CN106242461A - A kind of nanometer stony edema mill wall covering and construction method thereof - Google Patents
A kind of nanometer stony edema mill wall covering and construction method thereof Download PDFInfo
- Publication number
- CN106242461A CN106242461A CN201610550962.3A CN201610550962A CN106242461A CN 106242461 A CN106242461 A CN 106242461A CN 201610550962 A CN201610550962 A CN 201610550962A CN 106242461 A CN106242461 A CN 106242461A
- Authority
- CN
- China
- Prior art keywords
- nanometer
- wall covering
- metope
- stony edema
- mill wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of nanometer stony edema mill wall covering, including the raw material of following parts by weight: half-H 2 O calcium sulphate 30% 40%, titanium dioxide 3% 5%, sierozem power 35% 50%, calcium carbonate 8% 15%, redispersable latex powder 0.2% 1%, hydroxypropyl methyl cellulose 0.4% 1.5%, silicon dioxide 0.5% 1%, white cement 1% 5%, nanometer stone 0.2 0.5%, Gypsum Fibrosum retardant 0.2%～2%.Using nanometer stony edema of the present invention to grind wall covering, even if being polished off by outermost layer, also not interfering with hardness, resistance to water and breathability that metope is overall；Overcome the imitative porcelain of tradition and emulsion paint water proofing property is poor, the shortcoming that hardness is relatively low.After using nanometer stony edema of the present invention mill wall covering can metope is smooth, scrubbing resistance and have breathability, nanometer stony edema the most of the present invention mill wall covering environmental protection, health, without harmful substance.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of nanometer stony edema mill wall covering and construction method thereof.
Background technology
The most traditional inner, external wall coating mainly includes imitative porcelain, emulsion paint and wall finiss, and imitative porcelain is that one adds glue
Putty, tripolycyanamide and formaldehyde process, be typically used as coating, high be dried after form hard shelly, surface light
Sliding exquisiteness, slightly gloss, as the surface of porcelain, therefore gain the name, but melamine can be discharged in the environment of high temperature or acidity
Amine, and its surface the most easily produces the closeest fine cracks, affects attractive in appearance；Emulsion paint is latex paint
It is commonly called as, is the big class synthetic resin emulsion coating of with acrylate copolymer emulsion as representative.Emulsion paint is water-dispersible paint,
It is with synthetic resin emulsion as base material, and filler adds the coating that various auxiliary agent refines after grinding distribution.Emulsion paint
Possessed the many merits different from conventional wall coating materials, but emulsion paint there is loss of properties on aging, poor stability, be coated with
Brush of long duration after, easily cause and come off, deform, water resistance is poor, seepage, mouldy phenomenon easily occurs；And its composition contains
There are substantial amounts of Organic substance, especially formaldehyde, not only pollute environment, and health is worked the mischief, no matter be imitative simultaneously
The construction method of porcelain, emulsion paint or wall finiss is all at external coating, so surface thickness is the most relatively thin, hardness is the most relatively low, uses
Water sand tip-tap grinds off surface layer will lose effect, it is impossible to fully meet current needs.Therefore a kind of scene water is provided to adjust
Pairing human body and needs environmentally friendly, free from environmental pollution, that hardness is high coating becomes market.
Summary of the invention
The invention provides a kind of nanometer stony edema mill wall covering and construction method thereof, to solve above-mentioned technical problem.
In order to achieve the above object, the technical scheme is that and be achieved in that: a kind of nanometer stony edema mill wall covering,
Raw material including following parts by weight: half-H 2 O calcium sulphate 30%-40%, titanium dioxide 3%-5%, sierozem power 35%-50%, carbonic acid
Calcium 8%-15%, redispersable latex powder 0.2%-1%, hydroxypropyl methyl cellulose 0.4%-1.5%, silicon dioxide 0.5%-
1%, white cement 1%-5%, nanometer stone 0.2-0.5%, Gypsum Fibrosum retardant 0.2%～2%.
Further, including the raw material of following parts by weight: half-H 2 O calcium sulphate 32%, titanium dioxide 5%, sierozem power 44%,
Calcium carbonate 11%, redispersable latex powder 0.8%, hydroxypropyl methyl cellulose 1%, silicon dioxide 0.8%, white cement 4%, receive
Rice stone 0.4%, Gypsum Fibrosum retardant 1%.
Further, including the raw material of following parts by weight: half-H 2 O calcium sulphate 40%, titanium dioxide 4%, sierozem power 35%,
Calcium carbonate 13%, redispersable latex powder 1%, hydroxypropyl methyl cellulose 1.5%, silica 1 %, white cement 2%, nanometer
Stone 0.5%, Gypsum Fibrosum retardant 2%.
Further, including the raw material of following parts by weight: half-H 2 O calcium sulphate 30%, titanium dioxide 3%, sierozem power 47%,
Calcium carbonate 12%, redispersable latex powder 0.2%, hydroxypropyl methyl cellulose 0.8%, silica 1 %, white cement 4%, receive
Rice stone 0.5%, Gypsum Fibrosum retardant 1.5%.
The construction method of a kind of above-mentioned nanometer stony edema mill wall covering, comprises the following steps:
(1) this nanometer stony edema mill wall covering is stirred into thick shape coating with water according to the ratio of 100:40；
(2) with the thick shape coating in step (1) metope criticized and scrape 2～3 times；
With water, metope is drenched maintenance after (3) 12 hours, after 12 hours, metope is polished smooth.
Further, after 15～30 days, wall covering hardness reaches optimum.
Further, in step (1), this nanometer stony edema mill wall covering is mixed according to the ratio of 100:40 with water
After, stir, wait 5～10 minutes, after making each raw material in this nanometer stony edema mill wall covering fully react, be again stirring for
To without dry powder or dough.
Further, in step (3), using vibrating ball-mill to be polished smooth by metope, vibrating ball-mill uses 800-1000 purpose
White sand paper.
The construction method of a kind of above-mentioned nanometer stony edema mill wall covering, comprises the following steps:
(1) with water-proof putty powder metope criticized and scrape 2～3 times, repeat 2～3 times；
(2) sand paper is used to be polished flat by the metope after step (1)；
(3) water is used to be cleaned by the dust on the metope after step (2)；
(4) this nanometer stony edema mill wall covering is stirred into thick shape coating with water according to the ratio of 100:40；
(5) method of being scraped by the metope crosspoint tip screwdriver after step (3) by the thick shape coating in step (4) is floating, and 12 is little
Metope is drenched maintenance by Shi Houyong water, is polished smooth by metope after 12 hours.
Compared with prior art, it is an advantage of the current invention that: nanometer stony edema of the present invention mill wall covering is that a kind of innovation is changed
The novel nano technology universal lacquer in generation, strengthens metope porcelain handle effect, the water mill polishing hard anti-scratch of metope smooth surface
Wash, anti-soil, anti-scratch, alkali resistant, the environment-friendly materials of superpower color inhibition.Half-H 2 O calcium sulphate has big excellent of fast solidifying, porosity
Point, makes have ventilative feature after wall on this invention nanometer stony edema mill wall covering, and titanium dioxide is B101 titanium dioxide, has nothing
Malicious, harmless feature, redispersable latex powder composition, increase caking property and the cohesiveness of coating, hydroxypropyl methyl cellulose is made
For adhesive, improving smear and extend operable time, its water retention property makes the coating will not be because of dry too fast after smearing
Be full of cracks, strengthens intensity after hardening, and sierozem power main component is Ca (OH)2, CaO and a small amount of CaCO3Mixture, Ca (OH)2Deposit
After the effect making sierozem power have sterilization, upper wall, Ca (OH)2Hard carbon can be formed with the carbon dioxide reaction in air
Acid calcium, makes metope harder, and nanometer stone enhances the hardness on nanometer stony edema of the present invention mill wall covering after wall, makes whole metope
The hardness of each degree of depth all reaches optimum.Using nanometer stony edema of the present invention to grind wall covering, its intensity is also not only present in surface,
Even if surface layer water sand tip-tap is ground off, do not interfere with the overall effect of metope, smoothness, hardness, resistance to water yet and breathe freely
Property, on nanometer stony edema of the present invention mill wall covering, the hardness of whole thickness after wall all equals to marmorean hardness, metope hard
Degree can't weaken along with the lower thickness of metope；Overcome the imitative porcelain of tradition and emulsion paint water proofing property is poor, relatively low the lacking of hardness
Point.After using nanometer stony edema of the present invention mill wall covering can metope is smooth, scrubbing resistance and have breathability, nanometer the most of the present invention
Stony edema mill wall covering environmental protection, health, without harmful substance.
Detailed description of the invention
The technical scheme of various embodiments of the present invention will be carried out clear, complete description below, it is clear that described enforcement
Example is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, this area is general
All other embodiments that logical technical staff is obtained on the premise of not making creative work, broadly fall into the present invention and are protected
The scope protected.
Below by specific embodiment, the present invention is described in further detail.
Embodiment 1
The embodiment of the present invention 1 relates to a kind of nanometer stony edema mill wall covering, including the raw material of following parts by weight: half water sulfur
Acid calcium 30%-40%, titanium dioxide 3%-5%, sierozem power 35%-50%, calcium carbonate 8%-15%, redispersable latex powder
0.2%-1%, hydroxypropyl methyl cellulose 0.4%-1.5%, silicon dioxide 0.5%-1%, white cement 1%-5%, nanometer stone
0.2-0.5%, Gypsum Fibrosum retardant 0.2%～2%.
The advantage that half-H 2 O calcium sulphate water stone cream has fast solidifying, porosity is big, makes this invention nanometer stony edema grind metope
Having ventilative feature on coating after wall, titanium dioxide is B101 titanium dioxide, have nontoxic, harmless, brighten acidproof feature, can be again
Dispersed latex meal component, increases caking property and the cohesiveness of coating, and hydroxypropyl methyl cellulose, as adhesive, improves smear
With prolongation operable time, its water retention property makes coating will not strengthen intensity after hardening because of so dry that to chap too soon after smearing,
Sierozem power main component is Ca (OH)2, CaO and a small amount of CaCO3Mixture, Ca (OH)2Existence make sierozem power have sterilization
Effect, after upper wall, Ca (OH)2Hard calcium carbonate can be formed with the carbon dioxide reaction in air, make metope harder, receive
Meter Shi enhances the hardness on nanometer stony edema of the present invention mill wall covering after wall, makes the hardness of whole each degree of depth of metope all reach
Optimum.Using nanometer stony edema of the present invention to grind wall covering, even if being polished off by outermost layer, also not interfering with the hard of metope entirety
Degree, resistance to water and breathability；Overcome the imitative porcelain of tradition and emulsion paint water proofing property is poor, scrubbing resistance, hardness is not relatively low shortcoming.Use
Nanometer stony edema of the present invention mill wall covering, its intensity is also not only present in surface, even if surface layer water sand tip-tap being ground off, also
Do not interfere with effect, smoothness, hardness, resistance to water and breathability that metope is overall, on nanometer stony edema of the present invention mill wall covering
The hardness of the whole thickness after wall all equals to marmorean hardness, and the hardness of metope can't subtract along with the lower thickness of metope
Weak；Overcome the imitative porcelain of tradition and emulsion paint water proofing property is poor, the shortcoming that hardness is relatively low.Nanometer stony edema of the present invention is used to grind wall covering
After can metope is smooth, scrubbing resistance and have breathability, nanometer stony edema the most of the present invention mill wall covering environmental protection, health, do not contain
Pest matter.
The construction method of the nanometer stony edema mill wall covering of a kind of the present embodiment, comprises the following steps:
(1) this nanometer stony edema mill wall covering is stirred into thick shape coating with water according to the ratio of 100:40；
(2) with the thick shape coating in step (1) metope criticized and scrape 2～3 times；
With water, metope is drenched maintenance after (3) 12 hours, after 12 hours, metope is polished smooth.
Preferably, after 15～30 days, wall covering hardness reaches optimum.Wall on nanometer stony edema of the present invention mill wall covering
After, Ca (OH) in the sierozem power in its raw material2Hard calcium carbonate can be formed with the carbon dioxide reaction in air, make metope more
Hard, As time goes on, with the Ca (OH) of carbon dioxide reaction2The most, its calcium carbonate generated is the most, makes metope more
Ca (OH) firmly, after 15～30 days, in raw material2Carbon dioxide reaction fully and in air, makes the hardness of metope reach
Excellent, equal to marmorean hardness, i.e. use hard object to draw metope, also only can leave trace.
Preferably, in step (1), after this nanometer stony edema mill wall covering is mixed according to the ratio of 100:40 with water,
Stir, wait 5～10 minutes, make this nanometer stony edema mill wall covering in each raw material fully react after, be again stirring for
Without dry powder or dough.
Preferably, in step (3), using vibrating ball-mill to be polished smooth by metope, vibrating ball-mill uses 800-1000 purpose white
Smalt paper.
Embodiment 2
The embodiment of the present invention 2 relates to a kind of nanometer stony edema mill wall covering, including the raw material of following parts by weight: half water sulfur
Acid calcium 32%, titanium dioxide 5%, sierozem power 44%, calcium carbonate 11%, redispersable latex powder 0.8%, hydroxypropyl methyl cellulose
1%, silicon dioxide 0.8%, white cement 4%, nanometer stone 0.4%, Gypsum Fibrosum retardant 1%.
The construction method of the nanometer stony edema mill wall covering of a kind of the present embodiment, comprises the following steps:
(1) with water-proof putty powder metope criticized and scrape 2～3 times, repeat 2～3 times；
(2) sand paper is used to be polished flat by the metope after step (1)；
(3) water is used to be cleaned by the dust on the metope after step (2)；
(4) this nanometer stony edema mill wall covering is stirred into thick shape coating with water according to the ratio of 100:40；
(5) method of being scraped by the metope crosspoint tip screwdriver after step (3) by the thick shape coating in step (4) is floating, and 12 is little
Metope is drenched maintenance by Shi Houyong water, is polished smooth by metope after 12 hours.
Metope first criticized before wall to scrape 2～3 times be also the present invention by nanometer stony edema of the present invention mill wall covering with powder of lacquer putty for use on
The one of construction method, it is as using nanometer stony edema of the present invention mill wall covering directly to go up the effect of wall.
Embodiment 3
The embodiment of the present invention 3 relates to a kind of nanometer stony edema mill wall covering, including the raw material of following parts by weight: half water sulfur
Acid calcium 40%, titanium dioxide 4%, sierozem power 35%, calcium carbonate 13%, redispersable latex powder 1%, hydroxypropyl methyl cellulose
1.5%, silica 1 %, white cement 2%, nanometer stone 0.5%, Gypsum Fibrosum retardant 2%.
Embodiment 4
The embodiment of the present invention 4 relates to a kind of nanometer stony edema mill wall covering, including the raw material of following parts by weight: half water sulfur
Acid calcium 30%, titanium dioxide 3%, sierozem power 47%, calcium carbonate 12%, redispersable latex powder 0.2%, hydroxypropyl methyl cellulose
0.8%, silica 1 %, white cement 4%, nanometer stone 0.5%, Gypsum Fibrosum retardant 1.5%.
The Product Status of nanometer stony edema of the present invention mill wall covering is ultrawhite pulverulence and multiple colored powder body state.
Job site only need to be allocated according to the ratio of powder and water after stirring and batch scrape (crosspoint tip screwdriver scrapes method) upper wall, upper wall complete after 2
～within 7 days, be curing period, need not do any emulsion paint, wall finiss brushing again after water mill polishing.At the construction field (site) directly by powder
End adds water to stir and is only environmental protection.
Nanometer stony edema of the present invention mill wall covering products characteristics:
1, national up-to-date industry standard is performed；
2, after child scribbles on the wall and scratches, after easily removing with liquid honing, metope porcelain is still kept
Handle effect；
3, the most water funk, sanitation and hygiene can directly clean metope with mop；
4, after on nanometer stony edema of the present invention mill wall covering, wall is the most outmoded, then shine after liquid honing polishing
Right one new；
5, weather moisture regain can keep metope not play the globule season, and this product uses person of outstanding talent's shape paste batch to scrape, and whole metope has
Small hair pore, meeting own absorption steam, so can keep metope anhydrous state season in moisture regain；During dry weather, body of wall
Nexine moisture can also be evaporated from small hair pore, so the phenomenon expanded with heat and contract with cold will not be produced, prevents mouldy expansion
Come off and more have the quality assurance.
The above, be only presently preferred embodiments of the present invention, and the present invention not makees any pro forma restriction, appoints
What those skilled in the art, in the range of without departing from technical solution of the present invention, when in the technology of available the disclosure above
Hold and make a little change or be modified to the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention,
Any simple modification, equivalent variations and the modification made above example according to the technical spirit of the present invention, all still falls within this
In the range of inventive technique scheme.
Claims (9)
1. nanometer stony edema mill wall covering, it is characterised in that include the raw material of following parts by weight: half-H 2 O calcium sulphate
30%-40%, titanium dioxide 3%-5%, sierozem power 35%-50%, calcium carbonate 8%-15%, redispersable latex powder 0.2%-
1%, hydroxypropyl methyl cellulose 0.4%-1.5%, silicon dioxide 0.5%-1%, white cement 1%-5%, nanometer stone 0.2-
0.5%, Gypsum Fibrosum retardant 0.2%～2%.
2. nanometer stony edema mill wall covering as claimed in claim 1, it is characterised in that include the raw material of following parts by weight:
Half-H 2 O calcium sulphate 32%, titanium dioxide 5%, sierozem power 44%, calcium carbonate 11%, redispersable latex powder 0.8%, hydroxypropyl methyl
Cellulose 1%, silicon dioxide 0.8%, white cement 4%, nanometer stone 0.4%, Gypsum Fibrosum retardant 1%.
3. nanometer stony edema mill wall covering as claimed in claim 1, it is characterised in that include the raw material of following parts by weight:
Half-H 2 O calcium sulphate 40%, titanium dioxide 4%, sierozem power 35%, calcium carbonate 13%, redispersable latex powder 1%, hydroxypropyl methyl are fine
Dimension element 1.5%, silica 1 %, white cement 2%, nanometer stone 0.5%, Gypsum Fibrosum retardant 2%.
4. nanometer stony edema mill wall covering as claimed in claim 1, it is characterised in that include the raw material of following parts by weight:
Half-H 2 O calcium sulphate 30%, titanium dioxide 3%, sierozem power 47%, calcium carbonate 12%, redispersable latex powder 0.2%, hydroxypropyl methyl
Cellulose 0.8%, silica 1 %, white cement 4%, nanometer stone 0.5%, Gypsum Fibrosum retardant 1.5%.
5. the construction method of the nanometer stony edema mill wall covering as described in Claims 1 to 4 is arbitrary, it is characterised in that bag
Include following steps:
(1) this nanometer stony edema mill wall covering is stirred into thick shape coating with water according to the ratio of 100:40；
(2) with the thick shape coating in step (1) metope criticized and scrape 2～3 times；
With water, metope is drenched maintenance after (3) 12 hours, after 12 hours, metope is polished smooth.
6. the construction method of a nanometer stony edema as claimed in claim 5 mill wall covering, it is characterised in that: 15～30 days
After, wall covering hardness reaches optimum.
7. the construction method of a nanometer stony edema as claimed in claim 6 mill wall covering, it is characterised in that: in step (1)
In, after this nanometer stony edema mill wall covering is mixed according to the ratio of 100:40 with water, stir, wait 5～10 minutes, make
After each raw material in this nanometer stony edema mill wall covering fully reacts, it is again stirring for without dry powder or dough.
8. the construction method of a nanometer stony edema as claimed in claim 6 mill wall covering, it is characterised in that: in step (3)
In, use vibrating ball-mill to be polished smooth by metope, vibrating ball-mill uses the white sand paper of 800-1000 mesh.
9. the construction method of the nanometer stony edema mill wall covering as described in Claims 1 to 4 is arbitrary, it is characterised in that bag
Include following steps:
(1) with water-proof putty powder metope criticized and scrape 2～3 times, repeat 2～3 times；
(2) sand paper is used to be polished flat by the metope after step (1)；
(3) water is used to be cleaned by the dust on the metope after step (2)；
(4) this nanometer stony edema mill wall covering is stirred into thick shape coating with water according to the ratio of 100:40；
(5) the metope crosspoint tip screwdriver after step (3) is scraped method by the thick shape coating in step (4) floating, after 12 hours
With water, metope is drenched maintenance, after 12 hours, metope is polished smooth.