CN106193278A - A kind of integrated house made by silicon magnesium base composite material and building method thereof - Google Patents

A kind of integrated house made by silicon magnesium base composite material and building method thereof Download PDF

Info

Publication number
CN106193278A
CN106193278A CN201610718907.0A CN201610718907A CN106193278A CN 106193278 A CN106193278 A CN 106193278A CN 201610718907 A CN201610718907 A CN 201610718907A CN 106193278 A CN106193278 A CN 106193278A
Authority
CN
China
Prior art keywords
floor
integrated house
wallboard
adjuvant
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610718907.0A
Other languages
Chinese (zh)
Inventor
石文杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610718907.0A priority Critical patent/CN106193278A/en
Publication of CN106193278A publication Critical patent/CN106193278A/en
Pending legal-status Critical Current

Abstract

The invention belongs to building construction technology field, particularly relate to a kind of integrated house made by silicon magnesium base composite material and building method thereof.Each ingredient of integrated house of the present invention is raw materials used the most cheap and easy to get, synthesizes in conjunction with wastes straw, wood flour etc., economizes on resources and the energy；Mixing between raw material, without mould and stripping operation, saves technique, reduces cost；The construction material prepared possess good fire prevention, waterproof, do not fire, be incubated, ageing-resistant, moistureproof, anti-deformation, for green structural material.The present invention can process each ingredient needed for house according to design drawing, on-the-spot without cutting, in the way of " playing with building blocks ", tenon structure and steel girth member is used assembling between beam, post, wallboard, floor to be built, time and labour saving, easy transportation and installation, it is achieved construction and installation, building heat preservation and construction and decoration synchronous integrated.

Description

A kind of integrated house made by silicon magnesium base composite material and building method thereof
Technical field
The invention belongs to building construction technology field, particularly relate to a kind of integrated house made by silicon magnesium base composite material and Its building method.
Background technology
Existing house/building generally uses armored concrete and brick masonry, suffers a disadvantage in that building site cast-type building Can cause large-area noise pollution and environmental pollution, construction intensity is big, long in time limit, and after completion, usually blank is built, and deposits In yielding, the moisture absorption, the problem such as resistance to ag(e)ing is poor, heat insulation effect is poor.
Summary of the invention
The present invention is directed to the deficiency that above-mentioned prior art exists, it is provided that a kind of function admirable, site-assembled answered by silicon magnesium The integrated house of condensation material making and building method thereof.
The technical scheme is that a kind of integrated house made by silicon magnesium base composite material Room, including beam, post, wallboard, floor, floor, decorative panel and roofing tile；
Wherein, described beam, post, floor, floor and roofing tile is by major ingredient, adjuvant, glass fabric and garbage powder It is prepared from；
Described wallboard is single wallboard or combined wall board: described single wallboard is by major ingredient, adjuvant, glass fabric, useless Gurry powder and granular polystyrene are prepared from；Described combined wall board is prepared by major ingredient, adjuvant, glass fabric and garbage powder Wallboard, then be composited with warming plate；
Described decorative panel is prepared from by major ingredient, adjuvant and glass fabric；
Described major ingredient includes that 5-15 part silicate, 20-30 part kieselguhr, 5-20 part Gypsum Fibrosum, 1-10 part are swollen by weight Profit soil, 75-90 part magnesium chloride, 75-90 part magnesium oxide, 2-18 part cellulose, 5-10 part Pulvis Talci and 100-150 part water；
Described adjuvant includes 20-40 part wood flour, 5-30 part stalk powder and 5-10 part glass fibre by weight.
Further, described warming plate is polyurethane sheet, rock cotton board or extruded polystyrene board.
Further, described glass fabric is alkali-free glass fiber cloth or medium alkali fiber cloth.
Further, described garbage powder is wood flour powder or agricultural straw powder.
Further, described silicate is calcium silicates or magnesium silicate.
Further, described glass fibre is that 2-3cm length is thread.
The building method of the above-mentioned integrated house made by silicon magnesium base composite material: use the fourth of the twelve Earthly Branches between beam, post, wallboard, floor Tenon structure and steel girth member are mutually combined and build.
Wherein, the gap between the beam that erects, post, wallboard, floor uses sealing compound bonding, and described sealing compound is by leading Material is made.
Illustrate: in the adjuvant of described wallboard, the consumption of wood flour and stalk powder is more, described decorative panel, floor, floor and In the adjuvant of roofing tile, the consumption of wood flour and stalk powder is less, described beam, post adjuvant in wood flour and the consumption of stalk powder It is between the two.
The beneficial effects of the present invention is:
1, each ingredient of integrated house of the present invention is raw materials used the most cheap and easy to get, in conjunction with wastes straw, wood flour etc. Synthesis, it is achieved renewable resource utilization, economizes on resources and the energy；Mixing between raw material, without mould and stripping operation, saves work Skill, reduces cost；The construction material prepared possess good fire prevention, waterproof, do not fire, be incubated, ageing-resistant, moistureproof, resistance Shape performance, plasticity is strong, for green structural material.
2, the present invention can process each ingredient needed for house according to design drawing, on-the-spot without cutting, " to take Building blocks " mode, use tenon structure and steel girth member assembling between beam, post, wallboard, floor to be built, save time province Work, easy transportation and installation, reduce building cost, 5-6 workman can complete a set of 300m in 7-9 days2House build, comply with The economic construction development advocated at present, is the development trend of following real estate sector.
3, according to different geographical, different cities and the building demand of different client, beam of the present invention, post, wallboard, building are adjusted The consumption of each major ingredient, adjuvant and other raw materials in plate, floor, decorative panel and roofing tile, thus realize building, the individual character of finishing Change.Utilizing the integrated house that material of the present invention is built, in house, sheet material class decoration and furniture all can pass through major ingredient, adjuvant and accordingly Other performance materials combine and prepare, it is achieved construction and installation, building heat preservation and construction and decoration synchronous integrated, and the house built is anti- Fiery, waterproof, do not fire, be incubated, the aspect performance such as waterproof anti-corrosion all shows excellence.
Detailed description of the invention
Being described principle and the feature of the present invention below in conjunction with example, example is served only for explaining the present invention, and Non-for limiting the scope of the present invention.
Embodiment 1
A kind of integrated house made by silicon magnesium base composite material, including beam, post, wallboard, floor, floor, decorative panel and room Face watt, uses tenon structure and steel girth member to be mutually combined and build between described beam, post, wallboard, floor；
Wherein, described beam, post, floor, floor and roofing tile are by major ingredient, adjuvant, alkali-free glass fiber cloth and wood dust End is prepared from；
Described wallboard is single wallboard, by major ingredient, adjuvant, alkali-free glass fiber cloth, wood flour powder and granular polystyrene system For forming；
Described decorative panel is prepared from by major ingredient, adjuvant and alkali-free glass fiber cloth；
The major ingredient of described beam, post, floor, floor, roofing tile, wallboard and decorative panel include by weight 5 parts of calcium silicates, 20 Part kieselguhr, 10 parts of Gypsum Fibrosum, 5 parts of bentonite, 80 parts of magnesium chlorides, 80 parts of magnesium oxide, 2 parts of celluloses, 10 parts of Pulvis Talci and 100 parts Water；
Described beam, the adjuvant of post include 30 parts of wood flours, 20 parts of stalk powders and 8 parts of glass fibre by weight.
The adjuvant of described wallboard includes 40 parts of wood flours, 30 parts of stalk powders and 8 parts of glass fibre by weight.
Described decorative panel, floor, floor and roofing tile include 20 parts of wood flours, 5 parts of stalk powders and 8 parts of glass by weight Fiber.
Embodiment 2
A kind of integrated house made by silicon magnesium base composite material, including beam, post, wallboard, floor, floor, decorative panel and room Face watt, uses tenon structure and steel girth member to be mutually combined and build between described beam, post, wallboard, floor；
Wherein, described beam, post, floor, floor and roofing tile is by major ingredient, adjuvant, medium alkali fiber cloth and agricultural straw Stalk powder is prepared from；
Described wallboard is single wallboard, by major ingredient, adjuvant, medium alkali fiber cloth, agricultural straw powder and polyphenyl Grain is prepared from；
Described decorative panel is prepared from by major ingredient, adjuvant and medium alkali fiber cloth；
The major ingredient of described beam, post, floor, floor, roofing tile, wallboard and decorative panel include by weight 15 parts of magnesium silicates, 30 parts of kieselguhr, 5 parts of Gypsum Fibrosum, 10 parts of bentonite, 75 parts of magnesium chlorides, 75 parts of magnesium oxide, 18 parts of celluloses, 5 parts of Pulvis Talci and 120 Part water；
Described beam, the adjuvant of post include 30 parts of wood flours, 20 parts of stalk powders and 5 parts of glass fibre by weight.
The adjuvant of described wallboard includes 40 parts of wood flours, 30 parts of stalk powders and 5 parts of glass fibre by weight.
Described decorative panel, floor, floor and roofing tile include 20 parts of wood flours, 5 parts of stalk powders and 5 parts of glass by weight Fiber.
Embodiment 3
A kind of integrated house made by silicon magnesium base composite material, including beam, post, wallboard, floor, floor, decorative panel and room Face watt, uses tenon structure and steel girth member to be mutually combined and build between described beam, post, wallboard, floor；
Wherein, described beam, post, floor, floor and roofing tile is by major ingredient, adjuvant, medium alkali fiber cloth and agricultural straw Stalk powder is prepared from；
Described wallboard is combined wall board, major ingredient, adjuvant, medium alkali fiber cloth and agricultural straw powder prepare wallboard, It is composited with polyurethane thermal insulation board again；
Described decorative panel is prepared from by major ingredient, adjuvant and medium alkali fiber cloth；
The major ingredient of described beam, post, floor, floor, roofing tile, wallboard and decorative panel include by weight 10 parts of magnesium silicates, 25 parts of kieselguhr, 20 parts of Gypsum Fibrosum, 1 part of bentonite, 90 parts of magnesium chlorides, 90 parts of magnesium oxide, 9 parts of celluloses, 8 parts of Pulvis Talci and 150 Part water；
Described beam, the adjuvant of post include 30 parts of wood flours, 20 parts of stalk powders and 10 parts of glass fibre by weight.
The adjuvant of described wallboard includes 40 parts of wood flours, 30 parts of stalk powders and 10 parts of glass fibre by weight.
Described decorative panel, floor, floor and roofing tile include 20 parts of wood flours, 5 parts of stalk powders and 10 parts of glass by weight Glass fiber.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.

Claims (7)

1. the integrated house made by silicon magnesium base composite material, it is characterised in that include beam, post, wallboard, floor, floor, dress Plaque and roofing tile；
Wherein, described beam, post, floor, floor and roofing tile is prepared by major ingredient, adjuvant, glass fabric and garbage powder Form；
Described wallboard is single wallboard or combined wall board: described single wallboard is by major ingredient, adjuvant, glass fabric, garbage Powder and granular polystyrene are prepared from；Described combined wall board is prepared wall by major ingredient, adjuvant, glass fabric and garbage powder Plate, then be composited with warming plate；
Described decorative panel is prepared from by major ingredient, adjuvant and glass fabric；
Described major ingredient include by weight 5-15 part silicate, 20-30 part kieselguhr, 5-20 part Gypsum Fibrosum, 1-10 part bentonite, 75-90 part magnesium chloride, 75-90 part magnesium oxide, 2-18 part cellulose, 5-10 part Pulvis Talci and 100-150 part water；
Described adjuvant includes 20-40 part wood flour, 5-30 part stalk powder and 5-10 part glass fibre by weight.
Integrated house the most according to claim 1, it is characterised in that described warming plate be polyurethane sheet, rock cotton board or Extruded polystyrene board.
Integrated house the most according to claim 1, it is characterised in that described glass fabric is alkali-free glass fiber cloth Or medium alkali fiber cloth.
Integrated house the most according to claim 1, it is characterised in that described garbage powder is wood flour powder or agricultural Stalk powder.
Integrated house the most according to claim 1, it is characterised in that described silicate is calcium silicates or magnesium silicate.
Integrated house the most according to claim 1, it is characterised in that described glass fibre is that 2-3cm length is thread.
7. the building method of the integrated house made by silicon magnesium base composite material described in a claim 1, it is characterised in that beam, Tenon structure and steel girth member is used to be mutually combined and build between post, wallboard, floor.
CN201610718907.0A 2016-08-25 2016-08-25 A kind of integrated house made by silicon magnesium base composite material and building method thereof Pending CN106193278A (en)