CN105649240A - Folded plate type inorganic high-strength keel light wall - Google Patents
Folded plate type inorganic high-strength keel light wall Download PDFInfo
- Publication number
- CN105649240A CN105649240A CN201511014131.6A CN201511014131A CN105649240A CN 105649240 A CN105649240 A CN 105649240A CN 201511014131 A CN201511014131 A CN 201511014131A CN 105649240 A CN105649240 A CN 105649240A
- Authority
- CN
- China
- Prior art keywords
- strength
- inorganic high
- draconis
- flap type
- type inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a folded plate type inorganic high-strength keel light wall which comprises an inorganic high-strength inner panel, an inorganic high-strength outer panel and folded plate type inorganic high-strength keels, wherein the folded plate type inorganic high-strength keelsare pasted between the inorganic high-strength inner panel and the inorganic high-strength outer panel through an inorganic gelling agent; filling layers are formed between the folded plate type inorganic high-strength keels and the inorganic high-strength inner panel and between the folded plate type inorganic high-strength keels and the inorganic high-strength outer panel; and one or more pipeline grooves are preset in the positions, near the end parts, of the folded plate type inorganic high-strength keels. According to the folded plate type inorganic high-strength keel light wall, the self weight is light and is 1/5 to 1/2 of the self weight of a traditional composite solid wall system, the seismic performance is excellent, and the overall bending strength and impact strength are twice or abovethose of the traditional composite solid wall system; a single board of the folded plate type inorganic high-strength keel light wall is large in size, simple in assembly, convenient to operate, and good in flatness, and can be sawed, driven with a nail and riveted; and the construction speed is twice or abovethe speed of traditional site construction, the comprehensive cost of constructional engineering is reduced, and the engineering quality is improved.
Description
Technical field
The present invention relates to Building technology apparatus field, specifically a kind of flap type inorganic high-strength Os Draconis light weight wall.
Background technology
Through advancing by leaps and bounds of economic construction decades, the ecological balance exacerbated of China, available resources significantly reduces. The green building new concept of " energy-conservation, save land, economize on water, material-saving and environmental conservation " is started to widely popularize for this country.
In China, popularization and application along with building industrialization and green building theory, masonry panel is because of from great, long construction period and the inferior position such as environmental pollution is serious and be eliminated, instead Light trabs technology emerges in an endless stream, from lath Light trabs the earliest to light steel keel gypsum board wallboard, the compound solid slab of light-weight foam core is added from Prefabricated porous lightweight concrete wall panel to calcium silicate board surface layer, although at material with technically achieved with great progress, but still also exist such as from great, bulk strength is poor, poor seismic behavior, sound insulation and fire protecting performance are poor, easily go mouldy, environmental pollution, toxic gas is easily discharged during fire, construction complexity and pipeline installation need to destroy the quality problems such as surface layer.
Light steel keel gypsum board body of wall has the drawback that intensity difference, fire prevention and water resistance are poor, paper easily goes mouldy, hanging ability is low, crashworthiness is poor, construction period length etc.; Although compound solid slab solves above-mentioned some drawbacks, but also exist from great, board material splice is loosely easily caused poor seismic behavior, piece is that straight joint easy to crack causes fire prevention and sound insulation property to decline, pipeline fluting directly destroys the panel providing intensity and causes the series of problems such as potential safety hazard.
Summary of the invention
It is an object of the invention to provide a kind of flap type inorganic high-strength Os Draconis light weight wall, with the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of flap type inorganic high-strength Os Draconis light weight wall, including inorganic high-strength wainscot, inorganic high-strength outer panels and flap type inorganic high-strength Os Draconis, flap type inorganic high-strength Os Draconis are pasted onto between inorganic high-strength wainscot and inorganic high-strength outer panels by inorganic gel agent, and form packed layer between inorganic high-strength wainscot and inorganic high-strength outer panels, reserve one or multi-channel chase at flap type inorganic high-strength Os Draconis near end position.
As the further scheme of the present invention: described flap type inorganic high-strength Os Draconis are with magnesium oxide, magnesium chloride for binding agent, with glass fibre or other Plant fiber for strengthening thing, with flyash, wood flour, expanded perlite, straw for inserts, add modifying agent and maintain into the flap type Os Draconis of type through equipment roll-in.
As the further scheme of the present invention: the sheet material preparation method of described flap type inorganic high-strength Os Draconis is:
(1) by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes slurry;
(2) add in the slurry that step (1) is made quality accounts for the silicon dioxide of magnesium oxide quality 40-60%, flyash, sawdust or straw, be sufficiently stirred for obtain secondary slurry;
(3) all laying the glass-fiber-fabric of one layer of 80g-120g at the upper and lower surface of mould, the secondary serosity in step (2) carries out injection molding, the thickness controlling sheet forming is 4-6mm, and the sheet material after injection molding carries out roll-forming, must complete plate;
(4) completing plate by what step (3) obtained, under 30 degree Celsius of-45 degrees celsius, the demoulding after maintenance 12 hours, then through the room temperature maintenance of 4-7 days, cuts into the size of 1200mm*3000mm, stands 28 days, obtain flap type inorganic high-strength Os Draconis sheet material.
As the further scheme of the present invention: described inorganic high-strength wainscot, inorganic high-strength outer panels preparation method be:
(1) by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes slurry;
(2) add in the slurry that step (1) is made quality accounts for the silicon dioxide of magnesium oxide quality 40-60%, flyash, sawdust or straw, be sufficiently stirred for obtain secondary slurry;
(3) all laying the glass-fiber-fabric of one layer of 60g-120g at the upper and lower surface of mould, the secondary serosity in step (2) carries out injection molding, the thickness controlling sheet forming is 8-12mm, and the sheet material after injection molding carries out roll-forming, must complete plate;
(4) plate is completed by what step (3) obtained, under 30 degree Celsius of-45 degrees celsius, the demoulding after maintenance 12 hours, then through the room temperature maintenance of 4-7 days, cuts into the size of 1200mm*2400mm, stand 28 days, obtain inorganic high-strength wainscot, inorganic high-strength outer panels sheet material.
As the further scheme of the present invention: the preparation method of described inorganic gel agent is: by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes inorganic gel agent.
As the further scheme of the present invention: described packed layer is tolerant noise-insulating warm-keeping layer.
As the further scheme of the present invention: described tolerant noise-insulating warm-keeping layer is rock wool, glass cotton or foamed concrete.
As the further scheme of the present invention: described inorganic high-strength outer panels and flap type inorganic high-strength Os Draconis utilize inorganic gel agent to carry out pasting maintenance to have pasted in factory, described inorganic high-strength wainscot and flap type inorganic high-strength Os Draconis utilize inorganic gel agent to carry out pasting maintenance to have pasted 70% in factory, and remaining 30% carries out on-the-spot maintenance stickup.
Compared with prior art, the invention has the beneficial effects as follows:
1, flap type inorganic high-strength Os Draconis light weight wall is from heavy and light, is 1st/1st to five/2nd of conventional composite solid wall system, and anti-seismic performance is superior; Integral bending and impact strength are more than 2 times of conventional composite solid wall system;
2, flap type inorganic high-strength Os Draconis light weight wall individual plates area is big, assembled easily can saw, can follow closely, rivet clasp, easy to operate, flatness good, faster than traditional site operation more than two times, reduce architectural engineering comprehensive cost, improve construction quality;
3, inorganic high-strength panel and flap type inorganic high-strength Os Draconis adopt inorganic gel agent bonding, and the harmful gass such as adhesion strength is high, and durability is strong, formaldehydeless are polluted;
4, body of wall carries out pipeline installation, easy construction, accurate positioning after installing and being basically completed again, does not affect structural strength, does not produce a large amount of garbage, job site civilization.
Accompanying drawing explanation
Fig. 1 is the structural representation of flap type inorganic high-strength Os Draconis light weight wall.
Fig. 2 is the structural representation of the local, inside of flap type inorganic high-strength Os Draconis light weight wall.
In figure: 1-inorganic high-strength wainscot, 2-inorganic high-strength outer panels, 3-flap type inorganic high-strength Os Draconis, 4-packed layer, 5-provided pipe wire casing.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the technical scheme of this patent is described in more detail.
Refer to Fig. 1-2, a kind of flap type inorganic high-strength Os Draconis light weight wall, including inorganic high-strength wainscot 1, inorganic high-strength outer panels 2 and flap type inorganic high-strength Os Draconis 3, flap type inorganic high-strength Os Draconis 3 are pasted onto between inorganic high-strength wainscot 1 and inorganic high-strength outer panels 2 by inorganic gel agent, and form packed layer 4 between inorganic high-strength wainscot 1 and inorganic high-strength outer panels 2, reserve one or multi-channel chase 5 at flap type inorganic high-strength Os Draconis 3 near end position.
Described flap type inorganic high-strength Os Draconis 3 are with magnesium oxide, magnesium chloride for binding agent, with glass fibre or other Plant fiber for strengthening thing, with flyash, wood flour, expanded perlite, straw for inserts, add modifying agent and maintain into the flap type Os Draconis of type through equipment roll-in.
The sheet material preparation method of described flap type inorganic high-strength Os Draconis 3 is:
(1) by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes slurry;
(2) add in the slurry that step (1) is made quality accounts for the silicon dioxide of magnesium oxide quality 40-60%, flyash, sawdust or straw, be sufficiently stirred for obtain secondary slurry;
(3) all laying the glass-fiber-fabric of one layer of 80g-120g at the upper and lower surface of mould, the secondary serosity in step (2) carries out injection molding, the thickness controlling sheet forming is 4-6mm, and the sheet material after injection molding carries out roll-forming, must complete plate;
(4) completing plate by what step (3) obtained, under 30 degree Celsius of-45 degrees celsius, the demoulding after maintenance 12 hours, then through the room temperature maintenance of 4-7 days, cuts into the size of 1200mm*3000mm, stands 28 days, obtain flap type inorganic high-strength Os Draconis sheet material.
Described inorganic high-strength wainscot, inorganic high-strength outer panels preparation method be:
(1) by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes slurry;
(2) add in the slurry that step (1) is made quality accounts for the silicon dioxide of magnesium oxide quality 40-60%, flyash, sawdust or straw, be sufficiently stirred for obtain secondary slurry;
(3) all laying the glass-fiber-fabric of one layer of 60g-120g at the upper and lower surface of mould, the secondary serosity in step (2) carries out injection molding, the thickness controlling sheet forming is 8-12mm, and the sheet material after injection molding carries out roll-forming, must complete plate;
(4) plate is completed by what step (3) obtained, under 30 degree Celsius of-45 degrees celsius, the demoulding after maintenance 12 hours, then through the room temperature maintenance of 4-7 days, cuts into the size of 1200mm*2400mm, stand 28 days, obtain inorganic high-strength wainscot, inorganic high-strength outer panels sheet material.
The preparation method of described inorganic gel agent is: by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes inorganic gel agent.
Described packed layer 4 is tolerant noise-insulating warm-keeping layer, and described tolerant noise-insulating warm-keeping layer is rock wool, glass cotton or foamed concrete.
Described inorganic high-strength outer panels and flap type inorganic high-strength Os Draconis utilize inorganic gel agent to carry out pasting maintenance to have pasted in factory, described inorganic high-strength wainscot and flap type inorganic high-strength Os Draconis utilize inorganic gel agent to carry out pasting maintenance to have pasted 3 70% in factory, and remaining 30% carries out on-the-spot maintenance stickup. Position to be bonded at flap type inorganic high-strength Os Draconis and inorganic high-strength panel, pre-water spray is moistening, dry in the air to without substantially water stain, the inorganic gel agent of above-mentioned preparation is brushed respectively and bonds behind position to be bonded, after maintenance under 10MPa pressure room temperature 4 days can removal pressure, can use after continuing maintenance 20 days.
In the present invention, flap type inorganic high-strength Os Draconis light weight wall is from heavy and light, is 1st/1st to five/2nd of conventional composite solid wall system, and anti-seismic performance is superior; Integral bending and impact strength are more than 2 times of conventional composite solid wall system; Flap type inorganic high-strength Os Draconis light weight wall individual plates area is big, assembled easily can saw, can follow closely, rivet clasp, easy to operate, flatness good, faster than traditional site operation more than two times, reduce architectural engineering comprehensive cost, improve construction quality; Inorganic high-strength panel and flap type inorganic high-strength Os Draconis adopt inorganic gel agent bonding, and the harmful gass such as adhesion strength is high, and durability is strong, formaldehydeless are polluted; Body of wall install be basically completed after carry out pipeline installation, easy construction, accurate positioning again, do not affect structural strength, do not produce a large amount of garbage, job site civilization, keep in repair later circuit, transformation circuit also very convenient.
Above the better embodiment of this patent is explained in detail, but this patent is not limited to above-mentioned embodiment, in the ken that one skilled in the relevant art possesses, it is also possible to make a variety of changes under the premise without departing from this patent objective.
Claims (8)
1. a flap type inorganic high-strength Os Draconis light weight wall, it is characterized in that, including inorganic high-strength wainscot, inorganic high-strength outer panels and flap type inorganic high-strength Os Draconis, flap type inorganic high-strength Os Draconis are pasted onto between inorganic high-strength wainscot and inorganic high-strength outer panels by inorganic gel agent, and form packed layer between inorganic high-strength wainscot and inorganic high-strength outer panels, reserve one or multi-channel chase at flap type inorganic high-strength Os Draconis near end position.
2. flap type inorganic high-strength Os Draconis light weight wall according to claim 1, it is characterized in that, described flap type inorganic high-strength Os Draconis are with magnesium oxide, magnesium chloride for binding agent, with glass fibre or other Plant fiber for strengthening thing, with flyash, wood flour, expanded perlite, straw for inserts, add modifying agent and maintain into the flap type Os Draconis of type through equipment roll-in.
3. flap type inorganic high-strength Os Draconis light weight wall according to claim 2, it is characterised in that the sheet material preparation method of described flap type inorganic high-strength Os Draconis is:
(1) by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes slurry;
(2) add in the slurry that step (1) is made quality accounts for the silicon dioxide of magnesium oxide quality 40-60%, flyash, sawdust or straw, be sufficiently stirred for obtain secondary slurry;
(3) all laying the glass-fiber-fabric of one layer of 80g-120g at the upper and lower surface of mould, the secondary slurry in step (2) carries out injection molding, the thickness controlling sheet forming is 4-6mm, and the sheet material after injection molding carries out roll-forming, must complete plate;
(4) completing plate by what step (3) obtained, under 30 degree Celsius of-45 degrees celsius, the demoulding after maintenance 12 hours, then through the room temperature maintenance of 4-7 days, cuts into the size of 1200mm*3000mm, stands 28 days, obtain flap type inorganic high-strength Os Draconis sheet material.
4. flap type inorganic high-strength Os Draconis light weight wall according to claim 1, it is characterised in that described inorganic high-strength wainscot, inorganic high-strength outer panels preparation method be:
(1) by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes slurry;
(2) add in the slurry that step (1) is made quality accounts for the silicon dioxide of magnesium oxide quality 40-60%, flyash, sawdust or straw, be sufficiently stirred for obtain secondary slurry;
(3) all laying the glass-fiber-fabric of one layer of 60g-120g at the upper and lower surface of mould, the secondary slurry in step (2) carries out injection molding, the thickness controlling sheet forming is 8-12mm, and the sheet material after injection molding carries out roll-forming, must complete plate;
(4) plate is completed by what step (3) obtained, under 30 degree Celsius of-45 degrees celsius, the demoulding after maintenance 12 hours, then through the room temperature maintenance of 4-7 days, cuts into the size of 1200mm*2400mm, stand 28 days, obtain inorganic high-strength wainscot, inorganic high-strength outer panels sheet material.
5. flap type inorganic high-strength Os Draconis light weight wall according to claim 1, it is characterised in that the preparation method of described inorganic gel agent is: by MgO:MgCl2: H2O three is 6-8:1:12-16 according to mol ratio, and adds different additives according to ambient temperature height, makes inorganic gel agent.
6. flap type inorganic high-strength Os Draconis light weight wall according to claim 1, it is characterised in that described packed layer is tolerant noise-insulating warm-keeping layer.
7. flap type inorganic high-strength Os Draconis light weight wall according to claim 6, it is characterised in that described tolerant noise-insulating warm-keeping layer is rock wool, glass cotton or foamed concrete.
8. flap type inorganic high-strength Os Draconis light weight wall according to claim 1, it is characterized in that, described inorganic high-strength outer panels and flap type inorganic high-strength Os Draconis utilize inorganic gel agent to carry out pasting maintenance to have pasted in factory, described inorganic high-strength wainscot and flap type inorganic high-strength Os Draconis utilize inorganic gel agent to carry out pasting maintenance to have pasted 70% in factory, and remaining 30% carries out on-the-spot maintenance stickup.