CN106280999A - A kind of weather-proof aging-resistant cell panel dirt resistance coatings - Google Patents
A kind of weather-proof aging-resistant cell panel dirt resistance coatings Download PDFInfo
- Publication number
- CN106280999A CN106280999A CN201610745467.8A CN201610745467A CN106280999A CN 106280999 A CN106280999 A CN 106280999A CN 201610745467 A CN201610745467 A CN 201610745467A CN 106280999 A CN106280999 A CN 106280999A
- Authority
- CN
- China
- Prior art keywords
- parts
- cell panel
- methyl
- silicone oil
- weather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of weather-proof aging-resistant cell panel dirt resistance coatings, it includes the raw material of following parts by weight: methyl trifluoro propyl silicone oil 100 parts, methylchlorophenyl silicone oil 15 ~ 25 parts, methyl vinyl silicon oil 20 ~ 40 parts, 20 ~ 80 parts of argentum powder, copper powder 50 ~ 120 parts, Hydroxypropyl acrylate 5 ~ 15 parts, isocyanuric acid three-glycidyl ester 1 ~ 10 part, 2 methyl piperazine 1 ~ 3 part, aerosil 1 ~ 3 part, silane coupler 3 ~ 10 parts, titanium chelate catalyst 0.05 ~ 0.15 part.The one weather-proof aging-resistant cell panel dirt resistance coatings that the present invention provides passes through many experiments, obtain the dirt resistance coatings formula with good weatherability properties and ageing resistace, it is coated in cell panel surface, have excellent heat conduction, heat radiation, bonding, seal, insulate, the performance such as moistureproof, shockproof, the material such as metal, plastics is had good bonding force.
Description
Technical field
The present invention relates to battery ingredients technical field, be specifically related to a kind of weather-proof aging-resistant cell panel dirt resistance coatings.
Background technology
The surface dirt resistance coatings of cell panel is a kind of electrical insulating property both with excellence, has again the organic of excellent heat conductivity
Silicon materials, can extensively be coated on various electronic product surface, the contact surface between heater and heat radiation facility in electric equipment,
Play heat catalysis effect and protection against the tide, dust-proof, anticorrosion, the effect such as shockproof.These type of silicon materials, to producing hot electronic component, carry
Supply splendid heat-conducting effect.As: transistor, CPU assembling, critesistor, temperature sensor, power module, automotive electronics zero
Parts, refrigerator of vehicle, printer are first-class.Owing to being applied to cell panel surface, it is desirable to dirt resistance coatings have certain weatherability and
Ageing resistace, but existing dirt resistance coatings weatherability and ageing resistace are bad, have impact on the normal use of electronic component.
Summary of the invention
Not enough for prior art, the invention provides a kind of weather-proof aging-resistant cell panel dirt resistance coatings.
The present invention solves the technical scheme of above-mentioned technical problem employing: a kind of weather-proof dust-proof painting of aging-resistant cell panel
Material, including the raw material of following parts by weight: methyl trifluoro propyl silicone oil 100 parts, methylchlorophenyl silicone oil 15 ~ 25 parts, methyl second
Thiazolinyl silicone oil 20 ~ 40 parts, 20 ~ 80 parts of argentum powder, copper powder 50 ~ 120 parts, Hydroxypropyl acrylate 5 ~ 15 parts, isocyanuric acid three shrink sweet
Grease 1 ~ 10 part, 2-methyl piperazine 1 ~ 3 part, aerosil 2 ~ 6 parts, silane coupler 1 ~ 3 part, titanium chelate catalyst
0.05 ~ 0.15 part.
Preferably, described one weather-proof aging-resistant cell panel dirt resistance coatings, including the raw material of following parts by weight: methyl
Trifluoro propyl silicone oil 100 parts, methylchlorophenyl silicone oil 20 parts, methyl vinyl silicon oil 30 parts, 50 parts of argentum powder, copper powder 90 parts, third
Olefin(e) acid hydroxypropyl acrylate 10 parts, isocyanuric acid three-glycidyl ester 6 parts, 2-methyl piperazine 2 parts, aerosil 4 parts, silane coupled
Agent 2 parts, titanium chelate catalyst 0.1 part.
Compared with prior art, the advantage that the present invention possesses is:
The one weather-proof aging-resistant cell panel dirt resistance coatings that the present invention provides passes through many experiments, it is thus achieved that have the most weather-proof
Property and the dirt resistance coatings formula of ageing resistace, be coated in cell panel surface, have excellent heat conduction, heat radiation, bonding, seal,
Insulation, the performance such as moistureproof, shockproof, have good bonding force to the material such as metal, plastics.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1: a kind of weather-proof aging-resistant cell panel dirt resistance coatings, including the raw material of following parts by weight: methyl three
Fluoropropyl silicone oil 100 parts, methylchlorophenyl silicone oil 20 parts, methyl vinyl silicon oil 30 parts, 50 parts of argentum powder, copper powder 90 parts, propylene
Acid hydroxypropyl acrylate 10 parts, isocyanuric acid three-glycidyl ester 6 parts, 2-methyl piperazine 2 parts, aerosil 4 parts, silane coupler
2 parts, titanium chelate catalyst 0.1 part.
Embodiment 2: a kind of weather-proof aging-resistant cell panel dirt resistance coatings, including the raw material of following parts by weight: methyl three
Fluoropropyl silicone oil 100 parts, methylchlorophenyl silicone oil 15 parts, methyl vinyl silicon oil 20 parts, 20 parts of argentum powder, copper powder 50 parts, propylene
Acid hydroxypropyl acrylate 5 parts, isocyanuric acid three-glycidyl ester 1 part, aerosil 2 parts, silane coupler 1 part, titanium chelate are urged
Agent 0.05 part.
Embodiment 3: a kind of weather-proof aging-resistant cell panel dirt resistance coatings, including the raw material of following parts by weight: methyl three
Fluoropropyl silicone oil 100 parts, methylchlorophenyl silicone oil 25 parts, methyl vinyl silicon oil 40 parts, 80 parts of argentum powder, copper powder 120 parts, propylene
Acid hydroxypropyl acrylate 15 parts, isocyanuric acid three-glycidyl ester 10 parts, aerosil 6 parts, silane coupler 3 parts, titanium chelate
Catalyst 0.15 part.
Embodiment 4: a kind of weather-proof aging-resistant cell panel dirt resistance coatings, including the raw material of following parts by weight: methyl three
Fluoropropyl silicone oil 100 parts, methylchlorophenyl silicone oil 18 parts, methyl vinyl silicon oil 25 parts, 70 parts of argentum powder, copper powder 100 parts, propylene
Acid hydroxypropyl acrylate 8 parts, isocyanuric acid three-glycidyl ester 8 parts, 2-methyl piperazine 3 parts, aerosil 5 parts, silane coupler 2
Part, titanium chelate catalyst 0.08 part.
Embodiment 5: a kind of weather-proof aging-resistant cell panel dirt resistance coatings, including the raw material of following parts by weight: methyl three
Fluoropropyl silicone oil 100 parts, methyl vinyl silicon oil 20 parts, 80 parts of argentum powder, copper powder 50 parts, Hydroxypropyl acrylate 15 parts, isocyanide are urinated
Acid three-glycidyl ester 1 part, aerosil 6 parts, silane coupler 2 parts, titanium chelate catalyst 0.15 part.
One weather-proof aging-resistant cell panel dirt resistance coatings described in embodiment 1-5, presses the raw material of described parts by weight
Use can be coated after being sufficiently mixed uniformly according to Conventional processing methods in the industry.
It should be noted that, foregoing is not limitation of the present invention, present invention is also not necessarily limited to the example above, all
The those of ordinary skill of technical field, the change made, retrofits, adds or replaces within the essential scope of the present invention, all answers
Belong to protection scope of the present invention.
Claims (4)
1. a weather-proof aging-resistant cell panel dirt resistance coatings, it is characterised in that include the raw material of following parts by weight: methyl three
Fluoropropyl silicone oil 100 parts, methylchlorophenyl silicone oil 15 ~ 25 parts, methyl vinyl silicon oil 20 ~ 40 parts, 20 ~ 80 parts of argentum powder, copper powder
50 ~ 120 parts, Hydroxypropyl acrylate 5 ~ 15 parts, isocyanuric acid three-glycidyl ester 1 ~ 10 part, 2-methyl piperazine 1 ~ 3 part, gas phase two
Silicon oxide 2 ~ 6 parts, silane coupler 1 ~ 3 part, titanium chelate catalyst 0.05 ~ 0.15 part.
One the most according to claim 1 weather-proof aging-resistant cell panel dirt resistance coatings, it is characterised in that include following heavy
The raw material of amount number: methyl trifluoro propyl silicone oil 100 parts, methylchlorophenyl silicone oil 20 parts, methyl vinyl silicon oil 30 parts, argentum powder
50 parts, copper powder 90 parts, Hydroxypropyl acrylate 10 parts, isocyanuric acid three-glycidyl ester 6 parts, 2-methyl piperazine 2 parts, gas phase dioxy
SiClx 4 parts, silane coupler 2 parts, titanium chelate catalyst 0.1 part.
One the most according to claim 1 weather-proof aging-resistant cell panel dirt resistance coatings, it is characterised in that include following heavy
The raw material of amount number: methyl trifluoro propyl silicone oil 100 parts, methylchlorophenyl silicone oil 15 parts, methyl vinyl silicon oil 20 parts, argentum powder
20 parts, copper powder 50 parts, Hydroxypropyl acrylate 5 parts, isocyanuric acid three-glycidyl ester 1 part, 2-methyl piperazine 1 part, gas phase dioxy
SiClx 2 parts, silane coupler 1 part, titanium chelate catalyst 0.05 part.
One the most according to claim 1 weather-proof aging-resistant cell panel dirt resistance coatings, it is characterised in that include following heavy
The raw material of amount number: methyl trifluoro propyl silicone oil 100 parts, methylchlorophenyl silicone oil 25 parts, methyl vinyl silicon oil 40 parts, argentum powder
80 parts, copper powder 120 parts, Hydroxypropyl acrylate 15 parts, isocyanuric acid three-glycidyl ester 10 parts, 2-methyl piperazine 3 parts, gas phase two
Silicon oxide 6 parts, silane coupler 3 parts, titanium chelate catalyst 0.15 part.