CN106221548A - High ferro flame-resistant polyurethane waterproof coating and preparation method thereof - Google Patents
High ferro flame-resistant polyurethane waterproof coating and preparation method thereof Download PDFInfo
- Publication number
- CN106221548A CN106221548A CN201610614307.XA CN201610614307A CN106221548A CN 106221548 A CN106221548 A CN 106221548A CN 201610614307 A CN201610614307 A CN 201610614307A CN 106221548 A CN106221548 A CN 106221548A
- Authority
- CN
- China
- Prior art keywords
- flame
- waterproof coating
- high ferro
- parts
- polyurethane waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high ferro flame-resistant polyurethane waterproof coating and preparation method thereof, described high ferro flame-resistant polyurethane waterproof coating is prepared from by the raw material of following weight parts: polyether polyol 45 55 parts, 1,6 hexamethylene diisocyanates 10 20 parts, n-butyl phthalate 0.4 0.8 parts, dimethylbenzene 10 20 parts, chlorinated paraffin 10 20 parts, Kaolin 15 25 parts, calcium carbonate 5 15 parts, 3 ethoxy 1,3 oxazolidine 49 parts, dibutyl tin laurate 0.3 0.6 parts, inorganic antiseptic 28 parts, fire retardant 15 parts.High ferro flame-resistant polyurethane waterproof coating that the present invention provides and preparation method thereof, by rational proportioning, preferably go out the fire retardant of applicable high ferro flame-resistant polyurethane waterproof coating, inorganic antiseptic kind and consumption, improve mildew resistance, antibiotic property, anti-flammability, there is physical and mechanical properties, temperature tolerance, weatherability, resistant to chemical media and the prominent wearability of excellence, easy construction, efficiency is high.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of high ferro flame-resistant polyurethane waterproof coating and preparation side thereof
Method.
Background technology
High-speed railway is called for short " high ferro ", refers to, by transforming original circuit (linearization(-sation), gauge standardization), make the highest operation
Speed reaches not less than 200 kilometers per hour, or builds new " the newest line " specially, makes operation speed reach the most extremely
The railway system of few 250 kilometers.
Waterproof material mainly has three classes: waterproof roll, polyurethane waterproof material, new polymers cement group water-proofing material.
It is wet that waterproof material is primarily used to prevent in rainwater, subsoil water, industrial and civilian plumbing, corrosive liquids and air
Gas, steam etc. invade building.
Railway line is mainly made up of roadbed, bridge and tunnel, and due to high ferro, the operation characteristic of Line for Passenger Transportation, the line is busy for bridge
Road ratio is significantly increased, more than 50%.Waterproof layer is set at bridge concrete bridge floor, can effectively intercept water and penetrate into floorings
In structure, slow down steel bar corrosion in the aging of concrete and floorings, thus reach to improve the mesh of concrete bridge structure durability
's.So bridge deck water-proof is an important component part in concrete-bridge engineering, current high ferro water-repellent paint modulus and
Elasticity can not be taken into account.
Existing high ferro polyurethane water-proof paint, because hot strength needs, it is generally two component polyurethane, is divided into first
Component and second component, in use need to mix first, second component according to a certain percentage, could use after stirring.
General first component is base polyurethane prepolymer for use as, and second component is curing system.Because bi-component high ferro polyurethane water-proof paint is being executed
There is burden process before work, so being susceptible to measure mistake, causing waterproof coating physical property and waterproof effect to reduce;Coating
Whipping process easily bubbles, makes easily to occur in the middle of waterproof coating dark bubble, pin hole, affect outward appearance and waterproof effect;First, second group
Dividing after stirring, it is necessary to make to be finished material within its hardening time, otherwise material can make viscosity rise, after retrogradation because of reaction
Cannot scratch or roller coat.
The invention provides a kind of high ferro flame-resistant polyurethane waterproof coating, there is the effect waterproof, fire-retardant, antibacterial of excellence
Really.
Summary of the invention
For above-mentioned deficiency present in prior art, one of the technical problem to be solved is to provide a kind of high
Ferrum flame-resistant polyurethane waterproof coating.
The two of the technical problem to be solved are to provide the preparation of a kind of high ferro flame-resistant polyurethane waterproof coating
Method.
The present invention seeks to be achieved through the following technical solutions:
A kind of high ferro flame-resistant polyurethane waterproof coating, is prepared from by the raw material of following weight parts: polyether polyol 45-
55 parts, hexamethylene diisocyanate 10-20 part, n-butyl phthalate 0.4-0.8 part, dimethylbenzene 10-20 part, chlorination stone
Wax 10-20 part, Kaolin 15-25 part, calcium carbonate 5-15 part, 3-ethoxy-1,3-oxazolidine 4-9 part, di lauric dibutyl
Stannum 0.3-0.6 part, inorganic antiseptic 2-8 part, fire retardant 1-5 part.
Preferably, described inorganic antiseptic is the mixing of one or more in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate
Thing.
It is highly preferred that described inorganic antiseptic is mixed by Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate, described bromination
Silver, zinc dihydrogen phosphate, the mass ratio of Zinc Tungstate are (1-3): (1-3): (1-3).
Preferably, described fire retardant is the mixing of one or more in deca-BDE, eight bromo ether, TDE
Thing.
It is highly preferred that described fire retardant is mixed by deca-BDE, eight bromo ether, TDE, described ten
Dibromodiphenyl ether, eight bromo ether, the mass ratio of TDE are (1-3): (1-3): (1-3).
Preferably, the hydroxyl value of described polyether polyol is 18-38mgKOH/g, can be polyethers HPOP40, polyethers EP-
One or more compositions in 330N (G).
Present invention also offers the preparation method of above-mentioned high ferro flame-resistant polyurethane waterproof coating, comprise the following steps:
(1) by proportioning, polyether polyol is added in reactor, temperature is risen to 100-110 DEG C and be decompressed to-
Remove vacuum after 0.092MPa~-0.096MPa vacuum dehydration 20-40 minute, be cooled to 75-85 DEG C and add 1, oneself two isocyanides of 6-
Acid esters stirs 2-3 hour with rotating speed for 300-600 rev/min, is subsequently adding n-butyl phthalate with rotating speed as 300-600
Rev/min stirring 20-40 minute, cooling discharge, obtain component A;
(2) by proportioning, dimethylbenzene, chlorinated paraffin are added in reactor, temperature is risen to 85-95 DEG C and adds Kaolin, carbon
Acid calcium, inorganic antiseptic, fire retardant stir 10-20 minute with rotating speed for 300-600 rev/min, temperature rise to 120-130 DEG C also
Remove vacuum after being decompressed to-0.092MPa~-0.096MPa vacuum dehydration 1.5-2.5 hour, be then cooled to 55-65 DEG C of addition
3-ethoxy-1,3-oxazolidine stirs 20-40 minute for 300-600 rev/min with rotating speed, is eventually adding dibutyl tin laurate
Stir 30-90 minute for 300-600 rev/min with rotating speed, cooling discharge, obtain B part;
(3) component A it is uniformly mixed with B component and get final product.
High ferro flame-resistant polyurethane waterproof coating that the present invention provides and preparation method thereof, by rational proportioning, preferably
Go out the fire retardant of applicable high ferro flame-resistant polyurethane waterproof coating, inorganic antiseptic kind and consumption, improve mildew resistance, antibacterial
Property, anti-flammability, have excellence physical and mechanical properties, temperature tolerance, weatherability, resistant to chemical media and prominent wearability, execute
Work is convenient, and efficiency is high.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further, the following stated, is only the preferable enforcement to the present invention
Example, not does the restriction of other forms to the present invention, and any those skilled in the art are possibly also with the disclosure above
Technology contents be changed to the Equivalent embodiments that changes on an equal basis.Every without departing from the present invention program content, according to the present invention
Technical spirit any simple modification that following example are done or equivalent variations, all fall within protection scope of the present invention.
Each raw material introduction in embodiment:
Chlorinated paraffin, No. CAS: 106232-86-4, the concrete chlorination stone using Jinan Yin Ju Chemical Co., Ltd. to provide
Wax-70.
1, hexamethylene-diisocyanate, No. CAS: 822-06-0.
N-butyl phthalate, No. CAS: 84-74-2.
Dimethylbenzene, No. CAS: 1330-20-7.
Kaolin, No. CAS: 1332-58-7, use 325 purposes that Shanghai Liang Jiang titanium white heavy chemicals company limited produces
Kaolin.
Calcium carbonate, No. CAS: 471-34-1, use the 325 mesh lightweight carbonic acid that Lingshou County Zhen Ling mineral products processing factory provides
Calcium.
3-ethoxy-1,3-oxazolidine, with reference to high and steep grade " 3-ethoxy-1, the synthesis of 3-oxazolidine and sign and just
Step application " in 1.2 joint methods prepare.
Dibutyl tin laurate, No. CAS: 77-58-7.
Polyethers HPOP40, the trade mark using Shandong Lanxing Dongda Chemical Co., Ltd to provide is HPOP40, and hydroxyl value is
The polyether polyol of 20-23mgKOH/g.
Polyethers EP-330N (G), the trade mark using Shandong Lanxing Dongda Chemical Co., Ltd to provide is EP-330N
(G), hydroxyl value is the polyether polyol of 32.5-35.5mgKOH/g.
Silver monobromide, No. CAS: 7785-23-1, particle diameter 800 mesh.
Zinc dihydrogen phosphate, No. CAS: 13598-37-3, particle diameter 800 mesh.
Zinc Tungstate, No. CAS: 13597-56-3, particle diameter 800 mesh.
Deca-BDE, No. CAS: 1163-19-5.
Eight bromo ether, No. CAS: 21850-44-2.
TDE, No. CAS: 84852-53-9.
Embodiment 1
High ferro flame-resistant polyurethane waterproof coating raw material (weight portion): polyethers HPOP40 15 parts, polyethers EP-330N (G) 35
Part, hexamethylene diisocyanate 14 parts, n-butyl phthalate 0.6 part, dimethylbenzene 16 parts, chlorinated paraffin 15 parts, kaolinite
18 parts of soil, calcium carbonate 10 parts, 3-ethoxy-1,3-oxazolidine 6 parts, dibutyl tin laurate 0.45 part, inorganic antiseptic 3
Part, fire retardant 1.5 parts.
Described inorganic antiseptic is uniformly mixed for 1:1:1 in mass ratio by Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate
Obtain.
Described fire retardant is by deca-BDE, eight bromo ether, TDE in mass ratio for 1:1:1 stirring mixing all
Even obtain.
The preparation of high ferro flame-resistant polyurethane waterproof coating:
(1) by proportioning, polyethers HPOP40, polyethers EP-330N (G) are added in reactor, temperature is risen to 105 DEG C and subtracts
Remove vacuum after being depressed into-0.095MPa vacuum dehydration 30 minutes, be cooled to 80 DEG C and to keep temperature be 80 DEG C, add 1,6-oneself two
Isocyanates is 400 revs/min with rotating speed and stirs 2.5 hours, be subsequently adding n-butyl phthalate with rotating speed be 400 turns/
Divide stirring 30 minutes, be cooled to 30 DEG C of dischargings, obtain component A;
(2) by proportioning, dimethylbenzene, chlorinated paraffin are added in reactor, temperature is risen to 90 DEG C and adds Kaolin, carbonic acid
Calcium, inorganic antiseptic, fire retardant are 400 revs/min with rotating speed and stir 15 minutes, temperature is risen to 125 DEG C and be decompressed to-
Remove vacuum after 0.094MPa vacuum dehydration 2 hours, be then cooled to 60 DEG C and to keep temperature be 60 DEG C, add 3-ethoxy-
1,3-oxazolidine is 400 revs/min with rotating speed and stirs 30 minutes, and being eventually adding dibutyl tin laurate with rotating speed is 400 revs/min
Stir 60 minutes, be cooled to 30 DEG C of dischargings, obtain B part;
(3) component A is uniformly mixed with B component.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 1.
Embodiment 2
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic by zinc dihydrogen phosphate, Zinc Tungstate by matter
Amount is uniformly mixed than for 1:1 and obtains.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 2.
Embodiment 3
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic is by Silver monobromide, Zinc Tungstate in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 3.
Embodiment 4
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic by Silver monobromide, zinc dihydrogen phosphate by matter
Amount is uniformly mixed than for 1:1 and obtains.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 4.
Embodiment 5
Substantially the same manner as Example 1, differ only in: described fire retardant by eight bromo ether, TDE by quality
Obtain than being uniformly mixed for 1:1.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 5.
Embodiment 6
Substantially the same manner as Example 1, differ only in: described fire retardant is pressed by deca-BDE, TDE
Mass ratio is that 1:1 is uniformly mixed and obtains.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 6.
Embodiment 7
Substantially the same manner as Example 1, differ only in: described fire retardant is by deca-BDE, eight bromo ether in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the high ferro flame-resistant polyurethane waterproof coating of embodiment 7.
Test case 1
The fire resistance of the high ferro flame-resistant polyurethane waterproof coating preparing embodiment 1-7 is tested.Specifically
Test result is shown in Table 1.
Table 1: fire resistance test table
Oxygen index (OI) LOI value, % | |
Embodiment 1 | 43.4 |
Embodiment 2 | 41.5 |
Embodiment 3 | 42.2 |
Embodiment 4 | 41.8 |
Embodiment 5 | 38.1 |
Embodiment 6 | 38.7 |
Embodiment 7 | 38.5 |
Comparing embodiment 1 and embodiment 2-4, embodiment 1 (Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate are compounding) fire resistance
It is substantially better than embodiment 2-4 (in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate, arbitrarily the two is compounding).
Comparing embodiment 1 and embodiment 5-7, embodiment 1 (deca-BDE, eight bromo ether, TDE are compounding) resistance
Combustion performance is substantially better than embodiment 5-7 (in deca-BDE, eight bromo ether, TDE, arbitrarily the two is compounding).
Test case 2
The anti-microbial property of the high ferro flame-resistant polyurethane waterproof coating preparing embodiment 1-7 is tested, antibacterial
Performance presses GB/T21866-2008 antibiotic paint anti-microbial property assay method and antibacterial effect, HG/T 3980-2007 antibiotic paint
Measure, escherichia coli ATYCC 25922, staphylococcus aureus ATCC 6538.Concrete test result is shown in Table 2.
Table 2: high ferro flame-resistant polyurethane waterproof coating anti-microbial property tests tables of data
Escherichia coli sterilizing rate, % | Staphylococcus aureus sterilizing rate, % | |
Embodiment 1 | 98.8 | 99.2 |
Embodiment 2 | 94.1 | 93.6 |
Embodiment 3 | 93.6 | 93.0 |
Embodiment 4 | 93.8 | 93.3 |
Embodiment 5 | 96.3 | 96.1 |
Embodiment 6 | 96.1 | 95.7 |
Embodiment 7 | 95.7 | 96.4 |
Comparing embodiment 1 and embodiment 2-4, embodiment 1 (Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate are compounding) anti-microbial property
It is substantially better than embodiment 2-4 (in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate, arbitrarily the two is compounding).
Comparing embodiment 1 and embodiment 5-7, embodiment 1 (deca-BDE, eight bromo ether, TDE are compounding) is anti-
Bacterium performance is substantially better than embodiment 5-7 (in deca-BDE, eight bromo ether, TDE, arbitrarily the two is compounding).
Claims (7)
1. a high ferro flame-resistant polyurethane waterproof coating, it is characterised in that be prepared from by the raw material of following weight parts: polyethers
Polyhydric alcohol 45-55 part, hexamethylene diisocyanate 10-20 part, n-butyl phthalate 0.4-0.8 part, dimethylbenzene 10-20
Part, chlorinated paraffin 10-20 part, Kaolin 15-25 part, calcium carbonate 5-15 part, 3-ethoxy-1,3-oxazolidine 4-9 part, two Laurels
Acid dibutyl tin 0.3-0.6 part, inorganic antiseptic 2-8 part, fire retardant 1-5 part.
2. high ferro flame-resistant polyurethane waterproof coating as claimed in claim 1, it is characterised in that: described inorganic antiseptic is
The mixture of one or more in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate.
3. high ferro flame-resistant polyurethane waterproof coating as claimed in claim 2, it is characterised in that: described inorganic antiseptic by
Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate mix, and described Silver monobromide, zinc dihydrogen phosphate, the mass ratio of Zinc Tungstate are (1-3):
(1-3): (1-3).
4. the high ferro flame-resistant polyurethane waterproof coating as according to any one of claim 1-3, it is characterised in that: described resistance
Combustion agent is the mixture of one or more in deca-BDE, eight bromo ether, TDE.
5. high ferro flame-resistant polyurethane waterproof coating as claimed in claim 4, it is characterised in that: described fire retardant is by ten bromines
Diphenyl ether, eight bromo ether, TDE mix, described deca-BDE, eight bromo ether, the mass ratio of TDE
For (1-3): (1-3): (1-3).
6. the high ferro flame-resistant polyurethane waterproof coating as according to any one of claim 1-3, it is characterised in that: described is poly-
The hydroxyl value of ethoxylated polyhydric alcohol is 18-38mgKOH/g, can be one or more compositions in polyethers HPOP40, polyethers EP-330N (G).
7. the preparation method of the high ferro flame-resistant polyurethane waterproof coating as described in any one of claim 1-6, it is characterised in that
Comprise the following steps:
(1) by proportioning, polyether polyol is added in reactor, temperature is risen to 100-110 DEG C and be decompressed to-0.092MPa~-
0.096MPa vacuum dehydration removed vacuum after 20-40 minute, is cooled to 75-85 DEG C and adds 1, and hexamethylene-diisocyanate with rotating speed is
300-600 rev/min is stirred 2-3 hour, is subsequently adding n-butyl phthalate with rotating speed for 300-600 rev/min of stirring 20-
40 minutes, cooling discharge, obtain component A;
(2) by proportioning, dimethylbenzene, chlorinated paraffin are added in reactor, temperature is risen to 85-95 DEG C and adds Kaolin, carbonic acid
Calcium, inorganic antiseptic, fire retardant stir 10-20 minute with rotating speed for 300-600 rev/min, temperature rises to 120-130 DEG C and subtracts
Remove vacuum after being depressed into-0.092MPa~-0.096MPa vacuum dehydration 1.5-2.5 hour, be then cooled to 55-65 DEG C and add 3-
Ethoxy-1,3-oxazolidine with rotating speed for 300-600 rev/min stir 20-40 minute, be eventually adding dibutyl tin laurate with
Rotating speed is 300-600 rev/min and stirs 30-90 minute, and cooling discharge obtains B part;
(3) component A it is uniformly mixed with B component and get final product.