CN106280589A - A kind of inorganic silicate coating and preparation method thereof - Google Patents
A kind of inorganic silicate coating and preparation method thereof Download PDFInfo
- Publication number
- CN106280589A CN106280589A CN201610781579.9A CN201610781579A CN106280589A CN 106280589 A CN106280589 A CN 106280589A CN 201610781579 A CN201610781579 A CN 201610781579A CN 106280589 A CN106280589 A CN 106280589A
- Authority
- CN
- China
- Prior art keywords
- inorganic silicate
- preparation
- silicate coating
- emulsion
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to coating applied technical field, it is specifically related to a kind of inorganic silicate coating and preparation method thereof, following raw material is prepared from: water, antibacterial, dispersant, defoamer, emulsion, cellulose, antifreezing agent, Ludox, coalescents, stabilizer, bentonite, triple superphosphate, titanium dioxide, Pulvis Talci；The invention have the benefit that and select the excellent emulsion of ion stabilized performance can improve the pliability of film and cohesive force prevents flocculation, by selecting corresponding thickened systems to improve the storage stability of finished product, by the problem selecting stabilizer thoroughly to solve flocculation simultaneously.The coating of manufacture of the present invention has the breathability of excellence；Anti-microbial type is grown with lichen；Noninflammability；Radiation heat radiation；Excellent is antiacid, alkali resistance；Environmental protection.
Description
Technical field
The present invention relates to coating applied technical field, be specifically related to a kind of inorganic silicate coating and preparation method thereof.
Background technology
Silicate paint of the prior art exists that cohesive force is weak mostly, and integral system is not sufficiently stable, and often produces flocculation
Problem, the pliability of film there is also problem simultaneously.
Summary of the invention
In order to effectively solve the problems referred to above, the present invention provides a kind of inorganic silicate coating and preparation method thereof.
Technical scheme is specific as follows: a kind of inorganic silicate coating, the raw material of following weight ratio prepare
Form:
The preparation method of a kind of inorganic silicate coating, for preparing above-mentioned inorganic silicate coating, described preparation side
Method comprises the steps:
First cellulose is uniformly dispersed with bentonite in water, sequentially adds dispersant and be uniformly dispersed with defoamer, then
Adding titanium dioxide, triple superphosphate, Pulvis Talci high-speed stirred reaches standard to fineness, sequentially adds coalescents, emulsion, antifreezing agent,
Defoamer, Ludox, stabilizer mix homogeneously, finally pack.
The invention have the benefit that the emulsion selecting ion stabilized performance excellent can improve pliability and the bonding of film
Power prevents flocculation simultaneously, by selecting corresponding thickened systems to improve the storage stability of finished product, by selecting stabilizer thoroughly to solve
The certainly problem of flocculation.The coating of manufacture of the present invention has the breathability of excellence；Anti-microbial type is grown with lichen；Noninflammability；Radiation heat
Radiation；Excellent is antiacid, alkali resistance；Environmental protection.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, to the present invention
It is explained in further detail.Should be appreciated that specific embodiment described herein is used only for explaining the present invention, be not used to
Limit the present invention.
On the contrary, the present invention contain any be defined by the claims the replacement done in the spirit and scope of the present invention, repair
Change, equivalent method and scheme.Further, in order to make the public that the present invention to be had a better understanding, thin to the present invention below
During joint describes, detailed describe some specific detail sections.There is no these detail sections for a person skilled in the art
Description can also understand the present invention completely.
The first embodiment of the present invention provides a kind of inorganic silicate coating, by the raw material preparation of following weight ratio
Become:
Described antibacterial is LXE sterilization antiseptic；Described dispersant is low-molecular-weight wax class dispersant；Described defoamer is ore deposit
Thing oil defoamer；Described emulsion is PRIMALAC-808A emulsion or PrimalTM DirtShield K2 emulsion, but described breast
Liquid is not to be limited above-mentioned two emulsion；Described cellulose is hydroxyethyl cellulose, methylcellulose, carboxymethyl cellulose, second
Base cellulose or hydroxypropyl cellulose therein one or more；Described antifreezing agent is alcohols antifreezing agent；Described coalescents is
Alcohol ester 12；Described stabilizer is UV light stabilizing agent；
Described emulsion is modified guar, and the preparation method of modified guar comprises the steps of
1) intensification deionized water is to 100-115 DEG C, puts into melon glue subsequently and makes it dissolve；
2) put into 90min after melon glue, there was added vinyl methacrylate, organic silicon monomer and carry out heating up, adding
Pressure, high-speed stirred, described in be warming up to 250-270 DEG C；Being forced into two atmospheric pressure, mixing speed is 300-320r/min simultaneously；
3) constant temperature 7-8 hour subsequently；Regulation pH value is to 6-7 simultaneously, completes modified preparation；
Wherein, the consumption of the material of above steps calculates by weight and is respectively as follows: deionized water 100 parts, melon glue
70-80 part, organic silicon monomer 35-40 part, vinyl methacrylate 2-3 part；Described vinyl methacrylate is used for regulating
The dispersion of melon glue and polymerization so that it is dispersion effect reaches optimum, and in whipping process, vinyl methacrylate self has
Suspended dispersed effect, is attached on guar gum, and in quick whipping process, ceaselessly breaks up and depend on so that overall dispersion
Uniformly, finally disperse up and down unanimously reaching whole modified guar.
The preparation method of a kind of inorganic silicate coating, for preparing above-mentioned inorganic silicate coating, described preparation side
Method comprises the steps: first to be uniformly dispersed in water with bentonite by cellulose, sequentially adds dispersant and disperses with defoamer
Uniformly, adding titanium dioxide, triple superphosphate, Pulvis Talci high-speed stirred reaches standard to fineness, sequentially adds coalescents, emulsion,
Antifreezing agent, defoamer, Ludox, stabilizer mix homogeneously, finally pack.
Claims (2)
1. an inorganic silicate coating, it is characterised in that be prepared from by the raw material of following weight ratio:
2. a preparation method for inorganic silicate coating, for preparing the inorganic silicate coating described in the claims 1,
It is characterized in that, described preparation method comprises the steps:
First cellulose is uniformly dispersed with bentonite in water, sequentially adds dispersant and be uniformly dispersed with defoamer, add
Titanium dioxide, triple superphosphate, Pulvis Talci high-speed stirred reaches standard to fineness, sequentially adds coalescents, emulsion, antifreezing agent, froth breaking
Agent, Ludox, stabilizer mix homogeneously, finally pack.