CN106282657A - 一种铜合金新材料 - Google Patents

一种铜合金新材料 Download PDF

Info

Publication number
CN106282657A
CN106282657A CN201610791038.4A CN201610791038A CN106282657A CN 106282657 A CN106282657 A CN 106282657A CN 201610791038 A CN201610791038 A CN 201610791038A CN 106282657 A CN106282657 A CN 106282657A
Authority
CN
China
Prior art keywords
copper alloy
new material
alloy new
described copper
surplus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610791038.4A
Other languages
English (en)
Inventor
裴秀琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610791038.4A priority Critical patent/CN106282657A/zh
Publication of CN106282657A publication Critical patent/CN106282657A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种铜合金新材料，所述铜合金新材料的主要成分为Zn、Mg、Sc、Sn、NI和Cu，且按照质量百分比计，所述铜合金新材料包括以下组分：Zn7.5～9.0％，Mg1.5～3.0％，Sc0.1～0.2％，Sn0.1～0.2％，NI0.15～0.25％，Si0～0.05％，Fe0～0.05％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。制备得到的铜合金材料具有良好的抗拉强度和伸长率。

Description

一种铜合金新材料
技术领域
本发明涉及合金材料，尤其涉及一种铜合金新材料。
背景技术
在柱塞泵的设计中，滑靴副是关键的摩擦副之一。具体有以下要求：一、其滑动面应保证必要的润滑条件。所以要具有一定的强度和耐磨性。二滑靴是和柱塞旋压或者扣压结合，必须要具有很好的延展性能。三柱塞泵工作的时候温度最高可达到120℃，又是在高压下，所以滑靴材料必须保证耐腐蚀和耐高温的性能。现有的用于制造高压柱塞泵的核心零件如滑靴和配流盘的铜合金材料的缺点是强度较低、不耐磨、不耐腐蚀、延展性不好、不易加工，质量稳定性很差。
发明内容
本发明所要解决的技术问题是提供一种铜合金新材料。
本发明解决上述技术问题的技术方案如下：一种铜合金新材料，所述铜合金新材料的主要成分为Zn、Mg、Sc、Sn、NI和Cu，且按照质量百分比计，所述铜合金新材料包括以下组分：
Zn7.5～9.0％，Mg1.5～3.0％，Sc0.1～0.2％，Sn0.1～0.2％，NI0.15～0.25％，Si0～0.05％，Fe0～0.05％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。
本发明的有益效果是：制备得到的铜合金材料具有良好的抗拉强度和伸长率。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，按照质量百分比计，所述铜合金新材料包括以下组分：
Zn8.0～9.0％，Mg2.0～2.8％，Sc0.15～0.2％，Sn0.15～0.2％，NI0.15～0.20％，Si0.02～0.05％，Fe0.03～0.05％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。
进一步，按照质量百分比计，所述铜合金新材料包括以下组分：
Zn8.5％，Mg2.6％，Sc0.2％，Sn0.18％，NI0.2％，Si0.04％，Fe0.04％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。
进一步，所述铜合金新材料的抗拉强度为600～700MPa。
进一步，所述铜合金新材料的屈服强度600～700Mpa。
进一步，所述铜合金新材料的延伸率为8.0％～10％。
进一步，所述铜合金新材料的焊接系数为0.74～0.87。
具体实施方式
将各原料依次加入熔化炉中，熔化炉的温度为1000℃，熔炼55s后，浇注到模具中，自然冷却。
抗拉强度 屈服强度 延伸率 焊接系数
实施例1 623 683 8.3 0.8
实施例2 689 662 8.8 0.82
实施例3 668 690 9 0.86
实施例4 695 633 9.1 0.82
实施例5 648 651 9 0.7
尽管上面已经示出和描述了本发明的实施例，可以理解的是，上述实施例是示例性的，不能理解为对本发明的限制，本领域的普通技术人员在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。

Claims (7)

1.一种铜合金新材料，其特征在于，所述铜合金新材料的主要成分为Zn、Mg、Sc、Sn、NI和Cu，且按照质量百分比计，所述铜合金新材料包括以下组分：
Zn7.5～9.0％，Mg1.5～3.0％，Sc0.1～0.2％，Sn0.1～0.2％，NI0.15～0.25％，Si0～0.05％，Fe0～0.05％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。
2.根据权利要求1所述的铜合金新材料，其特征在于，按照质量百分比计，所述铜合金新材料包括以下组分：
Zn8.0～9.0％，Mg2.0～2.8％，Sc0.15～0.2％，Sn0.15～0.2％，NI0.15～0.20％，Si0.02～0.05％，Fe0.03～0.05％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。
3.根据权利要求1所述的铜合金新材料，其特征在于，按照质量百分比计，所述铜合金新材料包括以下组分：
Zn8.5％，Mg2.6％，Sc0.2％，Sn0.18％，NI0.2％，Si0.04％，Fe0.04％，Er0.02％，Ce0.01％，杂质≤0.1％，余量为Cu。
4.根据权利要求1所述的铜合金新材料，其特征在于，所述铜合金新材料的抗拉强度为600～700MPa。
5.根据权利要求1所述的铜合金新材料，其特征在于，所述铜合金新材料的屈服强度600～700Mpa。
6.根据权利要求1所述的铜合金新材料，其特征在于，所述铜合金新材料的延伸率为8.0％～10％。
7.根据权利要求1所述的铜合金新材料，其特征在于，所述铜合金新材料的焊接系数为0.74～0.87。
CN201610791038.4A 2016-08-31 2016-08-31 一种铜合金新材料 Pending CN106282657A (zh)