CN106222776A - A kind of jade is felt nice and cool regenerated celulose fibre and preparation method thereof - Google Patents
A kind of jade is felt nice and cool regenerated celulose fibre and preparation method thereof Download PDFInfo
- Publication number
- CN106222776A CN106222776A CN201610601268.XA CN201610601268A CN106222776A CN 106222776 A CN106222776 A CN 106222776A CN 201610601268 A CN201610601268 A CN 201610601268A CN 106222776 A CN106222776 A CN 106222776A
- Authority
- CN
- China
- Prior art keywords
- jade
- cool
- preparation
- regenerated celulose
- celulose fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of jade to feel nice and cool regenerated celulose fibre, containing jade in described regenerated celulose fibre;In described regenerated celulose fibre, jade content is: 3.96 14.68%.The present invention also provides for a kind of jade and feels nice and cool the preparation method of regenerated celulose fibre, and described method includes configuring dispersion liquid step;Described configuration dispersion liquid step includes: deionized water is heated to 30 40 DEG C, adds cellulose derivative class dispersant, with sodium hydroxide regulation aqueous solution pH 8 10, is subsequently adding dodecylbenzene sodium sulfonate.Jade cool fiber cellulose fiber prepared by the present invention, the performance such as fibre strength highlights;Jade cool fiber cellulose fiber prepared by the present invention, containing appropriate jade so that fabric prepared by this fiber has good nice and cool sensation.
Description
Technical field
The present invention relates to a kind of regenerated celulose fibre and preparation method thereof, specifically, relate to a kind of jade nice and cool again
Raw cellulose fibre and preparation method thereof, belongs to textile technology field.
Background technology
Along with fast development and the improving constantly of people's living standard of science and technology, people are to the requirement of clothing the most not only
It is only to cover body resisting cold, but pursues safe, comfortable, attractive in appearance and more practical function.During the broiling summer, wear one to feel nice and cool thoroughly
The clothes of gas can not only improve the comfort level of health, moreover it is possible to brings good mood to people, is conducive to work and life.
The most just there is the good name of state of jade in China, containing the abundant mineral useful to human body and micro-in jade
Secondary element, is attached to for a long time on the skin of human body, discharges, and can improve blood microcirculation, enhance metabolism, thus reach
Prevention disease, the effect of allaying tiredness.Proving through mineral medical research, jade can produce the photoelectric effect of high intensity, in processing
During can focusing energy storage, formed magnetic field, can produce when wearing and be of value to the resonance of human body.Existing investigative technique shows, adds
The textile adding jade can allow human body have preferable cooling feeling, particularly during high temperature, and fabric energy relative reduction temperature, allow people feel
Comfortable.
The most more about the research of jade fiber, but all it is confined to synthetic fibers aspect, as Shanghai De Fulun chemical fibre has
The super cool cool feeling health care polyester fiber that limit company prepares with polyester fiber production technology, Jin Hui new fiber materials company limited produces
The refreshing Liz etc. containing jade material, but in terms of regenerated celulose fibre, there are no elaboration.
Patent 200710023666.9 discloses a kind of infinitesimal jade fiber, is by Subnano-class jade granule and spinning
The fiber with preferable cooling feeling is prepared in melt spinning together.Patent 201410354049.7 discloses one and has core-skin knot
The fire-retardant ice of structure is felt well recycled polyester filament fiber, nice and cool master batch that cortex is made up of lamellar jade, titanium dioxide, zinc oxide and again
Raw polyester slice melt spinning obtains, and sandwich layer is cut into slices what melt spinning obtained by fire-retardant master granule and recycled polyester, and this fiber has
There is nice and cool and fire resistance.Patent 201310497670.4 discloses the preparation method of a kind of chinlon 6 cool jade fiber, this fiber
Jade and other beneficial mineral materials are prepared as Subnano-class particle diameter, fuse into spinning processing among chinlon 6 melt and obtain,
Comparing cooling feeling with common Silk shell fabric strong, wearability is strong.
Above technology is all jade to be prepared as powder body carry out blend melt spinning, does not mention and jade is prepared as slurry
Technology with cellulose carries out solution blending spinning, during this has resulted in fibre spinning, is susceptible to particle aggregation, causes
Blocking spinning head, fiber spinnability is poor.
The most existing technical scheme is all interpolation jade material in synthetic fibers;Owing to synthetic fibers itself do not have again
The moisture absorption giving birth to cellulose fibre, the characteristic perspired, the fabric cool feeling therefore prepared is general.
Summary of the invention
For the deficiencies in the prior art, the present invention provides a kind of jade to feel nice and cool regenerated celulose fibre and preparation method thereof,
To realize following goal of the invention:
1, the jade cool fiber cellulose fiber that prepared by the present invention, the performance such as fibre strength highlights;
2, the jade cool fiber cellulose fiber that prepared by the present invention, containing appropriate jade so that fabric prepared by this fiber has
Good nice and cool sensation;
3, during preparing regenerated celulose fibre, spinnability is preferable, and the fibre defect of preparation is less;
4, the jade cool fiber cellulose fiber of preparation, nice and cool sensation is substantially;
5, the present invention is at the jade slurry of preparation, it is possible to not producing reunion in ensureing 12 hours, jade is uniformly distributed in the slurry,
It is difficult to layering, can directly utilize and spin front injecting systems and join in spinning liquid;
6, the regenerated celulose fibre in the present invention is with bamboo pulp as raw material, and the fiber prepared has the nice and cool of bamboo fibre and relaxes
Fit, resist the advantages such as antibacterial;
7, jade slurry is joined in spinning glue by injection before spinning by the present invention, and addition manner is easy, it is easy to PROCESS FOR TREATMENT.
In order to realize foregoing invention purpose, the technical solution used in the present invention is:
A kind of jade is felt nice and cool regenerated celulose fibre, it is characterised in that: containing jade in described regenerated celulose fibre.
The following is and the further of technique scheme is improved:
In described regenerated celulose fibre, jade content is: 3.96-14.68%.
It is 1.51-2.49 cN/dtex that described regenerated celulose fibre does fracture strength;Wet breaking strength is 0.83-1.50
cN/dtex;Dry elongation at break is 14.2-18.9%.
A kind of jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described method includes configuration dispersion
Liquid step;Described configuration dispersion liquid step includes: deionized water is heated to 30-40 DEG C, adds the dispersion of cellulose derivative class
Agent, with sodium hydroxide regulation aqueous solution pH at 8-10, is subsequently adding dodecylbenzene sodium sulfonate.
Described cellulose derivative class dispersant is carboxymethyl cellulose, carboxyethyl cellulose, hydroxyethyl cellulose, crystallite
One or more of cellulose;In described dispersion liquid, the concentration of cellulose derivative class dispersant is 0.5-1.5wt%.
Described method also includes configuring slurry stage;In described slurry, the concentration of jade powder is 10-30%wt.
Described method also includes grinding steps;Described grinding steps includes: added in ball mill by the jade slurry of preparation
It is ground, within every 20 minutes, changes a rotating, after grinding 2-4 hour, use ultrasonic echography 8-15min, supersonic frequency
20KHz。
Described method also includes filtration step;Described filtration step: by particle diameter in the jade slurry after grinding steps more than 2
The jade particle of μm leaches.
Described method also includes spinning glue preparation process;The pulp material that described spinning glue uses is to use bamboo pulp;Institute
State in spinning glue preparation process, slow release forming agent need to be added;Described slow release forming agent is Polyethylene Glycol;Described slow release forming agent
Addition is the 0.1-0.5wt% of cellulose in spinning glue.
Described method also includes co-blended spinning liquid preparation process;Described co-blended spinning liquid preparation process includes: by configuration well
Jade slurry be stirred mixing with the spinning glue of preparation;Described mixing time is 40-60min, and whipping temp is 18-22
℃;Described method also includes spinning and post-processing step;In described spinning process, coagulating bath is: sulphuric acid 80-125g/L, sulphuric acid
Sodium 260-340g/L, zinc sulfate 8-15g/L;Described coagulation bath temperature is 40-55 DEG C.
Owing to have employed technique scheme, what the present invention reached has the technical effect that
1, the jade cool fiber cellulose fiber that prepared by the present invention, dry fracture strength is 1.51-2.49 cN/dtex;Prepared by the present invention
Jade cool fiber cellulose fiber, wet breaking strength is 0.83-1.50 cN/dtex;Jade cool fiber element prepared by the present invention
Fiber, dry elongation at break is 14.2-18.9%;
2, the jade cool fiber cellulose fiber that prepared by the present invention, line density is 1.64-1.68 dtex;Jade prepared by the present invention
Cool fiber cellulose fiber, fault is 2-4 mg/100g;Jade cool fiber cellulose fiber prepared by the present invention, in fiber, jade contains
Amount is 3.96-14.68%;The interpolation speciality jade slurry in cellulose solution of the invention, is prepared as having jade ice
The regenerated celulose fibre of refreshing characteristic, is greatly improved fiber spinnability;When in fiber, jade content is 3.96-14.68%, with
The cellulose have moisture absorption, perspiring combines, the fiber of preparation most cool feeling, and the fibre structure intensity etc. of preparation is best;
3, the fabric that the jade cool fiber cellulose fiber using the present invention to prepare is made, fabric maximum transient heat flow weight range is
0.253-0.350 w/cm2, higher by more than 100% than general fibre;Jade cool fiber cellulose fiber prepared by the present invention, fabric is put down
All temperature are 30.3-32.1 DEG C, lower 1.1-2.9 DEG C than conventional cellulosic fibers temperature;
4, the jade slurry that prepared by the present invention, processes through special process, does not produce reunion in 12 hours, and jade is uniformly distributed
In the slurry, it is difficult to layering, can directly utilize and spin front injecting systems and join the stability that can make spinning fibre in spinning liquid
Improve;
5, the regenerated celulose fibre in the present invention is with bamboo pulp as raw material, and the fiber prepared has the nice and cool of bamboo fibre and relaxes
Fit, resist the advantages such as antibacterial;
6, jade slurry is joined in spinning glue by injection before spinning by the present invention, and addition manner is easy, it is easy to PROCESS FOR TREATMENT.
Specific embodiment
The preparation of 1 one kinds of jade cool fiber cellulose fibers of embodiment
Step 1, the preparation of jade slurry
(1) pulverize: pulverize after jade leftover bits and pieces is dried, by the D90=1.693 μm of laser fineness gage detection powder body.
(2) preparation dispersion liquid: deionized water is heated to 30 DEG C, continuously stirred under be slowly added to carboxymethyl cellulose, join
The solution of concentration 0.5 wt% processed, by sodium hydroxide regulation pH value of water solution to 8, adds the dodecane to jade powder 1.0wt %
Base benzene sulfonic acid sodium salt, continues stirring in uniform solution.
(3) preparation slurry: the jade powder in (1) is joined in continuously stirred dispersion liquid, is configured to the dense of 10wt%
Degree slurry, stirs 30min.
(4) grind: jade slurry step (3) prepared is ground in adding ball mill, within every 20 minutes, change once
Rotating, after grinding 2 hours, uses ultrasonic echography 8min, supersonic frequency 20KHz.
(5) filter: the jade slurry filter cloth after grinding leaches the particle diameter particle more than 2 μm;Remaining slurry laser
The D90=1.235 μm of particles distribution instrument detection powder body, standby.
Prepared by step 2, spinning glue:
It is prepared as spinning glue with bamboo pulp for raw material adhering process routinely, and adds in dissolution process first fibre in viscose glue is contained
Amount is the Polyethylene Glycol of 0.1wt%.
Prepared by step 3, co-blended spinning liquid:
The above-mentioned jade slurry prepared is joined in blend tank stirring 40min, temperature 22 DEG C in tank, be stirred jade
After the grinding of slurry the most ground pump, filter filtration, vacuum defoamation, liquid level equilibrium bucket steady pressure, inject spinning by syringe pump
In sebific duct road, the spinning glue prepared through dynamic mixer and step 2 is sufficiently mixed, and prepares being blended of jade slurry and spinning glue
Spinning liquid.
Described jade slurry addition is the jade effective content 4wt% to viscose glue alpha cellulose.
Step 4, spinning and post processing:
Above-mentioned co-blended spinning liquid enters coagulating bath and carries out spinning, and tow obtains molding tow after multistage drafting.Gained tow
Through cut-out, desulfurization, wash, oil, the postprocessing working procedures such as drying, prepared jade is felt nice and cool regenerated celulose fibre.
Described coagulating bath includes sulphuric acid 125g/L, sodium sulfate 260g/L, zinc sulfate 15g/L, acid temperature 40 DEG C.
The preparation of 2 one kinds of jade cool fiber cellulose fibers of embodiment
Step 1, the preparation of jade slurry
(1) pulverize: pulverize after jade leftover bits and pieces is dried, by the D90=1.433 μm of laser fineness gage detection powder body.
(2) preparation dispersion liquid: deionized water is heated to 40 DEG C, continuously stirred under be slowly added to carboxymethyl cellulose, join
Concentration 1.5 wt% processed, by sodium hydroxide regulation pH value of water solution to 10, adds the detergent alkylate to jade powder 3.0wt %
Sodium sulfonate, continues stirring in uniform solution.
(3) preparation slurry: the jade powder in (1) is joined in continuously stirred dispersion liquid, is configured to the dense of 30wt%
Degree, stirs 50min.
(4)) grind: be ground in jade slurry is added ball mill, within every 20 minutes, change a rotating, grind 4
After hour, use ultrasonic echography 15min, supersonic frequency 20KHz.
(5) filter: the jade slurry filter cloth after grinding leaches the particle diameter particle more than 2 μm;Remaining slurry laser
The D90=1.326 μm of particles distribution instrument detection powder body, standby.
Prepared by step 2, spinning glue:
It is prepared as spinning glue with bamboo pulp for raw material adhering process routinely, and adds viscose glue first fine in dissolution process
The Polyethylene Glycol of 0.5wt%.
Prepared by step 3, co-blended spinning liquid:
Jade slurry above-mentioned steps 1 prepared joins stirring 60min in blend tank, and in tank, temperature 22 DEG C, are stirred
The grinding of jade slurry the most ground pump, filter filtration, vacuum defoamation, after liquid level equilibrium bucket steady pressure, by injection infusion
Enter in spinning sebific duct road, be sufficiently mixed through dynamic mixer with the spinning glue of step 2 preparation, prepare jade slurry and spinning glue
Co-blended spinning liquid.
Described jade slurry addition is the jade effective content 15wt% to viscose glue alpha cellulose.
Step 4, spinning and post processing:
Above-mentioned co-blended spinning liquid enters coagulating bath and carries out spinning, and tow obtains molding tow after multistage drafting.Gained tow
Through cut-out, desulfurization, wash, oil, the postprocessing working procedures such as drying, prepared jade is felt nice and cool regenerated celulose fibre.
Described coagulating bath includes sulphuric acid 80g/L, sodium sulfate 340g/L, zinc sulfate 8g/L, acid temperature 46 DEG C.
The preparation of 3 one kinds of cool fiber cellulose fibers of embodiment
Step 1, the preparation of jade slurry
(1) pulverize: pulverize after jade leftover bits and pieces is dried, by the D90=1.536 μm of laser fineness gage detection powder body.
(2) preparation dispersion liquid: deionized water is heated to 33 DEG C, continuously stirred under be slowly added to carboxymethyl cellulose, join
Concentration 0.8 wt% processed, by sodium hydroxide regulation pH value of water solution to 9, adds the detergent alkylate sulphur to jade powder 1.5wt %
Acid sodium, continues stirring in uniform solution.
(3) preparation slurry: the jade powder in (1) is joined in continuously stirred dispersion liquid, is configured to the dense of 20wt%
Degree, stirs 40min.
(4)) grind: be ground in jade slurry is added ball mill, within every 20 minutes, change a rotating, grind 3
After hour, use ultrasonic echography 10min, supersonic frequency 20KHz.
(5) filter: the jade slurry filter cloth after grinding leaches the particle diameter particle more than 2 μm;Remaining slurry laser
The D90=1.428 μm of particles distribution instrument detection powder body, standby.
Prepared by step 2, spinning glue:
It is prepared as spinning glue with bamboo pulp for raw material adhering process routinely, and adds viscose glue first fine in dissolution process
The Polyethylene Glycol of 0.3wt%.
Prepared by step 3, co-blended spinning liquid:
The above-mentioned jade slurry prepared is joined in blend tank stirring 50min, temperature 20 DEG C in tank, be stirred jade
After the grinding of slurry the most ground pump, filter filtration, vacuum defoamation, liquid level equilibrium bucket steady pressure, inject spinning by syringe pump
In sebific duct road, it is sufficiently mixed through dynamic mixer with the spinning glue of step 2 preparation, prepares being blended of jade slurry and spinning glue
Spinning liquid.
Described jade slurry addition is the jade effective content 10wt% to viscose glue alpha cellulose.
Step 4, spinning and post processing:
Above-mentioned co-blended spinning liquid enters coagulating bath and carries out spinning, and tow obtains molding tow after multistage drafting.Gained tow
Through cut-out, desulfurization, wash, oil, the postprocessing working procedures such as drying, prepared jade is felt nice and cool regenerated celulose fibre.
Described coagulating bath includes sulphuric acid 100g/L, sodium sulfate 320g/L, zinc sulfate 10g/L, acid temperature 45 DEG C.
Jade prepared by the present invention is felt nice and cool regenerated celulose fibre, and related physical Indexs measure is as shown in table 1.
Jade cool fiber cellulose fiber prepared by table 1 present invention, index of correlation detection is as follows
As can be seen from the above table, jade cool fiber cellulose fiber prepared by the present invention, dry fracture strength is 1.51-2.49 cN/
dtex;Jade cool fiber cellulose fiber prepared by the present invention, wet breaking strength is 0.83-1.50 cN/dtex;Prepared by the present invention
Jade cool fiber cellulose fiber, dry elongation at break is 14.2-18.9%.
Jade cool fiber cellulose fiber prepared by the present invention, detects its line density, spinneret orifice plugging rate, fault, relevant inspection
Survey index and be shown in Table 2.
Jade cool fiber cellulose fiber prepared by table 2 present invention, jade content detection in line density, defect detection, fiber
See table
As can be seen from the above table, jade cool fiber cellulose fiber prepared by the present invention, line density is 1.64-1.68 dtex;This
The jade cool fiber cellulose fiber of bright preparation, fault is 2-4 mg/100g;Jade cool fiber cellulose fiber prepared by the present invention,
In fiber, jade content is 3.96-14.68%.
Fabric that regenerated celulose fibre is made into carries out contact coldness detection to use the jade prepared of the present invention to feel nice and cool, used
Instrument is KES-F7 thermal performance test instrument, tests maximum instantaneous heat flow, and test result and fabric temperature are as shown in table 3.
Table 3 tests maximum instantaneous heat flow, test result and fabric temperature, and testing result is as follows
As can be seen from the above table, jade cool fiber cellulose fiber fabric prepared by the present invention, fabric maximum thermal transient flow are used
Scope is 0.253-0.350 w/cm2, higher by more than 100% than general fibre;Jade cool fiber cellulose fiber prepared by the present invention,
Fabric mean temperature is 30.3-32.1 DEG C, lower 1.1-2.9 DEG C than conventional cellulosic fibers temperature.
Except as otherwise noted with unit commonly used in the art, the percent employed in the present invention is percetage by weight, this
Ratio described in invention, is mass ratio.
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention,
Although being described in detail the present invention with reference to previous embodiment, for a person skilled in the art, it still may be used
So that the technical scheme described in foregoing embodiments to be modified, or wherein portion of techniques feature is carried out equivalent.
All within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included in the present invention's
Within protection domain.
Claims (10)
1. a jade is felt nice and cool regenerated celulose fibre, it is characterised in that: containing jade in described regenerated celulose fibre.
A kind of jade the most according to claim 1 is felt nice and cool regenerated celulose fibre, it is characterised in that: described regenerated cellulose
In fiber, jade content is: 3.96-14.68%.
A kind of jade the most according to claim 1 is felt nice and cool regenerated celulose fibre, it is characterised in that: described regenerated cellulose
Fracture strength done by fiber is 1.51-2.49 cN/dtex;Wet breaking strength is 0.83-1.50 cN/dtex.
4. a jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described method includes preparing dispersion liquid
Step;Described preparation dispersion liquid step includes: deionized water is heated to 30-40 DEG C, adds cellulose derivative class dispersant,
With sodium hydroxide regulation aqueous solution pH at 8-10.
A kind of jade of preparing the most according to claim 4 is felt nice and cool the method for regenerated celulose fibre, it is characterised in that: described
Cellulose derivative class dispersant is the one of carboxymethyl cellulose, carboxyethyl cellulose, hydroxyethyl cellulose, microcrystalline Cellulose
Or it is several;In described dispersion liquid, the concentration of cellulose derivative class dispersant is 0.5-1.5wt%.
A kind of jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described side
Method also includes configuring slurry stage;In described slurry, the concentration of jade powder is 10-30%wt.
A kind of jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described side
Method also includes grinding steps;Described grinding steps includes: be ground in the jade slurry of preparation is added ball mill, every 20 points
Clock changes a rotating, after grinding 2-4 hour, uses ultrasonic echography 8-15min, supersonic frequency 20KHz.
A kind of jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described side
Method also includes filtration step;Described filtration step: particle diameter in the jade slurry after grinding steps is filtered more than the jade particle of 2 μm
Go out.
A kind of jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described side
Method also includes spinning glue preparation process;The pulp material that described spinning glue uses is to use bamboo pulp;Prepared by described spinning glue
Cheng Zhong, need to add slow release forming agent;Described slow release forming agent is Polyethylene Glycol;The addition of described slow release forming agent is spinning glue
The 0.1-0.5wt% of middle cellulose.
A kind of jade is felt nice and cool the preparation method of regenerated celulose fibre, it is characterised in that: described
Method also includes co-blended spinning liquid preparation process;Described co-blended spinning liquid preparation process includes: by the jade slurry that configured with
The spinning glue of preparation is stirred mixing;Described mixing time is 40-60min, and whipping temp is 18-22 DEG C;Described method is also
Including spinning and post-processing step;In described spinning process, coagulating bath is: sulphuric acid 80-125g/L, sodium sulfate 260-340g/L,
Zinc sulfate 8-15g/L;Described coagulation bath temperature is 40-55 DEG C.