CN107298914A - A kind of aqueous woodware paint and preparation method thereof - Google Patents
A kind of aqueous woodware paint and preparation method thereof Download PDFInfo
- Publication number
- CN107298914A CN107298914A CN201710530324.XA CN201710530324A CN107298914A CN 107298914 A CN107298914 A CN 107298914A CN 201710530324 A CN201710530324 A CN 201710530324A CN 107298914 A CN107298914 A CN 107298914A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- defoamer
- aqueous woodware
- woodware paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous woodware paint, it is made up of the component of following parts by weight：Including 10 90 parts of organosilicon-modified acrylic micro emulsion, 26 parts of coalescents, 0.2 0.8 parts of nanometer anion powder, 0.2 1.0 parts of surface modifier wax emulsion, 0.5 2 parts of fire retardant, 0.1 0.5 parts of substrate wetting agents, 0.1 0.6 parts of wetting dispersing agent, 0.1 0.5 parts of moistening flatting agent, 0.2 1 parts of defoamer, 0.1 1 parts of association type polyurethane thickener, 0.1 1 parts of slip agent, 0.1 0.3 parts of antimildew disinfectant, 6 15 parts of deionized water.The equal environmental protection of material of this use of the invention, not using organic solvent, water paint is brushed to tasteless on woodenware, also toxic and harmful gas will not be discharged, VOC content will not be damaged well below paint to environment and human body, its preparation method condition is controllable, is adapted to industrialized production.
Description
Technical field
The present invention relates to technical field of paint preparation, and in particular to a kind of aqueous woodware paint, aqueous the invention further relates to this
The preparation method of woodcare paint.
Background technology
In recent years, environmental pollution situation is increasingly serious, and country is also increasingly stricter for the environmental protection standard of coating, by tradition
Paint be substituted for water paint and favored by customer and producer.Water paint environmental protection, with water as diluent, is not used
Harmful organic solvent, to the harm very little of human body, does not endanger the healthy of production and workmen.But water paint is also deposited
Many the problem of, using water as dispersant, higher temperature is needed because the evaporation latent heat of water is higher, when drying and longer
Time；Water soluble paint contains relatively low molecular mass and substantial amounts of hydrophilic radical, can make the water resistance of film and reduce.In addition,
As the improvement of people's living standards, having more higher performance requirements, and Market competition, the property produced for product
More comprehensively it can could improve the market competitiveness of enterprise by water paint.Although so water paint environmental protection, pollution-free, more
Some combination properties of water paint are taken into account to meet the demand of customer.
The content of the invention
It is an object of the invention to provide a kind of aqueous woodware paint, solve traditional water paint due to water evaporation latent heat compared with
Height, the problem of needing higher temperature and longer time when drying.
It is a further object to provide a kind of preparation method of aqueous woodware paint.
The technical solution adopted in the present invention is that a kind of aqueous woodware paint is made up of the component of following parts by weight：Include
10-90 parts of machine fluorine-silicon modified acrylic micro emulsion, 2-6 parts of coalescents, 0.2-0.8 parts of nanometer anion powder, surface modifier wax emulsion
0.2-1.0 parts, 0.5-2 parts of fire retardant, 0.1-0.5 parts of substrate wetting agents, 0.1-0.6 parts of wetting dispersing agent, moistening flatting agent
0.1-0.5 parts, 0.2-1 parts of defoamer, 0.1-1 parts of association type polyurethane thickener, 0.1-1 parts of slip agent, antimildew disinfectant
0.1-0.3 parts, 6-15 parts of deionized water.
The features of the present invention is also resided in,
Also include antifreezing agent, ultra-violet absorber and color stuffing, wherein antifreezing agent is ethylene glycol or propane diols；Color stuffing point
It is dissipated to fineness and is not more than 30 μm.
Fire retardant is nitrogen phosphorus system water-soluble flame retardant.
Another technical scheme of the present invention is that a kind of preparation method of aqueous woodware paint comprises the following steps：
Step 1, following components is weighed respectively by weight：Including 10-90 parts of organosilicon-modified acrylic micro emulsion, film forming is helped
2-6 parts of agent, 0.2-0.8 parts of nanometer anion powder, 0.2-1.0 parts of surface modifier wax emulsion, 0.5-2 parts of fire retardant, base material wetting
0.1-0.5 parts of agent, 0.1-0.6 parts of wetting dispersing agent, 0.1-0.5 parts of moistening flatting agent, 0.2-1 parts of defoamer, the poly- ammonia of association type
0.1-1 parts of ester thickener, 0.1-1 parts of slip agent, 0.1-0.3 parts of antimildew disinfectant, 6-15 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder and fire retardant, stir 5min-15min；The weight of the defoamer wherein added is the 1/3-2/3 of defoamer gross weight；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, stir 30min-60min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 5min-10min, and aqueous woodware paint is made in filtering.
The features of the present invention is also resided in,
Color stuffing is also added with step 2.
Antifreezing agent and ultra-violet absorber are also added with step 3, antifreezing agent is ethylene glycol or propane diols；Color stuffing disperses
It is not more than 30 μm to fineness.
Fire retardant in step 1 is nitrogen phosphorus system water-soluble flame retardant.
The present invention a kind of aqueous woodware paint beneficial effect be,
1) the equal environmental protection of material that uses of the present invention, not using organic solvent, water paint be brushed to it is tasteless on woodenware,
Toxic and harmful gas will not be discharged, VOC content will not be damaged well below paint to environment and human body；
2) film-forming resin organosilicon-modified acrylic micro emulsion of the present invention, particle size is small and solid content is high, and filming performance is good,
More common acrylic emulsion, paint film has more excellent weatherability, water resistance, light shine, resistance to active oxygen, gloss retention, anti-
Pulverability, pollution resistance；
3) aqueous woodware paint of the invention is with health role.Contain negative ion powder in water paint, can forever discharge beneficial
Anion, the aqueous woodware paint of the present invention is brushed on furniture, germ and purification air can be killed, while can promote human body
Metabolism, improves body immunity, and dispelling fatigue improves sleep quality, has good therapeutic action to more than 30 kinds of diseases；
4) present invention, which has in good flame retardant effect, formula, adds water-soluble flame retardant, there is good protection to woodenware
Effect.
Preparation method of the present invention is simple, and condition is controllable, is adapted to industrialized production.
Embodiment
With reference to embodiment, the present invention is described in detail.
A kind of aqueous woodware paint of the present invention, is made up of the component of following parts by weight：It is micro- including organosilicon-modified acrylic
It is newborn 10-90 parts, 2-6 parts of coalescents, 0.2-0.8 parts of nanometer anion powder, 0.2-1.0 parts of surface modifier wax emulsion, fire retardant
0.5-2 parts, 0.1-0.5 parts of substrate wetting agents, 0.1-0.6 parts of wetting dispersing agent, 0.1-0.5 parts of moistening flatting agent, defoamer
0.2-1 parts, 0.1-1 parts of association type polyurethane thickener, 0.1-1 parts of slip agent, 0.1-0.3 parts of antimildew disinfectant, deionized water
6-15 parts.
Color stuffing is also added with step 2；Color stuffing is dispersed to fineness and is not more than 30 μm.
Also include antifreezing agent, ultra-violet absorber and color stuffing, wherein antifreezing agent is ethylene glycol or propane diols.
Fire retardant is nitrogen phosphorus system water-soluble flame retardant.
A kind of preparation method of above-mentioned aqueous woodware paint, comprises the following steps：
Step 1, following components is weighed respectively by weight：Including 10-90 parts of organosilicon-modified acrylic micro emulsion, film forming is helped
2-6 parts of agent, 0.2-0.8 parts of nanometer anion powder, 0.2-1.0 parts of surface modifier wax emulsion, 0.5-2 parts of fire retardant, base material wetting
0.1-0.5 parts of agent, 0.1-0.6 parts of wetting dispersing agent, 0.1-0.5 parts of moistening flatting agent, 0.2-1 parts of defoamer, the poly- ammonia of association type
0.1-1 parts of ester thickener, 0.1-1 parts of slip agent, 0.1-0.3 parts of antimildew disinfectant, 6-15 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder and fire retardant, stir 5min-15min；The weight of the defoamer wherein added is the 1/3-2/3 of defoamer gross weight；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, stir 30min-60min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 5min-10min, and aqueous woodware paint is made in filtering.
Color stuffing is also added with step 2；Antifreezing agent and ultra-violet absorber are also added with step 3, antifreezing agent is
Ethylene glycol or propane diols；Color stuffing is dispersed to fineness and is not more than 30 μm.
Fire retardant in step 1 is nitrogen phosphorus system water-soluble flame retardant.
Embodiment 1
Step 1, following components is weighed respectively by weight：Including 10 parts of organosilicon-modified acrylic micro emulsion, coalescents 2
Part, 0.2 part of nanometer anion powder, 0.2 part of surface modifier wax emulsion, 0.5 part of nitrogen phosphorus system water-soluble flame retardant, substrate wetting agents
0.1 part, 0.1 part of wetting dispersing agent, 0.1 part of moistening flatting agent, 0.2 part of defoamer, 0.1 part of association type polyurethane thickener increases
0.1 part of lubrication prescription, 0.1 part of antimildew disinfectant, 6 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder and nitrogen phosphorus system water-soluble flame retardant, stir 5min；The weight of the defoamer wherein added is the 1/ of defoamer gross weight
3；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, stir 30min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 5min, and the aqueous woodware paint is made in filtering.
Embodiment 2
Step 1, following components is weighed respectively by weight：Including 90 parts of organosilicon-modified acrylic micro emulsion, coalescents 6
Part, 0.8 part of nanometer anion powder, 1.0 parts of surface modifier wax emulsion, 2 parts of nitrogen phosphorus system water-soluble flame retardant, substrate wetting agents 0.5
Part, 0.6 part of wetting dispersing agent, 0.5 part of moistening flatting agent, 1 part of defoamer, 1 part of association type polyurethane thickener, 1 part of slip agent,
0.3 part of antimildew disinfectant, 15 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder and nitrogen phosphorus system water-soluble flame retardant, stir 15min；The weight of the defoamer wherein added is the 2/ of defoamer gross weight
3；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, stir 60min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 10min, and the aqueous woodware paint is made in filtering.
Embodiment 3
Step 1, following components is weighed respectively by weight：Including 45 parts of organosilicon-modified acrylic micro emulsion, coalescents 4
Part, 0.6 part of nanometer anion powder, 0.6 part of surface modifier wax emulsion, 1.0 parts of nitrogen phosphorus system water-soluble flame retardant, substrate wetting agents
0.2 part, 0.4 part of wetting dispersing agent, 0.2 part of moistening flatting agent, 0.5 part of defoamer, 0.3 part of association type polyurethane thickener increases
0.5 part of lubrication prescription, 0.15 part of antimildew disinfectant, 10 parts of color stuffing, 15 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder, nitrogen phosphorus system's water-soluble flame retardant and color stuffing, color stuffing are ground to fineness for less than 30 μm；The defoamer wherein added
Weight be defoamer gross weight 1/2；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, stir 50min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 7min, and the aqueous woodware paint is made in filtering.
Embodiment 4
Step 1, following components is weighed respectively by weight：Including 80 parts of organosilicon-modified acrylic micro emulsion, coalescents 6
Part, 0.7 part of nanometer anion powder, 0.8 part of surface modifier wax emulsion, 1.2 parts of nitrogen phosphorus system water-soluble flame retardant, substrate wetting agents
0.4 part, 0.6 part of wetting dispersing agent, 0.3 part of moistening flatting agent, 0.6 part of defoamer, 0.6 part of association type polyurethane thickener increases
0.7 part of lubrication prescription, 0.2 part of antimildew disinfectant, 0.2 part of propane diols, 0.1 part of ultra-violet absorber, 8 parts of color stuffing, deionized water 8
Part；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder, nitrogen phosphorus system's water-soluble flame retardant and color stuffing, color stuffing are ground to fineness for less than 30 μm；The defoamer wherein added
Weight be defoamer gross weight 1/3；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, antifreezing agent, ultra-violet absorber and face are filled out
Material, stirs 40min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 12min, and the aqueous woodware paint is made in filtering.
Embodiment 5
Step 1, following components is weighed respectively by weight：Including 90 parts of organosilicon-modified acrylic micro emulsion, coalescents 6
Part, 0.8 part of nanometer anion powder, 1.0 parts of surface modifier wax emulsion, 2 parts of nitrogen phosphorus system water-soluble flame retardant, substrate wetting agents 0.5
Part, 0.3 part of wetting dispersing agent, 0.5 part of moistening flatting agent, 1 part of defoamer, 1 part of association type polyurethane thickener, 1 part of slip agent,
0.3 part of antimildew disinfectant, 0.3 part of ethylene glycol, 0.1 part of ultra-violet absorber, 10 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nanometer is added and bears
Ion powder and nitrogen phosphorus system water-soluble flame retardant, stir 10min；The weight of the defoamer wherein added is the 3/ of defoamer gross weight
2；
Step 3：Organosilicon-modified acrylic micro emulsion, surface modifier wax breast are added in the mixed solution obtained into step 2
Liquid, coalescents, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, antifreezing agent, ultra-violet absorber stirring
60min；
Step 4：Continue addition association type polyurethane thickener and remaining froth breaking in the mixed solution that is obtained into step 3
Agent, stirs 15min, and the aqueous woodware paint is made in filtering.
A kind of aqueous woodware paint of the present invention has the following advantages：
1) the equal environmental protection of material that uses of the present invention, not using organic solvent, water paint be brushed to it is tasteless on woodenware,
Toxic and harmful gas will not be discharged, VOC content will not be damaged well below paint to environment and human body；
2) film-forming resin organosilicon-modified acrylic micro emulsion of the present invention, particle size is small and solid content is high, and filming performance is good,
More common acrylic emulsion, paint film has more excellent weatherability, water resistance, light shine, resistance to active oxygen, gloss retention, anti-
Pulverability, pollution resistance；
3) aqueous woodware paint of the invention is with health role.Contain negative ion powder in water paint, can forever discharge beneficial
Anion, the aqueous woodware paint of the present invention is brushed on furniture, germ and purification air can be killed, while can promote human body
Metabolism, improves body immunity, and dispelling fatigue improves sleep quality, has good therapeutic action to more than 30 kinds of diseases；
4) present invention, which has in good flame retardant effect, formula, adds water-soluble flame retardant, there is good protection to woodenware
Effect.
Preparation method of the present invention is simple, and condition is controllable, is adapted to industrialized production.
Claims (7)
1. a kind of aqueous woodware paint, it is characterised in that be made up of the component of following parts by weight：It is micro- including organosilicon-modified acrylic
It is newborn 10-90 parts, 2-6 parts of coalescents, 0.2-0.8 parts of nanometer anion powder, 0.2-1.0 parts of surface modifier wax emulsion, fire retardant
0.5-2 parts, 0.1-0.5 parts of substrate wetting agents, 0.1-0.6 parts of wetting dispersing agent, 0.1-0.5 parts of moistening flatting agent, defoamer
0.2-1 parts, 0.1-1 parts of association type polyurethane thickener, 0.1-1 parts of slip agent, 0.1-0.3 parts of antimildew disinfectant, deionized water
6-15 parts.
2. a kind of aqueous woodware paint according to claim 1, it is characterised in that also including antifreezing agent, ultra-violet absorber
And color stuffing, wherein the antifreezing agent is ethylene glycol or propane diols；The color stuffing is dispersed to fineness and is not more than 30 μm.
3. a kind of aqueous woodware paint according to claim 1 or 2, it is characterised in that the fire retardant is that nitrogen phosphorus system is water-soluble
Sex flame retardant.
4. a kind of preparation method of aqueous woodware paint, it is characterised in that comprise the following steps：
Step 1, following components is weighed respectively by weight：Including 10-90 parts of organosilicon-modified acrylic micro emulsion, coalescents 2-
6 parts, 0.2-0.8 parts of nanometer anion powder, 0.2-1.0 parts of surface modifier wax emulsion, 0.5-2 parts of fire retardant, substrate wetting agents
0.1-0.5 parts, 0.1-0.6 parts of wetting dispersing agent, 0.1-0.5 parts of moistening flatting agent, 0.2-1 parts of defoamer, associate type polyurethane
0.1-1 parts of thickener, 0.1-1 parts of slip agent, 0.1-0.3 parts of antimildew disinfectant, 6-15 parts of deionized water；
Step 2：Deionized water, wetting dispersing agent and part defoamer are put into container and stirred, nano-negative ion is added
Powder and fire retardant, stir 5min-15min；The weight of the defoamer wherein added is the 1/3-2/3 of defoamer gross weight；
Step 3：In the mixed solution obtained into step 2 add organosilicon-modified acrylic micro emulsion, surface modifier wax emulsion, into
Film auxiliary agent, substrate wetting agents, moistening flatting agent, slip agent, antimildew disinfectant, stir 30min-60min；
Step 4：Continue addition association type polyurethane thickener and remaining defoamer in the mixed solution that is obtained into step 3, stir
5min-10min is mixed, aqueous woodware paint is made in filtering.
5. a kind of preparation method of aqueous woodware paint as claimed in claim 4, it is characterised in that be also added with step 2
Color stuffing；The color stuffing is dispersed to fineness and is not more than 30 μm.
6. a kind of preparation method of aqueous woodware paint as claimed in claim 5, it is characterised in that in step 3 also added with anti-
Freeze agent and ultra-violet absorber, the antifreezing agent is ethylene glycol or propane diols.
7. according to a kind of preparation method of any described aqueous woodware paint in claim 4,5 or 6, it is characterised in that the step
Fire retardant in rapid 1 is nitrogen phosphorus system water-soluble flame retardant.