CN106278137A - A kind of marmite and preparation method thereof - Google Patents

A kind of marmite and preparation method thereof Download PDF

Info

Publication number
CN106278137A
CN106278137A CN201610613684.1A CN201610613684A CN106278137A CN 106278137 A CN106278137 A CN 106278137A CN 201610613684 A CN201610613684 A CN 201610613684A CN 106278137 A CN106278137 A CN 106278137A
Authority
CN
China
Prior art keywords
parts
mud
base substrate
marmite
glazing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201610613684.1A
Other languages
Chinese (zh)
Inventor
赵续鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANXI PINGDING LIANGJINGJING MARMITE Co Ltd
Original Assignee
SHANXI PINGDING LIANGJINGJING MARMITE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANXI PINGDING LIANGJINGJING MARMITE Co Ltd filed Critical SHANXI PINGDING LIANGJINGJING MARMITE Co Ltd
Priority to CN201610613684.1A priority Critical patent/CN106278137A/en
Publication of CN106278137A publication Critical patent/CN106278137A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to a kind of marmite and preparation method thereof, mainly solve existing marmite and have that heat-transfer effect is the best and technical problem not environmentally.The present invention is prepared from the following raw materials in parts by weight blank: Kaolin 40 55 parts, kieselguhr 10 15 parts, white clay 15 20 parts, Pulvis Talci 5 10 parts, spodumene 5 10 parts and loess 28 parts, without heavy metals such as any lead, cadmiums in dispensing, by experiment, determine that moil fineness is 0.026 0.03% so that inner surface of pot body is readily cleaned, good heat conduction effect, only at the external surface glazing of base substrate, inner surface not glazing, environmentally-friendly sanitary, and with low cost.

Description

A kind of marmite and preparation method thereof
Technical field
The invention belongs to sand container and preparation method thereof, be specifically related to a kind of marmite and preparation method thereof.
Background technology
Tradition marmite is the ceramic fitted in by raw materials such as the quartz not readily conducted heat, Anhydrite, clays, burns through high temperature System forms, and has aeration, adsorptivity, the features such as heat transfer is uniform, and heat radiation is slow.Due to processing technology and raw material problem, existing sand Pot exists that heat-transfer effect is the best and technical problem not environmentally.
Summary of the invention
Present invention aim to address that existing marmite exists that heat-transfer effect is the best and technical problem not environmentally, it is provided that a kind of Marmite and preparation method thereof.
For solving above-mentioned technical problem, the technical solution used in the present invention is:
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: Kaolin 40-55 part, kieselguhr 10-15 Part, white clay 15-20 part, Pulvis Talci 5-10 part, spodumene 5-10 part and loess 2-8 part.
A kind of method making described marmite, comprises the following steps:
1) dispensing: weigh Kaolin 40-55 part, kieselguhr 10-15 part, white clay 15-20 part, Pulvis Talci 5-10 part, lithium brightness Stone 5-10 part and loess 2-8 part, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 4-7 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to the programming rate of 4 DEG C/min 1250-1270 DEG C, and at a temperature of 1250-1270 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
The present invention uses above technical scheme, without heavy metals such as any lead, cadmiums in dispensing, by experiment, determines mud Fineness is 0.026-0.03% so that inner surface of pot body is readily cleaned, good heat conduction effect, only at the external surface glazing of base substrate, interior Surface not glazing, environmentally-friendly sanitary, and with low cost.
Detailed description of the invention
Embodiment 1
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: Kaolin 40 parts, kieselguhr 10 parts, white clay 15 parts, Pulvis Talci 5 parts, spodumene 5 parts and loess 2 parts.
A kind of method making marmite described in the present embodiment, comprises the following steps:
1) dispensing: weigh Kaolin 40 parts, kieselguhr 10 parts, white clay 15 parts, Pulvis Talci 5 parts, spodumene 5 parts and loess 2 Part, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 4 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1250 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1250 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
Embodiment 2
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: Kaolin 55 parts, kieselguhr 15 parts, white clay 20 parts, Pulvis Talci 10 parts, spodumene 10 parts and loess 8 parts.
A kind of method making marmite described in the present embodiment, comprises the following steps:
1) dispensing: weigh Kaolin 55 parts, kieselguhr 15 parts, white clay 20 parts, Pulvis Talci 10 parts, spodumene 10 parts and loess 8 parts, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 7 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1270 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1270 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
Embodiment 3
A kind of marmite, it is to be prepared from the following raw materials in parts by weight blank: Kaolin 46 parts, kieselguhr 13 parts, white clay 18 parts, Pulvis Talci 7 parts, spodumene 8 parts and loess 5 parts.
A kind of method making marmite described in the present embodiment, comprises the following steps:
1) dispensing: weigh Kaolin 46 parts, kieselguhr 13 parts, white clay 18 parts, Pulvis Talci 7 parts, spodumene 8 parts and loess 5 Part, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud by vacuum pugging device Section, and seal with plastic sheeting, old 6 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to aqueous Divide 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to containing Moisture less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1260 with the programming rate of 4 DEG C/min DEG C, and at a temperature of 1260 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.

Claims (2)

1. a marmite, it is characterised in that: it is to be prepared from the following raw materials in parts by weight blank: Kaolin 40-55 part, knaur Soil 10-15 part, white clay 15-20 part, Pulvis Talci 5-10 part, spodumene 5-10 part and loess 2-8 part.
2. the method making marmite described in claim 1, it is characterised in that: comprise the following steps:
1) dispensing: weigh Kaolin 40-55 part, kieselguhr 10-15 part, white clay 15-20 part, Pulvis Talci 5-10 part, spodumene 5- 10 parts and loess 2-8 part, and mix homogeneously；
2) mud processed: by step 1) dispensing put in ball mill, the water adding 80 parts grinds to form mud；
3) filter mud device is used by step 2) moisture content in the mud prepared leaches, and makes mud section by vacuum pugging device, and Seal with plastic sheeting, old 4-7 days, then make molding standby mud section by vacuum pugging device；
4) use molding rolling device that standby for molding mud section is made the base substrate of required form, and by body drying to moisture content 5%；
5) base substrate oral area is sealed, and at the external surface glazing of base substrate, open sealing, by the body drying of first-class glaze to moisture content Less than 3%；
6) fire: by step 5) base substrate after glazing is positioned in kiln, is warming up to 1250-with the programming rate of 4 DEG C/min 1270 DEG C, and at a temperature of 1250-1270 DEG C, it is incubated 80min, naturally cool to room temperature, kiln discharge.
CN201610613684.1A 2016-07-29 2016-07-29 A kind of marmite and preparation method thereof Withdrawn CN106278137A (en)