CN106244228A - 一种焦化粗苯加氢脱硫工艺 - Google Patents
一种焦化粗苯加氢脱硫工艺 Download PDFInfo
- Publication number
- CN106244228A CN106244228A CN201610695510.4A CN201610695510A CN106244228A CN 106244228 A CN106244228 A CN 106244228A CN 201610695510 A CN201610695510 A CN 201610695510A CN 106244228 A CN106244228 A CN 106244228A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- fixed bed
- hydrodesulfurization
- hydrogen
- sapo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种焦化粗苯加氢脱硫工艺，焦化粗苯与氢气混合物从塔顶进入预反应器，预反应器中装填有NiMo催化剂，其反应温度为220‑230℃，加氢压力为3.2‑3.8MPa，预反应的产物进入固定床反应器，所述固定床反应器中装填有加氢脱硫催化剂，所述催化剂包括载体和活性组分；所述载体为合成骨架结构中掺入杂原子Cu2+的SAPO‑5；所述活性组分为氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的混合物；所述的催化剂还含有催化助剂，所述催化助剂为Cr2O3、ZrO2、CeO2、V2O5和NbOPO4的混合物；所述固定床反应器的反应条件为：反应温度为320‑380℃，氢气压力3.0‑3.6MPa，氢油体积比500‑800，体积空速1.5‑2h‑1；固定床加氢反应后的产物进入萃取蒸馏单元，得到芳烃。该工艺可以将焦化粗苯中的总硫含量降低到0.1ppm以下，能满足其广泛的用途。
Description
技术领域
本发明涉及一种加氢脱硫工艺，具体涉及一种焦化粗苯加氢脱硫工艺。
背景技术
焦化是煤炭加工的主要方式之一，通常也称之为煤的高温干馏，即由适合炼焦的烟煤，适当处理后，在焦炉内隔绝空气加热到950-1050℃，经过干燥、热解、烧融、粘结、固化和收缩等阶段最终制得焦炭。炼焦过程中析出的挥发物包括煤气、焦油、氨和粗苯等化学产品。另外，焦化过程中得到的煤焦油中也含有一定量的苯等芳烃。
焦化粗苯精制是以焦化粗苯为原料，经过物理或者化学等方法脱除其中含硫、含氮等有害物质，以便得到可作为原料使用的高纯度苯、甲苯、二甲苯等。目前，我国工业上主要采用酸洗法和加氢脱硫工艺对粗苯进行精制。
催化加氢法作为焦化粗苯化学脱硫方法，是在临氢条件下将噻吩转化成硫化氢和相应的烷烃而脱除，一般分两个步骤，第一步：预加氢反应，主要用常规的催化剂脱除焦化粗苯中的不稳定物质，也可以脱除部分含硫物质；第二步，主加氢反应，脱除焦化粗苯中噻吩、二硫化碳等主要硫化物和有机氮化物。粗苯加氢工艺根据催化反应温度分为高温加氢和低温加氢两种工艺。
高温催化加氢工艺中最典型就是莱托尔法，即Litol法，该工艺是在20世纪60年代由美国胡德利(Hondry)空气产品公司成功开发的一种高温粗苯加氢精制法，后来日本旭化成公司又对其进行了改进，形成了日本Litol高温、高压气相加氢技术。该法首先将粗苯在预分馏塔中分离为轻苯和重苯，轻苯经高压泵进入蒸发器与循环氢气混合后，芳烃蒸汽和氢气混合物从塔顶进入预反应器。该法的加氢条件为：预反应器温度为230℃，压力为5.7MPa，催化剂为CoMo催化剂；主反应器温度为压力为5l0MPa，催化剂为Cr系催化剂。预反应器是在较低温度下()把高温状态下容易聚合的苯乙烯等同系物进行加氢反应，防止其在主反应器内聚合，使催化剂活性降低，在两个主反应器内完成加氢裂解、脱烷基、脱硫等反应。由主反应器排出的油气经冷凝冷却系统，分离出的液体为加氢油，分离出的氢气和低分子烃类脱除H2S后，一部分送往加氢系统，一部分送往转化制氢系统制取氢气。由于Litol工艺可以将苯环上的烷基脱除，因此纯苯产率可以达到114％。
由于Litol法需要在高温高压下操作，又有氢脆(在高温高压下，氢气分解的氢原子渗透到钢材晶粒中，使钢材晶粒间的原子结合力降低，从而降低钢材的延伸率和断面收缩率)和氢腐蚀(在高温高压下，氢分子和氢原子慢慢渗透到钢材材质的缺陷处，聚集成分子缺陷后与周围含碳化合物发生加氢反应)，所以对设备要求要高，制造难度较大，需要从国外全套引进。20世纪90年代，我国的宝钢化工一期工程就曾全套引进日本的莱托尔法高温脱烷基加氢工艺，于1986年投产，年处理粗苯5万t，可以得到纯度99.9％、结晶点5.52℃：、全硫含量低于lppm、噻吩含量小于0.5ppm的特号纯苯。河南神马公司随后也全套引进了日本的莱托尔法高温脱烷基加氢工艺。Litol法理论产率91.53％，但从2004年实绩來看却只有88.96％。
低温加氢法主要包括三个关键单元：焦炉煤气变压吸附制纯氢(纯度大于99.9％)；催化加氢精制过程(预加氢和主加氢)；产品提纯过程(萃取或萃取蒸馏)。由于在焦化粗苯低温加氢工艺中主要得到的产品是芳香烃和非芳香烃，工业上很难直接通过常规的蒸馏方法将其分离出来，加入一定的萃取剂后(萃取剂要求不与其它组分形成共沸物且沸点较高)，可以明显地改变各组分在其中的溶解度，从而改变它们的相对挥发度和饱和蒸汽压，再通过蒸馏的方法就可以达到分离产品的作用，工艺上可以分为萃取蒸馏和液/液萃取。
萃取蒸馏加氢法理论产率为99.41％，但2004年实绩来看却只有98.30％。液/液萃取工艺中最具代表性的就是环丁砜法，其理论产率也在99％以上。但上述工艺方法得到的纯苯含硫量均在0.5ppm左右，这对芳烃产品的使用产生很大限制
因此如何提供一种加氢脱硫工艺，能有效将焦化粗苯产品的硫含量控制在0.1ppm以下，以满足其应用标准，是本领域面临的一个难题。
发明内容
本发明的目的在于提出一种焦化粗苯加氢脱硫工艺，该工艺可以将焦化粗苯中的总硫含量降低到0.1ppm以下，最低到0.05ppm，以满足产品的应用要求。
为达此目的，本发明采用以下技术方案：
一种焦化粗苯加氢脱硫工艺，焦化粗苯与氢气混合物从塔顶进入预反应器，预反应器中装填有NiMo催化剂，其反应温度为220-230℃，加氢压力为3.2-3.8MPa，其产物随后进入固定床反应器，所述固定床反应器中装填有加氢脱硫催化剂，所述催化剂包括载体和活性组分。
所述载体为合成骨架结构中掺入杂原子Cu2+的SAPO-5。
所述活性组分为氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的混合物。
所述的催化剂还含有催化助剂，所述催化助剂为Cr2O3、ZrO2、CeO2、V2O5和NbOPO4的混合物。
所述固定床反应器的反应条件为：反应温度为320-380℃，氢气压力3.0-3.6MPa，氢油体积比500-800，体积空速1.5-2h-1。
固定床加氢反应后的产物进入萃取蒸馏单元，得到芳烃。
经过检测，得到的芳烃中全硫含量低于0.1ppm，产品的纯度也大于99.9％。
需要说明的是，本发明采用的焦化粗苯加氢脱硫工艺中，预加氢反应采用常规设备及工艺，本发明对焦化粗苯加氢脱硫工艺的改进，更多的体现在主加氢反应的设计。
SAPO-5分子筛是磷酸硅铝(SAPO)系列分子筛中的一种，它的孔道系统是由六方对称性的四元环与六元环构成的十二元环构成的，具有大孔径结构，其孔径为0.8nm。SAPO-5分子筛酸性温和，并且具有微弱的可调节性，还具有阳离子交换能力。某种程度上，其物化性质不仅具有铝磷酸盐分子筛的特性，并且还类似于硅铝沸石的特性。由于其具有新型的晶体结构、良好的热稳定性和水热稳定性，在间二甲苯异构化和正己烷催化裂解等反应中具有广泛应用。但其用于加氢精制而不是加氢裂解领域，鲜见文献报道。
本发明经过在众多磷酸硅铝分子筛中，比如SAPO-11、SAPO-17、SAPO-20、SAPO-31、SAPO-34、SAPO-44、SAPO-46、SAPO-47等，逐一进行对比试验选择，发现只有SAPO-5能够达到本发明的发明目的，其他介孔材料都有这样那样的缺陷，在应用到本发明中时存在难以克服的技术困难，因此本发明选择将用于加氢裂化的SAPO-5改性转做用于加氢精制的载体基础。
发明人经过研究发现，对于影响磷酸硅铝分子筛性能的硅铝比、磷铝比，在本发明中，经改性之后，硅铝比和磷铝比的变化对加氢精制效果影响较小，因此本发明不再对硅铝比和磷铝比进行限定。为便于说明本发明，一般将其限定为摩尔比均小于1。
由于现有的SAPO-5分子筛催化温度高，且易导致原料加氢裂解，因此，本发明对其进行改性，以增加其催化活性，降低催化温度并使其适用于催化精制，减少加氢裂化。本发明对SAPO-5介孔分子筛改性的途径是：向成品的全硅SAPO-5介孔分子筛孔道内表面引入Cu2+，这种途径可以通过离子交换将Cu2+负载在SAPO-5的内表面，从而在整体上改善了SAPO-5介孔分子筛的催化活性、吸附以及热力学稳定性能等。
尽管对SAPO-5介孔分子筛进行改性的方法或途径很多，发明人发现，本发明的催化剂只能采用掺杂Cu2+的SAPO-5作为载体才能实现硫含量控制与辛烷值损失的平衡，发明人尝试了在SAPO-5中掺杂：Ca2+、Fe3+、Zn2+、Ti2+、Ga3+以及碱金属等产生阴离子表面中心的离子，发现都不能实现所述效果。尽管所述机理目前并不清楚，但这并不影响本发明的实施，发明人根据已知理论与实验证实，其与本发明的活性成分之间存在协同效应。
所述活性组分的总含量为载体SAPO-5重量的1％-15％，优选3-12％，进一步优选5-10％。例如，所述含量可以为2％、2.5％、3％、3.5％、4％、4.5％、5％、5.5％、6％、6.5％、7％、7.5％、8％、8.5％、9％、9.5％、10％、10.5％、11％、11.5％、12％、12.5％、13％、13.5％、14％、14.5％等。
本发明中，特别限定活性组分为氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的混合比例，发明人发现，不同的混合比例达到的效果完全不同。发明人发现，氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的混合比例(摩尔比)为1:(0.4-0.6):(0.28-0.45):(0.8-1.2)，只有控制氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的摩尔比在该范围内，才能够实现焦化粗苯中含硫量控制在0.1ppm以下。也就是说，本发明的四种活性组分只有在摩尔比为1:(0.4-0.6):(0.28-0.45):(0.8-1.2)时，才具备协同效应。除开该摩尔比范围之外，或者省略或者替换任意一种组分，都不能实现协同效应。
优选的，氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的摩尔比为1:(0.45-0.5):(0.35-0.45):(0.8-1.0)，进一步优选为1:(0.45-0.48):(0.4-0.45):(0.9-1.0)，最优选1:0.48:0.42:0.95。
本发明的目的之三在于提供所述催化剂的助催化剂。本发明所述的催化剂还含有催化助剂，所述催化助剂为Cr2O3、ZrO2、CeO2、V2O5和NbOPO4(磷酸铌)的混合物。
尽管在加氢精制特别是加氢脱硫领域，已经有成熟的催化助剂，比如P、F和B等，其用于调节载体的性质，减弱金属与载体间强的相互作用，改善催化剂的表面结构，提高金属的可还原性，促使活性组分还原为低价态，以提高催化剂的催化性能。但上述P、F和B催化助剂在应用与本发明的载体与活性组分时，针对高硫组分，其促进催化脱硫/精制的作用了了。
本发明经过在众多常用助催化剂组分，以及部分活性组分中进行遴选、复配等，最终发现采用Cr2O3、ZrO2、CeO2、V2O5和NbOPO4(磷酸铌)的混合物对本发明的催化剂促进作用明显，能显著提高其水热稳定性，并提高其防结焦失活能力，从而提高其使用寿命。
所述Cr2O3、ZrO2、CeO2、V2O5和NbOPO4之间没有固定的比例，也就是说，Cr2O3、ZrO2、CeO2、V2O5和NbOPO4每一种各自的含量达到有效量即可。优选的，本发明采用的Cr2O3、ZrO2、CeO2、V2O5和NbOPO4各自的含量均为(分别为)载体质量的1-7％，优选2-4％。
尽管本发明所述的催化助剂之间没有特定的比例要求，但每一种助剂必须能够达到有效量的要求，即能够起到催化助剂作用的含量，例如载体质量的1-7％。本发明在遴选过程中发现，省略或者替换所述助剂中的一种或几种，均达不到本发明的技术效果(提高水热稳定性，减少结焦提高使用寿命)，也就是说，本发明的催化助剂之间存在特定的配合关系。
事实上，本发明曾经尝试将催化助剂中的磷酸铌NbOPO4替换为五氧化二妮Nb2O5，发现尽管助剂中也引入了Nb，但其技术效果明显低于磷酸铌NbOPO4，其不仅水热稳定性稍差，其催化剂床层结焦相对快速，从而导致催化剂孔道堵塞，催化剂床层压降上升相对较快。本发明也曾尝试引入其他磷酸盐，但这种尝试尽管引入了磷酸根离子，但同样存在水热稳定性相对稍差，其催化剂床层结焦相对快速，从而导致催化剂孔道堵塞，催化剂床层压降上升相对较快。
尽管本发明引入催化助剂有如此之多的优势，但本发明必须说明的是，引入催化助剂仅仅是优选方案之一，即使不引入该催化助剂，也不影响本发明主要发明目的的实施。不引入本发明的催化助剂特别是磷酸铌，其相较于引入催化助剂的方案，其缺陷仅仅是相对的。即该缺陷是相对于引入催化助剂之后的缺陷，其相对于本发明之外的其他现有技术，本发明所提及的所有优势或者新特性仍然存在。该催化助剂不是解决本发明主要技术问题所不可或缺的技术手段，其只是对本发明技术方案的进一步优化，解决新的技术问题。
所述催化剂的制备方法可以采取常规的浸渍法以及其他替代方法，本领域技术人员可以根据其掌握的现有技术自由选择，本发明不再赘述。
优选的，所述固定床反应器的反应条件为：反应温度为340-360℃，氢气压力3.2-3.4MPa，氢油体积比600-800，体积空速1.5-1.8h-1。
优选的，所述固定床反应器包括1-5个催化剂床层，进一步优选2-3个催化剂床层。
本发明的焦化粗苯加氢脱硫工艺通过选取特定的催化剂，所述催化剂通过掺入杂原子Cu2+的SAPO-5作为载体，以及选取特定比例的氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC作为活性成分，所述的催化剂还含有催化助剂，所述催化助剂为Cr2O3、ZrO2、CeO2、V2O5和NbOPO4的混合物，使得该催化剂产生协同效应，对焦化粗苯的加氢脱硫能控制在总硫含量低于0.1ppm。
具体实施方式
本发明通过下述实施例对本发明的加氢脱硫工艺进行说明。
实施例1
通过浸渍法制备得到催化剂，载体为掺杂Cu2+的SAPO-5，Cu2+在SAPO-5中的掺杂量控制在载体质量的0.65％。所述活性组分氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的总含量为载体质量的10％，其摩尔比为1:0.4:0.3:0.8。
将所述催化剂装填入固定床反应器，所述反应器的反应管由内径50mm的不锈钢制成，催化剂床层温度用UGU808型温控表测量，原材料轻质油由北京卫星制造厂制造的双柱塞微量泵连续输送，氢气由高压气瓶供给并用北京七星华创D07-11A/ZM气体质量流量计控制流速，催化剂装填量为2kg。
焦化粗苯与氢气混合物从塔顶进入预反应器，预反应器中装填有NiMo催化剂，其反应温度为230℃，加氢压力为3.5MPa，其产物随后进入所述固定床反应器。控制主反应条件为：反应温度为340℃，氢气压力3.4MPa，氢油体积比650，体积空速1.5h-1。得到的产物随后进入萃取蒸馏单元，萃取溶剂采用环丁砜，萃取温度控制在100℃，萃取压力控制在200kPa。
测试最终的产品，其总硫含量降低到0.07ppm。
实施例2
通过浸渍法制备得到催化剂，载体为掺杂Cu2+的SAPO-5，Cu2+在SAPO-5中的掺杂量控制在载体质量的0.7％。所述活性组分氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的总含量为载体质量的10％，其摩尔比为1:0.6:0.45):1.2。
其余条件与实施例1相同。
测试最终的产品，其总硫含量降低到0.06ppm。
对比例1
将实施例1的载体替换为γ-Al2O3，其余条件不变。
测试最终的产品，其总硫含量为10ppm。
对比例2
将实施例1的载体替换为未掺杂的SAPO-5，其余条件不变。
测试最终的产品，其总硫含量为8ppm。
对比例3
将实施例1的Cu2+替换为Zn2+，其余条件不变。
测试最终的产品，其总硫含量为12ppm。
对比例4
将实施例1中的Cu2+在SAPO-5中的掺杂量控制在载体质量的0.5％，其余条件不变。
测试最终的产品，其总硫含量为16ppm。
对比例5
将实施例1中的Cu2+在SAPO-5中的掺杂量控制在载体质量的0.8％，其余条件不变。
测试最终的产品，其总硫含量为12ppm。
实施例1与对比例1-5表明，本申请采用的特定含量范围和特定负载金属离子的SAPO-5载体，当替换为本领域的其他已知载体时，或者载体相同但Cu2+掺杂量不同时，均达不到本发明的技术效果，因此本发明的特定含量范围的Cu2+掺杂SAPO-5载体与催化剂其他组分之间具备协同效应，所述加氢脱硫工艺产生了预料不到的技术效果。
对比例6
省略实施例1中的MO2N，其余条件不变。
测试最终的产品，其总硫含量为9ppm。
对比例7
省略实施例1中的WC，其余条件不变。
测试最终的产品，其总硫含量为14ppm。
上述实施例及对比例6-7说明，本发明的加氢脱硫工艺的催化剂几种活性组分之间存在特定的联系，省略或替换其中一种或几种，都不能达到本申请的特定效果，证明其产生了协同效应。
实施例3
催化剂中含有催化助剂Cr2O3、ZrO2、CeO2、V2O5和NbOPO4，其含量分别为1％、2％、1.5％、1％和3％，其余与实施例1相同。
测试最终的产品，其使用3个月后，催化剂床层压降无任何变化，相较于同样使用时间实施例1的催化剂床层压降减少13.6％。
对比例8
相较于实施例3，将其中的NbOPO4省略，其余条件相同。
测试最终的产品，其使用3个月后，催化剂床层压降升高，相较于同样使用时间实施例1的催化剂床层压降只减少3.5％。
对比例9
相较于实施例3，将其中的CeO2省略，其余条件相同。
测试最终的产品，其使用3个月后，催化剂床层压降升高，相较于同样使用时间实施例1的催化剂床层压降只减少2.3％。
实施例3与对比例8-9表明，本发明的催化助剂之间存在协同关系，当省略或替换其中一个或几个组分时，都不能达到本发明加入催化助剂时的减少结焦从而阻止催化剂床层压降升高的技术效果。即，其验证了本发明的催化助剂能够提高所述催化剂的使用寿命，而其他催化助剂效果不如该特定催化助剂。
申请人声明，本发明通过上述实施例来说明本发明的工艺，但本发明并不局限于上述工艺，即不意味着本发明必须依赖上述详细催化剂才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
Claims (7)
1.一种焦化粗苯加氢脱硫工艺，其特征在于，焦化粗苯与氢气混合物从塔顶进入预反应器，预反应器中装填有NiMo催化剂，其反应温度为220-230℃，加氢压力为3.2-3.8MPa，预反应的产物进入固定床反应器，所述固定床反应器中装填有加氢脱硫催化剂，所述催化剂包括载体和活性组分；所述载体为合成骨架结构中掺入杂原子Cu2+的SAPO-5；所述活性组分为氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的混合物；所述的催化剂还含有催化助剂，所述催化助剂为Cr2O3、ZrO2、CeO2、V2O5和NbOPO4的混合物；所述固定床反应器的反应条件为：反应温度为320-380℃，氢气压力3.0-3.6MPa，氢油体积比500-800，体积空速1.5-2h-1；固定床加氢反应后的产物进入萃取蒸馏单元，得到芳烃。
2.如权利要求1所述的加氢脱硫工艺，其特征在于，杂原子Cu2+的掺杂量为SAPO-5重量的0.63％-0.72％。
3.如权利要求1所述的加氢脱硫工艺，其特征在于，所述活性组分的总含量为载体SAPO-5重量的3-12％，优选5-10％。
4.如权利要求1所述的加氢脱硫工艺，其特征在于，氮化二钼MO2N、氮化钨W2N、碳化钼Mo2C和碳化钨WC的摩尔比为1:(0.45-0.5):(0.35-0.45):(0.8-1.0)，进一步优选为1:(0.45-0.48):(0.4-0.45):(0.9-1.0)，最优选1:0.48:0.42:0.95。
5.如权利要求1所述的加氢脱硫工艺，其特征在于，所述固定床反应器的反应条件为：反应温度为340-360℃，氢气压力3.2-3.4MPa，氢油体积比600-800，体积空速1.5-1.8h-1。
6.如权利要求1所述的加氢脱硫工艺，其特征在于，所述固定床反应器包括1-5个催化剂床层，优选包括2-3个催化剂床层。
7.如权利要求1所述的加氢脱硫工艺，其特征在于，Cr2O3、ZrO2、CeO2、V2O5和NbOPO4各自的含量分别为载体质量的1-7％，优选2-4％。