CN106243973A - High ferro antibacterial water-repellent paint and preparation method thereof - Google Patents
High ferro antibacterial water-repellent paint and preparation method thereof Download PDFInfo
- Publication number
- CN106243973A CN106243973A CN201610615494.3A CN201610615494A CN106243973A CN 106243973 A CN106243973 A CN 106243973A CN 201610615494 A CN201610615494 A CN 201610615494A CN 106243973 A CN106243973 A CN 106243973A
- Authority
- CN
- China
- Prior art keywords
- high ferro
- repellent paint
- antibacterial water
- parts
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of high ferro antibacterial water-repellent paint and preparation method thereof, described high ferro is prepared from by the raw material of following weight parts with antibacterial water-repellent paint: polyether polyol 95 105 parts, 10 20 parts of double (4 isocyanatophenyl) methane, calcium carbonate 5 15 parts, sodium hydroxymethane sulfonate 4 14 parts, dimethicone 0.1 0.5 parts, hollow glass micropearl 45 55 parts, inorganic antiseptic 28 parts, fire retardant 15 parts.High ferro antibacterial water-repellent paint and preparation method thereof that the present invention provides, by rational proportioning, preferably go out the fire retardant of the antibacterial water-repellent paint of applicable high ferro, inorganic antiseptic kind and consumption, improve mildew resistance, antibiotic property, anti-flammability, there is physical and mechanical properties, temperature tolerance, weatherability, resistant to chemical media and the prominent wearability of excellence, easy construction, efficiency is high.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of high ferro antibacterial water-repellent paint and preparation method thereof.
Background technology
High-speed railway is called for short " high ferro ", refers to, by transforming original circuit (linearization(-sation), gauge standardization), make the highest operation
Speed reaches not less than 200 kilometers per hour, or builds new " the newest line " specially, makes operation speed reach the most extremely
The railway system of few 250 kilometers.
Waterproof material mainly has three classes: waterproof roll, polyurethane waterproof material, new polymers cement group water-proofing material.
It is wet that waterproof material is primarily used to prevent in rainwater, subsoil water, industrial and civilian plumbing, corrosive liquids and air
Gas, steam etc. invade building.
Railway line is mainly made up of roadbed, bridge and tunnel, and due to high ferro, the operation characteristic of Line for Passenger Transportation, the line is busy for bridge
Road ratio is significantly increased, more than 50%.Waterproof layer is set at bridge concrete bridge floor, can effectively intercept water and penetrate into floorings
In structure, slow down steel bar corrosion in the aging of concrete and floorings, thus reach to improve the mesh of concrete bridge structure durability
's.So bridge deck water-proof is an important component part in concrete-bridge engineering, current high ferro is with antibacterial water-repellent paint mould
Amount and elasticity can not be taken into account.
Existing high ferro polyurethane water-proof paint, because hot strength needs, it is generally two component polyurethane, is divided into first
Component and second component, in use need to mix first, second component according to a certain percentage, could use after stirring.
General first component is base polyurethane prepolymer for use as, and second component is curing system.Because bi-component high ferro polyurethane water-proof paint is being executed
There is burden process before work, so being susceptible to measure mistake, causing waterproof coating physical property and waterproof effect to reduce;Coating
Whipping process easily bubbles, makes easily to occur in the middle of waterproof coating dark bubble, pin hole, affect outward appearance and waterproof effect;First, second group
Dividing after stirring, it is necessary to make to be finished material within its hardening time, otherwise material can make viscosity rise, after retrogradation because of reaction
Cannot scratch or roller coat.
The invention provides a kind of antibacterial water-repellent paint of high ferro, there is waterproof, fire-retardant, the antibacterial effect of excellence.
Summary of the invention
For above-mentioned deficiency present in prior art, one of the technical problem to be solved is to provide a kind of high
The antibacterial water-repellent paint of ferrum.
The two of the technical problem to be solved are to provide a kind of high ferro preparation method with antibacterial water-repellent paint.
The present invention seeks to be achieved through the following technical solutions:
A kind of antibacterial water-repellent paint of high ferro, is prepared from by the raw material of following weight parts: polyether polyol 95-105 part,
Double (4-isocyanatophenyl) methane 10-20 part, calcium carbonate 5-15 part, sodium hydroxymethane sulfonate 4-14 part, dimethicone
0.1-0.5 part, hollow glass micropearl 45-55 part, inorganic antiseptic 2-8 part, fire retardant 1-5 part.
Preferably, described inorganic antiseptic is the mixing of one or more in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate
Thing.
It is highly preferred that described inorganic antiseptic is mixed by Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate, described bromination
Silver, zinc dihydrogen phosphate, the mass ratio of Zinc Tungstate are (1-3): (1-3): (1-3).
Preferably, described fire retardant is the mixing of one or more in deca-BDE, eight bromo ether, TDE
Thing.
It is highly preferred that described fire retardant is mixed by deca-BDE, eight bromo ether, TDE, described ten
Dibromodiphenyl ether, eight bromo ether, the mass ratio of TDE are (1-3): (1-3): (1-3).
Preferably, the hydroxyl value of described polyether polyol is 50-120mgKOH/g, can be polyethers DL-1000D, polyethers
One or more compositions in MN-3050D.
Preferably, the heat conductivity of described hollow glass micropearl is 0.02-0.06W/m K, particle diameter 20-60 μm.
Present invention also offers the above-mentioned high ferro preparation method with antibacterial water-repellent paint, comprise the following steps:
(1) by proportioning, polyether polyol is added in reactor, temperature is risen to 100-110 DEG C and be decompressed to-
0.092MPa~-0.096MPa vacuum dehydration removed vacuum after 20-40 minute, is cooled to 75-85 DEG C and adds double (4-isocyanates
Base phenyl) methane with rotating speed for 300-600 rev/min stir 2-3 hour, cooling discharge, obtain component A;
(2) by proportioning, calcium carbonate, sodium hydroxymethane sulfonate, hollow glass micropearl, inorganic antiseptic, fire retardant are added reaction
In still, remove after temperature being risen to 110-120 DEG C and being decompressed to-0.092MPa~-0.096MPa vacuum dehydration 1.5-2.5 hour
Vacuum, is then cooled to 55-65 DEG C of addition dimethicone and stirs 10-20 minute for 300-600 rev/min with rotating speed, lower the temperature and
Material, obtains B part;
(3) component A it is uniformly mixed with B component and get final product.
High ferro antibacterial water-repellent paint and preparation method thereof that the present invention provides, by rational proportioning, preferably goes out applicable
The high ferro fire retardant of antibacterial water-repellent paint, inorganic antiseptic kind and consumption, improve mildew resistance, antibiotic property, anti-flammability, tool
There are physical and mechanical properties, temperature tolerance, weatherability, resistant to chemical media and prominent wearability, easy construction, the efficiency of excellence
High.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further, the following stated, is only the preferable enforcement to the present invention
Example, not does the restriction of other forms to the present invention, and any those skilled in the art are possibly also with the disclosure above
Technology contents be changed to the Equivalent embodiments that changes on an equal basis.Every without departing from the present invention program content, according to the present invention
Technical spirit any simple modification that following example are done or equivalent variations, all fall within protection scope of the present invention.
Each raw material introduction in embodiment:
Dimethicone, No. CAS: 63148-62-9.
Hollow glass micropearl, the heat conductivity using Zhejiang Hai Yue new material limited company to provide is 0.043W/m
K, the hollow glass micropearl of particle diameter 40 μm.
Sodium hydroxymethane sulfonate, No. CAS: 870-72-4.
Double (4-isocyanatophenyl) methane, No. CAS: 101-68-8.
Calcium carbonate, No. CAS: 471-34-1, use the 325 mesh lightweight carbonic acid that Lingshou County Zhen Ling mineral products processing factory provides
Calcium.
Polyethers DL-1000D, the trade mark using Shandong Lanxing Dongda Chemical Co., Ltd to provide is DL-1000D, hydroxyl
Value is the polyether polyol of 109-115mgKOH/g.
Polyethers MN-3050D, the trade mark using Shandong Lanxing Dongda Chemical Co., Ltd to provide is MN-3050D, hydroxyl
Value is the polyether polyol of 54.5-57.5mgKOH/g.
Silver monobromide, No. CAS: 7785-23-1, particle diameter 800 mesh.
Zinc dihydrogen phosphate, No. CAS: 13598-37-3, particle diameter 800 mesh.
Zinc Tungstate, No. CAS: 13597-56-3, particle diameter 800 mesh.
Deca-BDE, No. CAS: 1163-19-5.
Eight bromo ether, No. CAS: 21850-44-2.
TDE, No. CAS: 84852-53-9.
Embodiment 1
High ferro antibacterial water-repellent paint raw material (weight portion): polyethers DL-1000D 70 parts, polyethers MN-3050D 30 parts, double
16 parts of (4-isocyanatophenyl) methane, calcium carbonate 10 parts, sodium hydroxymethane sulfonate 8 parts, dimethicone 0.3 part, hollow glass
Glass microballon 50 parts, inorganic antiseptic 3 parts, fire retardant 1.5 parts.
Described inorganic antiseptic is uniformly mixed for 1:1:1 in mass ratio by Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate
Obtain.
Described fire retardant is by deca-BDE, eight bromo ether, TDE in mass ratio for 1:1:1 stirring mixing all
Even obtain.
The high ferro preparation of antibacterial water-repellent paint:
(1) by proportioning, polyethers DL-1000D, polyethers MN-3050D are added in reactor, temperature is risen to 105 DEG C and subtracts
Remove vacuum after being depressed into-0.095MPa vacuum dehydration 30 minutes, be cooled to 80 DEG C and to keep temperature be 80 DEG C, add that double (4-is different
Cyanatephenyl) methane is that 400 revs/min of stirrings are cooled to 30 DEG C of dischargings for 2.5 hours with rotating speed, obtains component A;
(2) by proportioning, calcium carbonate, sodium hydroxymethane sulfonate, hollow glass micropearl, inorganic antiseptic, fire retardant are added reaction
In still, remove vacuum after temperature being risen to 115 DEG C and being decompressed to-0.094MPa vacuum dehydration 2 hours, be then cooled to 60 DEG C also
Keeping temperature is 60 DEG C, and adding dimethicone with rotating speed is 400 revs/min of stirrings 15 minutes, is cooled to 30 DEG C of dischargings, obtains B
Part;
(3) component A is uniformly mixed with B component.Obtain the antibacterial water-repellent paint of high ferro of embodiment 1.
Embodiment 2
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic by zinc dihydrogen phosphate, Zinc Tungstate by matter
Amount is uniformly mixed than for 1:1 and obtains.Obtain the antibacterial water-repellent paint of high ferro of embodiment 2.
Embodiment 3
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic is by Silver monobromide, Zinc Tungstate in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the antibacterial water-repellent paint of high ferro of embodiment 3.
Embodiment 4
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic by Silver monobromide, zinc dihydrogen phosphate by matter
Amount is uniformly mixed than for 1:1 and obtains.Obtain the antibacterial water-repellent paint of high ferro of embodiment 4.
Embodiment 5
Substantially the same manner as Example 1, differ only in: described fire retardant by eight bromo ether, TDE by quality
Obtain than being uniformly mixed for 1:1.Obtain the antibacterial water-repellent paint of high ferro of embodiment 5.
Embodiment 6
Substantially the same manner as Example 1, differ only in: described fire retardant is pressed by deca-BDE, TDE
Mass ratio is that 1:1 is uniformly mixed and obtains.Obtain the antibacterial water-repellent paint of high ferro of embodiment 6.
Embodiment 7
Substantially the same manner as Example 1, differ only in: described fire retardant is by deca-BDE, eight bromo ether in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the antibacterial water-repellent paint of high ferro of embodiment 7.
Test case 1
The high ferro the preparing embodiment 1-7 fire resistance of antibacterial water-repellent paint is tested.Specifically test knot
Fruit is shown in Table 1.
Table 1: fire resistance test table
Comparing embodiment 1 and embodiment 2-4, embodiment 1 (Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate are compounding) fire resistance
It is substantially better than embodiment 2-4 (in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate, arbitrarily the two is compounding).
Comparing embodiment 1 and embodiment 5-7, embodiment 1 (deca-BDE, eight bromo ether, TDE are compounding) resistance
Combustion performance is substantially better than embodiment 5-7 (in deca-BDE, eight bromo ether, TDE, arbitrarily the two is compounding).
Test case 2
The high ferro the preparing embodiment 1-7 anti-microbial property of antibacterial water-repellent paint is tested, and anti-microbial property is pressed
GB/T21866-2008 antibiotic paint anti-microbial property assay method and antibacterial effect, HG/T3980-2007 antibiotic paint measure, greatly
Enterobacteria ATYCC 25922, staphylococcus aureus ATCC6538.Concrete test result is shown in Table 2.
Table 2: high ferro tests tables of data with antibacterial water-repellent paint anti-microbial property
Escherichia coli sterilizing rate, % | Staphylococcus aureus sterilizing rate, % | |
Embodiment 1 | 98.7 | 99.0 |
Embodiment 2 | 93.4 | 93.2 |
Embodiment 3 | 93.7 | 93.7 |
Embodiment 4 | 93.1 | 92.8 |
Embodiment 5 | 95.4 | 95.2 |
Embodiment 6 | 95.6 | 95.4 |
Embodiment 7 | 96.2 | 95.8 |
Comparing embodiment 1 and embodiment 2-4, embodiment 1 (Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate are compounding) anti-microbial property
It is substantially better than embodiment 2-4 (in Silver monobromide, zinc dihydrogen phosphate, Zinc Tungstate, arbitrarily the two is compounding).
Comparing embodiment 1 and embodiment 5-7, embodiment 1 (deca-BDE, eight bromo ether, TDE are compounding) is anti-
Bacterium performance is substantially better than embodiment 5-7 (in deca-BDE, eight bromo ether, TDE, arbitrarily the two is compounding).
Claims (7)
1. the antibacterial water-repellent paint of high ferro, it is characterised in that be prepared from by the raw material of following weight parts: polyether polyol
95-105 part, double (4-isocyanatophenyl) methane 10-20 part, calcium carbonate 5-15 part, sodium hydroxymethane sulfonate 4-14 part, diformazan
Base silicone oil 0.1-0.5 part, hollow glass micropearl 45-55 part, inorganic antiseptic 2-8 part, fire retardant 1-5 part.
2. the antibacterial water-repellent paint of high ferro as claimed in claim 1, it is characterised in that: described inorganic antiseptic is bromination
The mixture of one or more in silver, zinc dihydrogen phosphate, Zinc Tungstate.
3. the antibacterial water-repellent paint of high ferro as claimed in claim 2, it is characterised in that: described inorganic antiseptic is by bromination
Silver, zinc dihydrogen phosphate, Zinc Tungstate mix, and described Silver monobromide, zinc dihydrogen phosphate, the mass ratio of Zinc Tungstate are (1-3): (1-
3): (1-3).
4. the antibacterial water-repellent paint of the high ferro as according to any one of claim 1-3, it is characterised in that: described fire retardant is
The mixture of one or more in deca-BDE, eight bromo ether, TDE.
5. the antibacterial water-repellent paint of high ferro as claimed in claim 4, it is characterised in that: described fire retardant is by decabrominated dipheny
Ether, eight bromo ether, TDE mix, and described deca-BDE, eight bromo ether, the mass ratio of TDE are
(1-3): (1-3): (1-3).
6. the antibacterial water-repellent paint of the high ferro as according to any one of claim 1-3, it is characterised in that: described polyether polyols
The hydroxyl value of alcohol is 50-120mgKOH/g, can be one or more compositions in polyethers DL-1000D, polyethers MN-3050D.
7. the preparation method of antibacterial water-repellent paint of the high ferro as described in any one of claim 1-6, it is characterised in that include with
Lower step:
(1) by proportioning, polyether polyol is added in reactor, temperature is risen to 100-110 DEG C and be decompressed to-0.092MPa~-
0.096MPa vacuum dehydration removed vacuum after 20-40 minute, is cooled to 75-85 DEG C and adds double (4-isocyanatophenyl) methane
Stir 2-3 hour for 300-600 rev/min with rotating speed, cooling discharge, obtain component A;
(2) by proportioning, calcium carbonate, sodium hydroxymethane sulfonate, hollow glass micropearl, inorganic antiseptic, fire retardant are added reactor
In, remove true after temperature being risen to 110-120 DEG C and being decompressed to-0.092MPa~-0.096MPa vacuum dehydration 1.5-2.5 hour
Sky, is then cooled to 55-65 DEG C of addition dimethicone and stirs 10-20 minute for 300-600 rev/min with rotating speed, cooling discharge,
Obtain B part;
(3) component A it is uniformly mixed with B component and get final product.