故本发明中将其作为外包层，珍珠纤维作为芯丝，纺织成包芯纱，不但可以保留何首乌藤纤维自身的抗菌性能，而且可以和珍珠纤维相结合，进一步提高珍珠纤维的保健功效；将何首乌藤纤维作为外包层，涤纶纤维作为芯丝，纺织成包芯纱，不但可以保留涤纶纤维的硬挺度，克服何首乌藤纤维离散性较大，单纤维成纱较困难的缺点，而且可以显著改性纤维的着色性能（何首乌藤纤维是中空纤维，染色效果非常好），同时还保留了何首乌藤纤维自身的抗菌性能。
珍珠纤维有发射远红外线的功能，但是正常将珍珠纤维与其它纤维混纺后，在加工过程中酸或者其它化学制剂对其发射远红外线的功能会有影响，而本发明中将其与何首乌藤纤维制成包芯纱，不但不会影响其发射远红外线的功能，而且有利于减少外界对珍珠纤维的影响，延长珍珠纤维发射远红外线的时间和效果。
本发明具有以下有益效果：
1、本发明的混纺纤维不但具有抗菌保健功效，而且采用植物染色剂，健康、环保；2、本发明中使用的何首乌藤纤维是将废弃物的何首乌藤再利用，符合国家循环经济的要求；3、本发明将何首乌藤纤维作为外包层，珍珠纤维作为芯丝，纺织成包芯纱，不但克服了何首乌藤纤维离散性较大，单纤维成纱较困难的缺点，而且延长了珍珠纤维发射远红外线的时间和效果，还提升了面料的抗菌性能；将何首乌藤纤维作为外包层，涤纶纤维作为芯丝，纺织成包芯纱，不但可以保留涤纶纤维的硬挺度，而且可以显著改性纤维的着色性能，综上所述，本发明的面料的制备方法是一种新型天然纤维的优化利用工艺。
具体实施方式
以下对本发明的实施例进行详细说明，但是本发明可以根据权利要求限定和覆盖的多种不同方式实施。
实施例1
一种具有抗菌保健功能的衬衫用混纺面料的制备方法，包括以下步骤：
A、以珍珠纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成珍珠纤维包芯纱，以涤纶纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成涤纶纤维包芯纱；
B、将珍珠纤维包芯纱和涤纶纤维包芯纱进行混纺织成坯布；
C、将坯布进行上浆和上油处理；
D、采用低浴比高压喷射溢流机进行退浆精炼处理，具体条件如下：退浆浴pH值7.5-8，精炼剂：1.5g/L，氢氧化钠：2g/L，浴比：1：12，温度：85℃，时间：12min；
E、采用浸压法对面料进行染色，具体条件如下：浸轧温度控制在70℃，浸轧率82%，浸轧处理液中含有6%的天然植物染色剂，浴比：1：20，pH值6.5-7.5；
F、进行高温定型，温度：125℃，时间：28s；
G、印花并进行后定型烘干处理，先进行清水浸轧，再在165℃条件下烘干定型。
所述的何首乌藤纤维的单纤维长度为10-20mm，单纤维细度为15-25μm。
所述的具有抗菌保健功能的衬衫用混纺面料，包括以下重量百分比的成分：
珍珠纤维包芯纱 15%
涤纶纤维包芯纱 85%；
所述的珍珠纤维包芯纱中，珍珠纤维和何首乌藤纤维的重量比为2：1。
所述的涤纶纤维包芯纱中，涤纶纤维和何首乌藤纤维的重量比为1：1。
实施例2
一种具有抗菌保健功能的衬衫用混纺面料的制备方法，包括以下步骤：
A、以珍珠纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成珍珠纤维包芯纱，以涤纶纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成涤纶纤维包芯纱；
B、将珍珠纤维包芯纱和涤纶纤维包芯纱进行混纺织成坯布；
C、将坯布进行上浆和上油处理；
D、采用低浴比高压喷射溢流机进行退浆精炼处理，具体条件如下：退浆浴pH值7.5-8，精炼剂：2g/L，氢氧化钠：1g/L，浴比：1：15，温度：80℃，时间：15min；
E、采用浸压法对面料进行染色，具体条件如下：浸轧温度控制在60℃，浸轧率85%，浸轧处理液中含有2%的天然植物染色剂，浴比：1：15，pH值6.5-7.5；
F、进行高温定型，温度： 130℃，时间：20s；
G、印花并进行后定型烘干处理，先进行清水浸轧，再在170℃条件下烘干定型。
所述的何首乌藤纤维的单纤维长度为10-20mm，单纤维细度为15-25μm。
所述的具有抗菌保健功能的衬衫用混纺面料，包括以下重量百分比的成分：
珍珠纤维包芯纱 25%
涤纶纤维包芯纱 75%；
所述的珍珠纤维包芯纱中，珍珠纤维和何首乌藤纤维的重量比为4：1。
所述的涤纶纤维包芯纱中，涤纶纤维和何首乌藤纤维的重量比为1：1。
实施例3
一种具有抗菌保健功能的衬衫用混纺面料的制备方法，包括以下步骤：
A、以珍珠纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成珍珠纤维包芯纱，以涤纶纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成涤纶纤维包芯纱；
B、将珍珠纤维包芯纱和涤纶纤维包芯纱进行混纺织成坯布；
C、将坯布进行上浆和上油处理；
D、采用低浴比高压喷射溢流机进行退浆精炼处理，具体条件如下：退浆浴pH值7.5-8，精炼剂：1g/L，氢氧化钠：3g/L，浴比：1：10，温度：90℃，时间：10min；
E、采用浸压法对面料进行染色，具体条件如下：浸轧温度控制在75℃，浸轧率80%，浸轧处理液中含有8%的天然植物染色剂，浴比：1：15，pH值6.5-7.5；
F、进行高温定型，温度：130℃，时间：20s；
G、印花并进行后定型烘干处理，先进行清水浸轧，再在170℃条件下烘干定型。
所述的何首乌藤纤维的单纤维长度为10-20mm，单纤维细度为15-25μm。
所述的具有抗菌保健功能的衬衫用混纺面料，包括以下重量百分比的成分：
珍珠纤维包芯纱 24%
涤纶纤维包芯纱 76%；
所述的珍珠纤维包芯纱中，珍珠纤维和何首乌藤纤维的重量比为3：1。
所述的涤纶纤维包芯纱中，涤纶纤维和何首乌藤纤维的重量比为1：2。
对比实施例1
将实施例1中的珍珠纤维包芯纱替换为珍珠纤维，其余制备条件不变。
以下对实施例1-3和对比实施例1的面料进行测试，得到如下数据。
一、保健性能测试：
所述的面料对人体的影响测试条件为：在温度为19-21℃，湿度为48-52%R.H.的室内条件下，随机选取20-40岁的男士和女士进行测试，先适应环境10分钟，然后穿上测试面料30分钟，对穿衣前和穿衣后人体的小臂中部进行测试。
表一：面料对人体的影响测试：
表二：面料洗涤50次后，面料对人体的影响测试：
| 皮肤表面温度 | 皮肤微循环血流量 | 皮肤微循环血流速 | ||
| 穿着30min变化量 | 提高0.80℃ | 增加15.5% | 增加15.0% | 实施例1 |
| 穿着30min变化量 | 提高0.25℃ | 增加10.2% | 增加8.5% | 对比实施例1 |
由表一和表二的测试结果可以知道，本发明的珍珠纤维包芯纱替换为珍珠纤维后，对面料的保健功能没有明显影响，但是长期使用和洗涤后，本发明的面料保健功能的持久性比珍珠纤维好很多。
表三：面料洗涤50次后，抗菌性能测试：
| 大肠杆菌 | 白色念珠菌 | 金黄色葡萄球菌 | ||
| 抑菌率 | 91% | 91% | 95% | 实施例1 |
| 抑菌率 | 92% | 90% | 94% | 实施例2 |
| 抑菌率 | 91% | 90% | 93% | 实施例3 |
| 抑菌率 | 25% | 20% | 17% | 对比实施例1 |
由以上检测数据可知，本发明制备的具有抗菌保健功能的衬衫用混纺面料相比于传统珍珠纤维纱线具备更好的抗菌抑菌性能，对大肠杆菌、白色念珠菌和金黄色葡萄球菌的抑菌率均可以达到90%以上。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种具有抗菌保健功能的衬衫用混纺面料的制备方法，其特征在于，包括以下步骤：
A、以珍珠纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成珍珠纤维包芯纱，以涤纶纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成涤纶纤维包芯纱；
B、将珍珠纤维包芯纱和涤纶纤维包芯纱进行混纺织成坯布；
C、将坯布进行上浆和上油处理；
D、采用低浴比高压喷射溢流机进行退浆精炼处理，具体条件如下：退浆浴pH值7.5-8，精炼剂：1-2g/L，氢氧化钠：1-3g/L，浴比：1：（10-15），温度：80-90℃，时间：10-15min；
E、采用浸压法对面料进行染色，具体条件如下：浸轧温度控制在60-75℃，浸轧率80-85%，浸轧处理液中含有2-8%的天然植物染色剂，浴比：1：（15-25），pH值6.5-7.5；
F、进行高温定型，温度：120-130℃，时间：20-30s；
G、印花并进行后定型烘干处理，先进行清水浸轧，再在160-170℃条件下烘干定型；
所述的具有抗菌保健功能的衬衫用混纺面料，包括以下重量百分比的成分：
珍珠纤维 10-20%
何首乌藤纤维 40-60%
涤纶纤维 余量。
2.如权利要求1所述的具有抗菌保健功能的衬衫用混纺面料的制备方法，其特征在于，所述的何首乌藤纤维的单纤维长度为10-20mm，单纤维细度为15-25μm。
3.如权利要求1所述的具有抗菌保健功能的衬衫用混纺面料的制备方法，其特征在于，所述的珍珠纤维包芯纱中，珍珠纤维和何首乌藤纤维的重量比为（2-4）：1。
4.如权利要求1所述的具有抗菌保健功能的衬衫用混纺面料的制备方法，其特征在于，所述的涤纶纤维包芯纱中，涤纶纤维和何首乌藤纤维的重量比为1：（1-2）。
5.如权利要求1所述的具有抗菌保健功能的衬衫用混纺面料的制备方法，其特征在于，包括以下步骤：
A、以珍珠纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成珍珠纤维包芯纱，以涤纶纤维作为芯丝，以何首乌藤纤维作为外包层，采用涡流纺工艺纺织成涤纶纤维包芯纱；
B、将珍珠纤维包芯纱和涤纶纤维包芯纱进行混纺织成坯布；
C、将坯布进行上浆和上油处理；
D、采用低浴比高压喷射溢流机进行退浆精炼处理，具体条件如下：退浆浴pH值7.5-8，精炼剂：1.5g/L，氢氧化钠：2g/L，浴比：1：12，温度：85℃，时间：12min；
E、采用浸压法对面料进行染色，具体条件如下：浸轧温度控制在70℃，浸轧率82%，浸轧处理液中含有6%的天然植物染色剂，浴比：1：20，pH值6.5-7.5；
F、进行高温定型，温度：125℃，时间：28s；
G、印花并进行后定型烘干处理，先进行清水浸轧，再在165℃条件下烘干定型；
所述的何首乌藤纤维的单纤维长度为10-20mm，单纤维细度为15-25μm；
所述的具有抗菌保健功能的衬衫用混纺面料，包括以下重量百分比的成分：
珍珠纤维包芯纱 15%
涤纶纤维包芯纱 85%；
所述的珍珠纤维包芯纱中，珍珠纤维和何首乌藤纤维的重量比为2：1；
所述的涤纶纤维包芯纱中，涤纶纤维和何首乌藤纤维的重量比为1：1。