CN106243671B - 硅藻土百叶窗片及其制备方法 - Google Patents
硅藻土百叶窗片及其制备方法 Download PDFInfo
- Publication number
- CN106243671B CN106243671B CN201610715442.3A CN201610715442A CN106243671B CN 106243671 B CN106243671 B CN 106243671B CN 201610715442 A CN201610715442 A CN 201610715442A CN 106243671 B CN106243671 B CN 106243671B
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- diatomite
- louver
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
硅藻土百叶窗片及其制备方法，属于百叶窗技术领域。解决了现有技术中木材类百叶窗价格昂贵，PVC类百叶窗易变形、易燃烧、易老化、使用寿命短，废弃后不可降解造成污染的问题。该百叶窗片的材料包括100重量份硅藻土、100‑120重量份聚碳酸亚丙酯、4‑6重量份阻燃剂、3‑5重量份环氧大豆油、2‑4重量份蒙脱土、2‑4重量份木质素、1‑2重量份碳酸钙、0.5‑1重量份主抗氧剂、0.1‑0.3重量份辅助抗氧剂和1‑3重量份紫外线吸收剂。该百叶窗片绿色环保，既不释放污染物，又能吸附有害气体，废弃后可降解，且阻燃、不易变形，抗紫外线辐射、热稳定性和力学性能优异，耐久性好，使用寿命长。
Description
技术领域
本发明属于百叶窗技术领域，具体涉及一种硅藻土百叶窗片及其制备方法。
背景技术
随着国民经济的快速发展与人民物质生活水平的逐步提高，室内装修日益普及。人一生中有三分之二时间在室内度过，现代人生活和工作在室内环境中的时间已达到全天的80％-90％，因此室内环境质量的好坏直接影响人们的身体健康。装修耗材的使用不当所引起的室内空气污染日趋严重，最常见的有毒气体污染包括甲醛、苯系物、氨气、氡气以及挥发性有机物等，这五种有毒气体和有害物质被称为居室装修中的“5大隐形杀手”。其中，甲醛对人体的危害最为严重，被世界卫生组织确定为致癌和致畸形物质，是公认的变态反应源，也是潜在的强致突变物之一。如果能够使装修材料既不释放有毒气体，又具备除去有毒气体的功能，将对改善室内环境有突出效果。
百叶窗是窗子的一种，能够方便的调节光线的强弱，是现代家居装饰的常用材料。目前，市场上供应的百叶窗的叶片所使用的材料有木材和PVC材料。由于木材价格昂贵，因此PVC材料使用越来越多，但是，PVC材料制备的百叶窗叶片存在易腐蚀、易变形、易燃烧、易老化、使用寿命短，废弃后不可降解，对环境造成严重污染等缺陷。
发明内容
本发明的目的是解决现有技术中木材类百叶窗价格昂贵，PVC类百叶窗易变形、易燃烧、易老化、使用寿命短，废弃后不可降解造成污染的问题，提供一种硅藻土百叶窗片及其制备方法。
硅藻土百叶窗片，该百叶窗片的材料包括100重量份的硅藻土、100-120重量份的聚碳酸亚丙酯(PPC)、4-6重量份的阻燃剂、3-5重量份的环氧大豆油、2-4重量份的蒙脱土、2-4重量份的木质素、1-2重量份的碳酸钙、0.5-1重量份的主抗氧剂、0.1-0.3重量份的辅助抗氧剂和1-3重量份的紫外线吸收剂；
所述主抗氧剂为抗氧剂1010、抗氧剂1098、抗氧剂1076中的一种或多种按任意比例的混合；
所述辅助抗氧剂为抗氧剂168、抗氧剂626和抗氧剂618中的一种或多种按任意比例的混合。
优选的是，所述紫外线吸收剂为UV944、UV324、UV-770中的一种或多种按任意比例的混合。
优选的是，所述阻燃剂为聚磷酸铵、三聚氰胺中的一种或两种按任意比例的混合。
优选的是，所述硅藻土的粒径为800-1000目。
优选的是，所述蒙脱土的粒径为600-800目。
优选的是，所述碳酸钙的粒径为600-800目。
优选的是，所述百叶窗片的材料还包括1-3重量份的色粉。
上述硅藻土百叶窗片的制备方法：是按重量份配比，将原料加入混合搅拌机中，搅拌混合均匀，得到混合物料，然后将混合物料加入螺杆挤出机挤出造粒，得到粒料，再将粒料送入押出机中，得到片材，压纹，得到硅藻土百叶窗片。
优选的是，所述螺杆挤出机的温度为170-180℃。
与现有技术相比，本发明的有益效果：
本发明的硅藻土百叶窗片绿色环保，既不释放污染物，又能吸附空气中的有害物质，净化空气，即便使用废弃后，也可以降解为小分子，不会对环境造成永久伤害；
本发明的硅藻土百叶窗片阻燃，不易变形，抗紫外线辐射、热稳定性和力学性能优异，耐久性好，使用寿命长，成本低。
具体实施方式
以下结合实施例进一步说明本发明。
实施例1
硅藻土百叶窗片，该百叶窗片的材料由100重量份的硅藻土(800目)、100重量份的PPC、4重量份的聚磷酸铵、3重量份的环氧大豆油、2重量份的蒙脱土(800目)、2重量份的木质素、1重量份的碳酸钙(800目)、0.5重量份的抗氧剂1010、0.1重量份的抗氧剂168和1重量份的UV944组成。
上述硅藻土百叶窗片的制备方法：是按重量份配比，将原料加入混合搅拌机中，搅拌混合均匀，然后采用双螺杆挤出机挤出造粒，得到粒料，再将粒料送入押出机中，押出长条片体，压纹，得到硅藻土百叶窗片，螺杆挤出机的温度：一区170℃，二区为175℃，三区175℃，四区175℃，五区180℃，六区180℃，七区为175-180℃。
对实施例1得到的硅藻土百叶窗片进行性能检测，检测结果如表1所示。
实施例2
硅藻土百叶窗片，该百叶窗片的材料由100重量份的硅藻土(1000目)、120重量份的PPC、5重量份的聚磷酸铵、1重量份的三聚氰胺、5重量份的环氧大豆油、4重量份的蒙脱土(600目)、4重量份的木质素、1.5重量份的碳酸钙(700目)、1重量份的抗氧剂1076、0.2重量份的抗氧剂618、1.5重量份的UV324和3重量份的色粉(蓝色)。
上述硅藻土百叶窗片的制备方法：是按重量份配比，将原料加入混合搅拌机中，搅拌混合均匀，然后采用双螺杆挤出机挤出造粒，得到粒料，再将粒料送入押出机中，押出长条片体，压纹，得到硅藻土百叶窗片，螺杆挤出机的温度:一区170℃，二区为175℃，三区175℃，四区175℃，五区180℃，六区180℃，七区为175-180℃。
对实施例2得到的硅藻土百叶窗片进行检测，检测结果如表1所示。
实施例3
硅藻土百叶窗片，该百叶窗片的材料由100重量份的硅藻土(1000目)、105重量份的PPC、4.5重量份的聚磷酸铵、4重量份的环氧大豆油、4重量份的蒙脱土(700目)、3重量份的木质素、1.5重量份的碳酸钙(80目)、1重量份的抗氧剂1076、0.3重量份的抗氧剂618和3重量份的UV324。
上述硅藻土百叶窗片的制备方法：是按重量份配比，将原料加入混合搅拌机中，搅拌混合均匀，然后采用双螺杆挤出机挤出造粒，得到粒料，再将粒料送入押出机中，押出长条片体，压纹，得到硅藻土百叶窗片，螺杆挤出机的温度:一区170℃，二区为175℃，三区175℃，四区175℃，五区180℃，六区180℃，七区为175-180℃。
对实施例3得到的硅藻土百叶窗片进行检测，检测结果如表1所示。
表1实施例1-3的硅藻土百叶窗片的性能
其中，甲醛吸附率的检测方法是在1m3的密闭玻璃箱内放入盛有3uL甲醛的培养皿和300g硅藻土百叶窗片样品24h，箱内甲醛气体初始浓度0.7mg/m'S。热分解温度采用热重分析。拉伸性能采用GB/T1447检测。抗紫外线辐射的检测方法是采用UV-B型荧光紫外线灯连续照射样品500h后，观察样品被照射的表面。
Claims (9)
1.硅藻土百叶窗片，其特征在于，该百叶窗片的材料包括100重量份的硅藻土、100-120重量份的聚碳酸亚丙酯、4-6重量份的阻燃剂、3-5重量份的环氧大豆油、2-4重量份的蒙脱土、2-4重量份的木质素、1-2重量份的碳酸钙、0.5-1重量份的主抗氧剂、0.1-0.3重量份辅助抗氧剂和1-3重量份的紫外线吸收剂；
所述主抗氧剂为抗氧剂1010、抗氧剂1098、抗氧剂1076中的一种或多种按任意比例的混合；
所述辅助抗氧剂为抗氧剂168、抗氧剂626和抗氧剂618中的一种或多种按任意比例的混合。
2.根据权利要求1所述的硅藻土百叶窗片，其特征在于，所述紫外线吸收剂为UV944、UV324、UV-770中的一种或多种按任意比例的混合。
3.根据权利要求1所述的硅藻土百叶窗片，其特征在于，所述阻燃剂为聚磷酸铵、三聚氰胺中的一种或两种按任意比例的混合。
4.根据权利要求1所述的硅藻土百叶窗片，其特征在于，所述硅藻土的粒径为800-1000目。
5.根据权利要求1所述的硅藻土百叶窗片，其特征在于，所述蒙脱土的粒径为600-800目。
6.根据权利要求1所述的硅藻土百叶窗片，其特征在于，所述碳酸钙的粒径为600-800目。
7.根据权利要求1所述的硅藻土百叶窗片，其特征在于，所述百叶窗片的材料还包括1-3重量份的色粉。
8.权利要求1-7任何一项所述硅藻土百叶窗片的制备方法，其特征在于，按重量份配比，将原料加入混合搅拌机中，搅拌混合均匀，得到混合物料，然后将混合物料加入螺杆挤出机挤出造粒，得到粒料，再将粒料送入押出机中，得到片材，压纹，得到硅藻土百叶窗片。
9.根据权利要求8所述的硅藻土百叶窗片的制备方法，其特征在于，所述螺杆挤出机的温度为170-180℃。