CN103498346B - 天丝纤维和绢丝混纺的面料 - Google Patents

天丝纤维和绢丝混纺的面料 Download PDF

Info

Publication number
CN103498346B
CN103498346B CN201310425935.XA CN201310425935A CN103498346B CN 103498346 B CN103498346 B CN 103498346B CN 201310425935 A CN201310425935 A CN 201310425935A CN 103498346 B CN103498346 B CN 103498346B
Authority
CN
China
Prior art keywords
fabric
tencel fiber
silk
finishing agent
fiber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310425935.XA
Other languages
English (en)
Other versions
CN103498346A (zh
Inventor
张宏伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGZHOU WEIAI CLOTHING CO., LTD.
Original Assignee
Guangzhou Weiai Clothing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Weiai Clothing Co Ltd filed Critical Guangzhou Weiai Clothing Co Ltd
Priority to CN201310425935.XA priority Critical patent/CN103498346B/zh
Publication of CN103498346A publication Critical patent/CN103498346A/zh
Application granted granted Critical
Publication of CN103498346B publication Critical patent/CN103498346B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种天丝纤维和绢丝混纺的面料,由50-70wt%天丝纤维和30-50wt%绢丝混纺织造而成。本发明的面料冬暖夏凉,透气性与吸湿性强。

Description

天丝纤维和绢丝混纺的面料
技术领域
本发明涉及一种面料,尤其涉及一种天丝纤维和绢丝混纺的面料。
背景技术
天丝(Tencel)是一种溶剂型纤维素纤维,是英国Acordis公司通过十年开发,直至上世纪九十年代才完成商业应用,是最典型的绿色环保纤维。2004年5月由兰精公司合并后统一生产。其环保特点:原料来自木材,可不断自然再生,将木材制成木浆,采用(NMMO)纺丝工艺,将木浆溶解在氧化铵溶剂直接纺丝,完全在物理作用下完成,氧化铵溶剂循环使用,回收率达99%以上,无毒、无污染、天丝产品使用后可生化降解,不会对环境造成污染,故被称为“二十一世纪绿色纤维”。
它有棉的“舒适性、涤纶的“强度”、毛织物的“豪华美感”和真丝的“独特触感”及“柔软垂坠”,无论在于或湿的状态下,均极具韧性。在湿的状态下,它是第一种湿强力远胜于棉的纤维素纤维。这一新型环保可分解纤维,纤维性能独特,具备天然纤维和合成纤维的特点。吸湿透气、强力高、卷曲少、易伸直、纤维纠缠少。
绢丝具有色泽优雅、轻盈柔软.光泽美丽,吸湿性好.手感丰满、滑爽等特点,可以纺制高支纱,织造各种穿着舒适的高贵衣料,是春夏秋冬、老少皆宜之理想服装面料,具“天然纤维皇后”之美称,称为“人造皮肤”。
绢丝为多孔,动物蛋白纤维,可自动调节温度,冬暖夏凉,透气性与吸湿性强,含18种氨基酸,可促进人体新陈代谢,安定精神。光泽:优雅高贵,柔和亮丽。韧性:强韧拉力和同粗钢线略等,韧性比所以人造和天然纤维强,不易勾纱破损。吸湿:具棉纤维1.5倍的吸湿性,能迅速吸收并散发人体汗气。保暖:组织呈多孔性,能吸收大量气体,形成极佳的保暖层。透气:纤维细长又坚韧,可织成密度低,稀而透明的织物,凉爽而没有束缚感。舒适:带静电性低,亲肤性好,贴身舒适。安全:织物燃点在300~460℃间,发生火灾等意外时,难燃保身。卫生:吸湿又放湿,且少静电,防整滋生病菌,是最好的健康纤维。
本发明试图通过提供一种新的混纺面料,将天丝纤维与绢丝混纺。
发明内容
针对现有技术的不足,本发明所要解决的技术问题是提供一种天丝纤维和绢丝混纺的面料。
为解决上述技术问题,本发明通过以下技术方案来实现:
一种天丝纤维和绢丝混纺的面料,由50-70wt%天丝纤维和30-50wt%绢丝混纺织造而成。
优选地,
一种天丝纤维和绢丝混纺的面料,由50-70wt%天丝纤维和30-50wt%绢丝混纺织造而成,再经过抗菌后整理而成。
所述抗菌后整理步骤为,常温下在抗菌整理液中浸渍10-30分钟,所述抗菌整理液中抗菌整理剂用量为0.5-1.5%o.w.f,浴比为1:15-1:25。
所述抗菌整理剂,由如下重量份的组分组成:硫酸鱼精蛋白5-15份、2,4,4’-三氯-2’-羟基二苯醚50-70份、十二烷基硫酸钠5-15份、聚六亚甲基双胍盐酸盐15-25份。将上述各组分搅拌混合均匀,即可制得所述抗菌整理剂。
具体的,在本发明中:
硫酸鱼精蛋白,拼音名:LiusuanYujingdanbai,英文名:ProtamineSulfate,书页号:中国药典2005年版二部-742,本品系自适宜的鱼类新鲜成熟精子中提取的一种碱性蛋白质的硫酸盐。按干燥品计,为白色或类白色粉末,无臭,有吸湿性,易溶于水,不溶于乙醇、氯仿或乙醚中。
2,4,4’-三氯-2’-羟基二苯醚,别名:玉洁新、三氯生,缩写DP300,英文名:5-chloro-2-(2,4-dichlorophenoxy),CAS号:3380-34-5。
十二烷基硫酸钠,CAS号:151-21-3。
聚六亚甲基双胍盐酸盐,英文名:Poly(hexamethylenebiguanide)hydrochloride,CAS登录号:32289-58-0。
o.w.f,全称为Onweightthefabric,纺织染整用语,纺织染整工艺中浓度以织物重量为基准,相对织物百分比。
浴比,liquorratio,纺织染整用语,指浸渍方式中织物与染液的比值。
需要说明的是,在本发明中如无特别解释说明,各原料均以含量100%计。
在本发明中,突破性地将常用于医药、食品行业的原料硫酸鱼精蛋白应用于纺织抗菌处理,进一步的,本发明中首次将硫酸鱼精蛋白与抗菌剂2,4,4’-三氯-2’-羟基二苯醚、聚六亚甲基双胍盐酸盐复配使用,并在表面活性剂十二烷基硫酸钠的协同下,抗菌效果明显增效。
相对于现有技术,本发明技术方案的显著进步主要体现为:本发明的面料冬暖夏凉,透气性与吸湿性强。进一步的,通过抗菌后整理,面料抑菌率高,从而能够有效保护人体健康。
具体实施方式
实施例1
选用市售的天丝纤维和绢丝,质量比为60:40。
将按上述配比称取的天丝纤维开松预处理,在梳棉机上梳理成生条;将按上述配比称取的绢丝开松预处理,在梳棉机上梳理成生条;然后将天丝纤维生条和绢丝生条在并条机上并合,制成熟条;在粗纱机上进行牵伸和加捻,最后在细纱机上进一步牵伸加捻,制成绢丝和天丝纤维混纺纱。再将绢丝和天丝纤维混纺纱采用大圆机纬编织造方法进行织造,最终制得天丝纤维和绢丝混纺的面料。
显然,上述的混纺纱及面料的制备工艺均为本行业的通用方法,为本领域普通技术人员所熟知。
实施例2
取部分实施例1所制得的天丝纤维和绢丝混纺的面料,进一步进行抗菌后整理,具体步骤为:
(1)抗菌整理剂的配置:
按表1中实施例2对应的数据称取各原料,搅拌混合均匀,制得抗菌整理剂。
(2)浸渍:
将抗菌整理剂溶解在水中,制得抗菌整理液;
再将天丝纤维和绢丝混纺的面料常温(18-25℃)下在抗菌整理液中浸渍20分钟,所述抗菌整理液中抗菌整理剂用量为1.0%o.w.f,浴比为1:20。
(3)脱水;
(4)烘干:在100℃温度下将织物烘干。
即可制得本发明的抗菌后处理之后的天丝纤维和绢丝混纺的面料。
实施例3
制备方法与实施例2基本相同,唯一的区别在于选用的抗菌整理剂不同,抗菌整理剂用量相同均为1.0%o.w.f。本实施例采用表1中实施例3对应的数据来制备抗菌整理剂。
实施例4
制备方法与实施例2基本相同,唯一的区别在于选用的抗菌整理剂不同,抗菌整理剂用量相同均为1.0%o.w.f。本实施例采用表1中实施例4对应的数据来制备抗菌整理剂。
实施例5
制备方法与实施例2基本相同,唯一的区别在于选用的抗菌整理剂不同,抗菌整理剂用量相同均为1.0%o.w.f。本实施例采用表1中实施例5对应的数据来制备抗菌整理剂。
实施例6
制备方法与实施例2基本相同,唯一的区别在于选用的抗菌整理剂不同,抗菌整理剂用量相同均为1.0%o.w.f。本实施例采用表1中实施例6对应的数据来制备抗菌整理剂。
表1:抗菌整理剂配方表单位:公斤
实施例2 实施例3 实施例4 实施例5 实施例6
硫酸鱼精蛋白 10 / 20 10 10
2,4,4’-三氯-2’-羟基二苯醚 60 60 60 80 /
十二烷基硫酸钠 10 20 / 10 10
聚六亚甲基双胍盐酸盐 20 20 20 / 80
测试例1
采用国家标准GB/T20944.3-2008《纺织品抗菌性能的评价第3部分:振荡法》进行抗菌性定量测试,采用耐洗色牢度试验机洗涤方法,测试水洗30次后的织物,测试结果见表2。
表2:水洗30次后抑菌率测试表
洗涤次数,次 抑菌率(大肠杆菌),% 抑菌率(白色念珠菌),%
实施例230 86 84
实施例330 75 76
实施例430 74 76
实施例530 65 68
实施例630 68 70

Claims (1)

1.一种天丝纤维和绢丝混纺的面料,其特征在于:由50-70wt%天丝纤维和30-50wt%绢丝混纺织造而成,再经过抗菌后整理而成;
所述抗菌后整理步骤为,常温下在抗菌整理液中浸渍10-30分钟,所述抗菌整理液中抗菌整理剂用量为0.5-1.5%o.w.f,浴比为1:15-1:25;
所述抗菌整理剂,由如下重量份的组分组成:硫酸鱼精蛋白5-15份、2,4,4’-三氯-2’-羟基二苯醚50-70份、十二烷基硫酸钠5-15份、聚六亚甲基双胍盐酸盐15-25份。
CN201310425935.XA 2013-09-17 2013-09-17 天丝纤维和绢丝混纺的面料 Active CN103498346B (zh)