CN106336796A - Solar panel dustproof coating with heat resistant and anti-corrosion property - Google Patents
Solar panel dustproof coating with heat resistant and anti-corrosion property Download PDFInfo
- Publication number
- CN106336796A CN106336796A CN201610745447.0A CN201610745447A CN106336796A CN 106336796 A CN106336796 A CN 106336796A CN 201610745447 A CN201610745447 A CN 201610745447A CN 106336796 A CN106336796 A CN 106336796A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicone oil
- solar panel
- corrosion
- heat resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a solar panel dustproof coating of heat resistant and anti-corrosion property which comprises, by weight, 100 parts of methylphenyl silicone oil, 20 to 40 portions of ethyl hydrogen-containing silicone oil, 20 to 80 portions of aluminum powder, 50 to 120 portions of copper powder, 5 to 15 portions of diaminodiphenylmethane, 1 to 10 parts of triglycidyl isocyanurate, 2 to 6 parts of fumed silica, 3 to 10 parts of urea, and 0.05 to 0.15 part of catalyst. The solar panel coating of heat resistant and anti-corrosion property provided by the invention passes through many tests to acquire the formula for the solar panel dustproof coating of heat resistant and anti-corrosion property which provides excellent functions of heat-conducting, heat dissipating, sealing, dielectric, anti-moisture and anti-vibration properties by smearing the material on the surface of the solar panel. The coating has outstanding adhesion to the metal and plastic materials and good anti-aging property.
Description
Technical field
The present invention relates to battery ingredients technical field is and in particular to a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant.
Background technology
The surface dirt resistance coatings of cell panel be a kind of both there is excellent electrical insulating property, have the organic of excellent heat conductivity again
Silicon materials, can extensively be coated on various electronic products surface, the heater in electric equipment and the contact surface radiating between facility,
Play heat catalysis effect and moistureproof, dust-proof, anticorrosion, the effect such as shockproof.Such silicon materials, to the electronic component producing heat, carry
Supply splendid heat-conducting effect.As: transistor, cpu assembling, critesistor, temperature sensor, power module, automotive electronics zero
Part, refrigerator of vehicle, printer are first-class.Due to be applied to battery plate surface it is desirable to dirt resistance coatings have certain high temperature resistant and
Decay resistance, but existing dirt resistance coatings are high temperature resistant and decay resistance is bad, have impact on the normal use of electronic component.
Content of the invention
Not enough for prior art, the invention provides a kind of high temperature resistant, corrosion resistant cell panel dirt resistance coatings.
The technical scheme that the present invention solves that above-mentioned technical problem adopts is: a kind of dust-proof painting of the cell panel of corrosion-and high-temp-resistant
Material, including the raw material of following parts by weight: 100 parts of methyl phenyl silicone oil, 20 ~ 40 parts of ethyl containing hydrogen silicone oil, 20 ~ 80 parts of aluminium powder,
50 ~ 120 parts of copper powder, 5 ~ 15 parts of MDA, 1 ~ 10 part of isocyanuric acid three-glycidyl ester, aerosil 2 ~ 6
Part, 3 ~ 10 parts of carbamide, 0.05 ~ 0.15 part of catalyst.
Preferably, the cell panel dirt resistance coatings of described a kind of corrosion-and high-temp-resistant, including the raw material of following parts by weight: first
100 parts of base phenyl silicone oil, 30 parts of ethyl containing hydrogen silicone oil, 50 parts of aluminium powder, 90 parts of copper powder, 10 parts of MDA, isocyanide urine
6 parts of sour three-glycidyl ester, 4 parts of aerosil, 7 parts of carbamide, 0.1 part of catalyst.
Compared with prior art, the advantage that the present invention possesses is:
The present invention provide a kind of corrosion-and high-temp-resistant cell panel dirt resistance coatings pass through many experiments, obtain have well resistance to
High temperature, the dirt resistance coatings formula of decay resistance, are coated in battery plate surface, have excellent heat conduction, radiating, bonding, sealing,
Insulation, the performance such as moistureproof, shockproof, have good bonding force to materials such as metal, plastics, and ageing-resistant performance are good.
Specific embodiment
With reference to specific embodiment, the present invention is described further.
Embodiment 1: a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant, including the raw material of following parts by weight: methyl
100 parts of phenyl silicone oil, 30 parts of ethyl containing hydrogen silicone oil, 50 parts of aluminium powder, 90 parts of copper powder, 10 parts of MDA, isocyanuric acid
6 parts of three-glycidyl ester, 4 parts of aerosil, 7 parts of carbamide, 0.1 part of catalyst.
Embodiment 2: a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant, including the raw material of following parts by weight: methyl
100 parts of phenyl silicone oil, 20 parts of ethyl containing hydrogen silicone oil, 20 parts of aluminium powder, 50 parts of copper powder, 5 parts of MDA, isocyanuric acid three
1 part of ethylene oxidic ester, 2 parts of aerosil, 3 parts of carbamide, 0.05 part of catalyst.
Embodiment 3: a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant, including the raw material of following parts by weight: methyl
100 parts of phenyl silicone oil, 40 parts of ethyl containing hydrogen silicone oil, 80 parts of aluminium powder, 120 parts of copper powder, 15 parts of MDA, isocyanuric acid
10 parts of three-glycidyl ester, 6 parts of aerosil, 10 parts of carbamide, 0.15 part of catalyst.
Embodiment 4: a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant, including the raw material of following parts by weight: methyl
100 parts of phenyl silicone oil, 28 parts of ethyl containing hydrogen silicone oil, 35 parts of aluminium powder, 85 parts of copper powder, 12 parts of MDA, isocyanuric acid
9 parts of three-glycidyl ester, 3 parts of aerosil, 5 parts of carbamide, 0.12 part of catalyst.
Embodiment 5: a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant, including the raw material of following parts by weight: methyl
100 parts of phenyl silicone oil, 20 parts of ethyl containing hydrogen silicone oil, 80 parts of aluminium powder, 50 parts of copper powder, 15 parts of MDA, isocyanuric acid
1 part of three-glycidyl ester, 6 parts of aerosil, 3 parts of carbamide, 0.15 part of catalyst.
A kind of cell panel dirt resistance coatings of the corrosion-and high-temp-resistant described in embodiment 1-5, by the raw material of described parts by weight
Use can be coated after being sufficiently mixed uniformly according to industry routine processing method.
It should be noted that the above is not limitation of the present invention, present invention is also not necessarily limited to the example above, all
The those of ordinary skill of technical field, the change made within the essential scope of the present invention, remodeling, interpolation or replacement, all answer
Belong to protection scope of the present invention.
Claims (4)
1. a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant are it is characterised in that include the raw material of following parts by weight: methyl
100 parts of phenyl silicone oil, 20 ~ 40 parts of ethyl containing hydrogen silicone oil, 20 ~ 80 parts of aluminium powder, 50 ~ 120 parts of copper powder, MDA 5 ~ 15
Part, 1 ~ 10 part of isocyanuric acid three-glycidyl ester, 2 ~ 6 parts of aerosil, 3 ~ 10 parts of carbamide, 0.05 ~ 0.15 part of catalyst.
2. a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant according to claim 1 are it is characterised in that include following
The raw material of parts by weight: 100 parts of methyl phenyl silicone oil, 30 parts of ethyl containing hydrogen silicone oil, 50 parts of aluminium powder, 90 parts of copper powder, diaminourea two
10 parts of phenylmethane, 6 parts of isocyanuric acid three-glycidyl ester, 4 parts of aerosil, 7 parts of carbamide, 0.1 part of catalyst.
3. a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant according to claim 1 are it is characterised in that include following
The raw material of parts by weight: 100 parts of methyl phenyl silicone oil, 20 parts of ethyl containing hydrogen silicone oil, 20 parts of aluminium powder, 50 parts of copper powder, diaminourea two
5 parts of phenylmethane, 1 part of isocyanuric acid three-glycidyl ester, 2 parts of aerosil, 3 parts of carbamide, 0.05 part of catalyst.
4. a kind of cell panel dirt resistance coatings of corrosion-and high-temp-resistant according to claim 1 are it is characterised in that include following
The raw material of parts by weight: 100 parts of methyl phenyl silicone oil, 40 parts of ethyl containing hydrogen silicone oil, 80 parts of aluminium powder, 120 parts of copper powder, diaminourea two
15 parts of phenylmethane, 10 parts of isocyanuric acid three-glycidyl ester, 6 parts of aerosil, 10 parts of carbamide, 0.15 part of catalyst.