CN106277797A - A kind of processing technique of micro-crystal stone plate - Google Patents
A kind of processing technique of micro-crystal stone plate Download PDFInfo
- Publication number
- CN106277797A CN106277797A CN201510361989.3A CN201510361989A CN106277797A CN 106277797 A CN106277797 A CN 106277797A CN 201510361989 A CN201510361989 A CN 201510361989A CN 106277797 A CN106277797 A CN 106277797A
- Authority
- CN
- China
- Prior art keywords
- micro
- stone plate
- crystal stone
- shrend
- processing technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the processing technique of a kind of micro-crystal stone plate, relate to micro-crystal stone plate technical field, through raw material mixing, fusing, shrend, dry, sieve, die-filling, crystallization forming, the demoulding, post processing, prepare finished product micro-crystal stone plate.The processing technique of micro-crystal stone plate of the present invention, technological operation is simple, by to raw material mixing, fusing, shrend, dry, sieve, die-filling, crystallization forming, the demoulding, post processing, prepare finished product micro-crystal stone plate, the micro-crystal stone plate processed has the advantages that mechanical strength is big, toughness is strong, impact resistance is good, resistance to chemical corrosion is high, and has colour stable, bright, length in service life, the advantage of production cost.
Description
Technical field
The present invention relates to micro-crystal stone plate technical field, particularly relate to adding of a kind of micro-crystal stone plate
Work technique.
Background technology
Microlite is also called glass-ceramic clad plate, and it is high-new in architectural pottery field
Technical products, it with glittering and translucent, elegant and poised, naturally grow and change different imitative stone
Texture, painted level, the exterior decorative effect of superb craftsmanship, and the most contaminated,
Be readily cleaned, inherent excellent physical and chemical performance, the most also have the weather proofing more higher than stone material,
Against weather and favored by domestic and international high-end building materials market.Along with devitrified glass construction material
Appearance and expansion, glass-ceramic clad plate arises at the historic moment.It is devitrified glass and pottery
The plane composite material of sheet material, it is shown that many comprehensive advantages.Existing micro-crystal stone plate
Operating complexity in process of production, production efficiency is low, and the microlite produced exists face
The defect that color is unstable, service life is short.
Summary of the invention
The purpose of the present invention is for the defect problem of above-mentioned micro-crystal stone plate production and processing, it is provided that one
Planting the processing technique of micro-crystal stone plate, this processing technique is simple to operate, by raw material is mixed,
Fusing, shrend, dry, sieve, die-filling, crystallization forming, the demoulding, post processing, prepare into
Product micro-crystal stone plate, the micro-crystal stone plate processed has that mechanical strength is big, toughness is strong, resistance to
The feature that impact property is good, resistance to chemical corrosion is high, and it is fresh to have colour stable, color and luster
Bright, the advantage of length in service life, production cost.
For achieving the above object, the technical solution used in the present invention is:
The processing technique of a kind of micro-crystal stone plate, comprises the following steps:
1) raw material mixing: mine tailings are delivered to basin by ore slurry pump, calcium carbonate, quartz sand,
Borax, zinc oxide, brium carbonate and soda enter respective feed bin from raw material storage respectively, by certainly
Dynamic Ingredient Production Line controls to mix in each material proportion enters blender, wherein raw materials quality part,
Mine tailings 60-65 part, brium carbonate 2-3 part, calcium carbonate 20-22 part, quartz sand 4-5 part,
Borax 3-4 part, soda 2-3 part, zinc oxide 3-4 part；
2) fusing: after raw material is with certain proportioning mix homogeneously, enters glass furnace, warp
High-temperature fusion, forms liquid；
3) shrend: fusing stove liquid out enters in quenching device, by water spray, water
Rifle facility carries out shrend, and is controlled the size of shrend product by the exit of quenching device；
4) dry, sieve: dry in entering roller dehydrator after shrend particulate collection, warp
Screening machine controls particle diameter and obtains the microlite glass finished-product of different-grain diameter, carries out selling outside packaging, its
Remaining microlite glass enters in mould die-filling；
5) crystallization forming: after microlite glass loads mould, be contained on kiln car, enters crystallization
Kiln roasting, cooling and demolding after high-temperature calcination molding；
6) post processing: through polishing, cut, polishing cold treatment after micro-crystal stone plate shaping and demoulding
After obtain finished product micro-crystal stone plate, packaging is sold.
Further, mine tailings 63 parts, brium carbonate 3 parts, calcium carbonate 21 parts, quartz sand
4.5 parts, Borax 3.5 parts, soda 2 parts, zinc oxide 3 parts.
Further, the temperature of described glass furnace is 1500-1600 DEG C.
Further, the temperature of described crystallization kiln roasting is 1100-1200 DEG C.
Beneficial effects of the present invention: the processing technique of a kind of micro-crystal stone plate, this processing technique is grasped
Make simple, by raw material mixing, fusing, shrend, dry, sieve, die-filling, crystallization one-tenth
Type, the demoulding, post processing, prepare finished product micro-crystal stone plate, and the micro-crystal stone plate processed has
There is the feature that mechanical strength is big, toughness is strong, impact resistance is good, resistance to chemical corrosion is high,
And there is colour stable, bright, length in service life, the advantage of production cost.
Accompanying drawing explanation
Fig. 1 is the processing process figure of the present invention.
Detailed description of the invention
When being embodied as, in conjunction with Fig. 1 processing process figure.
Embodiment 1
The processing technique of a kind of micro-crystal stone plate, comprises the following steps:
1) raw material mixing: mine tailings are delivered to basin by ore slurry pump, calcium carbonate, quartz sand,
Borax, zinc oxide, brium carbonate and soda enter respective feed bin from raw material storage respectively, by certainly
Dynamic Ingredient Production Line controls to mix in each material proportion enters blender, wherein raw materials quality part,
Mine tailings 630kg, brium carbonate 30kg, calcium carbonate 210kg, quartz sand 45kg, Borax 35kg,
Soda 20kg, zinc oxide 30kg；
2) fusing: after raw material is with certain proportioning mix homogeneously, enters glass furnace, warp
1500 DEG C of high-temperature fusion, form liquid；
3) shrend: fusing stove liquid out enters in quenching device, by water spray, water
Rifle facility carries out shrend, and is controlled the size of shrend product by the exit of quenching device；
4) dry, sieve: dry in entering roller dehydrator after shrend particulate collection, warp
Screening machine controls particle diameter and obtains the microlite glass finished-product of different-grain diameter, carries out selling outside packaging, its
Remaining microlite glass enters in mould die-filling；
5) crystallization forming: after microlite glass loads mould, be contained on kiln car, enters crystallization
Kiln roasting, cooling and demolding after 1100 DEG C of high-temperature calcination molding；
6) post processing: through polishing, cut, polishing cold treatment after micro-crystal stone plate shaping and demoulding
After obtain finished product micro-crystal stone plate, packaging is sold.
Embodiment 2
The processing technique of a kind of micro-crystal stone plate, comprises the following steps:
1) raw material mixing: mine tailings are delivered to basin by ore slurry pump, calcium carbonate, quartz sand,
Borax, zinc oxide, brium carbonate and soda enter respective feed bin from raw material storage respectively, by certainly
Dynamic Ingredient Production Line controls to mix in each material proportion enters blender, wherein raw materials quality part,
Mine tailings 600kg, brium carbonate 30kg, calcium carbonate 220kg, quartz sand 40kg, Borax 40kg,
Soda 30kg, zinc oxide 40kg；
2) fusing: after raw material is with certain proportioning mix homogeneously, enters glass furnace, warp
1600 DEG C of high-temperature fusion, form liquid；
3) shrend: fusing stove liquid out enters in quenching device, by water spray, water
Rifle facility carries out shrend, and is controlled the size of shrend product by the exit of quenching device；
4) dry, sieve: dry in entering roller dehydrator after shrend particulate collection, warp
Screening machine controls particle diameter and obtains the microlite glass finished-product of different-grain diameter, carries out selling outside packaging, its
Remaining microlite glass enters in mould die-filling；
5) crystallization forming: after microlite glass loads mould, be contained on kiln car, enters crystallization
Kiln roasting, cooling and demolding after 1200 DEG C of high-temperature calcination molding；
6) post processing: through polishing, cut, polishing cold treatment after micro-crystal stone plate shaping and demoulding
After obtain finished product micro-crystal stone plate, packaging is sold.
Embodiment 3
The processing technique of a kind of micro-crystal stone plate, comprises the following steps:
1) raw material mixing: mine tailings are delivered to basin by ore slurry pump, calcium carbonate, quartz sand,
Borax, zinc oxide, brium carbonate and soda enter respective feed bin from raw material storage respectively, by certainly
Dynamic Ingredient Production Line controls to mix in each material proportion enters blender, wherein raw materials quality part,
Mine tailings 650kg, brium carbonate 20kg, calcium carbonate 200kg, quartz sand 50kg, Borax 30kg,
Soda 20kg, zinc oxide 30kg；
2) fusing: after raw material is with certain proportioning mix homogeneously, enters glass furnace, warp
1550 DEG C of high-temperature fusion, form liquid；
3) shrend: fusing stove liquid out enters in quenching device, by water spray, water
Rifle facility carries out shrend, and is controlled the size of shrend product by the exit of quenching device；
4) dry, sieve: dry in entering roller dehydrator after shrend particulate collection, warp
Screening machine controls particle diameter and obtains the microlite glass finished-product of different-grain diameter, carries out selling outside packaging, its
Remaining microlite glass enters in mould die-filling；
5) crystallization forming: after microlite glass loads mould, be contained on kiln car, enters crystallization
Kiln roasting, cooling and demolding after 1150 DEG C of high-temperature calcination molding；
6) post processing: through polishing, cut, polishing cold treatment after micro-crystal stone plate shaping and demoulding
After obtain finished product micro-crystal stone plate, packaging is sold.
The processing technique of a kind of micro-crystal stone plate, this processing technique is simple to operate, by raw material
Mixing, fusing, shrend, dry, sieve, die-filling, crystallization forming, the demoulding, post processing,
Preparing finished product micro-crystal stone plate, the micro-crystal stone plate processed has that mechanical strength is big, toughness
By force, impact resistance is good, resistance to chemical corrosion is high feature, and have colour stable,
Bright, length in service life, the advantage of production cost.
Embodiment described above is only to be described the preferred embodiment of the present invention, and
Non-the spirit and scope of the present invention are defined.In the premise without departing from design concept of the present invention
Under, various modification that technical scheme is made by this area ordinary person and improvement, all
Protection scope of the present invention should be dropped into.
Claims (4)
1. the processing technique of a micro-crystal stone plate, it is characterised in that comprise the following steps:
1) raw material mixing: mine tailings are delivered to basin by ore slurry pump, calcium carbonate, quartz sand,
Borax, zinc oxide, brium carbonate and soda enter respective feed bin from raw material storage respectively, by certainly
Dynamic Ingredient Production Line controls to mix in each material proportion enters blender, wherein raw materials quality part,
Mine tailings 60-65 part, brium carbonate 2-3 part, calcium carbonate 20-22 part, quartz sand 4-5 part,
Borax 3-4 part, soda 2-3 part, zinc oxide 3-4 part；
2) fusing: after raw material is with certain proportioning mix homogeneously, enters glass furnace, warp
High-temperature fusion, forms liquid；
3) shrend: fusing stove liquid out enters in quenching device, by water spray, water
Rifle facility carries out shrend, and is controlled the size of shrend product by the exit of quenching device；
4) dry, sieve: dry in entering roller dehydrator after shrend particulate collection, warp
Screening machine controls particle diameter and obtains the microlite glass finished-product of different-grain diameter, carries out selling outside packaging, its
Remaining microlite glass enters in mould die-filling；
5) crystallization forming: after microlite glass loads mould, be contained on kiln car, enters crystallization
Kiln roasting, cooling and demolding after high-temperature calcination molding；
6) post processing: through polishing, cut, polishing cold treatment after micro-crystal stone plate shaping and demoulding
After obtain finished product micro-crystal stone plate, packaging is sold.
2. according to the processing technique of a kind of micro-crystal stone plate described in claim 1, its feature
It is: described mine tailings 63 parts, brium carbonate 3 parts, calcium carbonate 21 parts, quartz sand 4.5 parts,
Borax 3.5 parts, soda 2 parts, zinc oxide 3 parts.
3. according to the processing technique of a kind of micro-crystal stone plate described in claim 1, its feature
It is: the temperature of described glass furnace is 1500-1600 DEG C.
4. according to the processing technique of a kind of micro-crystal stone plate described in claim 1, its feature
It is: the temperature of described crystallization kiln roasting is 1100-1200 DEG C.