CN106238881A - A kind of welding procedure of sheet material - Google Patents
A kind of welding procedure of sheet material Download PDFInfo
- Publication number
- CN106238881A CN106238881A CN201610737206.1A CN201610737206A CN106238881A CN 106238881 A CN106238881 A CN 106238881A CN 201610737206 A CN201610737206 A CN 201610737206A CN 106238881 A CN106238881 A CN 106238881A
- Authority
- CN
- China
- Prior art keywords
- weld part
- welding
- sheet material
- welding procedure
- described step
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the welding procedure of a kind of sheet material, comprise the steps: that weld part is cleaned by (1), removing the greasy dirt on weld part surface, oxide etc. affects the material of welding quality；(2) welding rod chosen heated and dry；(3) use the mode of electric welding that weld part is welded；(4) weld part is polished polishing, removes the oxide-film of weld part, it is ensured that the fineness on its surface；(5) weld part is put in ultrasonic sink wash；(6) weld part is carried out drying and processing.By before welding the weld part of sheet material sufficiently being cleaned, remove the greasy dirt on its surface, oxide etc. completely, it is ensured that welding quality.
Description
Technical field
The present invention relates to the welding procedure of a kind of sheet material, belong to welding technology field.
Background technology
Welding is a kind of jointing metal or system of other thermoplastics such as plastics in the way of heating, high temperature or high pressure
Make technique and technology.The energy source of modern welding has a variety of, including gas flame, electric arc, laser, electron beam, rubs and surpasses
Sound wave etc..But existing welding procedure is typically weld part not to be carried out deep clean, the greasy dirt on its surface, oxide etc.
The quality of welding can be badly influenced.
Summary of the invention
The technical problem to be solved is to provide a kind of sheet material welding procedure, by weldering to sheet material before welding
The portion that connects sufficiently cleans, and removes the greasy dirt on its surface, oxide etc. completely, it is ensured that welding quality.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
A kind of welding procedure of sheet material, it is characterised in that: comprise the steps
(1) being cleaned weld part, removing the greasy dirt on weld part surface, oxide etc. affects the material of welding quality；
(2) welding rod chosen heated and dry；
(3) use the mode of electric welding that weld part is welded；
(4) weld part is polished polishing, removes the oxide-film of weld part, it is ensured that the fineness on its surface；
(5) weld part is put in ultrasonic sink wash；
(6) weld part is carried out drying and processing.
The welding procedure of aforesaid a kind of sheet material, it is characterised in that: in described step (1) by the way of ultrasonic wave water washing
Weld part is cleaned.
The welding procedure of aforesaid a kind of sheet material, it is characterised in that: the core wire of the welding rod chosen in described step (2) is low
Carbon steel.
The welding procedure of aforesaid a kind of sheet material, it is characterised in that: described step (2) is heated to 80 DEG C-95 to welding rod
DEG C carry out dry insulation.
The welding procedure of aforesaid a kind of sheet material, it is characterised in that: in described step (3), the electric current of electric welding is 95A-
105A。
The welding procedure of aforesaid a kind of sheet material, it is characterised in that: the electric current 100A of electric welding in described step (3).
The invention has the beneficial effects as follows: by before welding the weld part of sheet material sufficiently being cleaned, remove completely
The greasy dirt on its surface, oxide etc., it is ensured that welding quality.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described further.
The welding procedure that the invention provides a kind of sheet material comprises the steps
(1) being cleaned weld part, removing the greasy dirt on weld part surface, oxide etc. affects the material of welding quality；
(2) welding rod chosen heated and dry；
(3) use the mode of electric welding that weld part is welded；
(4) weld part is polished polishing, removes the oxide-film of weld part, it is ensured that the fineness on its surface；
(5) weld part is put in ultrasonic sink wash；
(6) weld part is carried out drying and processing.
By before welding the weld part of sheet material sufficiently being cleaned, remove the greasy dirt on its surface, oxide completely
Deng, it is ensured that welding quality.Weld part is cleaned in step (1) by the way of ultrasonic wave water washing by the present embodiment, it is ensured that
Cleaning effect, and after welding completes, weld part surface is processed by shot blasting, the most again carry out ultrasonic wave water washing, it is ensured that weldering
Connect the smooth degree in portion.
The core wire of the welding rod chosen in described step 2 is mild steel, and its steel wire plasticity is good, and drawing welding wire is easier, side
Just weld.
In the present embodiment, welding rod is heated to 80 DEG C-95 DEG C by described step (2) and carries out drying insulation, after being effectively ensured
The welding quality of phase, is also convenient for workman's weld job.
Through repetition test, for the workpiece of sheet material class, when when welding, the electric current of electric welding is between 95A-105A, welding
Quality is higher, and welding current welding quality when 100A is optimal.
In sum, a kind of sheet material welding procedure that the present invention provides, by carrying out the weld part of sheet material before welding
Sufficiently cleaning, removes the greasy dirt on its surface, oxide etc., it is ensured that welding quality completely.
The ultimate principle of the present invention, principal character and advantage have more than been shown and described.The technical staff of the industry should
Understanding, the present invention is not restricted to the described embodiments, and the simply explanation present invention's described in above-described embodiment and description is former
Reason, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these changes and improvements
Both fall within scope of the claimed invention.Claimed scope is by appending claims and equivalent thereof
Boundary.
Claims (6)
1. the welding procedure of a sheet material, it is characterised in that: comprise the steps
(1) being cleaned weld part, removing the greasy dirt on weld part surface, oxide etc. affects the material of welding quality；
(2) welding rod chosen heated and dry；
(3) use the mode of electric welding that weld part is welded；
(4) weld part is polished polishing, removes the oxide-film of weld part, it is ensured that the fineness on its surface；
(5) weld part is put in ultrasonic sink wash；
(6) weld part is carried out drying and processing.
The welding procedure of a kind of sheet material the most according to claim 1, it is characterised in that: by ultrasonic in described step (1)
Weld part is cleaned by the mode of ripple washing.
The welding procedure of a kind of sheet material the most according to claim 1, it is characterised in that: the weldering chosen in described step (2)
The core wire of bar is mild steel.
The welding procedure of a kind of sheet material the most according to claim 3, it is characterised in that: welding rod is added in (2) by described step
Heat carries out drying insulation to 80 DEG C-95 DEG C.
The welding procedure of a kind of sheet material the most according to claim 1, it is characterised in that: the electricity of electric welding in described step (3)
Stream is 95A-105A.
The welding procedure of a kind of sheet material the most according to claim 5, it is characterised in that: the electricity of electric welding in described step (3)
Stream 100A.